Effect of the Etching Duration and Ultrasonic Cleaning on Microtensile Bond Strength Between Feldspathic Ceramic and Resin Cement

This study assessed the effect of different etching durations of feldspathic ceramic with hydrofluoric acid (HF) and ultrasonic cleaning of the etched ceramic surface on the microtensile bond strength stability of resin to a feldspathic ceramic. The research hypotheses investigated were: (1) different etching times would not affect the adhesion resistance and (2) ultrasonic cleaning would improve the adhesion. Ceramic blocks (6 x 6 x 5 mm) (N = 48) were obtained. The cementations surfaces were duplicated in resin composite. The six study groups (n = 8) were: G1Etching with 10% aqueous HF (30 s) + silane; G 210% HF (1 min) + silane; G3-10% HF (2 min) + silane; G4-10% HF (30 s) + ultrasonic cleaning (4 min) in distilled water + silane; G5-10% HF (1 min) + ultrasonic cleaning + silane; G6-10% HF (2 min) ultrasonic cleaning + silane. The cemented blocks were sectioned into microbars for the microtensile test. The etching duration did not create significant difference among the groups (p = .156) but significant influence of ultrasonic cleaning was observed (p = .001) (Two-way ANOVA and Tukey's test, p > 0.05). All the groups after ultrasonic cleaning presented higher bond strength (19.38-20.08 MPa) when compared with the groups without ultrasonic cleaning (16.2117.75 MPa). The bond strength between feldspathic ceramic and resin cement was not affected by different etching durations using HF. Ultrasonic cleaning increased the bond strength between ceramic surface and resin cement, regardless of the etching duration.

Increased durability of resin-dentin bonds following cross-linking treatment

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of finishing and polishing on color stability of a nanofilled resin immersed in different media

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Is there difference of Streptococcus mutans count and adherence on amalgam and resin occlusal restorations? A blind clinical study

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of Nd:YAG or Er:YAG laser surface treatment on microtensile bond strength of indirect resin composites to resin cement. Lasers surface treatment of indirect resin composites

This study evaluated the influence of the surface pretreatment of indirect resin composite (Signum, Admira Lab and Sinfony) on the microtensile bond strength of a resin cement. Sixty samples made of each brand were divided into 6 groups, according to surface treatment: (1) control; (2) controlled-air abrasion with Al2O3; (3) Er:YAG Laser 200 mJ, 10 Hz, for 10s; (4) Er: YAG Laser 300 mJ, 10 Hz, for 10 s; (5) Nd:YAG 80 mJ, S15Hz for 1 min; (6) Nd:YAG 120mJ, 15 Hz for 1 min. After treatments, all the groups received an application of 37% phosphoric acid and adhesive. The pair of blocks of the same brand were cemented to each other with dual resin cement. The blocks were sectioned to obtain resin-resin sticks (1 x1 mm) and analyzed by microtensile bond testing. The bond strength values were statistically different, irrespective of the surface treatment performed, with highest values for Sinfony (43.81 MPa) and lowest values for Signum (32.33 MPA). The groups treated with the Nd:YAG laser showed the lowest bond strength values and power did not interfere in the results, both for Nd:YAG laser and Er:YAG. Controlled-air abrasion with Al203 is an efficient surface treatment method and the use of the Nd:YAG and Er:YAG lasers reduced bond strength, irrespective of the intensity of energy used.

A method to investigate the shrinkage stress developed by resin-composites bonded to a single flat surface

Objectives. To purpose a method for predicting the shrinkage stress development in the adhesive layer of resin-composite cylinders that shrink bonded to a single flat surface, by measuring the deflection of a glass coverslip caused by the shrinkage of the bonded cylinders. The correlation between the volume of the bonded resin-composite and the stress-peak was also investigated. Methods. A glass coverslip deflection caused by the shrinkage of a bonded resin-composite cylinder (diameter: d = 8 mm, 4 mm, or 2 mm, height: h = 4 mm, 2 mm, 1 mm, or 0.5 mm) was measured, and the same set-up was simulated by finite element analysis (3D-FEA). Stresses generated in the adhesive layer were plotted versus two geometric variables of the resin-composite cylinder (C-Factor and volume) to verify the existence of correlations between them and stresses. Results. The FEA models were validated. A significant correlation (p < 0.01, Pearson's test) between the stress-peak and the coverslip deflection when the resin-composites were grouped by diameter was found for diameters of 2 and 4 mm. The stress-peak of the whole set of data showed a logarithmic correlation with the bonded resin-composite volume (p < 0.001, Pearson's test), but did not correlate with the C-Factor. Significance. The described method should be considered for standardizing the stress generated by the shrinkage of resin-composite blocks bonded to a single flat surface. (C) 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Degradation of resin-dentin bonds of etch-and-rinse adhesive system to primary and permanent teeth

The aim of this in vitro study was to compare the degradation of resin-dentin bonds of an etch-and-rinse adhesive system to primary and permanent teeth. Flat superficial coronal dentin surfaces from 5 primary second molars and 5 permanent third molars were etched with phosphoric acid and bonded with an adhesive system (Adper Single Bond 2, 3M ESPE). Blocks of resin composite (Z250, 3M ESPE) were built up and the teeth sectioned to produce bonded sticks with a 0.8 mm(2) cross-sectional area. The sticks of each tooth were randomly divided and assigned to be subjected to microtensile testing immediately (24 h) or after aging by water storage (6 months). Data were analyzed by two-way repeated measures ANOVA and Tukey post hoc test (alpha = 0.05). Failure mode was evaluated using a stereomicroscope (400x). Microtensile values significantly decreased after the 6 months aging, independent of the dentin substrate. In 24 h, the values obtained to primary dentin were lower compared with permanent dentin. This difference was not maintained after aging. Adhesive/mixed failure was predominant in all experimental groups. In conclusion, degradation of resin-dentin bonds of the etch-and-rinse adhesive system occurred after 6 months of water storage; however, the reduction in bond strength values was higher for permanent teeth.

Analysis of surface hardness of artificially aged resin composites

This study evaluated the effect of artificially accelerated aging (AAA) on the surface hardness of eight composite resins: Filtek Z250, Filtek Supreme, 4 Seasons, Herculite, P60, Tetric Ceram, Charisma, and Filtek Z100. Sixteen specimens were made from the test piece of each material, using an 8.0 × 2.0 mm teflon matrix. After 24 hours, eight specimens from each material were submitted to three surface hardness readings using a Shimadzu Microhardness Tester for 5 seconds at a load of 50 gf. The other eight specimens remained in the artificially accelerated aging machine for 382 hours and were submitted to the same surface hardness analysis. The means of each test specimen were submitted to the Kolmogorov-Smirnov test (p > 0.05), ANOVA and Tukey test (p < 0.05). With regard to hardness (F = 86.74, p < 0.0001) the analysis showed significant differences among the resin composite brands. But aging did not influence the hardness of any of the resin composites (F = 0.39, p = 0.53). In this study, there was interaction between the resin composite brand and the aging factors (F = 4.51, p < 0.0002). It was concluded that notwithstanding the type of resin, AAA did not influence surface hardness. However, with regard to hardness there was a significant difference among the resin brands.

The effect of polymerization procedure on Vickers hardness of dual-curing resin cements

To investigate the surface hardness (Vickers hardness, HVN) of one light-curing flowable resin composite and five dual-curing resin cements after different polymerization procedures.

[The stamp technique for direct composite restoration]

The indications for direct resin composite restorations are nowadays extended due to the development of modern resin materials with improved material properties. However, there are still some difficulties regarding handling of resin composite material, especially in large restorations. The reconstruction of a functional and individual occlusion is difficult to achieve with direct application techniques. The aim of the present publication was to introduce a new "stamp"-technique for placing large composite restorations. The procedure of this "stamp"-technique is presented by three typical indications: large single-tooth restoration, occlusal rehabilitation of a compromised occlusal surface due to erosions and direct fibre-reinforced fixed partial denture. A step-by-step description of the technique and clinical figures illustrates the method. Large single-tooth restorations can be built-up with individual, two- piece silicone stamps. Large occlusal abrasive and/or erosive defects can be restored by copying the wax-up from the dental technician using the "stamp"-technique. Even fiber-reinforced resin-bonded fixed partial dentures can be formed with this intraoral technique with more precision and within a shorter treatment time. The presented "stamp"-technique facilitates the placement of large restoration with composite and can be recommended for the clinical use.

Resin composites: Modulus of elasticity and marginal quality

OBJECTIVE To investigate how the modulus of elasticity of resin composites influences marginal quality in restorations submitted to thermocyclic and mechanical loading. METHODS Charisma, Filtek Supreme XTE and Grandio were selected as they were found to possess different moduli of elasticity but quite similar polymerization contraction. MOD cavities (n=30) were prepared in extracted premolars, restored and then subjected to thermocyclic and mechanical loading. Marginal quality of the restorations before and after loading was analyzed on epoxy replicas under a scanning electron microscope. The percentage of gap-free margins and occurrence of paramarginal fractures were registered. Modulus of elasticity and polymerization contraction were analyzed with parametric and margins with nonparametric ANOVA and post hoc Tukey HSD or Wilcoxon rank-sum tests, respectively. The number of paramarginal fractures was analyzed with exact Fisher tests (α=0.05). RESULTS Grandio demonstrated significantly more gap-free enamel margins than Charisma and Filtek Supreme XTE, before and after loading (p<0.01), whereas there was no difference between Charisma and Filtek Supreme XTE (p>0.05). No significant effect of resin composite (p=0.81) on the quality of dentine margins was observed, before or after loading. Deterioration of all margins was evident after loading (p<0.0001). More paramarginal enamel fractures were observed after loading in teeth restored with Grandio when compared to Charisma (p=0.008). CONCLUSIONS The resin composite with the highest modulus of elasticity resulted in the highest number of gap-free enamel margins but with an increased incidence of paramarginal enamel fractures. CLINICAL SIGNIFICANCE The results from this study suggest that the marginal quality of restorations can be improved by the selection of a resin composite with modulus of elasticity close to that of dentine, although an increase in paramarginal enamel fractures can result as a consequence.

Influence of increment thickness on microhardness and dentin bond strength of bulk fill resin composites

OBJECTIVES To investigate the influence of increment thickness on Vickers microhardness (HV) and shear bond strength (SBS) to dentin of a conventional and four bulk fill resin composites. METHODS HV and SBS were determined on specimens of the conventional resin composite Filtek Supreme XTE (XTE) and the bulk fill resin composites SDR (SDR), Filtek Bulk Fill (FBF), x-tra fil (XFIL), and Tetric EvoCeram Bulk Fill (TEBF) after 24h storage. HV was measured either as profiles at depths up to 6mm or at the bottom of 2mm/4mm/6mm thick resin composite specimens. SBS of 2mm/4mm/6mm thick resin composite increments was measured to dentin surfaces of extracted human molars treated with the adhesive system OptiBond FL, and the failure mode was stereomicroscopically determined at 40× magnification. HV profiles and failure modes were descriptively analysed whereas HV at the bottom of resin composite specimens and SBS were statistically analysed with nonparametric ANOVA followed by Wilcoxon rank sum tests (α=0.05). RESULTS HV profiles (medians at 2mm/4mm/6mm): XTE 105.6/88.8/38.3, SDR 34.0/35.5/36.9, FBF 36.4/38.7/37.1, XFIL 103.4/103.9/101.9, TEBF 63.5/59.7/51.9. HV at the bottom of resin composite specimens (medians at 2mm/4mm/6mm): XTE (p<0.0001) 105.5>85.5>31.1, SDR (p=0.10) 25.8=21.9=26.0, FBF (p=0.16) 26.6=25.3=28.9, XFIL (p=0.18) 110.5=107.2=101.9, TEBF (p<0.0001) 63.0>54.9>48.2. SBS (MPa, medians at 2mm/4mm/6mm): XTE (p<0.0001) 23.9>18.9=16.7, SDR (p=0.26) 24.6=22.7=23.4, FBF (p=0.11) 21.4=20.3=22.0, x-tra fil (p=0.55) 27.0=24.0=23.6, TEBF (p=0.11) 21.0=20.7=19.0. The predominant SBS failure mode was cohesive failure in dentin. SIGNIFICANCE At increasing increment thickness, HV and SBS decreased for the conventional resin composite but generally remained constant for the bulk fill resin composites.

Dynamic constitutive equation of GFRP obtained by Lagrange experiment

The note presents a method of constructing dynamic constitutive equations of material by means of Lagrange experiment and analysis. Tests were carried out by a light gas gun and the stress history profiles were recorded on multiple Lagrange positions. The dynamic constitutive equations were deduced from the regression of a series of data which was obtained by Lagrange analysis based upon recorded multiple stress histories. Here constitutive equations of glass fibre reinforced phenolic resin composite(GFRP) in uniaxil strain state under dynamic loading are given. The proposed equations of the material agree well with experimental results.

Avaliação dos métodos para análise da microinfiltração marginal em restaurações de resina composta classe V in vitro

O objetivo deste estudo foi comparar os resultados da microinfiltração marginal obtidos por diferentes meios de aquisição de imagens e métodos de mensuração da penetração de prata em restaurações de resina composta classe V, in vitro. Dezoito pré-molares humanos hígidos, recém extraídos, foram divididos em três grupos, de acordo com o tipo de instrumento para preparação cavitária utilizado. Grupo 1: ponta diamantada número 3100, em alta rotação. Grupo 2: broca carbide número 330, em alta rotação. Grupo 3: ponta CVDentus código 82137, em aparelho de ultrassom. Foram realizados preparos cavitários padronizados (3x4x2mm) classe V nas faces vestibular e lingual de todos os dentes, com margens oclusais em esmalte e cervicais em dentina/cemento. As cavidades foram restauradas com o sistema adesivo Solobond M (VOCO) e resina composta Grandio (VOCO), a qual foi inserida e fotoativada em três incrementos. Os corpos de prova ficaram imersos em água destilada por 24h a 37oC; receberam acabamento e polimento com discos SofLex (3M) e foram novamente armazenados em água destilada, por sete dias. Posteriormente, as superfícies dentárias foram coberta com duas camadas de esmalte para unhas vermelho, exceto as áreas adjacentes às restaurações. Os espécimes ficaram imersos em solução aquosa de nitrato de prata a 50% por 24h e em solução fotorreveladora por 2h e foram seccionados no sentido vestíbulo-lingual, passando pelo centro das restaurações, com disco diamantado em baixa rotação. As amostras foram polidas em politriz horizontal e analisadas por diferentes métodos. À extensão da microinfiltração foi atribuído escores de 0 a 3 através de análises por meio de estereomicroscópio tradicional e com leds e microscópio ótico. As imagens obtidas na lupa com leds e no microscópio ótico tiveram as áreas infiltradas medidas através do software AxioVision. O teste χ2 de McNemar-Bowker revelou concordância estatística entre estereomicroscópio tradicional e o com leds (p=0,809) durante análises semiquantitativas. Porém, houve diferenças significantes entre microscópio ótico e estereomicroscópios (p<0,001). Houve boa correlação entre análises semiquantitativas e quantitativas de acordo com o teste de Spearmann (p<0,001). O teste de Kruskall-Wallis não revelou diferenças estatisticamente significantes (p=0,174) entre os grupos experimentais na análise quantitativa por microscópio ótico, em esmalte. Ao contrário do que se observa com a mesma em lupa (p<0,001). Conclui-se que o método de atribuição de escores comumente aplicado com a lupa nos estudos da microinfiltração marginal é uma opção confiável para análise da microinfiltração.

Avaliação das fendas marginais em restaurações de resina composta com variação de alguns determinanates clínicos

O objetivo deste estudo foi comparar, por meio de mensuração das fendas na interface dentina - restauração de resina composta com utilização de algumas variáveis: fotoativação com lâmpada halógena e com LED; utilização de resina microhíbrida com partículas nanométricas Filtek Z350 ou sem estas partículas Filtek Z250; variação do sistema adesivo (Adper Single Bond 2 ou Adper Scotchbond Multi Purpose); variação da temperatura da resina composta; uso de dessensibilizante dentinário ou não; remoção do colágeno da dentina ou não e variação da intensidade de luz na fotoativação. Foram utilizados 70 molares humanos recém-extraídos, com cavidades circulares na dentina superficial de cada face proximal, foram divididos em 10 amostras para cada variável citada acima. Os dentes foram devidamente restaurados, seguindo as instruções dos fabricantes, para todos os grupos e mantidos em estufa bacteriológica por um período de 7 dias, após este período, foram polidos e as réplicas de resina epoxídica foram confeccionadas a partir de uma moldagem com silicone por adição, as mesmas foram levadas ao MEV, para a análise. As fendas foram mensuradas com o auxílio do software UTHSCSA Image tool e os dados foram submetidos à análise estatística pelo teste t de Student para a obtenção dos resultados. Com base nos resultados obtidos pode-se concluir que: os menores valores de fendas marginais foram obtidos quando da utilização de luz halógena (t=3,246 e p= 0,02) e com variação da intensidade desta luz (t= - 8,808 e p= 0,00). Os menores valores relativos de fendas, mas sem diferença estatística significante, foram encontrados, também, quando a resina Filtek Z350 foi comparada com a resina Filtek Z250 (t=-0,426 e p= 0,672) e quando o adesivo Adper Scotchbond Multi Purpose foi comparado com o Sistema Adper Single Bond 2 (t= 0,883 e p= 0,382). Os maiores valores de fendas marginais foram obtidos com a resina Filtek Z350 préaquecida a 60oC (t= -3,961 e p=0,000); com o uso de dessensibilizante dentinário (t=-3,062 e p=0,004) e com a remoção do colágeno pelo hipoclorito de sódio (t= -8,808 e p= 0,000).