提拉法生长镓酸锂晶体及缺陷研究

研究了提拉法生长的镓酸锂单晶的生长习性和结晶质量。晶体表面呈乳白色且表面粗糙。通过光学显微镜、四晶X射线衍射、透射光谱和电感耦合等离子体发射光谱对样品进行了表征，结果表明，在（001）面的抛光样品上存在三种缺陷：[110]和[-110]方向的十字线、[010]方向排列的气泡包裹物以及平行于（010）面的界面，界面的产生起因于（010）晶面的滑移；晶体的结晶质量从顶部到底部逐渐下降，这是由于在生长过程中氧化锂的挥发导致熔体成分偏离化学计量比造成的。

在Sr～2+α_BBO单晶衬底上生长β_BBO薄膜的研究

Crystalline beta-BBO thin films were successfully prepared on (001)-oriented Sr2+-doped alpha-BBO substrates by using liquid phase epitaxy, pulsed laser deposition and vapor transport equilibration techniques. The films were characterized by X-ray diffraction and X-ray rocking curve. The present results manifest that the beta-BBO thin films grown on Sr2+-doped alpha-BBO substrates have larger degree of orientation f value and smaller X-ray rocking curve FWHM than the ones grown on other reported substrates. Compared with other substrates, alpha-BBO has the similar structure, the same UV cutoff and the same chemical properties to beta-BBO. These results reveal that Sr2+-doped alpha-BBO single crystal may be a promising substrate proper to the growth of beta-BBO films.

Study on growth and properties of novel gamma-LiAlO2 substrate

Transparent gamma-LiAlO2 single crystal has been grown by Temperature Gradient technique. The surface of the wafer annealed in O-2-atmosphere at 1100 degrees C for 70 h became opaque and Li-poor phase (LiAl5O8); while, that annealed in Li-rich atmosphere kept transparent and smooth. The full-width at half maximum value dropped to 30 arcsecs when the wafer was annealed in Li-rich atmosphere. That annealed in O-2-atmosphere increased to 78 arcsec. Compared with absorption spectra, we can conclude that the 196 nm absorption peak was caused by Li vacancies and the 736 nm peak was caused by O vacancies.

Mg，Ti共掺Al2O3透明多晶陶瓷光谱性能研究

Transparent polycrystalline MgO and TiO2 codoped Al2O3 ceramics were fabricated by conventional solid-state pressureless processing. The absorption, emission and excitation spectra of ( Mg, Ti : Al2O3 ceramics were measured. Owing to charge compensation of Mg2+, only UV absorption around 250nm was observed due to O2- -> Ti4+ charge transfer transitions (CT) when Ti content was low. As a result, the emission peaks of isolated Ti4+ ion located at 280-290nm and 410-420nm were observed. Besides absorption peak of V, ion, the characteristic absorption peak of V, ion centered at 490nm was observed in Mg, Ti) : Al2O3 ceramics when Ti content was high. The emission spectra of Ti3+, ion in polycrystalline Al2O3 ceramics coincide with that of Ti: Al2O3 single crystal.

Structural, optical and electrical properties of ZnO films grown on c-plane sapphire and (100)gamma-LiAlO2 by pulse laser deposition

ZnO thin films were grown on single-crystal gamma-LiAlO2 (LAO) and sapphire (0001) substrate by pulsed laser deposition (PLD). The structural, optical and electrical properties of ZnO films were investigated. The results show that LAO is more suitable for fabricating ZnO films than sapphire substrate and the highest-quality ZnO film was attained on LAO at the substrate temperature of 550 degrees C. However, when the substrate temperature rises to 700 degrees C, lithium would diffuse from the substrate (LAO) into ZnO film which makes ZnO film on LAO becomes polycrystalline without preferred orientation, the stress in ZnO film increases dominantly and the resistivity of the film decreases exponentially. (c) 2005 Elsevier B.V. All rights reserved.

显微成像荧光屏用无机闪烁单晶薄膜的研究进展

随着第三代同步辐射源的出现，由荧光屏和CCD耦合组成的、具有亚微米级空间分辨率、快速在线成像功能的探测器在医疗、安检、工业、科研等领域将会得到广泛应用．本文主要综述了成像荧光屏用材料的概况和发展趋势，重点阐述了闪烁单晶薄膜的研究及发展情况．