Broadband near-infrared emission from transparent Ni2+-doped sodium aluminosilicate glass ceramics

Broadband neat-infrared emission from transparent Ni2+-doped sodium aluminosilicate glass-cermaics is observed. The broad emission is centered at 1290 nm and covers the whole telecommunication wavelength region (1100-1700 nm) with full width at half maximum of about 340 nm. The observed infrared emission could be attributed to the T-3(2)(F) -> (3)A(2)(F) transition of octahedral Ni2+ ions that occupy high-field sites in nanocrystals. The product of the lifetime and the stimulated emission cross section is 2.15 x 10(-24) cm(2)s. It is suggested that Ni2+-doped sodium aluminosilicate glass ceramics have potential applications in tunable broadband light sources and broadband amplifiers.

Spectroscopic properties of Nd3+-doped high silica glass prepared by sintering porous glass

A new kind of Nd3+, -doped high silica glass (SiO2 > 96% (mass fraction)) was obtained by sintering porous glass impregnated with Nd3+, ions. The absorption and luminescence properties of high silica glass doped with different Nd3+, concentrations were studied. The intensity parameters Omega(t) (t = 2, 4, 6), spontaneous emission probability, fluorescence lifetime, radiative quantum efficiency, fluorescence branching ratio, and stimulated emission cross section were calculated using the Judd-Ofelt theory. The optimal Nd3+ concentration in high silica glass was 0.27% (mole fraction) because of its high quantum efficiency and emission intensity. By comparing the spectroscopic parameters with other Nd3+ doped oxide glasses and commercial silicate glasses, the Nd3+-doped high silica glasses are likely to be a promising material used for high power and high repetition rate lasers.

高浓度掺Er^3＋铌酸锂晶体的光谱参数计算

用提拉法成功地生长了6mol％的高浓度掺铒铌酸锂晶体。测量了晶体的两个非偏振方向（X和Z）以及两个偏振方向（π和δ）的吸收光谱。高浓度掺铒铌酸锂晶体的吸收系数高，有利于提高泵浦效率。根据所测的吸收光谱用Judd-Ofelt理论拟合出了Er^3＋离子的强度参数Ωλ。所得的均方差结果显示偏振拟合的误差要小于非偏振拟合。利用偏振吸收数据计算了各能级跃迁的自发辐射跃迁几率（AJJ’）、辐射寿命（τ）、荧光分支比（β）和积分发射截面（σp）等参数，对计算结果进行了讨论并与其他文献的报道结果进行了比较。

氧化铝透明陶瓷中Cr3+的发光性能

采用传统无压烧结工艺制备出透明性良好的掺Cr3+氧化铝陶瓷;测定了陶瓷的吸收光谱、发射光谱和激发光谱。结果表明,氧化铝陶瓷吸收峰与红宝石单晶一致,吸收截面大小与单晶相近;陶瓷中Cr3+离子所处格位的晶体场强较单晶弱,但其发射谱仍有较好的锐线发射;陶瓷中微量添加剂以及晶界的存在使得Al2O3晶胞发生畸变,造成其发射峰宽化。

Yb:Y2-2xLa2xO3激光透明陶瓷的光谱性能

It was first reported the spectral properties of a low-temperature sintered transparent Yb: Y2-2x La-2x O-3 laser ceramics. Yb: Y2-2x La-2x O-3 laser ceramics have broad absorption band and large absorption cross- section of 4.0 x 10(-20) cm(2) at wavelengths 977nm of the highest absorption peak. Its fluorescence lifetime is 1.1 ms, and the emission cross-sections are 1.0 x 10(-20) cm(2) and 0.7 x 10(-20) cm(2) at wavelengths 1033nm and 1077nm, respectively. All the optical properties are similar to those of single crystals.

Spectral properties of Ho : GdVO4 single crystal

Absorption and emission spectral properties of GdVO4 single crystal doped with Ho3+ ions were investigated at room temperature. Polarized absorption cross section is calculated in the range of 400-2200nm. Results were analyzed and parameters were calculated based on Judd-Ofelt theory, the emission spectrum shows that the emission intensity around the wavelength of 546 nm associated with transition S-5(2) -> I-5(8) is much stronger than other bands in the observed range and potentially enable the green light output around this emission band in this crystal. (c) 2006 Elsevier B.V. All rights reserved.

Investigation of the spectroscopic properties of Yb3+-doped yttrium lanthanum oxide transparent ceramic

Spectroscopic properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic were studied. Two main absorption peaks of the specimen are centered at 940 and 970 nm, which are suitable for InGaAs laser diode pumping. The main emission peaks were located at 1032 and 1075 nm with larger emission cross-section and longer fluorescence lifetime than those of Yb:Y2O3. These properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic are favorable to achieve high efficiency and high power laser output. (c) 2007 Elsevier B.V. All rights reserved.

Spectral characterization of transparent (Nd0.01Y0.94La0.05)(2)O-3 laser ceramics

The spectrum properties of transparent (Nd0.01Y0.94La0.05)(2)O-3 ceramics were investigated. It was found that all absorption bands of (Nd0.01Y0.94La0.05)(2)O-3 ceramics are broadened, of which the full width at half maximum of the peak centered at 804 nm is 8 nm and its absorption cross section is 1.02x10(-20) cm(2). The emission cross section of (Nd0.01Y0.94La0.05)(2)O-3 ceramics located at 1078 nm is 5.71x10(-20) cm(2) and its fluorescent lifetime is 0.214 ms, which are similar to those of 1.0 at. %Nd:Y2O3 ceramics. These indicate that (Nd0.01Y0.94La0.05)(2)O-3 transparent ceramics has excellent spectroscopic properties.

Growth and spectral properties of Yb : FAP single crystal

In this paper, single crystal of ytterbium (Yb) doped Ca-5(PO4)(3)F (FAP) has been grown along the c-axis by using the Czochralski method. The segregation coefficients of Yb3+ in the Yb:FAP crystal has been determined by ICP-AES method. The absorption spectrum, fluorescence spectrum and fluorescence lifetime of the Yb:FAP crystal has been also measured at room temperature. In the absorption spectra, there are two absorption bands at 904 and 982 nm, respectively, which are suitable for InGaAs diode laser pumping. The absorption cross-section (sigma(abs)) is 5.117 x 10(-20) cm(2) with an FWHM of 4 nm at 982 nm. The emission cross-section is (sigma(em)) 3.678 x 10(-20) cm(2) at 1042 nm. Favorable values of the absorption cross-section at about 982 nm are promising candidates for laser diode (LD) pumping. (c) 2005 Elsevier B.V. All rights reserved.

Spectroscopic properties of Nd3+:(La,Sr)(Al,Ta)O-3 crystal

A new laser crystal Nd3+:(La, Sr)(Al, Ta)O-3 (abbreviated as Nd3+:LSAT) has been grown by the conventional Czochralski method. The absorption and luminescence spectra of trivalent neodymium in Nd3+:LSAT crystal were measured at room temperature. The value of absorption and emission cross-section was calculated. The Judd-Ofelt analysis was applied to the crystal to get the phenomenological parameters (Omega(i), i = 2,4,6), the line strengths, the radiative transition rates, the branching ratios and the radiative lifetime. (C) 2006 Elsevier B.V. All rights reserved.

Spectroscopic properties of Yb:YAP crystal

The 10at% Yb-YAP crystal has been grown by the Czochralski method. The absorption and emission spectra and fluorescence lifetime of Yb:YAP crystal at room temperature were studied. There is a strong absorption band centered at 959 nm and the absorption cross-section of 1.51 × 10^-20 cm². The emission cross-section at 1040 nm is 0.6 × 10^-20 cm² and the fluorescence lifetime is about 1.2 ms. The effects of O₂-annealing on the spectral properties were studied. The spectroscopic properties strongly depended on the axis direction and b axis was the best direction for laser output. The spectrum parameters of Yb:YAP and Yb:YAG crystal were compared.}

Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷的光谱性能研究

采用传统无压烧结工艺制备了Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷并对其光谱性能进行了研究．样品具有较大的吸收和发射截面．La2O3的添加使样品的荧光寿命（τs）与玻璃接近，当Yb^3＋和Er^3＋的掺杂量分别为5at％和0．5at％时，测得τs=9．65ms．这种荧光寿命长、发射截面大和线宽窄的特性有利于微型、可集成化和大功率激光输出的实现．

Yb:YAP与Yb:YAG晶体光谱性能比较

应用中频感应提拉法生长出掺杂浓度为10 at.-%的Yb:YAG与Yb:YAP晶体，对比了室温下两种晶体的吸收和发射光谱特性。结果表明，Yb:YAG晶体比Yb:YAP晶体有更好的激光性能和低的阈值；同时对比发现，Yb:YAP晶体的吸收截面是Yb:YAG晶体的2.16倍，它容易实现LD泵；由于Yb:YAP晶体的各向异性，它有轴向效应明显，它可以产生偏振激光。

Nd：YbVO4晶体的拉曼光谱和荧光光谱研究

用群论的方法计算了Nd：YbVO4晶体的拉曼活性振动模数目，在室温下测得了其极化拉曼谱线，并指认了在不同几何配置下，各振动模式所对应的频率。同时，测得了室温下晶体的吸收谱，得到了中心波长为808am吸收峰的半高宽为12nm，并在J-O理论的基础上计算了晶体的光学参数，其三个晶场参数分别为Ω2=6．88945×10^-20cm^2。Ω4=4．13394×10^-20cm^2、Ω6=4．54503×10^-20cm^2，并由此得到^4F3／2能级的荧光寿命为178．69炉，1062nm处的荧光分支比为48．85％，积分发射截面为2．786710^-18cm^2。分别在808nm、940nm激发下测得晶体室温发射谱，观察到了Nd→Yb以及Nd←Yb间的能量传递现象。

Sm:GdVO_4晶体的生长及光谱性能研究

应用中频感应提拉法生长出掺杂浓度为2%原子分数的Sm:GdVO4晶体,研究了室温下c轴方向Sm:GdVO4晶体的吸收和荧光光谱。通过J-O理论计算出强度参数(Ωt),同时计算了对应于4G5/2能级的自发跃迁几率、荧光分支比和辐射寿命。通过荧光光谱计算了对应于566、604和646nm三个发射峰对应的发射截面,结果表明,Sm:GdVO4在604nm的发射截面最大,是掺Sm:YAP在607nm处发射截面的4.4倍。