Increasing the wear resistance of molds for injection of glass fiber reinforced plastics

Abrasion by glass fibers during injection molding of fiber reinforced plastics raises new challenges to the wear performance of the molds. In the last few decades, a large number of PVD and CVD coatings have been developed with the aim of minimizing abrasion problems. In this work, two different coatings were tested in order to increase the wear resistance of the surface of a mold used for glass fiber reinforced plastics: TiAlSiN and CrN/CrCN/DLC. TiAlSiN was deposited as a graded monolayer coating while CrN/CrCN/DLC was a nanostructured coating consisting of three distinct layers. Both coatings were produced by PVD unbalanced magnetron sputtering and were characterized using scanning electron microscopy (SEM) provided with energy dispersive spectroscopy (EDS), atomic force microscopy (AFM), micro hardness (MH) and scratch test analysis. Coating morphology, thickness, roughness, chemical composition and structure, hardness and adhesion to the substrate were investigated. Wear resistance was characterized through industrial tests with coated samples and an uncoated reference sample inserted in a feed channel of a plastic injection mold working with 30 wt.% glass fiber reinforced polypropylene. Results after 45,000 injection cycles indicate that the wear resistance of the mold was increased by a factor of 25 and 58, by the TiAlSiN and CrN/CrCN/DLC coatings, respectively, over the uncoated mold steel.

Halting the fuse discharge propagation using optical fiber microwires

We report and analyze the halting of the fuse effect propagation in optical fiber microwires. The increase of the mode field diameter in the tapered region decreases the optical intensity resulting in the extinction of the fuse effect. This fiber element presents a low insertion loss and can be introduced in the optical network in order to protect the active equipment from the damage caused by the fuse effect.

Halting the fuse discharge propagation Using optical fiber microwires

We report and analyze the halting of the fuse effect propagation in optical fiber microwires. The increase of the mode field diameter in the tapered region decreases the optical intensity resulting in the extinction of the fuse effect. This fiber element presents a low insertion loss and can be introduced in the optical network in order to protect the active equipment from the damage caused by the fuse effect. (C) 2012 Optical Society of America

High-performance flexible hybrid field-effect transistors based on cellulose fiber paper

IEEE Electron Device Letters, VOL. 29, NO. 9,

Castor fiber na gruta do Caldeirão Existência, distribuição e extinção do castor em Portugal

Beaver only had been found in Portugal in a Chalcolithic locality, the Vila Nova de S. Pedro castrum. It has now been idenrified in the Upper Paleolithic (Solurrean) from Gruta do Caldeirão, near Tomar. The species has been found recently at «Gruta do Almonda»; 4 teeth were collected in bed C, older than a Solutrean sequence (see Anexo for details). The species seems to have been rare, as it was also the case with portuguese miocene Castoridae Enroxenomys minutus and Chalicomys jaegeri. If account is taken of the presence in the Middle Ages until Castille of words meaning beaver (related to the popular latin Fiber/Biber), it is obvious that these animals still existed then. Such nouns were largely predominant over the rather erudite larin (greek derived) words as Castor, -óris and derived ones, as it could be expected. This allowed us to recognize that veiro should be the corresponding word with Fiber affinities in archaic portuguese. It was previously supposed to mean only expensive furs then imported into Portugal. Indeed it was also a zoonym. Anyway, beaver should be scarce by XIIIth century since it is not included in the quite detailed price list imposed by the «Lei da Almotaçaria» from December 26, 1253 (see Quadro II). Toponyms in veiro and derived words (fig. 2; Quadro III) (plural, feminines, diminutives, inhabited places) give a restrictive view of the Middle Age distribution. Some of them are certainly older than Portugal itself (first half of XIIth century); others existed by the XIVth century but were probably older. Some rare toponyms seem to be derived from rhe erudite latin Castor, -óris. Nothing suggests that these words were still in use as zoonyms during the Middle Ages. All toponyms are located in regions near rivers and other freshwaters ecologically suitable for beavers, so wecan approximately retrace irs former, Middle Age distribution in Portugal (fig. 2; Quadro III). Most of them are located in the Center-West and Northwest of Portugal, with a suitable c1imate (rainfall in general over 800 milimeters per year); the only sure geographical exception is Veiros, in Alto Alentejo province, in a region with comparable precipitations and less dry climare conditions than most of the territories South of the Tagus. There are less and less of these toponyms towards the South and the inner part of the country, and they are enrirely lacking in ali drier regions from Trás-os-Montes, Beira, Alentejo beyond Tagus' basin, and in Algarve. Nothing suggests beavers lived there, No pose-medieval toponym is known, nor any reference after middle XVth century. No such locality was at, or close by to, any frontier. Hence the hypothesis of veiro (e: al.) as meaning but points where expensive furs(supposedly known as veiros in general but without clearly saying from what animal they were obtained from) is to be discarded. During the Middle Ages, beaver distribution concerned all the main river basins from Minho to Tagus ones. Quice racefied in the XIIIth, the beavers may have disappeared from Portugal during the XVth century. Ecological requirements restricted their former distribution. Vulnerability to natural causes (i.e., severe drought) and to human pressure may have accounted heavily for this species extinction. Last (1446) reference for Portugal known to us suggests the species was by then almost extinct.

A case study undertaken recycling & reuse of glass fiber reinforced thermoset polumer wastes of composite materials industry

Glass fibre-reinforced plastics (GFRP) have been considered inherently difficult to recycle due to both: crosslinked nature of thermoset resins, which cannot be remoulded, and complex composition of the composite itself. Presently, most of the GFRP waste is landfilled leading to negative environmental impacts and supplementary added costs. With an increasing awareness of environmental matters and the subsequent desire to save resources, recycling would convert an expensive waste disposal into a profitable reusable material. In this study, efforts were made in order to recycle grinded GFRP waste, proceeding from pultrusion production scrap, into new and sustainable composite materials. For this purpose, GFRP waste recyclates, were incorporated into polyester based mortars as fine aggregate and filler replacements at different load contents and particle size distributions. Potential recycling solution was assessed by mechanical behaviour of resultant GFRP waste modified polymer mortars. Results revealed that GFRP waste filled polymer mortars present improved flexural and compressive behaviour over unmodified polyester based mortars, thus indicating the feasibility of the GFRP industrial waste reuse into concrete-polymer composite materials.

Bioinspired polyethersulfone-based hollow fiber membranes as the scaffolds in renal assist device for protein-bound toxins removal from blood

Dissertation for obtaining the Master degree in Membrane Engineering

Fiber functionalization for biomedical applications

Deep-eutectic solvents (DES) are considered novel renewable and biodegradable solvents, with a cheap and easy synthesis, without waste production. Later it was discovered a new subclass of DES that even can be biocompatible, since their synthesis uses primary metabolites such as amino acids, organic acids and sugars, from organisms. This subclass was named natural deep-eutectic solvents (NADES). Due to their properties it was tried to study the interaction between these solvents and biopolymers, in order to produce functionalized fibers for biomedical applications. In this way, fibers were produced by using the electrospinning technique. However, it was first necessary to study some physical properties of NADES, as well as the influence of water in their properties. It has been concluded that the water has a high influence on NADES properties, which can be seen on the results obtained from the rheology and viscosity studies. The fluid dynamics had changed, as well as the viscosity. Afterwards, it was tested the viability of using a starch blend. First it was tested the dissolution of these biopolymers into NADES, in order to study the viability of their application in electrospinning. However the results obtained were not satisfactory, since the starch polymers studied did not presented any dissolution in any NADES, or even in organic solvents. In this way it was changed the approach, and it was used other biocompatible polymers. Poly(ethylene oxide), poly(vinyl alcohol) and gelatin were the others biopolymers tested for the electrospinning, with NADES. All polymers show good results, since it was possible to obtain fibers. However for gelatin it was used only eutectic mixtures, containing active pharmaceutical ingredients (API’s), instead of NADES. For this case it was used mandelic acid (antimicrobial properties), choline chloride, ibuprofen (anti-inflammatory properties) and menthol (analgesic properties). The polymers and the produced fibers were characterized by scanning electron microscope (SEM), Transmission electron microscopy (TEM) and Fourier transform infrared spectroscopy (FTIR). With the help of these techniques it was possible to conclude that it was possible to encapsulate NADES within the fibers. Rheology it was also study for poly(ethylene oxide) and poly(vinyl alcohol), in a way to understand the influence of polymer concentration, on the electrospinning technique. For the gelatin, among the characterization techniques, it was also performed cytotoxicity and drug release studies. The gelatin membranes did not show any toxicity for the cells, since their viability was maintained. Regarding the controlled release profile experiment no conclusion could be drawn from the experiments, due to the rapid and complete dissolution of the gelatin in the buffer solution. However it was possible to quantify the mixture of choline chloride with mandelic acid, allowing thus to complete, and confirm, the information already obtained for the others characterization technique.

Age related changes in the elastic fiber system of the interfoveolar ligament

In order to evaluate age related changes of the elastic fiber system in the interfoveolar ligament, we studied the deep inguinal ring from 33 male cadavers aged from stillborn to 76 years. Selective and alternated staining methods for elastic fibers were performed to differentiate oxytalan, elaunin, and mature elastic fibers. We confirmed quantitative changes of the elastic fiber system with aging. There was a significant and progressive reduction of the oxytalan fibers (responsible for tissue resistance) and a significant increment in the mature elastic and elaunin fibers (responsible for tissue elasticity). Furthermore, there were structural changes in the thickness, shortness and curling of these mature elastic fibers. These changes induced loss of the elastic fiber function and loss of the interfoveolar ligament compliance. These factors predispose individuals to the development of indirect inguinal hernias that frequently emerge in adults and aged individuals, especially above the fifth decade.

Dynamics of serotonergic neurons revealed by fiber photometry

This work was developed in the context of the MIT Portugal Program, area of Bioengineering Systems, in collaboration with the Champalimaud Research Programme, Champalimaud Center for the Unknown, Lisbon, Portugal. The project entitled Dynamics of serotonergic neurons revealed by fiber photometry was carried out at Instituto Gulbenkian de Ciência, Oeiras, Portugal and at the Champalimaud Research Programme, Champalimaud Center for the Unknown, Lisbon, Portugal

High performance fiber reinforced concrete for the shear reinforcement: experimental and numerical research

High performance fiber reinforced concrete (HPFRC) is developing rapidly to a modern structural material with unique rheological and mechanical characteristics. Despite applying several methodologies to achieve self15 compacting requirements, some doubts still remain regarding the most convenient strategy for developing a HPFRC. In the present study, an innovative mix design method is proposed for the development of high17 performance concrete reinforced with a relatively high dosage of steel fibers. The material properties of the developed concrete are assessed, and the concrete structural behavior is characterized under compressive, flexural and shear loading. This study better clarifies the significant contribution of fibers for shear resistance of concrete elements. This paper further discusses a FEM-based simulation, aiming to address the possibility of calibrating the constitutive model parameters related to fracture modes I and II.

Influence of oxygen plasma treatment parameters on poly(vinylidene fluoride) electrospun fiber mats wettability

Electrospun poly(vinylidene fluoride) (PVDF) fiber mats find applications in an increasing number of areas, such as battery separators, filtration and detection membranes, due to their excellent properties. However, there are limitations due to the hydrophobic nature and low surface energy of PVDF. In this work, oxygen plasma treatment has been applied in order to modify the surface wettability of PVDF fiber mats and superhydrophilic PVDF electrospun membranes have been obtained. Further, plasma treatment does not significantly influences fiber average size (~400 ± 200 nm), morphology, electroactive -phase content (~80-85%) or the degree of crystallinity (Xc of 42 ± 2%), allowing to maintain the excellent physical-chemical characteristics of PVDF. Plasma treatment mainly induces surface chemistry modifications, such as the introduction of oxygen and release of fluorine atoms that significantly changes polymer membrane wettability by a reduction of the contact angle of the polymer fibers and an overall decrease of the surface tension of the membranes.

Erratum: Influence of oxygen plasma treatment parameters on poly(vinylidene fluoride) electrospun fiber mats wettability

Electrospun poly(vinylidene fluoride) (PVDF) fiber mats find applications in an increasing number of areas, such as battery separators, filtration and detection membranes, due to their excellent properties. However, there are limitations due to the hydrophobic nature and low surface energy of PVDF. In this work, oxygen plasma treatment has been applied in order to modify the surface wettability of PVDF fiber mats and superhydrophilic PVDF electrospun membranes have been obtained. Further, plasma treatment does not significantly influences fiber average size (~400 ± 200 nm), morphology, electroactive -phase content (~80-85%) or the degree of crystallinity (Xc of 42 ± 2%), allowing to maintain the excellent physical-chemical characteristics of PVDF. Plasma treatment mainly induces surface chemistry modifications, such as the introduction of oxygen and release of fluorine atoms that significantly changes polymer membrane wettability by a reduction of the contact angle of the polymer fibers and an overall decrease of the surface tension of the membranes.

Mechanical performance of natural fiber-reinforced composites for the strengthening of masonry

The growing concerns regarding the environmental impact generated by the use of inorganic materials in different fields of application increased the interest towards products based on materials with low environmental impact. In recent years, researchers have turned their attention towards the development of materials obtained from renewable sources, easily recoverable or biodegradable at the end of use. In the field of civil structures, a few attempts have been done to replace the most common composites (e.g. carbon and glass fibers) by materials less harmful to the environment, as natural fibers. This work presents a comprehensive experimental research on the mechanical performance of natural fibers for the strengthening of masonry constructions. Flax, hemp, jute, sisal and coir fibers have been investigated both from physical and mechanical points of view. The fibers with better performance were tested together with three different matrices (two of organic nature) in order to produce composites. These experimental results represent a useful database for understanding the potentialities of natural fibers as strengthening systems.

Effect of chemical and plasma DBD treatments on pseudostem plantain fiber properties

Las fibras del seudotallo de plátano (FSP) fueron modificadas mediante epiclorhidrina (EP), anhídrido acético (AA), y su combinación (AA_EP), y con plasma a tres descargas de barrera dieléctrica (DBD) 1, 3 y 6 kW min m-2. Las FSP tratadas y sin tratar fueron caracterizadas mediante espectroscopia infrarroja por la transformada de Fourier (FT-IR), termogravimetría (TGA), microscopía electrónica de barrido (SEM) y pruebas mecánicas de tensión y de humectabilidad. Los espectros FT-IR, las micrografías SEM, y el análisis TGA indicaron pérdidas de lignina, hemicelulosa, impurezas y ceras. Estos efectos en conjunto con las reacciones de grupos OH y -C-C-, con los tratamientos químicos y de plasma respectivamente, incrementaron la hidrofobicidad de las FSP tratadas. Los tratamientos químicos produjeron reacciones de esterificación, eterificación y entrecruzamiento de los grupos OH libres en las FSP, lo que hizo que mostraran mayor rigidez que las expuestas al plasma. Las micrografías SEM mostraron que las FSP expuestas al plasma quedaron con superficie más irregular y rugosa que la de las FSP tratadas químicamente. La humectabilidad de las fibras, medida mediante pruebas de ángulo de contacto, se redujo como consecuencia de ambos tratamientos, característica importante para un relleno en los materiales compuestos.