Esterilização de limas endodônticas com plasma de oxigênio

No presente trabalho, analisou-se a eficácia de uma nova técnica de esterilização de instrumental odontológico. Limas endodônticas contaminadas com Escherichia coli, Pseudomonas aeruginosa e Staphylococcus aureus foram esterilizadas em plasma de oxigênio formado através de uma descarga elétrica contínua de 75 mA. Os resultados demonstraram efetiva eliminação dos microrganismos testados, utilizando-se um processo a baixas temperaturas e em tempos menores que os preconizados para processos convencionais (forno de Pasteur e autoclave). Microrganismos gram-negativos foram destruídos em 1 minuto de exposição e gram-positivos em 10 minutos.

Plasma immersion ion implantation of nitrogen into H13 steel under moderate temperatures

Ion implantation of nitrogen into samples of tempered and quenched H13 steel was carried out by plasma immersion technique. A glow discharge plasma of nitrogen species was the ion source and the negative high voltage pulser provided 10-12 kV, 60 mu s duration and 1.0-2.0 kHz frequency, flat voltage pulses. The temperatures of the samples remained between 300 and 450 degrees C, sustained solely by the ion bombardment. In some of the discharges, we used a N-2 + H-2 gas mixture with 1:1 ratio. PIII treatments as long as 3, 6, 9 and up to 12 h were carried out to achieve as thickest treated layer as possible, and we were able to reach over 20 mu m treated layers, as a result of ion implantation and thermal (and possibly radiation enhanced) diffusion. The nitrogen depth profiles were obtained by GDOS (Glow Discharge Optical Spectroscopy) and the exact composition profiles by AES (Auger Electron Spectroscopy). The hardness of the treated surface was increased by more than 250%, reaching 18.8 GPa. No white layer was seen in this case. A hardness profile was obtained which corroborated a deep hardened layer, confirming the high efficacy of the moderate temperature PIII treatment of steels. (c) 2005 Elsevier B.V. All rights reserved.

Physiological and genomic variations in rice cells recovered from direct immersion and storage in liquid nitrogen

The use of cryoprotectants and slow cooling rates are routine procedures for the cryopreservation of plant cell lines. However, our results with rice (Oryza sativa L,, ev. Taipei 309) show that calli can be cryopreserved by direct immersion and stored in liquid nitrogen without any cryoprotection, the efficiency of recovery using this method, as well as a conventional method was generally increased with a previous abscisic acid (ABA) treatment. Following cryopreservation, calli demonstrated some differences with respect to unfrozen calli of the same lines, Thus, resistance to freezing stress (- 20 degrees C for 2 h) increased significantly in all lines tested, irrespective of their pre-incubation with ABA, Calli that had been directly stored in liquid nitrogen also demonstrated a higher competence for genetic transformation than their unfrozen counterparts, as indicated by the transient gene expression levels obtained after particle bombardment, These differences might lead to further biotechnological applications, A genetic analysis of amplified DNA polymorphisms was performed with three independent lines that had been subjected to four combinations of ABA treatment and direct immersion in liquid nitrogen, At the loci screened with the randomly amplified polymorphic DNA (RAPD) markers tested, the genetic variations among lines and among calli of the same line appear to bd more related to tissue-culture-induced somaclonal variation than to cryoselection.

Hydrophilization of PVC surfaces by argon plasma immersion ion implantation

Commercial polyvinylchloride (PVC) sheets were treated by plasma immersion ion implantation, PIII. Samples were immersed in argon glow discharges and biased with 25 kV negative pulses. Exposure time to the bombardment plasma changed from 900 to 10,800 s. Through contact angle measurements, the effect of the exposure time on the PVC wettability was investigated. Independent of t, all samples presented contact angles, theta, equal to zero after the treatment. However, in some cases, surface hydrophilization was not stable, as revealed by the temporal evolution of theta. Samples bombarded for shorter periods recovered partially or totally the hydrophobic character while the one exposed for the longest time stayed highly hydrophilic. These modifications are ascribed to the Cl loss and O incorporation as shown by XPS measurements. Furthermore, the mobility of surface polar groups and the variation in the cross-linking degree can also affect the PVC wettability.

Helium ion irradiation of polymer films deposited from TMS-Ar plasmas

Polymer films synthesized from plasmas of a tetramethylsilane - Ar mixture were modified by irradiation with 170 keV He ions at fluences ranging from 1 x 10(14) to 1 x 10(16) cm(-2). As revealed by infrared spectroscopy, the ion beam produced intense bond rearrangements, such as the depletion of bonding groups (C-H and Si-H), and induced the formation of new ones, such as O-H and Si-O. From the nanoindentation measurements, a remarkable increase in the surface hardness of the films was observed as the ion fluence was increased. The increases in hardness were accompanied by an increase in the film compaction as shown by using a combination of RBS and film thickness measurements. From both hardness and infrared measurements A was concluded that, under the He ion bombardment, the polymer structure is transformed into a silicon oxycarbide network.

Effects of ion beam on nanoindentation characteristics of glassy polymeric carbon surface

Glassy polymeric carbon (GPC) is a useful material for medical applications due to its chemical inertness and biocompatible characteristics. Mitral and aortic and hydrocephalic valves are examples of GPC prosthetic devices that have been fabricated and commercialized in Brazil. In this work, ion beam was used to improve the mechanical characteristics of GPC surface and therefore to avoid the propagation of microcracks where the cardiac valves are more fragile. A control group of phenolic resin samples heat-treated at 300, 400, 700, 1000, 1500, and 2500 degrees C was characterized by measuring their hardness and Young's reduced elastic modulus with the depth of indentation. The control group was compared to results obtained with samples heat-treated at 700, 1000, and 1500 degrees C and bombarded with energetic ions of silicon, carbon, oxygen, and gold at energies of 5, 6, 8, and 10 MeV, respectively, with fluences between 10x10(13) and 10x10(16) ions/cm(2). GPC nonbombarded samples showed that hardness depends on the heat treatment temperature (HTT), with a maximum hardness for heat treatment at 1000 degrees C. The comparison between the control group and bombarded group also showed that hardness, after bombardment, had a greater increase for samples prepared at 700 degrees C than for samples prepared at higher temperatures. The Young's elastic modulus presents an exponential relationship with depth. The parameters obtained by fitting depend on the HTT and on the ion used in the bombardment more than on energy and fluence. The hardness results show clearly that bombardment can promote carbonization, increase the linkage between the chains of the polymeric material, and promote recombination of broken bonds in lateral groups that are more numerous for samples heat-treated at 700 degrees C. (c) 2004 Elsevier B.V. All rights reserved.

The effect of N+ ion energy on the properties of ion bombarded plasma polymer films

This work describes the influence of the ion bombardment on the electrical, optical and mechanical properties of polymer films deposited from radio-frequency plasmas of benzene. Irradiations were conducted using N+ at 5 x 10(19) ions/m(2), varying the ion energy, E-0, from 0 to 150 keV. Film elemental composition was determined by Rutherford backscattering spectroscopy. Electrical resistivity and hardness were obtained by the two-point probe and nanoindentation technique, respectively. Ultraviolet-visible spectroscopy was employed to investigate the optical constants of the samples. Etching rate was determined by exposure of the films to reactive oxygen plasmas. Ion bombardment induced gradual loss of H and increase in C and O concentrations with Eo. As a consequence the electrical, optical and mechanical properties were drastically affected. Interpretation of these results is proposed in terms of chain cross-linking and unsaturation. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Effect of the fluorination of DLC film on the corrosion protection of aluminum alloy (AA 5052)

It is presented a study conducted on the physical and electrochemical properties of fluorinated a-C:H films deposited onto a commercial aluminum alloy (AA 5052). The coatings were deposited from mixtures of 91% of acetylene and 9% of argon by plasma immersion ion implantation and deposition technique, PIIID. Total gas pressure was 44 Pa and deposition time (t(dep)) was varied from 300 to 1200 s. The depositing plasmas were generated by the application of radiofrequency power (13.56 MHz, 100W) to the upper electrode and high voltage negative pulses (2400 V. 300 Hz) to the sample holder. Fluorine was incorporated in a post-deposition plasma treatment (13.56 MHz, 70W, 13 Pa) generated from sulfur hexafluoride atmosphere. Chemical structure and composition of the films were investigated using infrared reflectance/absorbance spectroscopy and X-ray photoelectron spectroscopy. The corrosion resistance of the layers was determined by electrochemical impedance spectroscopy (EIS) in a 3.5% NaCl solution, at room temperature. Films presented good adhesion to the substrates and are classified as hydrogenated amorphous carbon (a-C:H) with oxygen traces. Fluorine was detected in all the samples after the post-deposition treatment being its proportion independent on the deposition time. Film thickness presented different tendencies with t(dep), revealing the variation of the deposition rate as a function of the deposition time. Such fluorinated a-C:H films improved the corrosion resistance of the aluminum surface. In a general way the corrosion resistance was higher for films prepared with lower deposition times. The variation of sample temperature with t(dep) was found to be decisive for the concentration of defects in the films and, consequently, for the performance of the samples in electrochemical tests. Results are interpreted in terms of the energy delivered to the growing layer by ionic bombardment. (C) 2010 Elsevier B.V. All rights reserved.

Plasma-polymerized acetylene nanofilms modified by nitrogen ion implantation

Thin films were prepared by plasma enhanced chemical vapour deposition (PECVD) from a mixture of acetylene and argon, and post deposition-treated by plasma immersion ion implantation (PIII). The effect of PIII on the nanofilms properties was evaluated as a function of treatment time. The average thickness and roughness were diminished upon PIII. On the other hand, hardness (0.7-3.9 GPa) and elastic modulus (29-54 GPa) increased upon 60 min of ion bombardment. Such results are ascribed mainly to the densification of the film structure caused by the increment in the crosslinking degree with increasing the energy deposited in the films. Wettability of the samples, investigated by contact angle measurements, was reduced (from 64 to 21°) right after PIII. This result, attributed to the introduction of polar groups in the film structure, was not preserved as the sample was aged in atmosphere. After aging, contact angles were larger than 70° but still smaller than 90°. Although the wettability has decreased with aging, the hydrophilic character of the samples was preserved. For certain treatment times, nitrogen PIII turned the plasma-polymerized acetylene films smoother, denser, mechanically and tribologicaly more resistant than the as-deposited material. © 2013 Elsevier B.V.

Embriogênese somática e transformação genética de soja via biobalística

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Propriedades mecânicas e tribológicas de filmes sintetizados mediante técnica de deposição e implantação iônica por imersão em plasma

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito protetivo produzido pela aplicação de um filme de carbono amorfo na superfície de um ferramental para conformação

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Síntese de filmes finos a-C:H pela técnica de implantação e deposição por imersão em plasma

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Revisão dos principais radiofármacos utilizados no Brasil e suas aplicações na detecção e terapia de patologias

Radiopharmaceuticals are substances marked with radionuclides that can be used for detection and treatment of cancer, infections and inflammatory diseases. They emit several types of radiation through different decay routes, each radioisotope with its specific properties and uses. They can usually be produced from several different materials, by bombardment with particle beams in a nuclear research reactor or cyclotron, depending on their characteristics. Brazil has four public institutions which produce - or import - and distribute radiopharmaceuticals to hospitals and clinics throughout its territory. The largest such institution, Ipen, distributes 97% of radiopharmaceuticals used in the country. Some radiopharmaceuticals decay very quickly, meaning they must be produced and quickly administered to the patient in the same location, presenting a logistical challenge. Nuclear medicine in Brazil is a promising field and has been steadily growing, although rigid laws and a lack of qualified work force hinder Research and Development efforts for new radiopharmaceuticals. The construction of a new nuclear research reactor, in 2016, should generate self-sufficiency and economy in radiopharmaceutical production and avoid a future crisis in the supply of technetium-99m, the most important radioisotope, used in over 80% of procedures with radiopharmaceuticals.

Técnica híbrida de plasma para a deposição de filmes de alumina

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)