Free energy of mixing of divalent basic oxides with silica

An expression derived for the free energy of mixing of a divalent basic oxide (MO) with SiO2 based on a model of silicate structure, takes into account the distribution of O2- (from MO) into the silica network, the mixing of silicate ions with O2- and the enthalpy of mixing. The resulting expression is ΔGmix=RT{N11n (2N1-N)2/4N1(1-N)+N21n N 2-N/1-N}, where N={(β+N1)-√(β+N 1)2-8βN1N2}/2β β=characteristic constant for the system N1=mol fraction of silica N2=mol fraction of MO. For the proper choice of β, calculated values of the activity of MO for the system PbO-SiO2, MnO-SiO2, FeO-SiO2 and CaO-SiO2 are in good agreement with experiment. The model predicts that the activity of the basic oxide decreases with increase in temperature.

Dielectric properties of some MM′O4 and MTiM′O6 (M=Cr, Fe, Ga; M′=Nb, Ta, Sb) rutile-type oxides

We describe an investigation of the structure and dielectric properties of MM'O-4 and MTiM'O-6 rutile-type oxides for M = Cr, Fe, Ga and M' = Nb. Ta and Sb. All the oxides adopt a disordered rutile structure (P4(2)/mnm) at ambient temperature. A partial ordered trirutile-type structure is confirmed for FeTaO4 from the low temperature (17 K) neutron diffraction studies While both the MM'O-4 oxides (CrTaO4 and FeTaO4) investigated show a normal dielectric property MTiM'O-6 oxides for M = Fe, Cr and M' = Nb/Ta/Sb display a distinct relaxor/relaxor-like response. Significantly the corresponding gallium analogs, GaTiNbO6 and GaTiTaO6, do not show a relaxor response at T<500K (C) 2010 Elsevier Inc All rights reserved

Oxygen chemistry in copper oxides: evidence for O− species

Core-level spectroscopic studies suggest that cuprates nominally supposed to contain Cu3+ions are likely to have the excess positive charge on oxygen instead, giving rise to O-type species (oxygen holes)

Electronic phase separation in correlated oxides: The phenomenon, its present status and future prospects

Many transition metal oxide materials of high chemical purity are not necessarily monophasic. Thus, single crystals of chemically pure rare earth manganites and cobaltates of the general formula Ln1-xAxMO3 (Ln=rare earth metal, A=alkaline earth metal, M=Mn, Co) exhibit the phenomenon of electronic phase separation wherein phases of different electronic and magnetic properties coexist. Such phase separation, the length scale of which can vary anywhere between a few nanometers to microns, gives distinct signatures in X-ray and neutron diffraction patterns, electrical and magnetic properties, as well as in NMR and other spectroscopies. While the probe one employs to investigate electronic phase separation depends on the length scale, it is noteworthy that direct imaging of the inhomogeneities has been accomplished. Some understanding of this phenomenon has been possible on the basis of some of the theoretical models, but we are far from unraveling the varied aspects of this new phenomenon. Herein, we present the highlights of experimental techniques and theoretical approaches, and comment on the future outlook for this fascinating phenomenon

Growth and characterization of germanium nanowires by electron beam evaporation

Germanium nanowires were grown on Au coated Si substrates at 380 degrees C in a high vacuum (5 x 10(-5) Torr) by e-beam evaporation of Germanium (Ge). The morphology observation by a field emission scanning electron microscope (FESEM) shows that the grown nanowires are randomly oriented with an average length and diameter of 600 nm and 120 nm respectively for a deposition time of 60 min. The nanowire growth ratewas measured to be similar to 10 nm/min. Transmission electron microscope (TEM) studies revealed that the Ge nanowires were single crystalline in nature and further energy dispersive X-ray analysis(EDAX) has shown that the tip of the grown nanowires was capped with Au nanoparticles, this shows that the growth of the Ge nanowires occurs by the vapour liquid solid (VLS) mechanism. HRTEM studies on the grown Ge nanowire show that they are single crystalline in nature and the growth direction was identified to be along [110]. (C) 2010 Elsevier B.V. All rights reserved.

Surface Structures of Silicon and Germanium

Si and Ge were cleaved on the (111) plane under ultra high vacuum and exposed to O and subsequent heat treatment. LEED and spot photometric measurements were taken. Cleaved surfaces for both Si and Ge gave the expected (2 x 1) structure. Results for O exposure were qualitatively for Si and Ge. The 1/2 orders disappeared after exposure to approx = 10 exp - exp 7. Integral orders started to weaken at 10 exp -6 to 10 exp - exp 2 torr min., disappearing at 10 exp -1 torr min. Heat treatment of Si at 900 deg C for several seconds restored the integral orders and further heating gave a new pattern with 1/3 orders. Exposure to 2 x 10 exp -6 torr min O without further heating weakened the fractional orders and at 10 exp -5 torr min they disappeared. Integral orders remained after further heating in O. For Ge integral orders were not restored after 0 exposure until heat treatment had continued at 550 deg C for several min. The (1 x 1) structure disappeared after heating at 590 deg C in 7 x 10 exp -1 torr O and further heating at 590 deg C without O restored the integral order Variations of intensity with voltage were measured for the (00) and (20) spots. The results supported a model proposed by Haneman (Phys. Rev., 1968, 170, 705) involving two kinds of atom sites on the cleaved surface. 20 ref.--E.J.S.

Evidence for holes on oxygen in some nickel oxides

Core-level spectroscopic studies show the presence of holes on oxygen in LaNiO3 and LiNiO2 Nickel in these oxides seems to be essentially in the 2+ state instead of the 3+ state-where it would formally be expected to be on the basis of the stoichiometry.

Chlorine-35 nuclear quadrupole resonance study of molecular torsional motion in some chloropyridine-N-oxides and chloroquinoline-N-oxides

Chlorine has been substituted at the 2- and 4-positions in the pyridine and quinoline rings of the corresponding N-oxides and 35Cl n.q.r. spectra have been studied in the temperature range 77–300 K. The change in the n.q.r. frequencies in N-oxides as compared to their parent compounds are interpreted in terms of the conjugative effect and the inductive effect of the N+—O– group. The negative temperature coefficients of the resonance frequencies in chloropyridine-N-oxides have been analysed using the Bayer, Kushida and Brown equations. The calculated torsional frequencies, which are in the range 52–78 cm–1, are found to be only slightly temperature dependent.

Superconductivity in layered nickel oxides

Likely presence of superconductivity in layered nickelates of K2NiF4 structure is pointed out.

A series of metallic oxides of the formula La3LnBaCu5O13+δ (Ln = rare earth or Y)

Oxides of the formula La3LnBaCu5O13+δ (Ln = Nd, Sm, Gd, Dy, or Y) exhibiting metallic resistivity have been prepared and characterized. In the case of yttrium, a composition close to La2Y2BaCu5O13+δ, which is also metallic, could be prepared.

A comparative study of the magnetic and electrical properties of perovskite oxides and the corresponding two-dimensional oxides of K2NiF4

Electrical and magnetic properties of several oxide systems of K2NiF4 structure have been compared to those of the corresponding perovskites. Members of the La1−xSr1+xCoO4 system are all semiconductors with a high activation energy for conduction unlike La1−xSrxCoO3 (x ≥ 0.3) which is metallic; the latter oxides are ferromagnetic. La0.5Sr1.5CoO4 shows a magnetization of 0.5 μB at 0 K (compared to 1.5 μB of La0.5Sr0.5CoO3), but the high-temperature susceptibilities of the two systems are comparable. In SrO · (La0.5Sr0.5MnO3)n, both magnetization and electrical conductivity increase with the increase in n approaching the value of the perovskite La0.5Sr0.5MnO3. LaSrMn0.5Ni0.5(Co0.5)O4 shows no evidence of long-range ferromagnetic ordering unlike the perovskite LaMn0.5Ni0.5(Co0.5)O3; high-temperature susceptibility behavior of these two insulating systems is, however, similar. LaSr1−xBaxNiO4 exhibits high electrical resistivity with the resistivity increasing proportionately with the magnetic susceptibility (note that LaNiO3 is a Pauli-paramagnetic metal). High-temperature susceptibility of LaSrNiO4 and LaNiO3 are comparable. Susceptibility measurements show no evidence for long-range ordering in LaSrFe1−xNixO4 unlike in LaFe1−xNixO3 (x ≤ 0.35) and the electrical resistivity of the former is considerably higher. Electrical resistivity of Sr2RuO4 is more than an order of magnitude higher than that of SrRuO3. Some generalizations of the properties of two- and three-dimensional oxide systems have emerged from these experimental observations.

Local structure and magneto-transport in Sr2FeMoO6 oxides

Double perovskite oxides Sr2FeMoO6 have attracted a great interest for their peculiar magneto-transport properties, and, ill particular, for the large values of low-field magneto-resistance (MR) which remains elevated even at room temperature, thanks to their high Curie temperature (T-c > 400 K). These properties are strongly influenced by chemical cation disorder, that is by the relative arrangement of Fe and Mo on their sublattices: the regular alternation of Fe and Mo enhances the M R and saturation magnetization. On the contrary the disorder generally depresses the magnetization and worsen the MR response. In this work the X-ray absorption fine structure (XAFS) technique has been employed in order to probe the cation order from a local point of view. XAFS spectra were collected at the Fe and Mo K edges on Sr2FeMoO6 samples with different degree of long-range chemical order. The XAFS results prove that a high degree of short-range cation order is preserved, despite the different long-range order: the Fe-Mo correlations are always preferred over the Fe-Fe and Mo-Mo ones in the perfectly ordered as well as in highly disordered samples.