Chemical and morphological features of dental composite resin: influence of light curing units and immersion media

Aims: The study evaluated the influence of light curing units and immersionmedia on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M)through the EDX analysis and SEM evaluation. Light curing units with different power densitiesand mode of application used were XL 3000 (480 mW/cm2), Jet Lite 4000 Plus (1230mW/cm2), andUltralume Led 5 (790 mW/cm2) and immersion media were artificial saliva, Coke1, tea and coffee,totaling 12 experimental groups. Specimens (10 mm 3 2 mm) were immersed in each respectivesolution for 5 min, three times a day, during 60 days and stored in artificial saliva at 378C 6 18Cbetween immersion periods. Topography and chemical analysis was qualitative. Findings: Groupsimmersed in artificial saliva, showed homogeneous degradation of matrix and deposition of calciumat the material surface. Regarding coffee, there was a reasonable chemical degradation with loss ofload particles and deposition of ions. For tea, superficial degradation occurred in specific areaswith deposition of calcium, carbon, potassium and phosphorus. For Coke1, excessive matrix degra-dation and loss of load particles with deposition of calcium, sodium, and potassium. Conclusion:Light curing units did not influence the superficial morphology of composite resin tested, but theimmersion beverages did. Coke1affected material’s surface more than did the other tested drinks.Microsc. Res. Tech. 73:176–181, 2010.

Effects of immersion media and repolishing on color stability and superficial morphology of nanofilled composite resin

This study evaluated the influence of fluoride mouth rinses and repolishing on the superficial morphology and color stability of nanofilled resin. About 150 specimens were prepared and polished using aluminum oxide discs for 15 s with a pressure of 2 kg. The experimental groups were divided according to the immersion medium (artificial saliva, 0.5% sodium fluoride, Fluordent Reach, Oral B, Fluorgard) and repolishing procedure (without and with). The specimens were continuously immersed for 1 week. Thereafter, half of each sample was repolished. A color reading was performed after 24 h of immersion in the artificial saliva baseline, after continuous immersion, and after repolishing. The superficial morphology was examined using scanning electron microscopy (SEM) in a qualitative way. Color change (∆E) data were submitted to a mixed analysis of variance using a Shapiro-Wilk test (p>0.05 for the different immersion media) and Sidak's test (p<0.05 for the differences between groups). In the interaction between the repolishing and the immersion media, Fluorgard showed a statistical difference between the ∆E values with and without repolishing (p<0.0001). On the SEM observations, both Fluordent Reach and Fluorgard caused degradation of the superficial resinous matrix of the composite after continuous immersion. This matrix was removed after repolishing.

Repair of composites: Effect of laser and different surface treatments

Objectives: This study investigated the repairs of resin composite restorations after using different surface treatments.Design: Eighty four truncated cones of Filtek Z350 were prepared and thermo-cycled (20,000 cycles). Surfaces were roughened with diamond bur and etched with 37% phosphoric acid. Those cones were divided into 7 groups (N=12): 1) Prime&Bond 2.1; 2) aluminum oxide sandblasting+Prime&Bond 2.1; 3) Er:YAG laser treatment+Prime&Bond 2.1; 4) 9.6% hydrofluoric acid for 2 min-Fsilane coupling agent.; 5) silane coupling agent; 6) auto-polymerized acrylic monomer+Prime&Bond 2.1; 7) Adper Scothbond SE. Teflon device was used to fabricate inverted truncated cones of repair composite over the surface-treated. The bonded specimens were stressed to failure under tension. The data were analyzed with oneway ANOVA and Tukey tests.Results: Mean repair strengths (SD, in MPa) were, Group-2: 18.8a; Group-1: 18.7a; Group-6: 13.4ab; Group-7: 9.5bc; Group-3: 7.5bcd; Group-4: 5.2cd; Group-5: 2.6d.Conclusions: The use of diamond bur and a conventional adhesive and the use of aluminum oxide sandblasting prior to adhesive provided a simple and cost-effective solutions to composite repair. Er:YAG laser, silane alone, 9.6% hydrofluoric acid plus silane or a self-etching adhesive results in inferior composite repair strengths. (C) 2015 Elsevier Ltd. All rights reserved.

Reestablishment of occlusion with prosthesis and composite resin restorations

Here, we present a case report on prosthetic reconstruction of posterior teeth and composite resin restoration of anterior teeth yielding considerable esthetic improvement, reestablishment of disocclusion guides and function.

Composite resin color stability: influence of light sources and immersion media

This study evaluated the influence of light sources and immersion media on the color stability of a nanofilled composite resin. Conventional halogen, high-power-density halogen and high-power-density light-emitting diode (LED) units were used. There were 4 immersion media: coffee, tea, Coke® and artificial saliva. A total of 180 specimens (10 mm x 2 mm) were prepared, immersed in artificial saliva for 24 h at 37±1ºC, and had their initial color measured with a spectrophotometer according to the CIELab system. Then, the specimens were immersed in the 4 media during 60 days. Data from the color change and luminosity were collected and subjected to statistical analysis by the Kruskall-Wallis test (p<0.05). For immersion time, the data were subjected to two-way ANOVA test and Fisher's test (p<0.05). High-power-density LED (ΔE=1.91) promoted similar color stability of the composite resin to that of the tested halogen curing units (Jet Lite 4000 plus--ΔE=2.05; XL 3000--ΔE=2.28). Coffee (ΔE=8.40; ΔL=-5.21) showed the highest influence on color stability of the studied composite resin. There was no significant difference in color stability regardless of the light sources, and coffee was the immersion medium that promoted the highest color changes on the tested composite resin.

Composite resin color stability: influence of light sources and immersion media

This study evaluated the influence of light sources and immersion media on the color stability of a nanofilled composite resin. Conventional halogen, high-power-density halogen and high-power-density light-emitting diode (LED) units were used. There were 4 immersion media: coffee, tea, Coke® and artificial saliva. A total of 180 specimens (10 mm x 2 mm) were prepared, immersed in artificial saliva for 24 h at 37±1ºC, and had their initial color measured with a spectrophotometer according to the CIELab system. Then, the specimens were immersed in the 4 media during 60 days. Data from the color change and luminosity were collected and subjected to statistical analysis by the Kruskall-Wallis test (p<0.05). For immersion time, the data were subjected to two-way ANOVA test and Fisher's test (p<0.05). High-power-density LED (ΔE=1.91) promoted similar color stability of the composite resin to that of the tested halogen curing units (Jet Lite 4000 plus--ΔE=2.05; XL 3000--ΔE=2.28). Coffee (ΔE=8.40; ΔL=-5.21) showed the highest influence on color stability of the studied composite resin. There was no significant difference in color stability regardless of the light sources, and coffee was the immersion medium that promoted the highest color changes on the tested composite resin.

Composite resin susceptibility to red wine staining after water sorption

Color stability of restorative materials is essential for longevity of esthetic composite restoration over time. The aim of this investigation was assess the effect of prior water immersion on the color stability of a composite resin to red wine staining. Seventy disccshaped specimens (6mm x 1.5mm) were carried out and randomized in 7 groups (n = 10), according to distilled water immersion time at 0 (control), 24, 48, 72,120,192, and 240 h. Baseline color was measured according to the ciel*a*b* system using a reflection spectrophotometer(uvc2450, shimadzu).After that, the specimens were storage in red wine for 7 days. Color difference (∆e) after aging was calculated based on the color coordinates before(baseline) and after storage period.Data were subjected to onecway anova(alpha=0.05).The different times of immersion in.Water before to the red wine storage showed similar behavior on the color stability, without statistical difference compared to control group, immersed directly in the wine(p=0.7057).The previous water uptake of composite resin evaluated did not decrease the susceptibility to red wine staining.

Clinical evaluation of a composite resin and a resin-modified glass-ionomer cement in non -carious cervical lesions: one year result

Objectives: The objective of this study was to evaluate the clinical performance of 124 non-carious cervical lesion restorations at 12 months. Materials And Methods: Three study groups were formed according to the material and technique used. All teeth received 37% phosphoric acid etching in enamel and dentin. The teeth of Group I received the conventional adhesive system Scotch Bond Multi Purpose, followed by resin composite Filtek Z350; teeth of Group II were restored with resin-modified glass-ionomer cement Fuji II LC; teeth of Group III were restored with the same resin-modified glass-ionomer cement however, before it was inserted, 2 coats of primer of the Scotch Bond Multi Purpose adhesive system were applied to dentinal tissue. The teeth were evaluated by 2 examiners with regard to the factors of retention, marginal adaptation, marginal discoloration, color alteration, presence of marginal caries lesion, anatomic shape, and sensitivity. Results: Application of the Kruskal-Wallis test showed no statistically significant difference for anatomic shape, marginal discoloration, color alteration, caries lesion, marginal adaptation, and sensitivity among the three study groups, but the variable retention presented statistically significant difference at 12 months, with Group III presenting a behavior superior to that of Group II but similar to that of Group I. Conclusion: The analyzed restorations of non-carious cervical lesions presented a good clinical performance at 12 months.

Chemical and morphological features of nanofilled composite resin: Influence of finishing and polishing procedures and fluoride solutions

This study evaluated the influence of finishing and polishing procedures and different fluoride solutions on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M) through the EDX analysis and SEM evaluation. Circular specimens (n = 30) of 10 mm diameter and 2 mm thickness were prepared, with half of the sample assays finished and polished with Super-Snap (R) sandpaper. The experimental groups were divided according to the presence or absence of finishing and polishing and solutions (artificial saliva, 0.05% of manipulated sodium fluoride solution, Fluordent Reach, Oral B, Fluorgard). Specimens were immersed in each respective solution for 1 min per day, during 60 days and stored in artificial saliva at 37 +/- 1 degrees C between immersion periods. Topography and chemical analysis was qualitative. It was observed that specimens submitted to finishing and polishing procedures had lower superficial degradation. Fluoride solutions promoted superficial alterations on specimens, being the highest degradation obtained with Fluordent Reach. It can be concluded that finishing and polishing procedures and the immersion media influence the superficial morphology of composite resin tested; the Fluordent Reach was the fluoride solution that most affected the material's surface. Microsc. Res. Tech. 2011., (c) 2011 Wiley Periodicals, Inc.

The influence of mouthrinses and simulated toothbrushing on the surface roughness of a nanofilled composite resin

The aim of this study was to determine the influence of mouthrinses on the surface roughness of a nanofilled composite resin after toothbrushing. One hundred nanofilled composite resin specimens were prepared and randomly distributed into two groups-brushed and non-brushed-and then assigned to five subgroups, according to the mouthrinse solutions (n = 10): Colgate Plax Fresh Mint, Oral B, Cepacol, Colgate Plax, and artificial saliva. Each sample was immersed in 20 mL of the mouthrinses for 1 minute, 5 days per week, twice a day, for a 3-week period. The control group used in the study was one in which the specimens were not subjected to brushing and remained only in artificial saliva. Toothbrushing was performed once a week for 1 minute, for 3 weeks. Surface roughness measurements (Ra) were performed after the immersion period and toothbrushing, by means of a profilometer. Data were analyzed by two-way ANOVA and Tukey's test. Analysis revealed that the association between toothbrushing and Colgate Plax Fresh Mint produced the lowest surface roughness (p < 0.05). All other groups tested (Oral B, Cepacol, Colgate Plax, artificial saliva) exhibited no statistically significant differences between surfaces, whether subjected to toothbrushing or not (p < 0.05). It was concluded that the surface roughness of the nanofilled composite resin tested can be influenced by the mouthrinse associated with toothbrushing.

Impact of filler size and distribution on roughness and wear of composite resin after simulated toothbrushing

Objectives: Nanofilled composite resins are claimed to provide superior mechanical properties compared with microhybrid resins. Thus, the aim of this study was to compare nanofilled with microhybrid composite resins. The null hypothesis was that the size and the distribution of fillers do not influence the mechanical properties of surface roughness and wear after simulated toothbrushing test. Material and methods: Ten rectangular specimens (15 mm x 5 mm x 4 mm) of Filtek Z250 (FZ2), Admira (A), TPH3 (T), Esthet-X (EX), Estelite Sigma (ES), Concept Advanced (C), Grandio (G) and Filtek Z350 (F) were prepared according to manufacturer's instructions. Half of each top surface was protected with nail polish as control surface (not brushed) while the other half was assessed with five random readings using a roughness tester (Ra). Following, the specimens were abraded by simulated toothbrushing with soft toothbrushes and slurry comprised of 2: 1 water and dentifrice (w/w). 100,000 strokes were performed and the brushed surfaces were re-analyzed. Nail polish layers were removed from the specimens so that the roughness (Ra) and the wear could be assessed with three random readings (mu m). Data were analyzed by ANOVA and Tukey's multiple-comparison test (alpha = 0.05). Results: Overall outcomes indicated that composite resins showed a significant increase in roughness after simulated toothbrushing, except for Grandio, which presented a smoother surface. Generally, wear of nanofilled resins was significantly lower compared with microhybrid resins. Conclusions: As restorative materials suffer alterations under mechanical challenges, such as toothbrushing, the use of nanofilled materials seem to be more resistant than microhybrid composite resins, being less prone to be rougher and worn.

Microtensile bond strength of composite resin to glass-infiltrated alumina composite conditioned with Er,Cr:YSGG laser

Tribochemical silica-coating is the recommended conditioning method for improving glass-infiltrated alumina composite adhesion to resin cement. High-intensity lasers have been considered as an alternative for this purpose. This study evaluated the morphological effects of Er,Cr:YSGG laser irradiation on aluminous ceramic, and verified the microtensile bond strength of composite resin to ceramic following silica coating or laser irradiation. In-Ceram Alumina ceramic blocks were polished, submitted to airborne particle abrasion (110 mu m Al(2)O(3)), and conditioned with: (CG) tribochemical silica coating (110 mu m SiO(2)) + silanization (control group); (L1-L10) Er,Cr:YSGG laser (2.78 mu m, 20 Hz, 0.5 to 5.0 W) + silanization. Composite resin blocks were cemented to the ceramic blocks with resin cement. These sets were stored in 37A degrees C distilled water (24 h), embedded in acrylic resin, and sectioned to produce bar specimens that were submitted to microtensile testing. Bond strength values (MPa) were statistically analyzed (alpha a parts per thousand currency sign0.05), and failure modes were determined. Additional ceramic blocks were conditioned for qualitative analysis of the topography under SEM. There were no significant differences among silicatization and laser treatments (p > 0.05). Microtensile bond strength ranged from 19.2 to 27.9 MPa, and coefficients of variation ranged from 30 to 55%. Mixed failure of adhesive interface was predominant in all groups (75-96%). No chromatic alteration, cracks or melting were observed after laser irradiation with all parameters tested. Surface conditioning of glass-infiltrated alumina composite with Er,Cr:YSGG laser should be considered an innovative alternative for promoting adhesion of ceramics to resin cement, since it resulted in similar bond strength values compared to the tribochemical treatment.

Microhardness of a dental restorative composite resin containing nanoparticles polymerized with argon ion laser

The objective of this study was to compare the microhardness of two resin composites (microhybrid and nanoparticles). Light activation was performed with argon ion laser 1.56J (L) and halogen light 2.6J (H) was used as control. Measurements were taken on the irradiated surfaces and those opposite them, at thicknesses of 1, 2 and 3 mm. To evaluate the quality of polymerization, the percentages of maximum hardness were calculated (PMH). For statistical analysis the ANOVA and Tukey tests were used (p <= 0.05). To microhybrid was shown that the hardness with laser was inferior to the hardness achieved with halogen light, for both the 1 mm and 2 mm. The nanoparticles polymerized with laser, presented lower hardness even on the irradiated surface, than the same surface light activated with halogen light. The microhybrid attained a minimum PMH of 80% up to the thickness of 2 mm with halogen light, and with laser, only up to 1 mm. The nanoparticles attained a minimum PMH of 80% up to 3 mm thickness with halogen light and with laser this minimum was not obtained at any thickness. Based on these results, it could be concluded that light activation with argon ion laser is contra-indicated for the studied nanoparticles. Published by Elsevier GmbH.

Effect of light sources and curing mode techniques on sorption, solubility and biaxial flexural strength of a composite resin

Adequate polymerization plays an important role on the longevity of the composite resin restorations. Objectives: The aim of this study was to evaluate the effect of light-curing units, curing mode techniques and storage media on sorption, solubility and biaxial flexural strength (BFS) of a composite resin. Material and Methods: Two hundred and forty specimens were made of one composite resin (Esthet-X) in a stainless steel mold (2 mm x 8 mm 0), and divided into 24 groups (n=10) established according to the 4 study factors: light-curing units: quartz tungsten halogen (QTH) lamp and light-emitting diodes (LED); energy densities: 16 J/cm(2) and 20 J/cm(2); curing modes: conventional (CM) and pulse-delay (PD); and permeants: deionized water and 75% ethanol for 28 days. Sorption and solubility tests were performed according to ISO 4049:2000 specifications. All specimens were then tested for BFS according to ASTM F394-78 specification. Data were analyzed by three-way ANOVA followed by Tukey, Kruskal-Wallis and Mann-Whitney tests (alpha=0.05). Results: In general, no significant differences were found regarding sorption, solubility or BFS means for the light-curing units and curing modes (p>0.05). Only LED unit using 16 J/cm(2) and PD using 10 s produced higher sorption and solubility values than QTH. Otherwise, using CM (16 J/cm(2)), LED produced lower values of BFS than QTH (p<0.05). 75% ethanol permeant produced higher values of sorption and solubility and lower values of BFS than water (p<0.05). Conclusion: Ethanol storage media produced more damage on composite resin than water. In general the LED and QTH curing units using 16 and 20 J/cm(2) by CM and PD curing modes produced no influence on the sorption, solubility or BFS of the tested resin.

Clinical strategies for esthetic excellence in anterior tooth restorations: understanding color and composite resin selection

Direct composite resin restorations have become a viable alternative for patients that require anterior restorative procedures to be integrated to the other teeth that compose the smile, especially for presenting satisfactory esthetic results and minimum wear of the dental structure. Technological evolution along with a better understanding of the behavior of dental tissues to light incidence has allowed the development of new composite resins with better mechanical and optical properties, making possible a more artistic approach for anterior restorations. The combination of the increasing demand of patients for esthetics and the capacity to preserve the dental structure resulted in the development of different incremental techniques for restoring fractured anterior teeth in a natural way. In order to achieve esthetic excellence, dentists should understand and apply artistic and scientific principles when choosing color of restorative materials, as well as during the insertion of the composite resin. The discussion of these strategies will be divided into two papers. In this paper, the criteria for color and material selection to obtain a natural reproduction of the lost dental structures and an imperceptible restoration will be addressed.