Inductively coupled plasma etching in fabrication of 2D InP-based photonic crystals

The authors developed an inductively coupled plasma etching process for the fabrication of hole-type photonic crystals in InP. The etching was performed at 70 degrees C using BCl3/Cl-2 chemistries. A high etch rate of 1.4 mu m/min was obtained for 200 nm diameter holes. The process also yields nearly cylindrical hole shape with a 10.8 aspect ratio and more than 85 degrees straightness of the smooth sidewall. Surface-emitting photonic crystal laser and edge emitting one were demonstrated in the experiments.

Bulge testing and fracture properties of plasma-enhanced chemical vapor deposited silicon nitride thin films

The mechanical properties and fracture behavior of silicon nitride (SiNx) thin film fabricated by plasma-enhanced chemical vapor deposition is reported. Plane-strain moduli, prestresses, and fracture strengths of silicon nitride thin film; deposited both oil a bare Si substrate and oil a thermally oxidized Si substrate were extracted using bulge testing combined with a refined load-deflection model of long rectangular membranes. The plane-strain modu i and prestresses of SiNx thin films have little dependence on the substrates, that is, for the bare Si substrate, they are 133 +/- 19 GPa and 178 +/- 22 MPa, respectively, while for the thermally oxidized substrate, they are 140 +/- 26 Gila and 194 +/- 34 MPa, respectively. However, the fracture strength values of SiNx films grown on the two substrates are quite different, i.e., 1.53 +/- 0.33 Gila and 3.08 +/- 0.79 GPa for the bare Si substrate a A the oxidized Si substrate, respectively. The reference stresses were computed by integrating the local stress of the membrane at the fracture over the edge, Surface, and volume of the specimens and fitted with the Weibull distribution function. For SiNx thin film produced oil the bare Si Substrate, the Volume integration gave a significantly better agreement between data and model, implying that the volume flaws re the dominant fracture origin. For SiNx thin film grown on the oxidized Si substrate, the fit quality of surface and edge integration was significantly better than the Volume integration, and the dominant surface and edge flaws could be caused by buffered HF attacking the SiNx layer during SiO2 removal. Crown Copyright (C) 2008 Published by Elsevier B.V. All rights reserved.

Amorphous silicon carbide films prepared by H-2 diluted silane-methane plasma

This paper reports on the preparation and characterization of hydrogenated amorphous silicon carbide films prepared by H-2 diluted silane-methane plasma. Carbon-rich a-SiC:H film with band gap of up to 3.3 eV has been achieved. IR and UV Vis spectra were employed to characterize the chemical bonding and optical properties of as-prepared films. It is shown that hydrogen dilution is crucial in obtaining these wide band gap carbon-rich films. Raman and PL measurements were performed to probe the microstructure and photoelectronic properties of these films before and after annealing. Films with intermediate carbon concentration seem more defective and exhibit stronger photoluminescence and subband absorption than others. Films with different compositions exhibit different annealing behaviours. For silicon rich and carbon rich films, high temperature annealing results in the formation of silicon crystallites and graphite clusters, respectively. (C) 2003 Elsevier B.V. All rights reserved.

High speed 2x2 optical switch in silicon-on-insulator based on plasma dispersion effect

Based on free carrier plasma dispersion effect, a 2 x 2 optical switch is fabricated in a silicon-on-insulator substrate by inductively coupled-plasma technology and ion implantation. The device has a Mach-Zehnder interferometer structure, in which two directional couplers serve as the power splitter and combiner. The switch presents an insertion loss of 3.04 dB and a response time of 496 ns.

Structure, stability and photoelectronic properties of transition films from amorphous to microcrystalline silicon

A series of hydrogenated silicon films near the threshold of crystallinity was prepared by very high frequency plasma enhanced chemical vapor deposition (VHF-PECVD) from a mixture of SiH4 diluted in H, The effect of hydrogen dilution ratios R-H = [H-2]/[SiH4] on microstructure of the films was investigated. Photoelectronic properties and stability of the films were studied as a function of crystalline fraction. The results show that more the crystalline volume fraction in the silicon films, the higher mobility life-time product (mu tau), better the stability and lower the photosensitivity. Those diphasic films contained 8%-31% crystalline volume fraction can gain both the fine photoelectronic properties and high stability. in the diphasic (contained 12% crystalline volume fraction) solar cell, we obtained a much lower light-induced degradation of similar to 2.9%, with a high initial efficiency of 10.01% and a stabilized efficiency of 9.72% (AM1.5, 100 mW/cm(2)). (c) 2005 Elsevier B.V. All rights reserved.