Twin and grain boundary in InP: A synchrotron radiation study

Experimentally observed X-ray reflectivity curves show bi-crystal(twin) characteristics. The study revealed that there was defect segregation at the twin boundary. Stress was relaxed at the edge of the boundary. Relaxation of the stress resulted in formation of twin and other defects. As a result of formation of such defects, a defect-free and stress-free zone or low defect density and small stress zone is created around the defects. So a twin model was proposed to explain the experimental results. Stress(mainly thermal stress), chemical stoichiometry deviation and impurities nonhomogeneous distributions are the key factors that cause twins in LEC InP crystal growth. Twins on (111) face in LEC InP crystal were studied. Experimental evidence of above mentioned twin model and suggestions on how to get twin-free LEC InP single crystals will be discussed.

Improved neutron radiation hardness for Si detectors: Application of low resistivity starting material and or manipulation of N-eff by selective filling of radiation-induced traps at low temperatures

Radiation-induced electrical changes in both space charge region (SCR) of Si detectors and bulk material (BM) have been studied for samples of diodes and resistors made on Si materials with different initial resistivities. The space charge sign inversion fluence (Phi(inv)) has been found to increase linearly with the initial doping concentration (the reciprocal of the resistivity), which gives improved radiation hardness to Si detectors fabricated from low resistivity material. The resistivity of the BM, on the other hand, has been observed to increase with the neutron fluence and approach a saturation value in the order of hundreds k Omega cm at high fluences, independent of the initial resistivity and material type. However, the fluence (Phi(s)), at which the resistivity saturation starts, increases with the initial doping concentrations and the value of Phi(s) is in the same order of that of Phi(inv) for all resistivity samples. Improved radiation hardness can also be achieved by the manipulation of the space charge concentration (N-eff) in SCR, by selective filling and/or freezing at cryogenic temperatures the charge state of radiation-induced traps, to values that will give a much smaller full depletion voltage. Models have been proposed to explain the experimental data.

Influence of nitrogen implantation into the buried oxide on the radiation hardness of silicon-on-insulator wafers

摘要: In order to improve the total-dose radiation hardness of the buried oxide of separation by implanted oxygen silicon-on-insulator wafers, nitrogen ions were implanted into the buried oxide with a dose of 10(16)cm(-2), and subsequent annealing was performed at 1100 degrees C. The effect of annealing time on the radiation hardness of the nitrogen implanted wafers has been studied by the high frequency capacitance-voltage technique. The results suggest that the improvement of the radiation hardness of the wafers can be achieved through a shorter time annealing after nitrogen implantation. The nitrogen-implanted sample with the shortest annealing time 0.5 h shows the highest tolerance to total-dose radiation. In particular, for the 1.0 and 1.5 h annealing samples, both total dose responses were unusual. After 300-krad(Si) irradiation, both the shifts of capacitance-voltage curve reached a maximum, respectively, and then decreased with increasing total dose. In addition, the wafers were analysed by the Fourier transform infrared spectroscopy technique, and some useful results have been obtained.