Ta2O5／SiO2硬膜双腔滤光片激光损伤特性研究

研究了Ta2O5／SiO2硬膜双腔干涉滤光片带内、带边及带外的吸收和激光损伤特性。实验发现，对于作用激光，带通滤光片的驻波场分布、吸收率和损伤阈值在带内、带边和带外的响应特性对作用激光波长均呈现出明显的选择性。根据实验结果，结合滤光片的驻波场分析，给出了带通滤光片的损伤机理。

1064nm倍频波长分离膜的制备与性能研究

通过对主膜系添加匹配层并借助计算机对膜系进行优化，设计出结构规整、性能优良的1064ilm倍频波长分离膜。用电子束蒸发及光电极值监控技术在K9玻璃基底上沉积薄膜，将样品置于空气中在260℃温度下进行3h热退火处理。然后用Lambda 900分光光度计测量了样品的光谱性能；用表面热透镜(STL)技术测量了样品的弱吸收值；用调Q脉冲激光装置测试了样品的抗激光损伤阈值(LIDT)。实验结果发现，样品的实验光谱性能与理论光谱性能有很好的一致性。退火前后其光谱性能几乎没有发生温漂，说明薄膜的温度稳定性好；同时退火使

窄带干涉滤光片抗击不同输出方式激光的损伤特性研究

利用Nd：YAG调Q单脉冲激光和自由脉冲激光对硬膜窄带干涉滤光片进行激光损伤阈值的测试，并且采用表面热透镜技术测量了滤光片的吸收率。实验发现：窄带干涉滤光片的吸收率和激光损伤阈值强烈依赖于辐照激光波长与窄带干涉滤光片通带的相对位置；在调Q单脉冲激光作用下，不同中心波长的滤光片损伤形貌存在明显的差别，而在自由脉冲激光作用下，各滤光片的损伤形貌则趋于相同．均表现为典型的热熔烧蚀破坏。根据实验结果，结合损伤形貌，通过驻波场理论对激光作用下滤光片内电场分布的分析与模拟．探讨了两种激光模式作用下滤光片的损伤特征和损

退火对ZrO2薄膜微结构及激光损伤阈值的影响

利用电子束蒸发方法在Yb:YAG晶体和熔融石英衬底上沉积单层ZrO2薄膜,分别在673 K和1 073 K的温度下经过12 h退火以后,通过X射线衍射(XRD)分析了薄膜晶相,计算了薄膜的晶粒尺寸;利用表面热透镜技术获得了薄膜的吸收;测量了退火后薄膜的激光损伤阈值.实验结果表明:两种衬底上的薄膜结构受到退火温度和衬底表面结构的影响,高温退火有利于单斜相的形成,含单斜相的ZrO2薄膜具有较高的激光损伤阈值,而由于衬底的吸收,Yb:YAG晶体上薄膜的损伤阈值远小于石英衬底上薄膜的损伤阈值.

高真空室中的水蒸气对HfO2薄膜性能的影响

本文研究了在镀膜过程中真空室内水蒸气的含量对HfO2薄膜物理性能的影响。用电子束蒸发和光电极值监控的方法在BK7基底上制备HfO2薄膜。利用残余气体分析仪在线监测了真空室内的残余气氛组成。分别用Lambda 900光谱仪、X射线衍射方法、表面热透镜技术和1064nm的激光器测试了薄膜的光学性能、微结构、吸收和激光损伤阈值。实验发现，附加冷阱装置有助于我们有效控制镀膜过程中的水汽含量，且在水蒸气含量较少的真空室内镀制的薄膜具有较高的折射率，较小的晶粒尺寸，较低的弱吸收值和较高的损伤阈值。

薄膜材料对TiO2基薄膜激光损伤阈值的影响

abstract {The optical property, structure, surface properties (roughness and defect density) and laser-induced damage threshold (LIDT) of TiO₂ films deposited by electronic beam (EB) evaporation of TiO₂ (rutile), TiO₂ (anatase) and TiO₂ + Ta₂O₅ composite materials are comparatively studied. All films show the polycrystalline anatase TiO₂ structure. The loose sintering state and phase transformation during evaporating TiO₂ anatase slice lead to the high surface defect density, roughness and extinction coefficient, and low LIDT of films. The TiO₂ + Ta₂O₅ composite films have the lowest extinction coefficient and the highest LIDT among all samples investigated. Guidance of selecting materials for high LIDT laser mirrors is given.}

真空中有机污染物对TiO2/SiO2介质膜损伤阈值的影响

本文主要研究了真空中有机污染物对薄膜阈值的影响。采用电子枪蒸镀的方式制备了由TiO2/SiO2两种材料组合而成的1064nm高反膜，分别在大气和真空中对其损伤阈值进行了测量。发现在真空中污染物易黏附于光学元件表面，导致损伤；真空中的氧分子会加速损伤过程，根据破斑形貌的分析认为是由于在激光作用下氧分子与有机污染物发生反应造成的；真空中的有机污染物被去除后，真空和大气中的损伤阈值差别不大，破斑形貌相似。结果表明有机污染物是真空中损伤阈值降低的主要原因。

用于掺钛蓝宝石激光系统的高反膜的激光损伤

用电子束蒸发制备了用于掺钛蓝宝石啁啾脉冲放大激光系统的TiO2/HfO2/SiO2高反膜，其带宽约为176nm（R>98%, λ0=800nm），激光损伤阈值（LIDT）为2.4 J/cm2。通过TiO2和HfO2单层膜的透过光谱计算了这两种材料的折射率和消光系数。高反膜的性能主要由高折射率材料决定：折射率越高，反射带越宽；消光系数越小，薄膜吸收越小，LIDT越高。最后，讨论了高反膜的激光损伤机制。

Ta2O5膜在532, 800 和 1064 nm波长的n-on-1体系下的激光损伤阈值研究

Ta2O5膜采用传统的电子束蒸发方法制备，并在氧气中673 K的条件下进行了退火12 h处理。首先在1-on-1体系下对Ta2O5膜进行了532和1064 nm波长下的激光损伤阈值（LIDT） 研究，然后在n-on-1体系下分别对532，800和1064 nm三种波长下的激光损伤阈值进行了研究。结果表明在n-on-1体系下Ta2O5膜在532和1064 nm波长下的阈值均高于1-on-1体系下的阈值。此外，在n-on-1体系下，薄膜的阈值随波长增加而增大。同时发现，在氧气中进行退火对Ta2O5膜的光学性能

Comparison of TiO2 and ZrO2 films deposited by electron-beam evaporation and by sol-gel process

TiO2 and ZrO2 films are deposited by electron-beam (EB) evaporation and by sol-gel process. The film properties are characterized by visible and Fourier-transform infrared spectrometry, x-ray diffraction analysis, surface roughness measure, absorption and laser-induced damage threshold (LIDT) test. It is found that the sol-gel Elms have lower refractive index, packing density and roughness than EB deposited films due to their amorphous structure and high OH group concentration in the film. The high LIDT of sol-gel films is mainly due to their amorphous and porous structure, and low absorption. LIDT of EB deposited film is considerably affected by defects in the Elm, and LIDT of sol-gel deposited film is mainly effected by residual organic impurities and solvent trapped in the film.

Characteristics of high reflection mirror with an SiO2 top layer for multilayer dielectric grating

The high reflection (HR) mirror composed of dielectric stacks with excellent spectrum characteristics and high damage resistant ability is critical for fabricating multilayer dielectric (MLD) grating for pulse compressor. The selection of the SiO2 material as the top layer of the HR mirror for grating fabrication is beneficial for improving the laser-induced damage threshold of MLD grating as well as minimizing the standing-wave effect in the photoresist during the exposure process. Based on an (HLL) H-9 design comprising quarter-waves of HfO2 ( H) and half-waves of SiO2 ( L), we obtain an optimal design of the HR mirror for MLD grating, the SiO2 top layer of which is optimized with a merit function including both the diffraction efficiency of the MLD grating and the electric field enhancement in the grating. Dependence of the performance of the MLD grating on the fabrication error of the dielectric mirror is analysed in detail. The HR mirror is also fabricated by E-beam evaporation, which shows good spectral characteristics at the exposure wavelength of 413 nm and at the operation wavelength of 1053 nm and an average damage threshold of 10 J cm(-2) for a 12 ns pulse.

Influence of substrate temperature on properties of MgF2 coatings

Thermal boat evaporation was employed to prepare MgF2 single-layer coatings upon both JGS1 and UBK7 substrates at different substrate temperatures. Microstructure, transmittance and residual stress of these coatings were measured by X-ray diffraction, spectrophotometer, and optical interferometer, respectively. Measurement of laser induced damage threshold (LIDT) of the samples was performed at 355 nm, 8 ns pulses. The results showed that high substrate temperature was beneficial to crystallization of the film. Above 244 degrees C, the refractive index increased gradually with the substrate temperature rising. Whereas, it was exceptional at 210 degrees C that the refractive index was higher than those deposited at 244 and 277 degrees C. The tensile residual stresses were exhibited in all MgF2 films, but not well correlated with the substrate temperature. In addition, the stresses were comparatively smaller upon JGS1 substrates. A tendency could be seen that the LIDTs reached the highest values at about 244 degrees C, and the films upon JGS1 had higher LIDTs than those upon UBK7 substrates at the same temperature. Meanwhile, the damage morphologies showed that the laser damage of the coating resulted from an absorbing center at the film-substrate interface. The features of the damages were displayed by an absorbing center dominated model. Furthermore, the reason of the difference in LIDT values was discussed in detail. (C) 2007 Elsevier B.V. All rights reserved.

三倍频分光膜在1064 nm的破斑特性研究

采用电子束蒸发方式制备了两种不同材料组合的分光膜,分别对其在波长1064 nm激光辐照下的损伤阈值进行了测试,用Alpha-Step 500台阶仪对破斑进行了深度测量。实验结果表明,破斑呈现出表面层的剥落和深坑破坏两种形态。表面层的剥落深度在一定范围内不随能量密度的变化而变化；深坑破坏深浅不一,是膜内缺陷融化、汽化及喷发的综合作用的结果,是损伤阈值降低的主要原因。

两种后处理方法对HfO2薄膜性能的影响

利用电子束蒸发和光电极值监控技术制备了氧化铪薄膜，并分别用两种后处理方法（空气中退火和氧等离子体轰击）对样品进行了处理．然后，对样品的透过率、吸收和抗激光损伤阈值进行了测试分析．实验结果表明，两种后处理方法都能不同程度地降低了氧化铪薄膜的吸收损耗、提高了抗激光损伤阈值．实验结果还表明，氧等离子体轰击的后处理效果明显优于热退火，样品的吸收平均值在氧等离子体后处理前后分别为34．8ppm和9．0ppm，而基频（1 064nm）激光损伤阈值分别为10．0J／cm^2和21．4J／cm^2．