Dielectric and piezoelectric properties of the mechanochemically prepared PZT ceramics

Mechanochemical synthesis was applied to obtain nanocrystalline powders of composition Pb(Zr0.52Ti0.48)O-3 (PZT). Milling was performed in a planetary ball mill using vials and balls made of zirconia or steel-in order to investigate influence of milling media on the electrical properties of resulting ceramics. PZT ceramics showed high values for dielectric constant (epsilon(r)), reaching 970 at room temperature, as well as low dielectric loss (tandelta) under the optimal processing conditions. High values of remanent polarization (P-r) indicate high internal polarizability. The best samples showed piezoelectric strain constant d(33) = 347 pC/N and planar coupling factor k(P) = 0.44. Milling in ZrO2 medium prevents powder contamination and provides reproducibility of milling process. Also, PZT obtained from the powders milled in ZrO2 exhibited lower values of dielectric loss, in comparison with the PTZ obtained from the powders milled in Fe. This suggests that contamination of the powder with Fe could result in an increase of conductivity in final product. (C) 2004 Kluwer Academic Publishers.

An approach to analyzing synthesis, structure and properties of bismuth titanate ceramics

The family of bismuth titanate, Bi(4)Ti(3)O(12) (BIT) layered-structured ferroelectrics materials is attractive from the viewpoint of such as their application as electronic materials dielectrics, piezoelectrics and pyroelectrics, because they are characterized by good stability of piezoelectric properties, a high Curie temperature and a good resistance vs temperature. Bismuth titanate (Bi(4)Ti(3)O(12)) powders can be prepared using different methods, depending if the creation will be film coating or ceramics. The structure and properties of bismuth titanate materials show a significance dependence on the applied synthesis method. In this review paper, we made an attempt to give an approach to analyszing the structure, synthesis methods and properties of bismuth titanate ferroelectrics materials.

Study of Ti-modified columbite route and the effect of lithium doping in 0.9PMN-0.1PT ceramics

The influence of lithium on the structural characteristics of PMN-PT ceramic was studied. The synthesis of PMN-PT powders using this precursor leads to the formation of high amount of perovskite phase. The insertion of Li(+) ions in B-site affects the microstructure because the rise in mass transport changes the mechanical characteristics of sintered ceramic. Higher values of K(m) and T(m) were gotten when lithium is inserted into perovskite phase. Secondary phase was found when lithium content increase beyond 1 mol%, besides the occurrence of transgranular fractures in sintered ceramic. Also, the additive acts increasing the relaxor behavior.

Dielectric properties of Na1-xLixNbO3 ceramics from powders obtained by chemical synthesis

Ultra-fine powders of Na1-xLixNbO3 (x=0; 0.06; 0.09; 0.12) were synthesized by the Polymeric Precursors Method. Such powders had their orthorhombic structures determined by X-ray diffraction and their surface area determined by BET isotherms (less than 10 m(2) g(-1)). Densification was followed by dilatometric study. The powders, calcined at 700 degrees C for 5 h, were sintered at 1290 degrees C during 2 h under ambient atmosphere with no application of extra pressure. The samples with relative densities higher than 95% were analyzed by impedance spectroscopy at room temperature, under a signal amplitude of 1 V-rms. Dielectric constants of about 180 and dielectric loss factor of about 0.03 were measured showing small dependence with frequency. The electrical properties were similar to those obtained for samples sintered by hot pressing. (C) 1999 Elsevier B.V. Limited and Techna S.r.l. All rights reserved.

Densification and electrical conductivity of fast fired manganese-doped ceria ceramics

Reactive pure and manganese-doped (5% and 10 at.%) ceria nanosized powders were prepared by the polymeric precursor technique. Physical properties of powder materials were studied by X-ray diffraction, nitrogen adsorption, and diffuse reflectance infrared Fourier transform spectroscopy. Characterization of powder compacts after fast firing at 1200 degrees C for 5 min was carried out by scanning electron microscopy and impedance spectroscopy measurements. The bulk apparent density of sintered pellets was determined for pellets of different compositions sintered at 1200 degrees C. A gradual decrease of the particle size occurs with increasing doping content. Relatively high values of apparent density were obtained after fast firing doped specimens at 1200 degrees C. DRIFT spectra evidence that a fraction of Mn ions was segregated onto particles surface. The electrical resistivity of sintered pellets reveals different mechanisms of conduction depending on the Mn content. (C) 2005 Elsevier B.V All rights reserved.

ANISOTROPY OF ELECTRICAL-PROPERTIES IN ALPHA-FE2O3 CERAMICS

Electrical conductivity and thermoelectric power measurements carried out in a heamatite ceramic showed a strong anisotropy in directions normal and parallel to the uniaxial pressing direction. This behaviour is similar to that verified in alpha-Fe2O3 single crystal. The results suggest that the extended structural defects, generated during sintering, disturb the magnetic order on the (001) planes of alpha-Fe2O3 and limit the mobility of n type carriers.