Glass transitions and state diagram for freeze-dried pineapple

Glass transition temperature of freeze-dried pineapple conditioned by adsorption at various water activities at 25 degreesC was determined by differential scanning calorimetry (DSC). High moisture content samples corresponding to water activities higher than 0.9, obtained by liquid water addition, were also analysed. The DSC traces showed a well-visible shift in baseline at the glass transition temperature (T(g)). Besides, no ice formation was observed until water activity was equal to 0.75. For water activities lower than 0.88, the glass transition curve showed that T(g) decreased with increasing moisture content and the experimental data could be well-correlated by the Gordon-Taylor equation. For higher water activities, this curve exhibited a discontinuity, with suddenly increasing glass transition temperatures approaching a constant value that corresponds to the T(g) of the maximally freeze-concentrated amorphous matrix. The unfreezable water content was determined through melting enthalpy dependence on the sample moisture content.

Thermal behavior of copper(II) pseudohalide complexes containing bidentate amines

Pseudohalide complexes of copper(II) with aliphatic bidentate amines, [Cu(N-3)(2)(N,N-diEten)](2) 1, [Cu(NCO)(2)(N,N-diEten)](2) 2, [Cu(NCO)(2)(N,N-diMeen)](2) 3, [Cu(N-3)(NCS)(N,N'-diMeen)](2) 4 and [Cu(N-3)(NCO)(N,N-diMeen)](2) 5 (N,N-diEten=N,N-diethylethylenediamine; N,N-diMeen=N,N- dimethyl-ethylenediamine and N,N'-diMeen = N,N'-dimethylethylenediamine), were prepared, characterized and their thermal behavior was investigated by TG curves. According to thermal analysis and X-ray diffraction patterns all compounds decomposed giving copper(II) oxide as final product. The mechanisms of decomposition were proposed and an order of thermal stability was established.

Structure and crystallization of lanthanum fluorozirconate glasses

Glasses with compositions (1-x)ZrF4-xLnF(3), 0.2 less than or equal to x less than or equal to 0.4 and Ln = La or La, Eu have been synthesized and investigated using differential scanning calorimetry, X-ray diffraction, Raman scattering and Eu3+ optical spectroscopy. Single-phase polycrystalline lanthanum fluorozirconates with Zr/Ln ratio equal to 1, 2 and 3 have been investigated using the same techniques for comparison. The crystalline phases LnZrF(7), LnZr(2)F(11), LT-LnZr(3)F(15) (orthorhombic) and HT-LnZr(3)F(15) (trigonal) have been characterized in the recrystallized glasses and in samples spontaneously crystallized from the melt. Another phase has also been observed but remains undefined, the Raman scattering spectra of the vitreous samples are related to the vibration modes of [ZrF6] isolated octahedra, and of [ZrF7] and [ZrF8] structural units with bridging fluorine ions. The Eu3+ fluorescence data are related to a predominant local environment of the lanthanide ions in the glasses similar to that of the lanthanide in LnZrF(7).

Polymerization of photocurable commercial dental methacrylate-based composites - Photocalorimetry study

Due to their excellent aesthetics, photopolymers have been extensively used in several dentistry applications. However, several problems are reported, e.g. low mechanical and abrasion resistance, shrinkage during polymerization, etc. Properties of the final restorations are intrinsically related to the polymerization stage, which can be conveniently studied by photocalorimetry. In the present work the polymerization reaction and the filler content of different photocurable commercial dental methacrylate-based composites were studied by means of photocalorimetry and thermogravimetry, respectively. The results show that the values of curing rate, the heat of polymerization and the filler content vary significantly from one composite to another.

Influence of the precursor salts in the synthesis of CaSnO3 by the polymeric precursor method

CaSnO3 was synthesized by the polymeric precursor method, using different precursor salts as (CH3COO)(2)Ca. H2O, Ca(NO3)(2). 4H(2)O, CaCl2. 2H(2)O and CaCO3, leading to different results. Powder precursor was characterized using thermal analysis. Depending on the precursor different thermal behaviors were obtained. Results also indicate the formation of carbonates, confirmed by IR spectra. After calcination and characterization by XRD, the formation of perovskite as single phase was only identified when calcium acetate was used as precursor. For other precursors, tin oxide was observed as secondary phase.

Synthesis, spectral and thermal studies on pyrazolate-bridged palladium(II) coordination polymers

Synthesis, spectroscopic characterization and thermal behavior of pyrazolate-bridged palladium complexes [Pd(mu-Pz)(2)](n) (1), [Pd(mu-mPz)(2)](n) (2), [Pd(mu-dmPz)(2)](n) (3), [Pd(mu-IPz)(2)](n) (4) {pyrazolate (Pz(-)), 4-methylpyrazolate (mPz(-)), 3,5-dimethylpyrazolate (dmPz(-)), 4-iodopyrazolate (IPz(-))} have been described in this work. The exobidentate coordination mode of pyrazolato ligands in 1-4 was inferred on basis of IR spectroscopic evidences. TG investigations indicated that the introduction of substituents at the 4 position in the pyrazolyl moiety into coordination polymers do not affect significantly their thermal stability, whereas at the 3 and 5 position reduced the stability of the main chain. Metal palladium was the final product of the thermal decompositions, which was identified by X-ray powder diffraction.

Study of the thermomechanical and electrical properties of conducting composites containing natural rubber and carbon black

This work describes the preparation and characterization of composite materials obtained by the combination of natural rubber (NR) and carbon black (CB) in different percentages, aiming to improve their mechanical properties, processability, and electrical conductivity, aiming future applications as transducer in pressure sensors. The composites NR/CB were characterized through optical microscopy (OM), DC conductivity, thermal analysis using differential scanning calorimetry (DSC), dynamic mechanical thermal analysis (DMA), thermogravimetry (TGA), and stress-strain test. The electrical conductivity varied between 10(-9) and 10 S m(-1), depending on the percentage of CB in the composite. Furthermore, a linear (and reversible) dependence of the conductivity on the applied pressure between 0 and 1.6 MPa was observed for the sample with containing 80 wt % of NR and 20% of CB. (C) 2007 Wiley Periodicals, Inc.

Crystallization kinetic of fluoro-zirconate glasses by non-isothermal analysis

Fluoride glasses have been extensively studied due to their high transparency in the infrared wavelength. The crystallization kinetics of these systems has been studied using DTA and DSC techniques. Most of the experimental data is frequently investigated in terms of the Johnson-Mehl-Avrami (JMA) model in order to obtain kinetic parameters.In this work, DSC technique has been used to study the crystallization of fluorozirconate glass under non-isothermal conditions. It was found that JMA model was not fit to be applied directly to these systems, therefore, the method proposed by Malek has been applied and the Sestak-Berggren (SB) model seems to be adequate to describe the crystallization process.

Attainment of lead titanate - Through the thermal decomposition of coprecipitated 8-hydroxyquinolinate precursors

Crystalline PbTiO3 was obtained through the thermal decomposition of 8-hydroxyquinolinate of lead(II) and that of titanium(IV), which was monitored by TG/DTG/DTA under different atmospheric conditions and with varying heating rates. The compound was prepared from adding 8-hydroxyquinoline solution in the solution of metallic ions Pb(II):Ti(IV) (1:1) Linder constant stirring at 3degreesC, having the pH adjusted to 10. The results of these investigations show that different thermal behavior related to the precursor occurred and also the consequent formation of residues which have different crystallinities. No carbonate residues from the thermal decomposition could be determined by XRD and IR. Only PbTiO3 was observed and confirmed by DSC at 470degreesC, temperature lower than the tetragonal-cubic transition.

Thermal behavior of the Cu-10 mass%Al and Cu-10 mass%Al-4 mass%Ag alloys

The thermal behavior of the Cu-10 mass%Al and Cu-10 mass% Al-4 mass%Ag alloys was studied using classical differential thermal analysis (DTA), optical microscopy (OM) and X-ray diffractometry (XRD). The DTA curves were obtained for annealed and quenched samples. The results indicated that the presence of silver introduces new thermal events, associated to the formation of a silver-rich phase, to the shift of the equilibrium concentration to higher A1 contents and to the decomposition of the silver-rich phase in the same temperature range of the beta(1) phase decomposition.

Electric characterization of a hybrid composite based on POMA/P(VDF- TrFE)/Zn2SiO4 : Mn using impedance spectroscopy

Understanding the microscopic origin of the dielectric properties of disordered materials has been a challenge for many years, especially in the case of samples with more than one phase. For polar dielectrics, for instance, the Lepienski approach has indicated that the random free energy barrier model of Dyre must be extended. Here we analyse the dielectric properties of a polymer blend made up with the semiconducting poly(o-methoxyaniline) and poly( vinylidene fluoride-trifluorethylene) POMA/P(VDF-TrFE), and of a hybrid composite of POMA/P(VDF-TrFE)/Zn2SiO4:Mn. For the blend, the Lepienski model, which takes into account the rotation or stretching of electric dipoles, provided excellent fitting to the ac impedance data. Because two phases had to be assumed for the hybrid composite, we had to extend the Lepienski model to fit the data, by incorporating a second transport mechanism. The two mechanisms were associated with the electronic transport in the polymeric matrix and with transport at the interfaces between Zn2SiO4: Mn microparticles and the polymeric matrix, with the relative importance of the interfacial component increasing with the percentage of Zn2SiO4: Mn in the composite. The analysis of impedance data at various temperatures led to a prediction of the theoretical model of a change in morphology at 190 +/- 40 K, and this was confirmed experimentally with a differential scanning calorimetry experiment.

Photo luminescence: A probe for short, medium and long-range self-organization order in ZrTiO4 oxide

Photoluminescent disordered ZrTiO4 powders were obtained by the polymeric precursor soft-chemical method. This oxide system (ordered and disordered) was characterized by photoluminescence, Raman spectroscopy, X-ray diffraction, differential scanning calorimetry and UV vis absorption experiments. The UV absorption tail formation in the disordered oxides was related to the diminution of optical band gap. In the disordered phase, this oxide displayed broad band photoluminescence caused by change in coordination number of titanium and zirconium with oxygen atoms. The gap decreased from 3.09 eV in crystalline oxide to 2.16 eV in disordered oxide. The crystalline oxide presented an orthorhombic alpha-PbO2-type structure in which Zr4+ and Ti4+ were randomly distributed in octahedral coordination polyhedra with oxygen atoms. The amorphous-crystalline transition occurred at almost 700 degrees C, at which point the photoluminescence vanished. The Raman peak at close to 80-200 cm(-1) indicated the presence of locally ordered Ti-O-n and Zr-O-n polyhedra in disordered photoluminescent oxides. (c) 2006 Elsevier B.V. All rights reserved.

Thermogenic activity of growth hormone transgenic mice

The objective was to determine the effect of a mouse metallothionein/bovine growth hormone transgene on resting metabolic rate (RMR), cold-induced thermogenesis, and beta-agonist stimulated nonshivering thermogenesis in mice. Non-transgenic littermates were used as controls. Open-circuit indirect calorimetry was used to assess RMR and cold-induced thermogenesis in 64 mice. Air temperature in the chamber was set at 31 degrees C for RMR and was decreased to 28, 25, 21, or 17 degrees C to determine cold-induced thermogenesis. Response to the beta-agonist isoproterenol was evaluated by monitoring changes in colonic temperature of 34 mice upon injection of the drug or saline. Despite the fact that RMR tended to be lower in transgenics than in nontransgenics, at 31 degrees C transgenic mice were able to regulate colonic temperature at the same level as nontransgenics, but colonic temperature decreased in transgenics relative to nontransgenics as air temperature was reduced. For each degree decrease in air temperature between 31 and 17 degrees C, nontransgenic mice increased heat production by 1.03 +/- .10 watt/kg, whereas transgenic mice increased it by only .56 +/- .08 watt/kg, indicating that the thermogenic response of transgenics to cold was inferior. The magnitude of the maximal increase in colonic temperature after isoproterenol injection was similar for both groups, but the response was slower in transgenics. We suggest that lean body mass and substrate availability for shivering thermogenesis are reduced in transgenics relative to total body weight, and that they allow colonic temperature to decrease to conserve energy.

Thermogravimetric investigations during the synthesis of silica-based MCM-41

MCM-41 material was synthesized starting from hydrogel containing colloidal fumed silica, sodium silicate, cetyltetramethylammonium bromide (CTMABr) as surfactant, and distilled water as solvent. These reactants were mixed to obtain a gel with the following composition: 4SiO(2):1Na(2)O:1CTMABr:200H(2)O. The hydrogel with pH=14 was hydrothermally treated at 100 degreesC, for 4 days. Each day, the pH was measured, and then adjusted to 9.5-10 by using 30% acetic acid solution. Thermogravimetry was the main technique, which was used to monitor the participation of the surfactant on the MCM-41 nanophase, being possible to determine the temperature ranges relative to water desorption as well as the surfactant decomposition and silanol condensation.

Scandium fluorophosphate glasses: a structural approach

A systematic investigation on glass formation in the ternary system InF3-BaF2-[Sc(PO3)(3)](n) has been carried out. Scandium polyphosphate [Sc(PO3)(3)](n) has been used as a third component in order to investigate the possibilities of obtaining new stable glasses. The above long-chain polyphosphate has been prepared using a specially elaborated cryo-technique, which allowed the preparation of high-purity product. Stable ternary compositions have been obtained within the compositions range (in mol%): 5-75 InF3, 0-80% BaF2, 0-50% [Sc(PO3)(3)](n). Glasses were characterized by Differential Scanning Calorimetry, vibrational spectroscopy (Raman) and P-31 NMR. Structural features for the glass were put forward. Isolated P(O,F)4 groups or fluoroindated metaphosphate units could be identified depending on glass compositions. (C) 2002 Academie des sciences / Editions scientifiques et medicales Elsevier SAS.