Fabrication of Silicon Crystal-Facet-Dependent Nanostructures by Electron-Beam Lithography

Silicon crystal-facet-dependent nanostructures have been successfully fabricated on a (100)-oriented silicon-on-insulator wafer using electron-beam lithography and the silicon anisotropic wet etching technique. This technique takes ad-vantage of the large difference in etching properties for different crystallographic planes in alkaline solution. The mini-mum size of the trapezoidal top for those Si nanostructures can be reduced to less than 10nm. Scanning electron microscopy(SEM) and atomic force microscopy (AFM) observations indicate that the etched nanostructures have controllable shapes and smooth surfaces.

An All-E-Beam Lithography Process for the Patterning of 2D Photonic Crystal Waveguide Devices

We present an all-e-beam lithography (EBL) process for the patterning of photonic crystal waveguides.The whole device structures are exposed in two steps. Holes constituting the photonic crystal lattice and defects are first exposed with a small exposure step size (less than 10nm). With the introduction of the additional proximity effect to compensate the original proximity effect, the shape, size, and position of the holes can be well controlled.The second step is the exposure of the access waveguides at a larger step size (about 30nm) to improve the scan speed of the EBL. The influence of write-field stitching error can be alleviated by replacing the original waveguides with tapered waveguides at the joint of adjacent write-fields. It is found experimentally that a higher exposure efficiency is achieved with a larger step size;however,a larger step size requires a higher dose.

1.3μm InGaAs/InAs/GaAs Self-Assembled Quantum Dot Laser Diode Grown by Molecular Beam Epitaxy

The growth of multi-layer InGaAs/InAs/GaAs self-assembled quantum dots （QDs） by molecular beam epitaxy （MBE） is investigated,and a QD laser diode lasing at 1.33μm in continuous operation mode at room temperature is reported. The full width at half maximum of the band edge emitting peaks of the photoluminescence （PL） spectra at room temperature is less than 35meV for most of the multi-layer QD samples,revealing good,reproducible MBE growth conditions. Moreover,atomic force microscopy images show that the QD surface density can be controlled in the range from 1×10^10 to 7 ×10^10 cm^-2 . The best PL properties are obtained at a QD surface density of about 4×10^10cm^-2. Edge emitting lasers containing 3 and 5 stacked QD layers as the active layer lasing at room temperature in continuous wave operation mode are reported.

A GaAs-Based MOEMS Tunable RCE Photodetector with Single Cantilever Beam

A GaAs-based micro-opto-electro-mech anical-systems(MOEMS) tunable resonant cavity enhanced(RCE)photodetector with a continuous tuning range of 31nm under a 6V tuning voltage is demonstrated. The single cantilever beam structure is adopted for this MOEMS tunable RCE photodetector. The maximum and minimum peak quantum efficiency during the tuning are 36.9 % and 30. 8 %, respectively. The maximum and minimum full-width-at-halfmaximum (FWHM) are 20nm and 14nm,respectively. The dark current density is 7.46A/m2 without bias.

High-Power and High-Efficiency 650nm-Band AlGaInP Visible Laser Diodes Fabricated by Ion Beam Etching

High power and high-slope efficiency 650nm band real-refractive-index ridge waveguide AlGaInP laser diodes with compressive strained MQW active layer are formed by pure Ar ion beam etching process.Symmetric laser mesas with high perpendicularity,which are impossible to obtain by traditional wet etching method due to the use of a 15°-misoriented substrate,are obtained by this dry etching method.Laser diodes with 4μm wide,600μm long and 10%/90% coat are fabricated.The typical threshold current of these devices is 46mA at room temperature,and a stable fundamental-mode operation over 40mW is obtained.Very high slope efficiency of 1.4W/A at 10mW and 1.1W/A at 40mW are realized.