Correlated conformation and charge transport in multiwall carbon nanotube-conducting polymer nanocomposites

The strikingly different charge transport behaviours in nanocomposites of multiwall carbon nanotubes (MWNTs) and conducting polymer polyethylenedioxythiophene-polystyrene-sulfonic-acid (PEDOT-PSS) at low temperatures are explained by probing their conformational properties using small-angle x-ray scattering (SAXS). The SAXS studies indicate the assembly of elongated PEDOT-PSS globules on the walls of nanotubes, coating them partially, thereby limiting the interaction between the nanotubes in the polymer matrix. This results in a charge transport governed mainly by small polarons in the conducting polymer despite the presence of metallic MWNTs. At T > 4 K, hopping of the charge carriers following one-dimensional variable range hopping is evident which also gives rise to a positive magnetoresistance (MR) with an enhanced localization length (similar to 5 nm) due to the presence of MWNTs. However, at T < 4 K, the observation of an unconventional positive temperature coefficient of resistivity is attributed to small polaron tunnelling. The exceptionally large negative MR observed in this temperature regime is conjectured to be due to the presence of quasi-1D MWNTs that can aid in lowering the tunnelling barrier across the nanotube-polymer boundary resulting in large delocalization.

Growth mechanism of phases, Kirkendall voids, marker plane position, and indication of the relative mobilities of the species in the interdiffusion zone

Often, wrong conclusions about the mobilities of species are drawn from the position of the Kirkendall marker plane or voids in the interdiffusion zone. To clarify, I have discussed the growth mechanism of the phases and the position of the marker plane depending on the relative mobilities of the species. The formation of different kinds of voids in the interdiffusion zone is discussed. Further, the microstructure that could be found because of the Kirkendall effect is also explained.

Advantage of the ether linkage between the positive charge and the cholesteryl skeleton in cholesterol-based amphiphiles as vectors for gene delivery

Twelve novel cationic cholesterol derivatives with different linkage types between the cationic headgroup and the cholesteryl backbone have been developed. These have been tested for their efficacies as gene transfer agents as mixtures with dioleoyl phosphatidylethanolamine (DOPE). A pronounced improvement in transfection efficiency was observed when the cationic center was linked to the steroid backbone using an ether type bond. Among these, cholest-5-en-3b-oxyethane-N, N,N-trimethylammonium bromide (2a) and cholest-5-en-3b-oxyethane-N, N-dimethyl-N-2-hydroxyethylammonium bromide (3d) showed transfection efficiencies considerably greater than commercially available reagents such as Lipofectin or Lipofectamine. To achieve transfection, 3d did not require DOPE. Increasing hydration at the headgroup level for both ester- and ether-linked amphiphiles resulted in progressive loss of transfection efficiency. Transfection efficiency was also greatly reduced when a 'disorder'-inducing chain like an oleyl (cis-9-octadecenyl) segment was added to these cholesteryl amphiphiles. Importantly, the transfection ability of 2a with DOPE in the presence of serum was significantly greater than for a commercially available reagent, Lipofectamine. This suggests that these novel cholesterol-based amphiphiles might prove promising in applications involving liposome-mediated gene transfection. This investigation demonstrates the importance of structural features at the molecular level for the design of cholesterol-based gene delivery reagents that would aid the development of newer, more efficient formulations based on this class of molecules.

Explicit codes uniformly reducing repair bandwidth in distributed storage

A distributed storage setting is considered where a file of size B is to be stored across n storage nodes. A data collector should be able to reconstruct the entire data by downloading the symbols stored in any k nodes. When a node fails, it is replaced by a new node by downloading data from some of the existing nodes. The amount of download is termed as repair bandwidth. One way to implement such a system is to store one fragment of an (n, k) MDS code in each node, in which case the repair bandwidth is B. Since repair of a failed node consumes network bandwidth, codes reducing repair bandwidth are of great interest. Most of the recent work in this area focuses on reducing the repair bandwidth of a set of k nodes which store the data in uncoded form, while the reduction in the repair bandwidth of the remaining nodes is only marginal. In this paper, we present an explicit code which reduces the repair bandwidth for all the nodes to approximately B/2. To the best of our knowledge, this is the first explicit code which reduces the repair bandwidth of all the nodes for all feasible values of the system parameters.

Explicit codes minimizing repair bandwidth for distributed storage

We consider the problem of minimizing the bandwidth required to repair a failed node when data is stored across n nodes in a distributed manner, so as to facilitate reconstruction of the entire data by connecting to any k out of the n nodes. We provide explicit and optimal constructions which permit exact replication of a failed systematic node.

An iterative auction mechanism for combinatorial exchanges

Combinatorial exchanges are double sided marketplaces with multiple sellers and multiple buyers trading with the help of combinatorial bids. The allocation and other associated problems in such exchanges are known to be among the hardest to solve among all economic mechanisms. In this paper, we develop computationally efficient iterative auction mechanisms for solving combinatorial exchanges. Our mechanisms satisfy Individual-rationality (IR) and budget-nonnegativity (BN) properties. We also show that our method is bounded and convergent. Our numerical experiments show that our algorithm produces good quality solutions and is computationally efficient.

Crystal structure and thermal and electrical properties of the perovskite solid solution Nd1-xSrxFeO3-delta (0 <= x <= 0.4)

The crystal structure, thermal expansion and electrical conductivity of strontium-doped neodymium ferrite (Nd1-xSrxFeO3-delta where 0less than or equal toxless than or equal to0.4) were investigated. All compositions had the GdFeO3-type orthorhombic perovskite structure. The lattice parameters were determined at room temperature by X-ray powder diffraction. The orthorhombic distortion decreases with increasing Sr substitution. The pseudocubic lattice parameter shows a minimum at x=0.3. The thermal expansion curves for x=0.2-0.4 displayed rapid increase in slope at higher temperatures. The electrical conductivity increased with Sr content and temperature. The calculated activation energies for electrical conduction decreased with increasing x. The electrical conductivity can be described by the small polaron hopping mechanism. The charge compensation for divalent ion on the A-site is provided by the formation of Fe4+ ions on the B site and vacancies on the oxygen sublattice. The results indicate two defect domains: for low values of x, the predominant defect is Fe4+ ions, whereas for higher values of x, oxygen vacancies dominate. (C) 2002 Elsevier Science B.V. All rights reserved.

Crystal structure, thermal expansion and electrical conductivity of Nd0.7Sr0.3Fe1-xCoxO3 (0 <= x <= 0.8)

The crystal structure, thermal expansion and electrical conductivity of the solid solution Nd0.7Sr0.3Fe1-xCoxO3 for 0 less than or equal to x less than or equal to 0.8 were investigated. All compositions had the GdFeO3-type orthorhombic perovskite structure. The lattice parameters were determined at room temperature by X-ray powder diffraction (XRPD). The pseudo-cubic lattice constant decreased continuously with x. The average linear thermal expansion coefficient (TEC) in the temperature range from 573 to 973 K was found to increase with x. The thermal expansion curves for all values of x displayed rapid increase in slope at high temperatures. The electrical conductivity increased with x for the entire temperature range of measurement. The calculated activation energy values indicate that electrical conduction takes place primarily by the small polaron hopping mechanism. The charge compensation for the divalent ion on the A-site is provided by the formation of Fe4+ ions on the B-site (in preference to Co4+ ions) and vacancies on the oxygen sublattice for low values of x. The large increase in the conductivity with x in the range from 0.6 to 0.8 is attributed to the substitution of Fe4+ ions by Co4+ ions. The Fe site has a lower small polaron site energy than Co and hence behaves like a carrier trap, thereby drastically reducing the conductivity. The non-linear behaviour in the dependence of log sigmaT with reciprocal temperature can be attributed to the generation of additional charge carriers with increasing temperature by the charge disproportionation of Co3+ ions. (C) 2002 Elsevier Science B.V. All rights reserved.

Growth mechanism of phases by interdiffusion and atomic mechanism of diffusion in the molybdenum-silicon system

Tracer diffusion coefficients are calculated in different phases in the Mo-Si system from diffusion couple experiments using the data available on thermodynamic parameters. Following, possible atomic diffusion mechanism of the species is discussed based on the crystal structure. Unusual diffusion behaviour is found in the Mo(5)Si(3) and Mo(3)Si phases, which indicate the nature of defects present on different sublattices. Further the growth mechanism of the phases is discussed and morphological evolution during interdiffusion is explained. (C) 2011 Elsevier Ltd. All rights reserved.

Grain size effects on charge-ordering, phase segregation and related properties of rare-earth manganates, Nd(0.5)A(0.5)MnO(3) (A = Ca or Sr)

Grain size has marked effects on charge-ordering and other properties of Nd(0.5)A(0.5)MnO(3) (A=Ca or Sr). Thus, the anti-ferromagnetic (AFM) transition in Nd0.5Ca0.5MnO3 is observed distinctly only in samples sintered at 1273 K or higher. The sample with a small grain size (sintered at 1173 K) shows evidence for greater ferromagnetic (FM) interaction at low temperatures, probably due to phase segregation. The FM transition as well as the charge-ordering transition in Nd0.5Sr0.5MnO3 becomes sharper in samples sintered at 1273 K or higher. The sample sintered at 1173 K does not show the AFM-CO transition around 150 K and is FM down to low temperatures; the apparent T-c-T-co gap decreases with the increase in the grain size. The samples sintered at lower temperatures (<1673 K) show evidence for greater segregation of the AFM and FM domains. (C) 2002 Elsevier Science Ltd. All rights reserved.

A determination of the structure of the intramolecular charge transfer state of 4-dimethylaminobenzonitrile (DMABN) by time-resolved resonance Raman spectroscopy

Picosecond time-resolved resonance Raman spectra of the A (intramolecular charge transfer, ICT) state of DMABN, DMABN-d(6) and DMABN-N-15 have been obtained. The isotopic shifts identify the nu (s)(ph-N) mode as a band at 1281 cm(-1). The similar to 96 cm(-1) downshift of this mode from its ground state frequency rules out the electronic coupling PICT model and unequivocally supports the electronic decoupling TICT model. However, our results suggest some pyramidal character of the A state amino conformation.

Structure, function, and mechanism of HhaI DNA methyltransferases

A vast amount of literature has accumulated on the characterization of DNA methyltransferases. The HhaI DNA methyltransferase, a C5-cytosine methyltransferase, has been the subject of investigation for the last 2 decades. Biochemical and kinetic characterization have led to an understanding of the catalytic and kinetic mechanism of the methyltransfer reaction. The HhaI methyltransferase has also been subjected to extensive structural analysis, with the availability of 12 structures with or without a cofactor and a variety of DNA substrates. The mechanism of base flipping, first described for the HhaI methyltransferase, is conserved among all DNA methyltransferases and is also found to occur in numerous DNA repair enzymes. Studies with other methyltransferase reveal a significant structural and functional similarity among different types of methyltransferases. This review aims to summarize the available information on the HhaI DNA methyltransferase.

Study of thickness dependence on electrical properties of (Pb,La)TiO3 thin films for memory applications

Lead-lanthanum-titanate (Pb0.72La0.28)TiO3 (PLT) is one of the interesting materials for DRAM applications due to its room temperature paraelectric nature and its higher dielectric permittivity. PLT thin films of different thickness ranging from 0.54- 0.9 mum were deposited on Pt coated Si substrates by excimer laser ablation technique. We have measured the voltage (field) dependence, the thickness dependence, temperature dependence of dc leakage currents and analysis is done on these PLT thin films. Current- voltage characteristics were measured at different temperatures for different thick films and the thickness dependence of leakage current has been explained by considering space charge limited conduction mechanism. The charge transport phenomena were studied in detail for films of different thicknesses for dynamic random access memory applications.