Deep levels in semi-insulating InP obtained by annealing under iron phosphide ambiance

Deep levels in semi-insulating (SI) InP obtained by annealing in iron phosphide (IP) ambiance have been characterized by optical transient current spectroscopy (OTCS). Compared with the OTCS result of the SI InP prepared by annealing in pure phosphorus (PP) ambiance, the IP SI InP presents only two traps with activation energies of 0.20 and 0.63 eV, respectively. The results suggest that the diffusion of Fe-atoms suppresses the formation of a few defects in the IP SI InP. The nature of deep levels in the IP and PP SI InP has been discussed on the basis of these results. The relation between material property and defects in those SI InP has also been revealed. (C) 2002 American Institute of Physics.

Characterization of deep levels in Pt-GaN Schottky diodes deposited on intermediate-temperature buffer layers

Gallium nitride (GaN)-based Schottky junctions were fabricated by RF-plasma-assisted molecular beam epitaxy (MBE). The GaN epitaxial layers were deposited on novel double buffer layers that consist of a conventional low-temperature buffer layer (LTBL) grown at 500 degreesC and an intermediate-temperature buffer layer (ITBL) deposited at 690 degreesC. Low-frequency excess noise and deep level transient Fourier spectroscopy (DLTFS) were measured from the devices. The results demonstrate a significant reduction in the density of deep levels in the devices fabricated with the GaN films grown with an ITBL. Compared to the control sample, which was grown with just a conventional LTBL, a three-order-of-magnitude reduction in the deep levels 0.4 eV below the conduction band minimum (Ec) is observed in the bulk of the thin films using DLTFS measurements.

Hole levels and exciton states in CdS nanocrystals

We have studied the hole levels and exciton states in CdS nanocrystals by using the hole effective-mass Hamiltonian for wurtzite structure. It is found that the optically passive P-x state will become the ground hole state for small CdS quantum dots of radius less than 69 Angstrom. It suggests that the "dark exciton" would be more easily observed in the CdS quantum dots than that in CdSe quantum dots. The size dependence of the resonant Stokes shift is predicted for CdS quantum dots. Including the Coulomb interaction, exciton energies as functions of the dot radius are calculated and compared with experimental data.

Effect of thermal annealing on hole trap levels in Mg-doped GaN grown by metalorganic vapor phase epitaxy

Deep trap levels in a Mg-doped GaN grown by metalorganic vapor phase epitaxy are studied with deep level transient spectroscopy (DLTS). The Mg concentration of the sample was 4.8 x 10(19) cm(-3), but the hole concentration was as low as 1.3x10(17) cm-3 at room temperature. The DLTS spectrum has a dominant peak D-1 with an activation energy of 0.41+/-0.05 eV, accompanied by two additional peaks with activation energies of 0.49+/-0.09 eV (D-2) and 0.59+/-0.05 eV (D-3). It was found that the dominant peak D-1 consists of five peaks, each of which has different activation energy and capture cross section. In order to investigate these deep levels further, we performed heat treatment on the same samples to observe the variations of activation energy, capture cross section, and amplitude of DLTS signals. It was found that the longer the heat treatment duration is, the lower the amplitude of DLTS peaks become. This suggests that the decrease of the DLTS signal originates from hydrogen atom outgoing from the film during the annealing process. The possible originality of multiple trap levels was discussed in terms of the Mg-N-H complex. (C) 2000 American Vacuum Society. [S0734-2101(00)01701-2].

Hole trap levels in Mg-doped GaN grown by metalorganic vapor phase epitaxy

Hole trap levels in a Mg-doped GaN grown by metalorganic vapor phase epitaxy (MOVPE) are studied with deep level transient spectroscopy (DLTS). The Mg concentration of the sample was 4.8 x 10(19) cm(-3), but the hole concentration was as low as 1.3 x 10(17) cm(-3) at room temperature. The DLTS spectrum has a dominant peak D-1 with activation energy of 0.41+/-0.05 eV, accompanied by two additional peaks with activation energies of 0.49+/-0.09 eV (D-2) and 0.59+/-0.05 eV (D-3). It was found that the dominant peak D-1 consists of five peaks, each of which has different activation energy and capture cross section. A relevant model for these levels is presented in relation to the Mg-N-H complexes. (C) 1998 American Institute of Physics. [S0003-6951(98)04340-X].