Addition of sedimentary rock to kaolinitic clays: influence on sintering process

Foram avaliadas, durante o processo de sinterização, as propriedades mecânicas de peças cerâmicas a base de argila com adição de rocha sedimentar. Foram preparados corpos de prova com 0, 20, 40, 60 e 80% em peso de rocha adicionada ao material argiloso. As peças foram sinterizadas nas temperaturas de 500, 800, 900, 1000, 1100 e 1200 °C e, posteriormente, submetidas à análise de difração de raios X e a ensaios tecnológicos Os resultados de difração de raios X mostram que a rocha sedimentar apresenta argilominerais micáceos enquanto o material argiloso possui a caulinita como fase principal. Técnicas de análises térmicas e difração de raios X das diferentes misturas mostram reações que indicam transformação (inversão do quartzo), decomposição (perda de hidróxidos) e formação de fase (mulita) durante o aquecimento das amostras. Os ensaios tecnológicos mostram que a adição da rocha sedimentar melhora algumas propriedades do material sinterizado, auxiliada pela presença de fundentes. Entretanto, a presença de quartzo na rocha dificulta a formação da fase mulita. A formação de novas fases e as transformações ocorridas no aquecimento e resfriamento das amostras ajuda explicar as propriedades tecnológicas dos materiais cerâmicos.

On Ti-18Si-6B and Ti-7.5Si-22.5B powder alloys prepared by high-energy ball milling and sintering

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis and sintering of PZT ceramics

Lead zirconate powder, with Zr/Ti ratio of 50/50 was prepared by polymeric precursor method and doped with 3, 5 and 7 mol% of Sr+2 Or Ba+2, as well as by 0.2 to 5 mol% of Nb+5. The powder was calcined at 750 degrees C by 4 hours and milled during 1.5 h in isopropilic alcohol. Powders were characterized by surface area measurements (BET method), by infrared spectroscopy and by X-ray diffraction to characterize the crystal structure. Isostatically pressed samples were sintered in a dilatometer furnace by using a constant heating rate of 10 degrees C/min from ambient to 1200 degrees C. Synthetic air and air with water vapor were used as atmospheres. Both Sr+2 and Ba+2 substitute Pb+2 and favor the formation of rhombohedral phase. Otherwise, Nb+5 substitute preferentially Zr+4 favoring tetragonal phase. The concentration of dopants and the atmosphere influence the densification and the microstructure of the PZT, which alters the dielectric and piezoelectric properties of the ceramics.

Synthesis and sintering of ZrO2-CeO2 powder by use of polymeric precursor based on Pechini process

Nanocrystalline ZrO2-12 mol % CeO2 powders were synthesized using a polymeric precursor method based on the Pechini process. X-ray diffraction (XRD) patterns showed that the method was effective to synthesize tetragonal zirconia single-phase. The mean crystallite size attained ranges from 6 to 15 nm. The BET surface areas were relatively high reaching 97 m(2)/g. Studies by nitrogen adsorption/desorption on powders, dilatometry of the compacts, and transmission electron microscopy (TEM) of the powders, were also developed to verify the particles agglomeration state. Both citric acid : ethylene glycol ratio and calcination temperature affected the powder morphology, which influenced the sinterability and microstructure of the sintered material, as showed by scanning electron microscopy (SEM). (C) 2001 Kluwer Academic Publishers.

Effects of powder preparation and sintering procedure on microstructure and dielectric properties of PLZT ceramics

PLZT ceramics belong to one of the very important groups of functional materials that make a basis for the production of a large range of electronic devices. The microstructure and properties of ceramics depend on the powder preparation and thermal processing conditions. Various techniques have been used to obtain chemically homogeneous and fine starting powders. PLZT powders have been prepared by two different production routes: by a modified Pechini method, using a polymeric precursor method (PMM) and by a partial oxalate method. A two-step sintering process, including a hot pressing, was carried out at 1100 and 1200degreesC Distinct phases obtained during the sintering process have been investigated by SEM and EDS techniques and dielectric properties such as permittivity and dielectric loss were measured in a frequency range from 1 to 20 kHz.. A significant difference in microstructure and dielectric properties, depending on powder origin and sintering procedure, has been noticed.

Sintering of tin oxide using zinc oxide as a densification aid

The physicochemical electronic characteristics of SnO2 render it useful in many technical applications, including ceramic varistors, stable electrodes used in electric glass-melting furnaces and electrometallurgy of aluminum, transparent windows and chemical sensors. The use of ZnO as a sintering aid was explored in this study to obtain SnO2 as a dense ceramic. Compacts were obtained by mechanical mixing of oxides, isostatic pressing at 210 MPa and sintering in situ inside a dilatometer at heating rates of 10degreesC/min. The grain size and microstructure were investigated by scanning and transmission electron microscopy (SEM/TEM). The phases and chemical composition were analyzed by energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results indicated that ZnO acts as a densification aid for SnO2, improving its grain growth with additions of up to 2 mol%. ZnO forms a solid solution with SnO2 UP to 1 mol%, above which SnZnO3 precipitates in the grain boundary, potentially inhibiting shrinkage and grain growth. (C) 2004 Kluwer Academic Publishers

Microstructural evolution during sintering of CoO doped SnO2 ceramics

Addition of 0.5 mol% of CoO into SnO2 promotes densification of this oxide to 99% of the theoretical density during sintering. TEM in this system reveals that after sintering at 1210 degrees C a secondary phase of Co2SnO4 is precipitated at the SnO2 grain boundaries during cooling. This phase is formed by diffusion of Co ions from the bulk to the grain boundary during sintering leaving needle-like defects at the grain bulk. The high resolution TEM micrograph of this system sintered at 1210 degrees C and 1400 degrees C showed an amorphous grain boundary region low in cobalt, indicating that the Co2SnO4 phase is precipitated from this region. (C) 1999 Elsevier B.V. Limited and Techna S.r.l. All rights reserved.

The effect of ZnO on the sintering and stabilization of ZrO2 center dot MgO system

The sintering of ZrO2. MgO . ZnO powder has been investigated by TMA (Thermal Mechanical Analyser) and its phases analysed by XRD (X-ray diffraction pattern). The data obtained from sintering was studied by the Bannister equation and its dominant sintering mechanism was calculated. It was observed that the ZnO addition in the ZrO2. MgO solid solution lead to increased zirconia stabilization, According to the vacancies model, the ZnO addition did not lead to zirconia phases stabilization (PSZ). An analysis of the rate control in the initial stage of the sintering (region I) showed a mechanism of volume diffusion type. In other regions (regions II and III), the grain growth did lead to the Bannister equation deviation, which was observed by SEM (Scanning Electron Microscopy). These results were different from those demonstrated by other authors who studied the ZrO2. Y2O3 solid solution and obtained a mechanism of grain boundary diffusion type. (C) 1999 Published by Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Sintering of ultrafine undoped SnO2 powder

The sintering process of nanometric undoped SnO2 powder was studied. No macroscopic shrinkage was observed during the sintening process. Grain growth kinetics investigation showed that surface diffusion is the dominant mechanism in the temperature range 500-1300 degreesC. For temperatures higher than 1300 degreesC, high weight loss was measured, suggesting evaporation-condensation as the dominant mass-transport mechanism. Thermogravimetric analysis (TG) and mass spectroscopy studies showed that the surface contamination of the SnO2 particles by chemical species like H2O, OH- and CO2, has a strong influence on the role of mass transport controlled by surface diffusion. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Sintering mechanisms of ZrO2 center dot MgO with addition of TiO2 and CuO

Substitutions of Ti and Cu in ZrO2.MgO (Z), cause transformation from monoclinic (m) to cubic (c) and tetragonal (t). According to the vacancy model and solid Solution formation models, neither CuO nor TiO2 cause zirconia stabilization, which derives front other phenomena. Data analysis by TMA using the CRH (constant rate of heating) method shows a solid state reaction of ZrO2.MgO.TiO2 (Z.TiO2) demonstrating a dominant mechanism of volume diffusion (n = 1). However, the sintering of ZrO2.MgO.CuO (Z.CuO) shows a viscous flow mechanism (n = 0), a similar phenomena to that of by sintering of glass. Transformations, such as: CuO to Cu2O at 1000 degreesC, ZrO2 (m) to ZrO2 (t) at 1100 degreesC and Cu2O (s) to Cu2O (l) at 1230 degreesC cause successive rearrangements of microstructure inside of region I (sintering process) and lead to interpretation errors when the Bannister equation is used. (C) 2003 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Sintering of ZnO doped SnO2

Dense SnO2 ceramics were obtained by doping with ZnO concentrations varies from 0.5 to 5.0 mel. The obtained powder was isostaticaly pressed to 210MPa in cylindrical shape and sintered from ambient to 1.500 degrees C using constant heating rate of 10 degrees C/min. Densities above 97% were obtained depending on the ZnO doping concentration. A maximum density was reached with the addition of 2 mol%. It can be concluded from shrinkage data and the observed microstructure obtained by SEM that the solid solution limit for ZnO in SnO2 is about 1.0 mol%. Above this concentration the formation of a second ceramic phase is observed.

Sintering and crystallite growth of nanocrystalline copper doped tin oxide

The effect of Cu2+ contents and of firing temperature on sintering and crystallite growth of nanocrystalline SnO2 xerogels was analyzed by thermoanalysis (mass loss (TG), linear shrinkage, and differential thermal analysis (DTA)), X-ray powder diffraction (XRPD), and EXAFS (extended X-ray absorption fine structures) measurements. Samples were prepared by two methods: (a) coprecipitation of a colloidal suspension from aqueous solution containing both Sn(IV) and Cu(II) ions and (b) grafting copper(II) species on the surface of tin pride gel. The thermoanalysis has shown that the shrinkage associated with the mass loss decreases by increasing the amount of copper. The EXAFS measurements carried out at the Cu K edge have evidenced the presence of copper in substitutional solid solution for the dried xerogel prepared with 0.7 mol % of copper, while for higher concentration of doping, copper has been observed also at the external surface of crystallites. The solid solution is metastable and copper migrates toward the surface during firing. The XRPD and DTA results have shown a recrystallization process near 320 degrees C, which leads to crystallite growth. The presence of copper segregated near the crystallite surface controls its growth.

Sintering and characterization of PLZT (9/65/35)

PLZT(9/65/35) obtained by association between the Pechini method (ZT) and partial oxalate (PLZT) was prepared. The stoichiometric phase and monophasic (cubic) PLZT obtained by calcination did not occur after sintering. The sintering process, by using two stages, caused a liquid phase formation due to a PbO excess (5 and 10 wt%). Samples with high density (similar to 8 g/cm(3)) and optical transparency(similar to 12%) were obtained. However, an equilibrium between the excess of PbO of sample/atmosphere PbO leads to a segregated PbO phase on the boundaries of the microstructure. A diffusion of Zr, Ti and La ions from PLZT to PbO phase promoted a stoichiometric deviation of the matrix and modified the optical and dielectric characteristics. (C) 2000 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Effect of ceria content on the sintering of ZrO2 based ceramics synthesized from a polymeric precursor

Zirconia-ceria powders with ceria concentration varying from 0 to 12 mol% were synthesized using a polymeric precursor route based on the Pechini process. Powder characteristics were evaluated with regard to the crystallite size, BET surface area, phase distribution, nitrogen adsorption/desorption behavior, and agglomeration state. Sintering was studied considering the shrinkage rate, densification, grain size, and phase evolution. It was demonstrated that the synthesis method is effective to prepare nanosized powders of tetragonal zirconia single-phase. Sinterability mainly depended on the agglomeration state of powders and the monoclinic phase content, fully tetragonal zirconia ceramic, with grain size of 2.4 mu m, was obtained after addition of at least 9 mol% ceria and sintering at 1500 degrees C for 4 h. (C) 2000 Elsevier B.V. Ltd. All rights reserved.

Sintering of zirconia composites obtained by slip casting

Composites containing a matrix of nanometric Ce-stabilized zirconia with an addition of micrometric monoclinic zirconia were processed by slip casting and sintered at a relatively low temperature. The ratio between nanometric and micrometric particles was determined according to the viscosity of the suspensions and the final density of the pellets. An optimum amount of micrometric particles was necessary to achieve improved suspension dispersion and higher pellet density. The amount of deflocculant in the suspensions containing the mixture of micrometric and nanometric particles was optimized by viscosity measurements. The pellets were characterized by dilatometry, Hg porosimetry, density measurement (the Archimedes method) and scanning electron microscopy. Despite the low green density obtained (35-38% of the theoretical density), densities as high as 97.5% were achieved after sintering. (C) 2001 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.