Shrinkage of nanocavities in silicon during electron beam irradiation

An internal shrinkage of nanocavity in silicon was in situ observed under irradiation of energetic electron on electron transmission microscopy. Because there is no addition of any external materials to cavity site, a predicted nanosize effect on the shrinkage was observed. At the same time, because there is no ion cascade effect as encountered in the previous ion irradiation-induced nanocavity shrinkage experiment, the electron irradiation-induced instability of nanocavity also provides a further more convincing evidence to demonstrate the predicted irradiation-induced athermal activation effect. (c) 2006 American Institute of Physics.

Nanoelectronic devices-resonant tunnelling diodes grown on InP substrates by molecular beam epitaxy with peak to valley current ratio of 17 at room temperature

This paper reports that lnAs/In0.53Ga0.47As/AlAs resonant tunnelling diodes have been grown on InP substrates by molecular beam epitaxy. Peak to valley current ratio of these devices is 17 at 300K. A peak current density of 3kA/cm(2) has been obtained for diodes with AlAs barriers of ten monolayers, and an In0.53Ga0.47As well of eight monolayers with four monolayers of InAs insert layer. The effects of growth interruption for smoothing potential barrier interfaces have been investigated by high resolution transmission electron microscope.

Fabrication of metallic air bridges using multiple-dose electron beam lithography

The techniques of fabricating metallic air bridges using different resists in a one-step electron beam lithography are presented. The exposure process employed a single-layer polymethyl methacrylate (PMMA) or photoresists with either different doses in the span and feet areas or with varying acceleration voltage of the electron beam. The process using photoresists with different doses has produced air bridges more stable than what the PMMA method using various acceleration voltages would achieve. Using this method, air bridges up to 12 mu m long have been fabricated. The length and height of these metallic air bridges vary with the photoresist thickness. (c) 2006 American Institute of Physics.

The role of Sb in the molecular beam epitaxy growth of 1.30-1.55 mu m wavelength GaInNAs/GaAs quantum well with high indium content

Sb-assisted GaInNAs/GaAs quantum wells (QWs) with high (42.5%) indium content were investigated systematically. Transmission electron microscopy, reflection high-energy electron diffraction and photoluminescence (PL) measurements reveal that Sb acts as a surfactant to suppress three-dimensional growth. The improvement in the 1.55 mu m range is much more apparent than that in the 1.3 mu m range.. which can be attributed to the difference in N composition. The PL intensity and the full-width at half maximum of the 1.55 mu m single-QW were comparable with that of the 1.3 Am QWs. (c) 2006 Elsevier B.V. All rights reserved.

Influence of growth parameters of frequency-radio plasma nitrogen source on extending emission wavelengths from 1.31 mu m to 1.55 mu m GaInNAs/GaAs quantum wells grown by molecular-beam epitaxy

High (42.5%) indium content GaInNAs/GaAs quantum wells with room temperature emission wavelength from 1.3 mu m to 1.5 mu m range were successfully grown by Radio Frequency Plasma Nitrogen source assisted Molecular Beam Epitaxy. The growth parameters of plasma power and N-2 How rate were optimized systematically to improve the material quality. Photoluminescence and transmission electron microscopy measurements showed that the optical and crystal quality of the 1.54 mu m GaInNAs/GaAs QWs was kept as comparable as that in 1.31 mu m.