Wear resistance of experimental titanium alloys for dental applications

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Matrizes poliméricas puras e modificadas para adsorção do gás sulfeto de hidrogênio

The underground natural gas found associated or not with oil is characterized by a mixture of hydrocarbons and residual components such as carbon dioxide (CO2), nitrogen gas (N2) and hydrogen sulfide (H2S), called contaminants. The H2S especially promotes itself as a contaminant of natural gas to be associated with corrosion of pipelines, to human toxicity and final applications of Natural Gas (NG). The sulfur present in the GN must be fully or partially removed in order to meet the market specifications, security, transport or further processing. There are distinct and varied methods of desulfurization of natural gas processing units used in Natural Gas (UPGN). In order to solve these problems have for example the caustic washing, absorption, the use of membranes and adsorption processes is costly and great expenditure of energy. Arises on such findings, the need for research to active processes of economic feasibility and efficiency. This work promoted the study of the adsorption of sulfide gas in polymer matrices hydrogen pure and modified. The substrates of Poly(vinyl chloride) (PVC), poly(methyl methacrylate) (PMMA) and sodium alginate (NaALG) were coated with vanadyl phosphate compounds (VOPO4.2H2O), vanadium pentoxide (V2O5), rhodamine B (C28H31N2O3Cl) and ions Co2+ and Cu2+, aiming to the adsorption of hydrogen sulfide gas (H2S). The adsorption tests were through a continuous flow of H2S in a column system (fixed bed reactor) adsorption on a laboratory scale. The techniques used to characterize the adsorbents were Infrared spectroscopy (FTIR), thermogravimetry analysis (TGA), X-ray fluorescence (XRF), the X-ray diffraction (XRD) electron microscopy (SEM). Such work indicates, the results obtained, the adsorbents modified PMMA, PVC and NaALG have a significant adsorptive capacity. The matrix that stood out and had the best adsorption capacity, was to ALG modified Co2+ with a score of 12.79 mg H2S / g matrix

Color tunability of intense upconversion emission from Er3+-Yb3+ co-doped SiO2-Ta2O5 glass ceramic planar waveguides

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Stress induced ordering due to interstitial elements in Nb and Ta by frequency analysis

It is well known that the interstitial elements present in solid solution in metals interact with the matrix by a relaxation process known as stress induced ordering. Traditionally this relaxation process is observed in the internal friction measurements. It is a common practice that researchers present the results of the frequency together with internal friction without giving any analysis. In this work we apply an expression which relates the variation of frequency with temperature and analyse the experimental results cited in the literature of the relaxation process due to the stress induced ordering of oxygen and nitrogen present in niobium and tantalum.

Influence of Ta2O5 on the electrical properties of ZnO- and CoO-doped SnO2 varistors

SnO2-based varistors doped with 0.5% cobalt, 0.5% zinc and various tantalum amounts were prepared by the solid-state route. Experimental evidence shows that small quantities of Ta2O5 improve the nonlinear properties of the samples significantly. It was found that samples doped with 0.05 mol% Ta2O5 exhibit the highest density (98.5%), the lowest electric breakdown field (E-b = 1050 V/cm) and the highest coefficient of nonlinearity (alpha = 11.5). The effect of Ta2O5 dopant could be explained by the substitution of Ta5+ by Sn4+. (C) 2004 Elsevier Ltd and Techna S.r.l. All rights reserved.

Immobilization and electrochemical properties of anionic complexes on a V2O5/surfactant nanocomposite

in this work, we report a new way of modifying an electrode by combining the intrinsic conductivity property of vanadium pentoxide xerogel with its water insolubility in the presence of the cationic surfactant N-cetyl-N,N,N,trimethyl-ammonium bromide (CTA(+)Br(-)). The obtained hybrid compound enables the immobilization of electroactive anions such as hexacyanoferrate (III) ([Fe(CN)(6)](3-)) and its analogue pentacyanonitrosylferrate (II) ([Fe(CN)(5)NO](2-)), rather than cations. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Crystallographic, dielectric and optical properties of SrBi2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (PvTi/SiO2/Si), n-type (100)-oriented and p-type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P-r values of 6.24 muC/cm(2) and 31.5 kV/cm for the film annealed at 800 degreesC. The film deposited onto fused silica and treated at 700 degreesC presented around 80 % of transmittance.

Structural and Spectroscopic Properties of Luminescent Er3+-Doped SiO2-Ta2O5 Nanocomposites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Crystallographic, dielectric and optical properties of SrBi 2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (Pt/Ti/SiO 2 /Si), n -type (100)-oriented and p -type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P r values of 6.24 μC/cm 2 and 31.5 kV/cm for the film annealed at 800 C. The film deposited onto fused silica and treated at 700 C presented around 80% of transmittance. © 2002 Taylor & Francis.

Caracterização textural e estrutural de V 2O 5/TiO 2 obtidos via sol-gel: Comparação entre secagem convencional e supercrítica

This work describes a modified sol-gel method for the preparation of V 2O 5/TiO 2 catalysts. The samples have been characterized by N 2 adsorption at 77K, x-ray diffractometry (XRD) and Fourier Transform Infrared (FT-IR). The surface area increases with the vanadia loading from 24 m 2 g -1, for pure TiO 2, to 87 m 2 g -1 for 9wt.% of V 2O 5. The rutile form is predominant for pure TiO 2 but became enriched with anatase phase when vanadia loading is increased. No crystalline V 2O 5 phase was observed in the catalysts diffractograms. Two species of surface vanadium observed by FT-IR spectroscopy a monomeric vanadyl and polymeric vanadates, the vanadyl/vanadate ratio remains practically constant.

Spectroscopic properties of Tm3+ doped fluoroindate glass

Optical absorption and fluorescence were investigated in Tm3+ doped fluoroindate glass. The spectroscopic parameters for transitions in the 4f11 configuration were determined. The fluorescence study revealed the origin of the frequency upconversion process as well as allowed to quantify the interaction between Tm3+ ions.

Histological analysis of the osseointegration of Ti-30Ta dental implants after surface treatment

Metallic biomaterials are used to reinforce or to restore the form and function of hard tissues. Implants and prosthesis are used to replace shoulders, knees, hips and teeth. When these materials are inserted in bone several biological reactions happen. This process can be associated to surface properties (topography, roughness and surface energy). In this work, the influence of biomimetic surface treatment in the osseointegration of Ti-30Ta dental implants was evaluated. Ingots were obtained from titanium and tantalum by using an arc-melting furnace. They were submitted to heat treatment at 1,100°C for 1 h, cooled in water and cold worked by swaging. Then, screw-shaped implants (2.0 mm diameter by 2.5 mm length) were manufactured and they were implanted in a rat's femur. Animals were divided into two groups: untreated (control group) and treated (biomimetic surface treatment). They were sacrificed 30 days after implantation. For histological analysis, implants with surrounding tissue were removed and immersed in formaldehyde. Samples were embedded in polymethyl methacrylate and after polymerization, cut with a saw, polished and mounted on glass slides. The results obtained suggest that biomimetic surface treatment was able to promote an increase osseointegration on the surface of dental implants. © Springer-Verlag Berlin Heidelberg 2013.

Crescimento da nanoapatita na liga Ti-30Ta, para aplicações odontológicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparação de filmes finos ferroelétricos de SrBi2'('TA IND.1-x''NB IND.x)ÍND.2 'O IND.9' puro e dopado com tungstênio, obtidos pelo método dos precursores poliméricos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Ensaio de citotoxicidade osteoblástica em amostras porosas das ligas Ti-6Al-4V, Ti-13Nb-13Zr, Ti-35Nb, Ti-35Nb-7Zr-5Ta e TiCP

Pós-graduação em Biopatologia Bucal - ICT