Non-isothermal crystallization behavior and kinetics of metallocene short chain branched polyethylene

The non-isothermal crystallization behavior and kinetics of metallocene short chain branched polyethylene were investigated via DSC at cooling rates from 2.5 to 20 degreesC/min, and subsequent heating at rate of 10 degreesC/min. To verify the effect of molecular weight and branching content on crystallization, three group samples were chosen: (1) linear polyethylene with low molecular weight and high molecular weight; (2) low molecular weight polyethylene with low branching content and high branching content; (3) high molecular weight polyethylene with low branching content and high branching content. The results show that crystallization temperature, crystallinity, melting temperature and crystallization rate are highly branching content-dependent. Molecular weight effect is less important, compared to branching content. A dramatic decrease of crystallization temperature, crystallinity, crystallization rate and melting temperature was observed for branched samples. The non-isothermal kinetics was analyzed via the methods, developed by Gupta and Mo Zhi-shen, and good agreement was obtained.

The polydispersity of ethylene sequence in metallocene ethylene/alpha-olefin copolymers III: crystallization and melting behavior of short ethylene sequence

Crystallization and melting behavior of short ethylene sequence of metallocene ethylene/alpha -olefin copolymer with high comonomer content have been studied by standard DSC and modulated-temperature differential scanning calorimetry (M-TDSC) technique. In addition to high temperature endotherm around 120 degreesC, a low temperature endotherm is observed at lower temperatures (40-80 degreesC), depending on time and temperature of isothermal crystallization. The peak position of the low temperature endotherm T-m(low) varies linearly with the logarithm of crystallization time and the slope, D, decreases with increasing crystallization temperature T-c. The T-m(low) also depends on the thermal history before the crystallization at T-c, and an extrapolation of T-m(low) (30.6 degreesC) to a few seconds has been obtained after two step isothermal crystallization before the crystallization at 30 degreesC. The T-m(low) is nearly equal to T-c, and it indicates that the initial crystallization at low temperature is nearly reversible. Direct evidence of conformational. entropy change of secondary crystallization has been obtained by using M-TDSC technique. Both the M-TDSC result and the activation energy analysis of temperature dependence suggest that crystal perfection process and conformational entropy decreasing in residual amorphous co-exist during secondary crystallization.

Crystallization kinetics of narrow molecular weight distribution metallocene short-chain-branched polyethylene

Isothermal and non-isothermal crystallization kinetics of three metallocene-catalysed short-chain-branched polyethylene (SCBPE) fractions with different degree of branching were investigated by using differential scanning calorimetry (DSC). Narrow molecular weight fractions (M-w = 20,000 and M-w/M-n < 1.15) are used and the degree of branching (CH3 per 1000C) are 1.6, 10.4, 40 respectively. The regime I - II transition temperature are 119.8C, 115.9 degreesC, 113.3 degreesC with the decreasing of degree of branching. Increasing the branch content decreases the rate of secondary nucleation, i,relative to the rate of surface spreading and so increases the range of supercooling over which regime I exists. The rate of bulk crystallization for both isothermal and non-isothermal crystallization decreases with the increasing of degree of branching. Both Ozawa Equation and Kissinger Equation are invalid for non-isothermal crystallization kinetics of SCBPE fractions,that means the effects of the branched chain on crystallization process are more complex than expected.

Networks with hexagonal circuits in co-ordination polymers of metal ions (Zn-II, Cd-II) with 1,1 '-(1,4-butanediyl)bis(imidazole)

Three new compounds, [ZnL1.5(H2O)(SO4)]. 6H(2)O 1, [ZnL1.5(H2O)(2)][NO3](2). 2H(2)O 2 and [CdL1.5(H2O)(2)(SO4)]. 4H(2)O 3 were obtained from self-assembly of the corresponding metal salts with 1,1'-(1,4-butanediyl)bis(imidazole) (L). In both 1 and 2 zinc ion is five-co-ordinated, showing a less-common trigonal bipyramidal co-ordination polyhedron, while cadmium ion of 3 is six-co-ordinated with a common octahedral arrangement. The sulfate ions of 1 and 3 are co-ordinated, however the nitrate ions of 2 are not. Each of the three compounds is composed of a (6, 3) network with the hexagonal smallest circuit containing six metal ions and six L; each L is co-ordinated to two metal ions, acting as a bridging ligand. In 1 the 2-D sheet of (6, 3) networks is interpenetrated in an inclined mode by symmetry related, identical sheets to give an interlocked 3-D structure, while the (6, 3) networks of both 2 and 3 stack in a parallel fashion to construct frameworks having channels.

Lateral habits of single crystals of metallocene-catalyzed low molecular weight short chain branched polyethylene from the melt

The lateral habits of low molecular weight short chain branched polyethylene single crystals from the melt were studied. Three crystallization temperatures (102, 104 and 106 degrees C) were selected for single crystal growth. It was found that the lateral habits of single crystals were asymmetric at all the crystallization temperatures selected. The electron diffraction patterns and tilting series experiments evidenced that there existed chain tilting in all the lamellae. It was the chain tilting that lead to the asymmetry of the growth rate and of lateral habits of the single crystals about the b-axis. The lateral habits substantially changed from the growth at 102 degrees C where the truncated lozenge single crystals formed with straight (110) faces to the growth at 104 degrees C where the lenticular single crystals appeared. This change occurred at 20 degrees C lower than that in a low molecular weight linear polyethylene with the same molecular weight. Furthermore, kinetics theory analysis evidenced that the change of lateral habits from truncated lozenge to lenticular shape resulted from the transition of growth regime. The results were the same as that of high molecular weight linear polyethylene but different to that of low molecular weight linear polyethylene. It may be attributed by the existence of short branched chains. (C) 2000 Elsevier Science Ltd. All rights reserved.

Molecular heterogeneity and crystal morphology in metallocene short chain branch polyethylene (SCBPE)

Metallocene, a newer generation of commercial polymerization catalysts for polyolefins, is best known for its "single sitednss", and the intermolecular structural homogeneity of metallocene polyethylene copolymer is a very interesting research issue. The molecular segregation effects on the crystallization, melting and crystal morphologies of metallocene SCBPE have been investigated with DSC and TEM. The multiple endothermic peaks were observed in the DSC thermograms during heating experiments. The heterogeneity increases as branching content increases, the lamellae becomes thinner, and lamellae distribution becomes broader. Both macroscopic segregation (between two crystal aggregates) and microscopic segreation (between two lamellae) have been observed when SCBPE crystallized from phase separated melt.

Influence of short chain branches on crystallization and melting behavior of low molecular weight polyethylenes

The crystallization and melting behavior of mellocene-catalized branched and linear polyethylenes of low molecular weight was studied. It was found that the crystalline lattice of branched polyethylene is larger than that of linear polyethylene because of the existence of branched chains. The melting behavior of branched polyethylene is similar to that of linear polyethylene since the branched chains can not enter the lattice. However, the crystalline behavior of low molecular weight branched polyethylene is the same as that of high molecular weight linear polyethylene, but different with that of low molecular weigh linear polyethylene. Kinetics theory analysis evidenced that the transition temperature of growth regime of the branched polyethylene is about 20 degreesC lower than that of linear polyethylene with the same molecular weight. It may be attributed to the existence of short branched chains.