Influence of oxygen post-treatment on laser-induced damage of antireflection coatings prepared by electron-beam evaporation and ion beam assisted deposition

Antireflection coatings at the center wavelength of 1053 nm were prepared on BK7 glasses by electron-beam evaporation deposition (EBD) and ion beam assisted deposition (IBAD). Parts of the two kinds of samples were post-treated with oxygen plasma at the environment temperature after deposition. Absorption at 1064 nm was characterized based on surface thermal lensing (STL) technique. The laser-induced damage threshold (LIDT) was measured by a 1064-nm Nd:YAG laser with a pulse width of 38 ps. Leica-DMRXE Microscope was applied to gain damage morphologies of samples. The results revealed that oxygen post-treatment could lower the absorption and increase the damage thresholds for both kinds of as-grown samples. However, the improving effects are not the same. (c) 2008 Elsevier B.V. All rights reserved.

Compensation of reflectance response deviations of guided-mode resonant filters induced by overetching fabrication

Unless the fabrication error control is well treated, it easily causes overetched fabrication errors, which causes the resonant peak value deviation during the fabrication process of guided-mode resonant filters (GMRFs). Hence, the fabrication error control becomes a key point for improving the performance of GMRF. We find that, within the range of the groove depth from 93 to 105 nm, the relationship between the overetched error and the resonant peak value deviation is nearly linear, which means that we can compensate the reflectance response deviation and reduce the resonant peak value deviation by the method of covering the layer film on the GMRF. Simulation results show that the deviation is compensated perfectly by this way. (C) 2008 Optical Society of America

Ultra-narrow bandwidth resonant reflection grating filters using the second diffracted orders

In this paper, we design resonant reflection grating filters employing the second diffracted orders as the leaky modes, then analyze the bandwidth of the reflection peak and the electric field distributions inside the wavegude under resonance. The numeric calculation confirms that ultra-narrow resonant reflection peaks can be observed in these structures. At the same time, strong electric field enhancement appears under resonance. It provides a new approach to diversify the resonant reflection filters and may open a new way to the realization of ultra-narrow bandwidth filters. (C) 2008 Elsevier B.V. All rights reserved.

High refractive index TiO2 film deposited by electron beam evaporation

The well known 'crystal seed' theory is first applied in this work to prepare TiO2 film: a high refractive index rutile TiO2 film is grown by electron beam evaporation on the rutile seed formed by 1100 degrees C annealing. The average n is larger than 2.4, by far the highest in all the authors' TiO2 films. The films are characterised by optical properties, microstructure and surface morphologies. It is found that the refractive index shows positive relation with the crystal structure, grain size, and packing density and roughness of the film. The film has lower density of granularity and nodule defects on the surface than those of the film deposited by magnetron sputtering. The result shows attractive application in complex filter and laser coatings.

Efficiency improvement of organic light-emitting diodes using 8-hydroxy-quinolinato lithium as an electron injection layer

Organic light-emitting diodes (OLEDs) using tris-(8-hydroxy-quinolinato) aluminum (Alq(3)) as an emitter, 8-hydroxy-quinolinato lithium (Liq) as an electron injection layer, were prepared. Experimental results show that the efficiency of device with Liq is three times higher than that without Liq. The device using Liq as an injection layer is less sensitive in efficiency to the Liq thickness than that using LiF. In addition to the Alq3 based devices, Liq is also very effective as an electron injection layer for 4,4'-bis(2,2-diphenylvinyl)-1,1'-biphenyl based blue OLED and poly (2-methoxy,5-(2-ethyl-hexyloxy)-1,4-phenylenevinylene) based orange polymer OLED. (c) 2004 Elsevier B.V. All rights reserved.