Thermostimulated sol-gel transition in suspensions of sulfate zirconium oxychloride

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Indirect determination of chloride and sulfate ions in alcohol fuel by capillary electrophoresis

A capillary zone electrophoresis method using indirect UV detection for the analysis of chloride and sulfate in alcohol fuel samples was developed. The anions were analyzed in less than 3 min using an electrolyte containing 10 mmol 1(-1) chromate and 0.75 mmol 1(-1) hexamethonium bromide (HMB) as electroosmotic flow modifier. Coefficients of variation were better than 0.6% for migration time (n = 10) and between 2.05 and 2.82% for peak area repeatabilities. Analytical curves of peak area versus concentration in the range of 0.065-0.65 mg kg(-1) for chloride and 0.25-4.0 mg kg(-1) for sulfate were linear with coefficients of correlation higher than 0.9996. The limits of detection for sulfate and chloride were 0.033 and 0.041 mg kg(-1), respectively. Recovery values ranged from 85 to 103%. The method was successfully applied for the quantification of sulfate and chloride in five alcohol fuel samples. The concentration of sulfate varied from 0.45 to 3.12 mg kg(-1). Chloride concentrations were below the method's LOD.

Rheological study of the thermoreversible sol-gel transition of sulfate modified zirconyl chloride aqueous sol

The sols prepared by mixing a ZrOCl2 acidified solution to a hot H2SO4 aqueous solutions were studied in order to clarify the mechanism of thermoreversible sol-gel transition observed in this system. The viscoelastic properties of these suspensions were analyzed during the sol-gel transition by dynamic rheological measurements and quasi-elastic light scattering. The rheological properties were correlated to mass fractal and nearly linear growth models, and percolation theory. The results evidence that the thermoreversible sol-gel transition in this system is due to the formation of a network of physically linked aggregates having fractal structure. The decrease of the SO42- contents in the initial solution leads to the decrease of the fractal dimensionality from 2.3 to 1.8, indicating a change of the kinetic mechanism of aggregate growth. Near the gel point these samples have the typical scaling expected from percolation theory. (C) 2004 Elsevier B.V. All rights reserved.

Microwave synthesis of calcium bismuth niobate thin films obtained by the polymeric precursor method

The crystal structure, surface morphology and electrical properties of layered perovskite calcium bismuth niobate thin films (CaBi2Nb2O9-CBN) deposited on platinum coated silicon substrates by the polymeric precursor method have been investigated. The films were crystallized in a domestic microwave and in a conventional furnace. X-ray diffraction and atomic force microscopy analysis confirms that the crystallinity and morphology of the films are affected by the different annealing routes. Ferroelectric properties of the films were determined with remanent polarization P-r and a drive voltage V-c of 4.2 mu C/cm(2) and 1.7 V for the film annealed in the conventional furnace and 1.0 mu C/cm(2) and 4.0 V for the film annealed in microwave furnace, respectively. A slight decay after 10(8) polarization cycles was observed for the films annealed in the microwave furnace indicating a reduction of the domain wall mobility after interaction of the microwave energy with the bottom electrode. (C) 2006 Elsevier Ltd. All rights reserved.

Study of the alkaline earth metals with 8-hydroxyquinolinate derivatives - Calcium complexes

Metal complexes of calcium with 5,7-dibromo, 7-iodo and 5-chloro-7-iodo-8-hydroxyquinolate were precipitated in aqueous ammonia and acetone medium, except for the solid state compound with 5,7-dichloro-8-hydroxyquinoline which hasn't been obtained under these conditions. The complexes obtained through the mentioned precipitation are Ca[(C9H4ONBr2)(2)](3).H2O, Ca[(C9H5ONI)(2)].2H(2)O and Ca[(C9H4ONICl)(2)].2.5H(2)O. Their intermediate from the thermal decomposition found through TG/DTA curves in air indicated the presence of different kinds of calcium carbonates related to the reversibility and crystalline structure, depending on the original compounds. The initial compounds and the intermediate from the thermal decomposition were also characterized through IR spectra and X-ray diffraction.

Vehicle influence on calcium hydroxide pastes diffusion in human and bovine teeth

The purpose of this study was to compare the pH and calcium ion liberation after use of calcium hydroxide pastes with different paste vehicles in human or bovine teeth. Ninety-two single-rooted human and bovine roots were used. The roots were instrumented and an external cavity preparation was performed. The roots were divided in to human and bovine groups. Each group was subdivided into four subgroups (SB) according to the vehicle:SB1, detergent; SB2, saline; SB3, polyethylenoglycol + camphorated paramonochlorophenol (Calen PMCC) and SB4, polyethylenoglycol + furacyn paramonochlorophenol (FPMC). Specimens were immersed into saline solution at 37 degrees C and after 7 and 14 days pH and calcium ion measurements were made. The results were analyzed by ANOVA and Tukey tests (P < 0.05). There was no statistical difference between bovine and human teeth in the pH analysis (P < 0.05), but bovine teeth provided larger calcium ion liberation than human teeth. Calen PMCC was statistically more effective for pH increase and calcium ion liberation in all analyses, followed by FPMC and saline. Detergent showed the lowest pH alterations and calcium ion liberation. The period of 14 days showed more calcium ionic liberation than the 7-day period.