Investigation on quality of cubic GaN/GaAs(100) by double-crystal X-ray diffraction

Cubic GaN was grown on GaAs(100) by low pressure metal organic chemical vapor deposition (MOCVD). X-ray diffraction, scanning electron microscope (SEM) and photoluminescence (PL) spectra were performed to characterize the quality of the GaN film. The PL spectra of cubic GaN thin films being thicker than 1.5 mu m were reported. Triple-crystal diffraction to analyze orientation distributions and strain of the thin films was also demonstrated.

AlGaInP visible quantum well lasers for information technology

650 nm-range AlGaInP multi-quantum well (MQW) laser diodes grown by low pressure metal organic chemical vapor deposition (LP-MOCVD) have been studied and the results are presented in this paper. Threshold current density of broad area contact laser diodes can be as low as 350 A/cm(2). Laser diodes with buried-ridge strip waveguide structures were made, threshold currents and differential efficiencies are (22-40) mA and (0.2-0.7) mW/mA, respectively. Typical output power for the laser diodes is 5 mW, maximum output power of 15 mW has been obtained. Their operation temperature can be up to 90 degrees C under power of 5 mW. After operating under 90 degrees C and 5 mW for 72 hrs, the average increments for the threshold currents of the lasers at 25 degrees C and the operation currents at 5 mW (at 25 degrees C) are (2-3) mA and (3-5) mA, respectively. Reliability tests showed that no obvious degradation was observed after 1400 hours of CW operation under 50 degrees C and 2.5 mW.

Using Fourier transform infrared grazing incidence reflectivity to study local vibrational modes in GaN

Both Fourier transform infrared (FTIR) grazing incidence reflectivity and FTIR transmission methods have been used to study GaN films grown on alpha-Al2O3 (0001) substrates by atmospheric pressure metal-organic chemical vapor deposition and low pressure metal-organic chemical vapor deposition. The results show that in the frequency range from 400 to 3500 cm(-1) the signal-to-noise ratio of the FTIR grazing incidence measurement is far higher than that of the FTIR transmission measurement. Some new vibrational structures appearing in the former measurement have been discussed. The features around 1460 and 1300 cm(-1) are tentatively assigned to scissoring and wagging local vibrational modes of CH2 in GaN, respectively. (C) 1999 American Institute of Physics. [S0021-8979(99)06509-3].

Cubic-phase GaN light-emitting diodes

The feasibility of growing device-quality cubic GaN/GaAs(001) films by metal organic chemical vapor deposition has been demonstrated. The optical quality of the GaN films was characterized by room-temperature photoluminescence measurements, which shows a full width at half maximum of 46 meV. The structural quality of the films was investigated by transmission electron microscopy. There are submicron-size grains free from threading dislocations and stacking faults. More importantly, a cubic-phase GaN blue light-emitting diode has been fabricated. The device process, which is very simple and compatible with current GaAs technology, indicates a promising future for the blue light-emitting diode. (C) 1999 American Institute of Physics. [S0003-6951(99)01416-3].

In composition dependence of lateral ordering in InGaAs quantum dots grown on (311)B GaAs substrates

Self-assembled InxGa1-xAs quantum dots (QDs) on (311)A/B GaAs surfaces have been grown by molecular beam epitaxy (MBE). Spontaneously ordering alignment of InxGa1-xAs with lower In content around 0.3 have been observed. The direction of alignment orientation of the QDs formation differs from the direction of misorientation of the (311)B surface, and is strongly dependent upon the In content x. The ordering alignment become significantly deteriorated as the In content is increased to above 0.5 or as the QDs are formed on (100) or (311)A substrates. (C) 1999 Elsevier Science B.V. All rights reserved.

Microstructure evolution of GaN buffer layer on MgAl2O4 substrate

Microstructure of GaN buffer layer grown on (111)MgAl2O4 substrate by metalorganic vapor phase epitaxy (MOVPE) was studied by transmission electron microscopy (TEM). It has been observed that the early deposition of GaN buffer layer on the substrate at a relatively low temperature formed a continual island-sublayer (5 nm thick) with hexagonal crystallographic structure, and the subsequent GaN buffer deposition led to crystal columns which are composed of nano-crystal slices with mixed cubic and hexagonal phases. After high-temperature annealing, the crystallinity of nano-crystal slices and island-sublayer in the buffer layer have been improved. The formation of threading dislocations in the GaN him is attributed not only to the lattice mismatch of GaN/MgAl2O4 interface, but also to the stacking mismatches at the crystal column boundaries. (C) 1998 Published by Elsevier Science B.V. All rights reserved.

Microstructure and photoluminescence of a-SiOx : H

Two strong photoluminescence (PL) bands in the spectral range of 550-900 nm have been observed at room temperature from a series of a-SiOx:H films fabricated by plasma-enhanced chemical vapor deposition (PECVD) technique. One is composed of a main band in the red-light region and a shoulder; the other is located at about 850 nm, only found after 1170 degrees C annealing in N-2 atmosphere. In conjunction with infrared (IR) and micro-Raman spectra, it is thought that the two PL bands are associated with a-Si clusters in the SiOx network and nanocrystalline silicon in SiO2, respectively.

Solid-phase crystallization and dopant activation of amorphous silicon films by pulsed rapid thermal annealing

An improved pulsed rapid thermal annealing method has been used to crystallize amorphous silicon films prepared by PECVD. The solid-phase crystallization and dopant activation process can be completed with time-temperature budgets such as 10 cycles of 60-s 550 degrees C thermal bias/l-s 850 degrees C thermal pulse. A mean grain size more than 1000 Angstrom and a Hall mobility of 24.9 cm(2)/V s are obtained in the crystallized films. The results indicate that this annealing method possesses the potential for fabricating large-area and good-quality polycrystalline silicon films on low-cost glass substrate. (C) 1998 Elsevier Science B.V. All rights reserved.