Resumo:
利用低速高电荷态Xeq+和Pbq+离子对在蓝宝石衬底上生长的GaN晶体膜样品进行辐照,并利用X射线光电子能谱(XPS)对样品表面化学组成和元素化合态进行了分析.结果表明,高电荷态离子对样品表面有显著的刻蚀作用;经高电荷态离子辐照的GaN样品表面氮元素贫乏而镓元素富集;随着入射离子剂量和所携带电荷数的增大,Ga—Ga键相对含量增大;辐照后,GaN样品中Ga—Ga键对应的Ga3d5/2电子的束缚能偏小,晶格损伤使内层轨道电子束缚能向低端方向偏移.
Resumo:
The surface structure of the iron oxide nanoparticles obtained by the co-precipitation method has been investigated, and a thin layer of alpha-FeOOH absorbed on surface of the nanoparticle is confirmed by analyses of Fourier transform infrared (FTIR), X-ray photoelectron spectra (XPS) and surface photovoltage spectroscopy (SPS). After annealed at 400 degrees C, the alpha-FeOOH can be converted to gamma-Fe2O3. The simple-annealed procedure resulted in the formation of Fe3O4@gamma-Fe2O3 core/shell structure with improved stability and a higher magnetic saturation value, and also the simple method can be used to obtain core/shell structure in other similar system.
Resumo:
By using a novel high-pressure, high-temperature method, perovskite oxides of La1-xNaxTiO3 (x = 0.05, 0.1-0.8) with mixed valence state were synthesized. XRD analysis shows a cubic cell for the samples. Cell volumes of the samples with 0.1 less than or equal to x less than or equal to 0.5 decreases as x increases, and the cell Volume for x = 0.05 is smaller than that for x = 0.1. XPS of surface and EPR measurements indicate that Ti ions are of mixed valence of +3 and +4 and that A-cations vacancies exist in the samples. As x increases, the amount of Ti3+ ions decreases and the amount of A-cations vacancies increases. The valence state of Ti ions can be altered by changing both pressure and temperature. (C) 2000 Elsevier Science B.V. All rights reserved.
Resumo:
Two series of layered mixed oxides La4BaCu5-xMxO13+lambda(M = Mn, Co, x = 0 similar to 5) were prepared and characterized by means of XRD, XPS, O-2-TPD and chemical analysis. The results show that their structures are 5-layered ABO(3) perovskite, and the XPS and O-2-TPD investigation confirms that there exists synergistic effect between Cu ion and M when M ion is doped into the lattice of La4BaCu5O13+lambda,, and the synergistic effect between Mn and Cu is stronger than that of Cu-Co.
Resumo:
X-ray photoelectron spectroscopy and mass spectrometry have been used to study the ten alpha-Amino Acids. The chemical shiftss of N-1s electron binding energy have been explained by means of the difference in the hydrocarbon group of amino acids. The influence of the hydrocarbon group on NH2 has been disscussed using the XPS and MS results.
Resumo:
The film by tetraphenylporphyrin((TPP)H-2) vapor deposition on iron was investigated by means of XPS, SEM and visible spectroscopy. N(1s) binding energy characteristic of(TPP)H-2 was gained directly from the deposited samples. N(1s) binding energy of the surface was greatly changed after the deposited sample was washed with solvent. It is indicated that the deposited film is composed of an outer-layer of physically adsorbed (TPP)H-2, and an inner-layer of chemically modified (TPP)H-2.
Resumo:
Self-assembled monolayers of 1-teradecanethiol on gold were characterized by means of FTIR-ATR measurements, XPS and contact angle measurements. Linear dichroism measurements using FTIR-ATR are used to estimate the orientation of the alkyl chains. An equation for calculating the orientation angles of the alkyls chains was deduced. (C) 1998 Elsevier Science Limited. All rights reserved.
Resumo:
A Co(salen)-Nafion modified electrode was prepared by immersing a glassy carbon electrode coated with the Nafion film into the aqueous solution with saturated Co(salen), The modified electrode showed a stable electrochemical reaction of Co(salen) at about 0 V(vs, SCE), The result of XPS indicated the valence of cobalt in Co(salen) changes from +2 before to +3 after Co(salen) enters the Nafion film, It is due to forming axis coordination of cobalt with sulfonic group in Nafion film, It was found that the mode of electron transfer in Co(salen)-Nafion modified electrode was controlled by physical diffusion and electron hopping, It was also found that the modified electrode could catalyze the reduction of O-2 to H2O2. The real catalyst may be the adduct of Co-I(salen) and O-2.
Resumo:
The mixed oxides LaNiO3, La0.1Sr0.9NiO3, La2NiO4 and LaSrNiO4 were prepared and used as catalysts for the direct decomposition of NO. The catalysts were characterized by means of XRD, XPS, O-2-TPD, NO-TPD and chemical analysis. By comparing the physico-chemical properties and catalytic activity for NO decomposition, a conclusion could be drawn as follows. The direct decomposition of NO over perovskite and related mixed oxide catalysts follows a redox mechanism. The lower valent metal ions Ni2+ and disordered oxygen vacancies seem to be the active sites in the redox process. The oxygen vacancy plays an important role favorable for the adsorption and activation of NO molecules on one hand and on the other hand for increasing the mobility of lattice oxygen which is beneficial to the reproduction of active sites. The presence of oxygen vacancies is one of the indispensable factors to give the mixed oxides a steady activity for NO decomposition.
Resumo:
The redox potential, surface composition and oxygen species of a series of complex oxides LaMn1-xFexO3 (x=0-1) having perovskite structure (ABO(3)) have been investigated by means of XI'S. The variation of binding energies referring to Mn2p and Fe 2p under different treatment offerred an obvious evidence of redox between Mn and Fe, which could be expressed as Mn4+ + Fe(3-delta)+ Mn(4-delta)+ Fe3+ Feat Through computer fit three kinds of adsorbed oxygen species (O-I, O-II, O-III) have been evaluated based on the XPS spectra of O1s. From the variation of contents of different oxygen species, it could be concluded that. the redox occuring in the surface might be related with the adsorbed oxygen species O-I and O-II, furthermore the possibility of transfer of electron between adsorption site and oxygen was also discussed.
Resumo:
The composition and structures of Li-Ti-La mixed oxides as well as their catalytic activity for methane oxidative coupling have been studied by means of XRD XPS, IR, SEM and so on. The results indicate that by changing x value in Li-La1-xTixO2 oxides phas
Resumo:
The type of oxygen species in perovskite-type oxides LaMnyCo1-yO3 (y = 0.0, 0.1, 0.3, 0.5, 0.7, 0.9, 1.0) has been studied by means of XRD, XPS and TPD. The catalytic activity in ammonia oxidation was also investigated. It was found that there were three desorption peaks in TPD curve corresponding to three types of oxygen species (alpha, beta, beta'). The desorption temperatures were 293 K less-than-or-equal-to T(alpha) less-than-or-equal-to 773 K, 773 K less-than-or-equal-to T(beta) less-than-or-equal-to K and T(beta') greater-than-or-equal-to 1073 K respectively. The relationship among the composition, structure and the catalytic property of.the catalyst was correlated and could be explainned with a model based on solid defect reaction and the interaction between Co and Mn ions. The adsorption strength and quantity of a oxygen are proportional to the catalytic activity. The, result indicates that the synergetic effect between B-site ions seems to the benefit of the ammonis oxidation reaction.
Resumo:
The electrochemically polymerized azure A film electrode was firstly reported in this paper. A quasi-reversible electrode processes of myoglobin with the formal heterogeneous electron transfer rate constant (k(sh)) of 1.73 x 10(-4) cm.s-1 at the polymerized azure A modified electrode have been achieved using in-situ UV-visible spectroelectrochemistry. The adsorption of myoglobin on the polymerized azure A film electrode surface was confirmed by XPS. With simultaneously studying of cyclic voltammetry and in-situ cyclic voltabsorptometry, the attribution of the voltammetry responses of myoglobin at the film electrode has been studied. The mechanism for the heterogeneous electron transfer of myoglobin at the polymerized azure A film modified electrode has been proposed as well.
Resumo:
The inhibitory effect of 2,3,5-triphenyl-2H-tetrazolium chloride (TTC) and 2,4,6-tri(2-pyridyl)-s-triazine (TPT) molecules on the corrosion of mild steel in 1 mol/L HCl and microcosmic inhibitory mechanism were investigated by X-ray photoelectron spectroscopy and ellipsometry. XPS results showed that C Is and N Is peaks of TTC, C Is and N Is peaks of TPT and their integral areas were obtained, which suggested the layer of the inhibitors (TTC or TPT) should have effectively protected the mild steel surface from the corrosion; and the depression from the inhibitors for the corrosion of mild steel surface was studied using ellipsometry combined with potentiodynamic polarization and the phasic difference was gained, which displayed the inhibitory coverage of the inhibitors formed.