Solid-core tellurite glass fiber for infrared and nonlinear applications

By optimizing glass composition and using a multistage dehydration process, a ternary 80TeO(2)-10ZnO-10Na(2)O glass is obtained that shows excellent transparency in the wavelength range from 0.38 mu m up to 6.10 mu m. Based on this optimized composition, we report on the fabrication of a single-mode solid-core tellurite glass fiber with large mode area of 103 mu m(2) and low loss of 0.24 similar to 0.7 dB/m at 1550 nm. By using the continuous-wave self-phase modulation method, the non-resonant nonlinear refractive index n(2) and the effective nonlinear parameter gamma of this made tellurite glass fiber were estimated to be 3.8x10(-1)9 m(2)/W and 10.6 W-1.m(-1) at 1550 nm, respectively. (C) 2009 Optical Society of America

Single-Mode Solid-Core Tellurite Glass Fiber with Large Mode Area and Low Loss for Infrared Applications

低损耗实芯碲酸盐光纤的非线性研究

Quakes in solid quark stars

A starquake mechanism for pulsar glitches is developed in the solid quark star model. It is found that the general glitch natures (i.e., the glitch amplitudes and the time intervals) could be reproduced if solid quark matter, with high baryon density but low temperature, has properties of shear modulus mu(c) = 10(30-34) erg/cm(3) and critical stress sigma(c) = 10(18similar to24) erg/cm(3). The post-glitch behavior may represent a kind of damped oscillations. (C) 2004 Elsevier B.V. All rights reserved.

PHYSICAL VAPOR TRANSPORT AND CRYSTAL-GROWTH OF GESEXTE1-X SOLID-SOLUTIONS

Physical vapor transport studies of GeSe(x)Te1 - x (x = 0.1, 0.2, 0.3, and 0.4) solid solutions demonstrated, that individual, large single crystals of these materials can be grown in closed ampoules. A compositional analysis of the grown crystals revealed, that the mass transport (crystal growth) process under steady-state conditions is pseudo-congruent and controlled by diffusion processes in the source material. From these experiments, the degree of non-stoichiometry (Ge-vacancy concentrations) of GeSe(x)Te1 - x single crystals could be estimated. The effects of the cubic to rhombohedral phase transformation during cooling on the microstructure and morphology of the grown mixed crystals are observed. This work provides the basis for subsequent defect studies and electrical measurements on these crystals.

Ge composition saturation behavior during low-temperature Si1-xGex growth by disilane and solid Ge molecular beam epitaxy

Ge composition dependence on the Ge cell temperature has been studied during the growth of Si1-xGex by disilane and solid Ge molecular beam epitaxy at a substrate temperature of 500 degrees C. It is found that the composition x increases and then saturates when the Ge cell temperature increases, which is different from the composition-dependent behavior in growth at high temperature as well as in growth by molecular beam epitaxy using disilane and germane. The enhanced hydrogen desorption from a Ge site alone cannot account for this abnormal composition-variation behavior. We attribute this behavior to the increase of rate constant of H desorption on a Si site when the Ge cell temperature increases.

COMPARISON OF PROPERTIES OF SOLID-PHASE EPITAXIAL SILICON-ON-SAPPHIRE FILMS RECRYSTALLIZED BY RAPID THERMAL ANNEALING AND FURNACE ANNEALING

Chemically vapour deposited silicon on sapphire (SOS) films 0.25 mu m thick were implanted with Si-28(+) and recrystallized in solid phase by furnace annealing (FA) and IR rapid thermal annealing (RTA) in our laboratory. An improvement in crystalline quality can be obtained using both annealing procedures. After FA, it is hard to retain the intrinsic high resistivity value(10(4)-10(5) Ohm cm) observed in as-grown SOS films, so the improvement process cannot be put to practical use effectively. However, it is demonstrated that by properly adjusting the implantation and RTA conditions, significant improvements in both film quality and film autodoping can be accomplished. This work describes a modified double solid phase epitaxy process in which the intrinsic high resistivities of the as grown SOS films are retained. The mechanism of suppression of Al autodoping is discussed.

GaInNAs/GaAs quantum well lasers grown by solid-source molecular beam epitaxy

The growth of GaInNAs/GaAs quantum wells (QW) was investigated by solid-source molecular beam epitaxy. N was introduced by a dc-active plasma source. The effect of growth conditions such as on the N incorporation and photoluminescence (PL) intensity of the QWs has been studied. The PL peak intensity decreased and the PL fun width at half maximum increased with increasing N concentrations. The highest N concentration of 2.6% in a GaInNAs/GaAs QW was obtained, and corresponding to a PL peak wavelength of 1.57 mum at 10K. Rapid thermal annealing at 850degreesC significantly improved the crystal quality of the QWs. An optimum annealing time of 5s at 850degreesC was obtained. A GaInNAs/GaAs SQW laser with the emitting wavelength of 1.2 mum and a high characteristic temperature of 115 K was achieved at room temperature.

Improvement of CMOS SOS devices characteristics by a modified solid phase epitaxy

CMOS/SOS devices have lower carriers mobility and higher channel leakage current than bulk silicon CMOS devices. These mainly results from the defects of heteroepitaxial silicon film, especially from the defects near Si-Sapphire interface. This paper describes the experiment results of CMOS/SOS devices characteristics improved by a better epitaxial silicon quality which is obtained by a modified solid phase epitaxy.

Improvement of thin silicon on sapphire (SOS) film materials and device performances by solid phase epitaxy

The increased emphasis on sub-micron CMOS/SOS devices has placed a demand for high quality thin silicon on sapphire (SOS) films with thickness of the order 100-200 nm. It is demonstrated that the crystalline quality of as-grown thin SOS films by the CVD method can be greatly improved by solid phase epitaxy (SPE) process: implantation of self-silicon ions and subsequent thermal annealing. Subsequent regrowth of this amorphous layer leads to a greater improvement in silicon layer crystallinity and channel carrier mobility, evidenced, respectively, by double crystal X-ray diffraction and electrical measurements. We concluded that the thin SPE SOS films are suitable for application to high-performance CMOS circuitry. (C) 2000 Elsevier Science S.A. All rights reserved.