Study of the thermomechanical and electrical properties of conducting composites containing natural rubber and carbon black

This work describes the preparation and characterization of composite materials obtained by the combination of natural rubber (NR) and carbon black (CB) in different percentages, aiming to improve their mechanical properties, processability, and electrical conductivity, aiming future applications as transducer in pressure sensors. The composites NR/CB were characterized through optical microscopy (OM), DC conductivity, thermal analysis using differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMA), thermogravimetry (TGA), and stress-strain test. The electrical conductivity varied between 10(-9) and 10 S m(-1), depending on the percentage of CB in the composite. Furthermore, a linear (and reversible) dependence of the conductivity on the applied pressure between 0 and 1.6 MPa was observed for the sample with containing 80 wt % of NR and 20% of CB. (C) 2007 Wiley Periodicals, Inc.

Crystallization kinetic of fluoro-zirconate glasses by non-isothermal analysis

Fluoride glasses have been extensively studied due to their high transparency in the infrared wavelength. The crystallization kinetics of these systems has been studied using DTA and DSC techniques. Most of the experimental data is frequently investigated in terms of the Johnson-Mehl-Avrami (JMA) model in order to obtain kinetic parameters.In this work, DSC technique has been used to study the crystallization of fluorozirconate glass under non-isothermal conditions. It was found that JMA model was not fit to be applied directly to these systems, therefore, the method proposed by Malek has been applied and the Sestak-Berggren (SB) model seems to be adequate to describe the crystallization process.

Attainment of lead titanate - Through the thermal decomposition of coprecipitated 8-hydroxyquinolinate precursors

Crystalline PbTiO3 was obtained through the thermal decomposition of 8-hydroxyquinolinate of lead(II) and that of titanium(IV), which was monitored by TG/DTG/DTA under different atmospheric conditions and with varying heating rates. The compound was prepared from adding 8-hydroxyquinoline solution in the solution of metallic ions Pb(II):Ti(IV) (1:1) Linder constant stirring at 3degreesC, having the pH adjusted to 10. The results of these investigations show that different thermal behavior related to the precursor occurred and also the consequent formation of residues which have different crystallinities. No carbonate residues from the thermal decomposition could be determined by XRD and IR. Only PbTiO3 was observed and confirmed by DSC at 470degreesC, temperature lower than the tetragonal-cubic transition.

Thermal behavior of the Cu-10 mass%Al and Cu-10 mass%Al-4 mass%Ag alloys

The thermal behavior of the Cu-10 mass%Al and Cu-10 mass% Al-4 mass%Ag alloys was studied using classical differential thermal analysis (DTA), optical microscopy (OM) and X-ray diffractometry (XRD). The DTA curves were obtained for annealed and quenched samples. The results indicated that the presence of silver introduces new thermal events, associated to the formation of a silver-rich phase, to the shift of the equilibrium concentration to higher A1 contents and to the decomposition of the silver-rich phase in the same temperature range of the beta(1) phase decomposition.

Electric characterization of a hybrid composite based on POMA/P(VDF- TrFE)/Zn2SiO4 : Mn using impedance spectroscopy

Understanding the microscopic origin of the dielectric properties of disordered materials has been a challenge for many years, especially in the case of samples with more than one phase. For polar dielectrics, for instance, the Lepienski approach has indicated that the random free energy barrier model of Dyre must be extended. Here we analyse the dielectric properties of a polymer blend made up with the semiconducting poly(o-methoxyaniline) and poly( vinylidene fluoride-trifluorethylene) POMA/P(VDF-TrFE), and of a hybrid composite of POMA/P(VDF-TrFE)/Zn2SiO4:Mn. For the blend, the Lepienski model, which takes into account the rotation or stretching of electric dipoles, provided excellent fitting to the ac impedance data. Because two phases had to be assumed for the hybrid composite, we had to extend the Lepienski model to fit the data, by incorporating a second transport mechanism. The two mechanisms were associated with the electronic transport in the polymeric matrix and with transport at the interfaces between Zn2SiO4: Mn microparticles and the polymeric matrix, with the relative importance of the interfacial component increasing with the percentage of Zn2SiO4: Mn in the composite. The analysis of impedance data at various temperatures led to a prediction of the theoretical model of a change in morphology at 190 +/- 40 K, and this was confirmed experimentally with a differential scanning calorimetry experiment.

Photo luminescence: A probe for short, medium and long-range self-organization order in ZrTiO4 oxide

Photoluminescent disordered ZrTiO4 powders were obtained by the polymeric precursor soft-chemical method. This oxide system (ordered and disordered) was characterized by photoluminescence, Raman spectroscopy, X-ray diffraction, differential scanning calorimetry and UV vis absorption experiments. The UV absorption tail formation in the disordered oxides was related to the diminution of optical band gap. In the disordered phase, this oxide displayed broad band photoluminescence caused by change in coordination number of titanium and zirconium with oxygen atoms. The gap decreased from 3.09 eV in crystalline oxide to 2.16 eV in disordered oxide. The crystalline oxide presented an orthorhombic alpha-PbO2-type structure in which Zr4+ and Ti4+ were randomly distributed in octahedral coordination polyhedra with oxygen atoms. The amorphous-crystalline transition occurred at almost 700 degrees C, at which point the photoluminescence vanished. The Raman peak at close to 80-200 cm(-1) indicated the presence of locally ordered Ti-O-n and Zr-O-n polyhedra in disordered photoluminescent oxides. (c) 2006 Elsevier B.V. All rights reserved.

Thermogenic activity of growth hormone transgenic mice

The objective was to determine the effect of a mouse metallothionein/bovine growth hormone transgene on resting metabolic rate (RMR), cold-induced thermogenesis, and beta-agonist stimulated nonshivering thermogenesis in mice. Non-transgenic littermates were used as controls. Open-circuit indirect calorimetry was used to assess RMR and cold-induced thermogenesis in 64 mice. Air temperature in the chamber was set at 31 degrees C for RMR and was decreased to 28, 25, 21, or 17 degrees C to determine cold-induced thermogenesis. Response to the beta-agonist isoproterenol was evaluated by monitoring changes in colonic temperature of 34 mice upon injection of the drug or saline. Despite the fact that RMR tended to be lower in transgenics than in nontransgenics, at 31 degrees C transgenic mice were able to regulate colonic temperature at the same level as nontransgenics, but colonic temperature decreased in transgenics relative to nontransgenics as air temperature was reduced. For each degree decrease in air temperature between 31 and 17 degrees C, nontransgenic mice increased heat production by 1.03 +/- .10 watt/kg, whereas transgenic mice increased it by only .56 +/- .08 watt/kg, indicating that the thermogenic response of transgenics to cold was inferior. The magnitude of the maximal increase in colonic temperature after isoproterenol injection was similar for both groups, but the response was slower in transgenics. We suggest that lean body mass and substrate availability for shivering thermogenesis are reduced in transgenics relative to total body weight, and that they allow colonic temperature to decrease to conserve energy.

Thermogravimetric investigations during the synthesis of silica-based MCM-41

MCM-41 material was synthesized starting from hydrogel containing colloidal fumed silica, sodium silicate, cetyltetramethylammonium bromide (CTMABr) as surfactant, and distilled water as solvent. These reactants were mixed to obtain a gel with the following composition: 4SiO(2):1Na(2)O:1CTMABr:200H(2)O. The hydrogel with pH=14 was hydrothermally treated at 100 degreesC, for 4 days. Each day, the pH was measured, and then adjusted to 9.5-10 by using 30% acetic acid solution. Thermogravimetry was the main technique, which was used to monitor the participation of the surfactant on the MCM-41 nanophase, being possible to determine the temperature ranges relative to water desorption as well as the surfactant decomposition and silanol condensation.

Scandium fluorophosphate glasses: a structural approach

A systematic investigation on glass formation in the ternary system InF3-BaF2-[Sc(PO3)(3)](n) has been carried out. Scandium polyphosphate [Sc(PO3)(3)](n) has been used as a third component in order to investigate the possibilities of obtaining new stable glasses. The above long-chain polyphosphate has been prepared using a specially elaborated cryo-technique, which allowed the preparation of high-purity product. Stable ternary compositions have been obtained within the compositions range (in mol%): 5-75 InF3, 0-80% BaF2, 0-50% [Sc(PO3)(3)](n). Glasses were characterized by Differential Scanning Calorimetry, vibrational spectroscopy (Raman) and P-31 NMR. Structural features for the glass were put forward. Isolated P(O,F)4 groups or fluoroindated metaphosphate units could be identified depending on glass compositions. (C) 2002 Academie des sciences / Editions scientifiques et medicales Elsevier SAS.

Non-isothermal kinetic applied to thermal decomposition of commercial alkyd varnish

Samples of commercial alkyd resin varnish were spread in a film form on slides, dried at room temperature and exposed to solar radiation from one day up to seven months.Thermogravimetric measurements have been done. Based on the TG data, the Flynn-Wall isoconversional method was applied. The activation energy varied between 176-154 kJ mol(-1) and logA was between 15.5-12.9 min(-1) for A, B and C samples at 95% confidence level.

Phase transition in poly(vinylidene fluoride) investigated with micro-Raman spectroscopy

The phase transition from the non-polar a-phase to the polar beta-phase of poly(vinylidene fluoride) (PVDF) has been investigated using micro-Raman spectroscopy, which is advantageous because it is a nondestructive technique. Films of alpha-PVDF were subjected to stretching under controlled rates at 80 degrees C, while the transition to P-PVDF was monitored by the decrease in the Raman band at 794 cm(-1) characteristic of the a-phase, along with the concomitant increase in the 839 cm-1 band characteristic of the P-phase. The alpha ->beta transition in our PVDF samples could be achieved even for the sample stretched to twice (2 X -stretched) the initial length and it did not depend on the stretching rate in the range between 2.0 and 7.0 mm/min. These conclusions were corroborated by differential scanning calorimetry (DSC) and X-ray diffraction experiments for PVDF samples processed under the same conditions as in the Raman scattering measurements. Poling with negative corona discharge was found to affect the a-PVDF morphology, improving the Raman bands related to this crystalline phase. This effect is minimized for films stretched to higher ratios. Significantly, corona-induced effects could not be observed with the other experimental techniques, i.e., X-ray diffraction and infrared spectroscopy.

Thermal study of cyclopalladated complexes of the type [Pd-2(dmba)(2)X-2(bpe)] - (X=NO3-, Cl-, N-3(-), NCO-, NCS-; bpe=trans-1,2-bis(4-pyridyl)ethylene)

The synthesis, characterization and thermal analysis of the novel cyclometallated compounds [Pd-2(dmba)(2)Cl-2(mu-bpe)] (1), [Pd-2(dmba)(2)(N-3)(2)(mu-bpe)] (2), [Pd-2(dmba)(2)(NCO)(2)(mu-bpe)] (3), [Pd-2(dmba)(2)(SCN)(2)(mu-bpe)] (4), [Pd-2(dmba)(2)(NO3)(2)(mu-bpe)] (5) (bpe=trans-1,2-bis(4-pyridyl)ethylene; dmba=N,N-dimethylbenzylamine) are described. The thermal stability of [Pd-2(dmba)(2)X-2(mu-bpe)] complexes varies in the sequence 1 > 4 > 3 > 2 > 5. The final residues of the thermal decompositions were characterized as metallic palladium by X-ray powder diffraction.

Structural organization of cetyltrimethylammonium sulfate in aqueous solution: the effect of Na2SO4

We used dynamic light scattering (DLS), a steady-state fluorescence, time resolved fluorescence quenching (TRFQ), tensiometry, conductimetry, and isothermal titration calorimetry (ITC) to investigate the self-assembly of the cationic surfactant cetyltrimethylammonium sulfate (CTAS) in aqueous solution, which has SO42- as divalent counterion. We obtained the critical micelled concentration (cmc), aggregation number (N-agg), area per monomer (a(0)), hydrodynamic radius (R-H), and degree of counterion dissociation (alpha) of CTAS micelles in the absence and presence of up to 1 M Na2SO4 and at temperatures of 25 and 40 degrees C. Between 0.01 and 0.3 M salt the hydrodynamic radius of CTAS micelle R-H approximate to 16 angstrom is roughly independent on Na2SO4 concentration; below and above this concentration range R-H increases steeply with the salt concentration, indicating micelle structure transition, from spherical to rod-like structures. R-H increases only slightly as temperature increases from 25 to 40 degrees C, and the cmc decreases initially very steeply with Na2SO4 concentration up to about 10 mM, and thereafter it is constant. The area per surfactant at the water/air interface, a(0), initially increases steeply with Na2SO4 concentration, and then decrases above ca. 10 mM. Conductimetry gives alpha = 0.18 for the degree of counterion dissociation, and N-agg obtained by fluorescence methods increases with surfactant concentration but it is roughly independent of up to 80 mM salt. The ITC data yield cmc of 0.22 mM in water, and the calculated enthalpy change of micelle formation, Delta H-mic = 3.8 kJ mol(-1), Gibbs free energy of micellization of surfactant molecules, Delta G(mic) = -38.0 kJ mol(-1) and entropy T Delta S-mic = 41.7 kJ mol(-1) indicate that the formation of CTAS micelles is entropy-driven. (c) 2006 Elsevier B.V. All rights reserved.

Thermal degradation of a composite solid propellant examined by DSC - Kinetic study

The thermal decomposition of ammonium perchlorate (AP)/hydroxyl-terminated-polybutadiene (HTPB), the AP/HTPB solid propellant, was studied at different heating rates in dynamic nitrogen atmosphere. The exothermic reaction kinetics was studied by differential scanning calorimetry (DSC) in non-isothermal conditions. The Arrhenius Parameters were estimated according to the Ozawa method. The calculated activation energy was 134.5 W mol(-1), the pre-exponential factor, A, was 2.04.10(10) min(-1) and the reaction order for the global composite decomposition was estimated in 0.7 by the kinetic Shimadzu software based on the Ozawa method. The Kissinger method for obtaining the activation energy value was also used for comparison. These results are discussed here.

Sublimation/volatilisation kinetics of 8-hydroxyquinolines and their nitro-derivatives

5-Nitro-8-hydroxyquinoline (B) and 5,7-dinitro-8-hydroxyquinoline (C) were obtained from nitration of 8-hydroxyquinoline (A) and purified in acetone medium and under heating in which the formation of (B) or (C) depends on the amount of HNO3 added. TG curves present mass loss in only one step before and after the melting point (T-m=76 degreesC (A) and 180 degreesC (B)) in different proportions as a function of the heating rate, characterising the sublimation and the volatilisation processes, respectively. The thermal stability of the compounds follow the order: A (77 degreesC)