Effect of OH- content on emission properties in Er3+-doped tellurite glasses

A series of tellurite glasses of composition, 75TeO(2)-20ZnO-(5 - x)La2O3-xEr(2)O(3) (x = 0.05, 0.1, 0.3, 0.6, 1.0, 2.0, and 3.0 mol%) with different hydroxl content were prepared. The effect of Er3+ and OH- groups concentration on the emission properties of Er3+: I-4(13/2) -> I-4(15/2) transition in tellurite glasses was investigated. The constant KOH-Er for Er3+ in tellurite glasses, which represents the strength of interaction between Er3+ and OH- groups in the case of energy migration, was about 14 x 10(-19) cm(4) s(-1). The interaction parameter C-Er,C-Er for the migration rate of Er3+ : 4I(13/2) -> I-4(13/2) transition in tellurite glass was 46 x 10(-40) cm(2), which indicates that concentration quenching in Er3+-doped modified tellurite glass for a given Er3+ concentration is much stronger than in silicate and phosphate glasses. (c) 2007 Elsevier B.V. All rights reserved.

Nd3+掺杂的氧化镧钇透明激光陶瓷的光谱性能研究

Nd3+-doped Y2-2x La-2x O-3 (x = 0.08) transparent ceramics were fabricated by conventional fabrication process. Spectroscopic properties of the samples were investigated. The absorption band of Nd3+ : Y1.84La0.16O3 was broad covering the wavelength range 780-850 nm. When doped with 1.5at% Nd3+, the cross sections of the sample at 820 nm and laser diode pumped 808 nm were 1.81 x 10(-20) cm(2) and 1.54 x 10(-20) cm(2), respectively. The strongest emission peak of the sample was centered at 1078 mn with long fluorescent lifetime, broad emission bandwidth and high quantum efficiency. Because of the additive La2O3, the spectroscopic quality parameter (X-Nd) of matrix was' decreased from 1.6 to 0.46, thus the fluorescence branch ratio of F-4(3/2) - (4) I-11/2 transition was increased to 56.82%. These properties of Nd3' : Y1.84La0.16O3 transparent ceramic are benefitial to achieve high efficient laser output and ultrashort modelocked pulse.

Investigation of the spectroscopic properties of (Y0.92-xLa0.08Ndx)(2)O-3 transparent ceramics

The spectroscopic properties of (Y0.92-xLa0.08Ndx)(2)O-3 transparent ceramics were investigated. According to three intensity parameters (Omega(2),Omega(4),Omega(6)) fitted by the Judd-Ofelt theory, the spectroscopic quality parameter (X-Nd), branching ratio (beta(J,J')), and quantum efficiency (eta) of Nd3+ were determined. It was found that X-Nd of the host, owing to the additive La2O3, was decreased from 1.6 to 0.46; thus beta(J,11/2) was increased from 46% to 56.82%. A figure of merit of the specimens was discussed and compared with Nd:YAG transparent ceramic. (c) 2007 Optical Society of America.

Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷的光谱性能研究

采用传统无压烧结工艺制备了Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷并对其光谱性能进行了研究．样品具有较大的吸收和发射截面．La2O3的添加使样品的荧光寿命（τs）与玻璃接近，当Yb^3＋和Er^3＋的掺杂量分别为5at％和0．5at％时，测得τs=9．65ms．这种荧光寿命长、发射截面大和线宽窄的特性有利于微型、可集成化和大功率激光输出的实现．

Cooperative up-conversion luminescence of ytterbium doped yttrium lanthanum oxide transparent ceramic

The up-conversion luminescence of Yb3+-doped yttriurn lanthanum oxide transparent ceramic was investigated. It was ascribed to cooperative luminescence originated from the coupled states of the Yb3+ ion pairs. The proper doping of La2O3 can remove the cooperative luminescence of Yb3+ ion. But excessive La2O3 (at least 10 at.%) the cooperative up-conversion of Yb3+:Y2O3 is obtained again, and the intensity of up-conversion luminescence strengthens with the increase of La2O3 content. (c) 2007 Elsevier B.V. All rights reserved.

Effect of a feeding stimulant on feeding adaptation of gibel carp Carassius auratus gibelio (Bloch), fed diets with replacement of fish meal by meat and bone meal

The objectives of the study were to investigate the effect of a feeding stimulant on feeding adaptation of gibel carp (Carassius auratus gibelio Bloch) fed diets with replacement of fish meal by meat and bone meal (MBM), and whether or not the juvenile gibel carp could adapt to higher MBM level in the diet. Juvenile and adult gibel carp were tested. Two and one replacement levels were used for juvenile and adult fish respectively. Each group of diets was set as two types with or without a unique rare earth oxide: Y2O3, Yb2O3, La2O3, Sm2O3, Nd2O3 or Gd2O3 (only the first four rare earth oxides were used in adult diets) for four adaptation periods of 3, 7, 14 and 28 days respectively. After mixing, an equal mixture of all six diets for juvenile or four diets for adult was offered in excess for 2 days. During the last 2 days of each experiment, no feed was offered and faeces from each tank were collected. Feeding preference was expressed as relative feed intake of each diet, which was estimated based on the relative concentration of each marker in the faeces. Given some adaptation period, such as 3-28 days, the effects of MBM and squid extract inclusion on the preference to each diet were reduced. After 28 days adaptation, the preferences between groups were not significantly different.

Effect of several feeding stimulants on diet preference by juvenile gibel carp (Carassius auratus gibelio), fed diets with or without partial replacement of fish meal by meat and bone meal

The objectives of this work were to study the effects of several feeding stimulants on gibel carp fed diets with or without replacement of fish meal by meat and bone meal (MBM). The feeding stimulants tested were betaine, glycine, L-lysine, L-methionine, L-phenylalanine, and a commercial squid extract. Three inclusion levels were tested for each stimulant (0.18, 0.5%, and 1% for betaine and 0.1, 0.25 and 0.5% for the other stimulants). Two basal diets (40% crude protein) were used. one with 26% fish meal (FM), and the other with 21% fish meal and 6% MBM, Betaine at 0.1% in the fish meal group and at 0.5% in the meat and bone meal group was used in all experiments for comparison among stimulants. In the experiment on each stimulant, six tanks of fish were equally divided into two groups, one fed the FM diet, and the other fed the MBM diet. After 7 days' adaptation to the basal diet, in which the fish were fed to satiation twice a day, the fish were fed for another 7 days an equal mixture of diets containing varying levels of stimulants. Each diet contained a unique rare earth oxide as inert marker (Y2O3, Yb2O3, La2O3, Sm2O3 or Nd2O3). During the last 3 days of the experiment, faeces from each tank were collected. Preference for each diet was estimated based on the relative concentration of each marker in the faeces. Gibel carp fed the FM diet had higher intake than those fed the MBM diet, but the difference was significant only in the experiments on betaine, glycine and L-methionine. None of the feeding stimulants tested showed feeding enhancing effects in FM diets. All feeding stimulants showed feeding enhancing effects in MBM diets. and the optimum inclusion level was 0.5% for betaine, 0.1% for glycine, 0.25% for L-lysine, 0.1% for L-methionine. 0.25% For L-phenylalanine. and 0.1% for squid extract. The squid extract had the strongest stimulating effect among all the stimulants tested. (C) 2001 Elsevier Science B.V. All rights reserved.

Light alkenes preparation by the gas phase oxidative cracking or catalytic oxidative cracking of high hydrocarbons

The preparation of light alkenes by the gas phase oxidative cracking (GOC) or catalytic oxidative cracking (COC) of model high hydrocarbons ( hexane, cyclohexane, isooctane and decane in the GOC process and hexane in the COC process) was investigated in this paper. The selection for the feed in the GOC process was flexible. Excellent conversion of hydrocarbons ( over 85%) and high yield of light alkenes ( about 50%) were obtained in the GOC of various hydrocarbons including cyclohexane at 750 degreesC. In the GOC process, the utilization ratio of the carbon resources was high; CO dominated the produced COX (the selectivity to CO2 was always below 1%); and the total selectivity to light alkenes and CO was near or over 70%. In the COC of hexane over three typical catalysts (HZSM-5, 10% La2O3/HZSM-5 and 0.25% Li/MgO), the selectivity to COX was hard to decrease and the conversion of hexane and yield of light alkenes could not compete with those in the GOC process. With the addition of H-2 in the feed, the selectivity to COX was reduced below 5% over 0.1% Pt/HZSM-5 or 0.1% Pt/MgAl2O4 catalyst. The latter catalyst was superior to the former catalyst due to its perfect performance at high temperature, and with the latter, excellent selectivity to light alkenes ( 70%) and the conversion of hexane (92%) were achieved at 850 degreesC ( a yield of light alkenes of 64%, correspondingly).

Phase transformation in the surface region of zirconia and doped zirconia detected by UV Raman spectroscopy

The phase evolution of yttrium oxide and lanthanum oxide doped zirconia (Y2O3-ZrO2 and La2O3-ZrO2, respectively) from their tetragonal to monoclinic phase has been studied using UV Raman spectroscopy, visible Raman spectroscopy and XRD. UV Raman spectroscopy is found to be more sensitive at the surface region while visible Raman spectroscopy and XRD mainly give the bulk information. For Y2O3-ZrO2 and La2O3-ZrO2, the transformation of the bulk phase from the tetragonal to the monoclinic is significantly retarded by the presence of yttrium oxide and lanthanum oxide. However, the tetragonal phase in the surface region is difficult to stabilize, particularly when the stabilizer's content is low. The phase in the surface region can be more effectively stabilized by lanthanum oxide than yttrium oxide even though zirconia seemed to provide more enrichment in the surface region of the La2O3-ZrO2 sample than the Y2O3-ZrO2 sample, based on XPS analysis. The surface structural tension and the enrichment of the ZrO2, component in the surface region of ZrO2-Y2O3 and ZrO2-La2O3 might be the reasons for the striking difference between the phase change in the surface region and the bulk. Accordingly, the stabilized tetragonal surface region can significantly prevent the phase transition from developing into the bulk when the stabilizer's content is high.

Influence of the deposition energy on the composition and thermal cycling behavior of La-2(Zr0.7Ce0.3)(2)O-7 coatings

Lanthanum-zirconium-cerium composite oxide (La-2(Zr0.7Ce0.3)(2)O-7, LZ7C3) coatings were prepared under different conditions by electron beam-physical vapor deposition (EB-PVD). The composition, crystal structure, surface and cross-sectional morphologies, cyclic oxidation behavior of these coatings were studied. Elemental analysis indicates that the coating composition has partially deviated from the stoichiometry of the ingot, and the existence of excess La2O3 is also observed.

Effects of deposition conditions on composition and thermal cycling life of lanthanum zirconate coatings

Lanthanum, zirconate (La2Zr2O7, LZ) coatings were prepared under four different deposition conditions by electron beam-physical vapor deposition (EB-PVD). The composition, crystal structure, surface and cross-sectional morphology, cyclic oxidation behavior of these coatings were studied. Elemental analysis indicates that the coating composition has partially deviated from the stoichiometry of pyrochlore, and the existence of excess La2O3 is also observed. The deviation could be reduced by properly controlling the electron beam current or by changing the ingot composition.

Double-ceramic-layer thermal barrier coatings of La2Zr2O7/YSZ deposited by electron beam-physical vapor deposition

Double-ceramic-layer(DCL) thermal barrier coatings (TBCs) of La2Zr2O7 (LZ) and yttria stabilized zirconia (YSZ) were deposited by electron beam-physical vapor deposition (EB-PVD). The composition, crystal structure, surface and cross-sectional morphologies and cyclic oxidation behavior of the DCL coating were studied. Both the X-ray diffraction (XRD) and thermogravimetric-differential thermal analysis (TG-DTA) prove that LZ and YSZ have good chemical applicability to form a DCL coating. The thermal cycling test at 1373 K in an air furnace indicates the DCL coating has a much longer lifetime than the single layer LZ coating. and even longer than that of the single layer YSZ coating. The failure of the DCL coating is a result of both the bond coat oxidation and the thermal strain between bond coat and ceramic layer generated by the thermal expansion mismatch.

Facile Surfactant- and Template-Free Synthesis and Luminescent Properties of One-Dimensional Lu2O3:Eu3+ Phosphors

Uniform Lu2O3:Eu3+ nanorods and nanowires have been successfully prepared through a simple solution-based hydrothermal process followed by a subsequent calcination process without using any surfactant, catalyst, or template. On the basis of X-ray diffraction, thermogravimetric analysis and differential scanning calorimetry, and Fourier transform infrared spectroscopy results, it can be assumed that the as-obtained precursors have the structure formula of Lu4O(OH)(9)(NO3), which is a new phase and has not been reported. The morphology of the precursors could be modulated from nanorods to nanowires with the increase of pH value using ammonia solution. The as-formed precursors could transform to cubic Lu2O3:Eu3+ with the same morphology and a slight shrinkage in size after an annealing process, Both the Lu2O3:Eu3+ nanorods and nanowires exhibit the strong red emission corresponding to the D-5(0)-F-7(2) transition of the Eu3+ ions under UV light excitation or low-voltage electron beam excitation.