Characteristic of rapid thermal annealing on GaIn(N)(Sb)As/GaAs quantum well grown by molecular-beam epitaxy

Effect of rapid thermal annealing on photoluminescence (PL) properties of InGaAs, InGaNAs, InGaAsSb, and InGaNAsSb quantum wells (QWs) grown by molecular-beam epitaxy was systematically investigated. Variations of PL intensity and full width at half maximum were recorded from the samples annealed at different conditions. The PL peak intensities of InGaAs and InGaNAs QWs initially increase and then decrease when the annealing temperature increased from 600 to 900 degrees C, but the drawing lines of InGaAsSb and InGaNAsSb take on an "M" shape. The enhancement of the PL intensity and the decrease of the full width at half maximum in our samples are likely due to the removal of defects and dislocations as well as the composition's homogenization. In the 800-900 degrees C high-temperature region, interdiffusion is likely the main factor influencing the PL intensity. In-N is easily formed during annealing which will prevent In out diffusion, so the largest blueshift was observed in InGaAsSb in the high-temperature region. (c) 2006 American Institute of Physics.

Magnetotransport in two-dimensional electron gas: The interplay between spin-orbit interaction and Zeeman splitting

We investigate theoretically the interplay between Zeeman splitting, Rashba spin-orbit interaction (RSOI), and Dresselhaus spin-orbit interaction (DSOI) and its influence on the magnetotransport property of two-dimensional electron gas (2DEG) at low temperature. Our theoretical results show that the nodes of the beating patterns of the magnetoresistivity rho(xx) for 2DEG with RSOI or DSOI alone depend sensitively on the total spin splitting induced by these three spin splitting mechanisms. It is interesting to find that the eigenstates in the presence of RSOI alone are connected with those in the presence of DSOI alone but with opposite Zeeman splitting by a time-reversal transformation. Consequently, the magnetoresistivities exhibit exactly the same oscillation patterns for these two cases. For strong RSOI or DSOI alone, the magneto-oscillation of rho(xx) shows two distinct periods. For 2DEG with both RSOI and DSOI, the beating patterns vanish for equal RSOI and DSOI strengths and vanishing Zeeman splitting. They will appear again, however, when Zeeman splitting or the difference between RSOI and DSOI strengths increases.

Electronic structures of wurtzite ZnO and ZnO/MgZnO quantum well

The band structures of wurtzite ZnO are calculated using the empirical pseudopotential method (EPM). The 8 parameters of the Zn and O atom pesudopotential form factors with Schluter's formula are obtained. The effective mass parameters are extracted by using k.p Hamiltonian to fit the EPM results. The calculated band edge energies (E-g, E-A, E-B, and E-C) at Gamma point are in good agreement with experimental results. The ordering of ZnO at the top of valence band is found to be A(Gamma(7))-B(Gamma(9))-C(Gamma(7)) due to a negative spin-orbit (SO) splitting. Based on the band parameters obtained, the valence hole subbands of wurzite ZnO/MgxZn1-xO tensile-strained quantum wells (QWs) with different well widths and Mg compositions are calculated using 6-band k.p method. (c) 2005 Elsevier B.V. All rights reserved.

Dual-wavelength distributed feedback laser for CWDM based on non-identical quantum well

Using non-identical quantum wells as the active material, a new distributed-feed back laser is fabricated with period varied Bragg grating. The full width at half maximum of 115 nm is observed in the amplified spontaneous emission spectrum of this material, which is flatter and wider than that of the identical quantum wells. Two wavelengths of 1.51 mu m and 1.53 mu m are realized under different work conditions. The side-mode suppression ratios of both wavelengths reach 40 dB. This device can be used as the light source of coarse wavelength division multiplexer communication systems.

Interband and intraband photocurrent of self-assembled InAs/InAlAs/InP nanostructures

The interband and intraband photocurrent properties of InAs/InAlAs/InP nanostructures have been studied. The doping effect on the photoluminescence properties of the quantum dots and the anisotropy of the quantum wire interband photocurrent properties are presented and discussed. With the help of interband excitation, an intraband photocurrent signal of the InAs nanostructures is observed. With the increase of the interband excitation power, the intraband photocurrent signal first increases and then decreases, which can be explained by the variance of the ground state occupation of the InAs nanostructures and the change of the mobility and lifetime of the electrons. The temperature dependence of the intraband photocurrent signal of the InAs nanostructures is also investigated.

A study of the growth and optical properties of AlInGaN alloys

We have studied the growth and optical properties of AlInGaN alloys in this article. By the measurement of three samples, we found that the incorporation of In decreases with the increase of temperature, while there is nearly no change for the incorporation of Al. The sample grown at the lowest temperature had the best material and optical properties, which owes to the high In component, because the In component can reduce defects and improve the material quality. We also used the time-resolved photoluminescence(PL) to study the mechanism of recombination of carriers, and found that the time dependence of PL intensity was not in exponential decay, but in stretched-exponential decay. Through the study of the character of this decay, we come to the conclusion that the emission comes from the recombination of localized excitons. Once more, this localization exhibites the character of quantum dots, and the stretched, exponential decay results from the hopping of carriers between different localized states. In addition, we have used the relation of emission energy dependence of carrier's lifetime and the character of radiative recombination and non-radiative combination to confirm our conclusion.

Theoretical analysis of characteristics of GaxIn1-xNyAs1-y/GaAs quantum well lasers with different intermediate layers

Based on the band anticrossing model, the effects of the strain-compensated layer and the strain-mediated layer on the band structure, gain and differential gain of GaInNAs/GaAs quantum well lasers have been investigated. The results show that the GaNAs barrier has a disadvantage in increasing the density of states in the conduction band. Meanwhile, the multilayer quantum wells need higher transparency carrier density than the GaInNAs/GaAs single quantum well with the same wavelength. However, they help to suppress the degradation of the differential gain. The calculation also shows that from the viewpoint of band structure, the strain-compensated structure and the strain-mediated structure have similar features.

Magnetic-field-induced nonthermal occupation of higher subbands in a three-barrier tunneling structure

When injected electrons in a quantum well first experience an intersubband relaxation process before their escaping by tunneling through a double-barrier structure behind, the magnetic suppression of intersubband LO or LA phonon scattering can give rise to a noticeable nonthermal occupation in higher-lying subbands. That is clearly verified by the relative intensity ratio of the interband photoluminescence spectra for E-2-HH1 and E-1-HH1 transitions. The observed phenomenon may provide an effective method for controlling intersubband scattering rate, a central issue in so-called quantum cascade lasers, and facilitating the population inversion between subbands in quantum wells.

Void formation and failure in InGaN/AlGaN double heterostructures

Condensed clusters of point defects within an InGaN/AlGaN double heterostructure grown by metal-organic vapor phase epitaxy on sapphire substrate have been observed using transmission electron microscopy. The existence of voids results in failure of the heterostructure in electroluminescence. The voids are 50-100 nm in diameter and are distributed inhomogeneously within In0.25Ga0.75N/AlGaN active layers. The density of the voids was measured as 10(15) cm(-3), which corresponds to a density of dangling bonds of 10(20) cm(-3). These dangling bonds may fully deplete free carriers in this double heterostructure and result in the heterostructure having high resistivity as confirmed by electrical measurement. (C) 2003 Elsevier Science B.V. All rights reserved.

Localized exciton dynamics in AlInGaN alloy

Carrier recombination dynamics in AlInGaN alloy has been studied by photoluminescence (PL) and time-resolved PL (TRPL) at various temperatures. The fast red-shift of PL peak energy is observed and well fitted by a physical model considering the thermal activation and transfer processes. This result provides evidence for the exciton localization in the quantum dot (QD)-like potentials in our AlInGaN alloy. The TRPL signals are found to be described by a stretched exponential function of exp[(-t/,tau)13], indicating the presence of a significant disorder in the material. The disorder is attributed to a randomly distributed QDs or clusters caused by indium fluctuations. By studying the dependence of the dispersive exponent beta on temperature and emission energy, we suggest that the exciton hopping dominate the diffusion of carriers localized in the disordered QDs. Furthermore, the localized states are found to have 0D density of states up to 250 K, since the radiative lifetime remains almost unchanged with increasing temperature. (C) 2003 Elsevier Science Ltd. All rights reserved.

Magnetic field tuning of the effective g factor in a diluted magnetic semiconductor quantum dot

The spin interaction and the effective g factor of a magnetic exciton (ME) are investigated theoretically in a diluted magnetic semiconductor (DMS) quantum dot (QD), including the Coulomb interaction and the sp-d exchange interaction. At low magnetic field, the ME energy decreases rapidly with increasing magnetic field and saturates at high magnetic field for high Mn concentration. The ground state of the ME exhibits an interesting crossing behavior between sigma(+)-ME and sigma(-)-ME for low Mn concentration. The g(ex) factor of the ME in a DMS QD displays a monotonic decrease with increasing magnetic field and can be tuned to zero by an external magnetic field. (C) 2003 American Institute of Physics.

The effect of inserting strain-compensated GaNAs layers on the luminescence properties of GaInNAs/GaAs quantum well

Photoluminescence (PL) properties of GaInNAs/GaAs quantum wells (QWs) with strain-compensated GaNAs layers grown by molecular beam epitaxy are investigated. The temperature-dependent PL spectra of GaInNAs/GaAs QW with and without GaNAs layers are compared and carefully studied. It is shown that the introduction of GaNAs layers between well and barrier can effectively extend the emission wavelength, mainly due to the reduction of the barrier potential. The PL peak position up to 1.41 mum is observed at the room temperature. After adding the GaNAs layers into QW structures, there is no essential deterioration of luminescence efficiency. N-induced localization states are also not remarkably influenced. It implies that with optimized growth condition, high-quality GaInNAs/GaAs QWs with strain-compensated GaNAs layers can be achieved. (C) 2003 Elsevier Science B.V. All rights reserved.

Structural and optical properties of InAlGaN films grown directly on low-temperature buffer layer with (0001)sapphire substrate

Quaternary InAlGaN film has been grown directly on top of low-temperature-deposited GaN buffer layer by low-pressure metalorganic vapor phase epitaxy. High-resolution X-ray diffraction and photoluminescence (PL) results show that the film has good crystal quality and optical property. Temperature-dependent PL and time-resolved PL (TRPL) have been employed to study the carriers recombination dynamics in the film. The TRPL signals can be well fitted as a stretched exponential function exp[-(t/tau)(beta)] from 14 to 250 K, indicating that the emission is attributed to the radiative recombination of excitons localized in disorder quantum nanostructures such as quantum disks originating from indium (In) clusters or In composition fluctuation. The cross-sectional high-resolution electron microscopy measurement further proves that there exist the disorder quantum nanostructures in the quaternary. By investigating the dependence of the exponential parameter beta on the temperature, it is shown that the multiple trapping-detrapping mechanism dominates the diffusion among the localized states. The localized states are considered to have two-dimensional density of states (DOS) at 250 K, since radiative recombination lifetime tau(r) increases linearly with increasing temperature. (C) 2002 Elsevier Science B.V. All rights reserved.

Abnormal effect of growth interruption on GaSb quantum dots formation grown by molecular beam epitaxy

The growth interruption (GI) effect on GaSb quantum dot formation grown on GaAs by molecular beam epitaxy was investigated. The structure characterization was performed by reflection high-energy electron diffraction (RHEED), along with photoluminescence measurements. It is found that the GI can significantly change the surface morphology of GaSb QDs. During the GI, the QDs structures can be smoothed out and turned into a 2D-like structure. The time duration of the GI required for the 3D/2D transition depends on the growth time of the GaSb layer. It increases with the increase of the growth time. Our results are explained by a combined effect of the stress relaxation process and surface exchange reactions during the GI. (C) 2002 Elsevier Science B.V. All rights reserved.

Polarization insensitive gain medium with hybrid strained quantum well

A polarization insensitive gain medium for optical amplifiers has been fabricated. The active layer is a structure with alternate tensile and compressive strain quantum wells. The waveguide is made into a taper with angled facets. In the experiment we found that the structure can suppress the lasing and decrease the polarization sensitivity. The gain imbalance between transverse electric and transverse magnetic gains is small, and 0.1 dB is obtained at a driving current of 100 mA. The full-width at half-maximum of amplified spontaneous emission is 40 nm within large current. (C) 2002 Elsevier Science Ltd. All rights reserved.