Preparation and characterization of composites from starch with sugarcane bagasse nanofibres

This paper reports on the results of using unbleached sugar cane bagasse nanofibres (average diameter 26.5 nm; aspect ratio 247 assuming a dry fibre density of 1,500 kg/m3) to improve the physico-chemical properties of starch-based films. The addition of bagasse nanofibres (2.5 to 20 wt%) to modified potato starch (i.e. soluble starch) reduced the moisture uptake by up to 17 % at 58 % relative humidity. The film’s tensile strength and Young’s modulus increased by up to 100 % (3.1 to 6.2 MPa) and 300 % (66.3 to 198.3 MPa) respectively with 10 and 20 wt% fibre addition. However, the strain at yield dropped by 50 % for the film containing 10 wt% fibre. Models for composite materials were used to account for the strong interactions between the nanofibres and the starch matrix. The storage and loss moduli as well as the glass transition temperature (Tg) obtained from dynamic mechanical thermal analysis, were increased with the starch-nanofibre films indicating decreased starch chain mobility due to the interacting effect of the nanofibres. Evidence of the existence of strong interactions between the starch matrix and the nanofibres was revealed from detailed Fourier transform infra-red and scanning electron microscopic evaluation.

Wood density : a tool to find complementary species for the design of mixed species plantations

The successful establishment and growth of mixed-species forest plantations requires that complementary or facilitatory species be identified. This can be difficult in many tropical areas because the growth characteristics of endemic species are often unknown, particularly when grown at potentially higher densities in plantations than in natural forests. Here, we investigate whether wood density is a useful and readily accessible trait for choosing complementary species for mixed species plantations. Wood density represents the carbon investment per unit volume of stem with a trade-off generally found between fast (low wood density) and slow (high wood density) growing species. To do this, we use data collected from 18 highly diverse mixed species plantations (4–23 mostly native species) aged from 6 to 11 years at the time of data collection located on Leyte Island, Philippines. We found significant negative correlations between wood densities and the height of the most abundant species, as well as with measures of overall stand growth and tree diameter size distribution. Not only do species with denser woods have slower growth rates, but also mixed-species plantations with higher average wood density and higher stem density were also less productive, at least in these young plantations. Similarly, stands with a high diversity in wood densities were less productive. There is growing interest in making greater use of native multi-species mixtures in smallholder and community planting programs in the tropics, and our results show databases of wood density values may help improve their design. In the early development stages of plantations, canopy closure and rapid height growth are usually key silvicultural targets, and wood density values can predict the rapid height development of species. If plantations are being grown for the livelihood of small landholders then the best target is to choose some species with different wood densities. This allows an early harvest of low-wood density species for early income, and will also reduce competition for slower growing trees with higher wood densities for later income generation.

Comparing the effectiveness of education and technology in reducing wood smoke pollution: A field experiment

This study describes a field experiment assessing the effectiveness of education and technological innovation in reducing air pollution generated by domestic wood heaters. Two-hundred and twenty four households from a small regional center in Australia were randomly assigned to one of four experimental conditions: (1) Education only – households received a wood smoke reduction education pack containing information about the negative health impacts of wood smoke pollution, and advice about wood heater operation and firewood management; (2) SmartBurn only – households received a SmartBurn canister designed to improve combustion and help wood fires burn more efficiently, (3) Education and SmartBurn, and (4) neither Education nor SmartBurn (control). Analysis of covariance, controlling for pre-intervention household wood smoke emissions, wood moisture content, and wood heater age, revealed that education and SmartBurn were both associated with significant reduction in wood smoke emissions during the post-intervention period. Follow-up mediation analyses indicated that education reduced emissions by improving wood heater operation practices, but not by increasing health risk perceptions. As predicted, SmartBurn exerted a direct effect on emission levels, unmediated by wood heater operation practices or health risk perceptions.

“This is not a burning issue for me”: How citizens justify their use of wood heaters in a city with a severe air pollution problem

Although wood smoke pollution has been linked to health problems, wood burning remains a popular form of domestic heating in many countries across the world. In this paper, we describe the rhetoric of resistance to wood heater regulation amongst citizens in the regional Australian town of Armidale, where wood smoke levels regularly exceed national health advisory limits. We discuss how this is related to particular sources of resistance, such as affective attachment to wood heating and socio-cultural norms. The research draws on six focus groups with participants from households with and without wood heating. With reference to practice theory, we argue that citizen discourses favouring wood burning draw upon a rich suite of justifications and present this activity as a natural and traditional activity promoting comfort and cohesion. Such discourses also emphasise the identity of the town as a rural community and the supposed gemeinschaft qualities of such places. We show that, in this domain of energy policy, it is not enough to present ‘facts’ which have little emotional association or meaning for the populace. Rather, we need understand how social scripts, often localised, inform identity and practice.

The affect heuristic and public support for three types of wood smoke mitigation policies

This study applied the affect heuristic model to investigate key psychological factors (affective associations, perceived benefits, and costs of wood heating) contributing to public support for three distinct types of wood smoke mitigation policies: education, incentives, and regulation. The sample comprised 265 residents of Armidale, an Australian regional community adversely affected by winter wood smoke pollution. Our results indicate that residents with stronger positive affective associations with wood heating expressed less support for wood smoke mitigation policies involving regulation. This relationship was fully mediated by expected benefits and costs associated with wood heating. Affective associations were unrelated to public support for policies involving education and incentives, which were broadly endorsed by all segments of the community, and were more strongly associated with rational considerations. Latent profile analysis revealed no evidence to support the proposition that some community members experience internal “heart versus head” conflicts in which their positive affective associations with wood heating would be at odds with their risk judgments about the dangers of wood smoke pollution. Affective associations and cost/benefit judgments were very consistent with each other.

Quantitative characterization of kaolinite dispersibility in styrene–butadiene rubber composites by fractal dimension

A fractal method was introduced to quantitatively characterize the dispersibility of modified kaolinite (MK) and precipitated silica (PS) in styrene–butadiene rubber (SBR) matrix based on the lower magnification transmission electron microscopic images. The fractal dimension (FD) is greater, and the dispersion is worse. The fractal results showed that the dispersibility of MK in the latex blending sample is better than that in the mill blending samples. With the increase of kaolinite content, the FD increases from 1.713 to 1.800, and the dispersibility of kaolinite gradually decreases. There is a negative correlation between the dispersibility and loading content. With the decrease of MK and increase of PS, the FD significantly decreases from 1.735 to 1.496 and the dipersibility of kaolinite remarkably increases. The hybridization can improve the dispersibility of fillers in polymer matrix. The FD can be used to quantitatively characterize the aggregation and dispersion of kaolinite sheets in rubber matrix.

Influence of the structural characteristic of pyrolysis products on thermal stability of styrene-butadiene rubber composites reinforced by different particle sized kaolinites

A series of rubber composites were prepared by blending styrene-butadiene rubber (SBR) latex and the different particle sized kaolinites. The thermal stabilities of the rubber composites were characterized using thermogravimetry, digital photography, scanning electron microscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and Raman spectroscopy. Kaolinite SBR composites showed much greater thermal stability when compared with that of the pure SBR. With the increase of kaolinite particle size, the pyrolysis products became much looser; the char layer and crystalline carbon content gradually decreased in the pyrolysis residues. The pyrolysis residues of the SBR composites filled with the different particle sized kaolinites showed some remarkable changes in structural characteristics. The increase of kaolinite particle size was not beneficial to form the compact and stable crystalline carbon in the pyrolysis process, and resulted in a negative influence in improving the thermal stability of kaolinite/SBR composites.

Influence of kaolinite particle size on cross-link density, microstructure and mechanical properties of latex blending styrene butadiene rubber composites

Cross-link density, microstructure and mechanical properties of styrene butadiene rubber (SBR) composites filled with different particle sized kaolinites are investigated. With the increase of kaolinite particle size, the cross-link density of the filled SBR composites, the dispersibility and orientation degree of kaolinite particles gradually decrease. Some big cracks in filled rubber composites are distributed along the fringe of kaolinite aggregates, and the absorbance of all the absorption bands of kaolinites gradually increase with the increase of kaolinite particle size. All mechanical property indexes of kaolinite filled SBR composites decrease due to the decrease of cross-linking and reduction of interface interaction between filler and rubber matrix.

Developing starch-based polymer composites

This project aim was to replace petroleum-based plastic packaging materials that pollute the environment, with biodegradable starch-based polymer composites. It was demonstrated that untreated sugar cane bagasse microfibres and unbleached nanofibres significantly improved the physical, mechanical and chemical properties of starch films, while thermal extrusion of starch with alcohol improved the stiffness and the addition of aconitic acid cross-linked the film making it moisture resistant and extensible.

High temperature deformation and densification in alumina-yttria composites

Pinning by second phase particles offers a potent means for limiting grain growth and enhancing superplasticity in alumina-based ceramics. In the present study, a colloidal technique was used to produce green bodies of alumina-yttria composites; at elevated temperatures, the yttria particles react with alumina to produce YAG particles. The densification and high temperature deformation characteristics of alumina-YAG composites were studied using conventional free sintering and sinter-forging, which involves the application of a compressive stress without any lateral constraints. It is shown that the YAG particles retard both densification and grain growth. The experiments indicate also that the presence of YAG particles does not significantly alter the stress exponent for creep deformation.

Nano-indentation studies on polymer matrix composites reinforced by few-layer graphene

The mechanical properties of polyvinyl alcohol (PVA) and poly(methyl methacrylate) (PMMA)-matrix composites reinforced by functionalized few-layer graphene (FG) have been evaluated using the nano-indentation technique. A significant increase in both the elastic modulus and hardness is observed with the addition of 0.6 wt% of graphene. The crystallinity of PVA also increases with the addition of FG. This and the good mechanical interaction between the polymer and the FG, which provides better load transfer between the matrix and the fiber, are suggested to be responsible for the observed improvement in mechanical properties of the polymers.