Synthesis and characterization of carbon-covered alumina (CCA) supported TiO2 nanocatalysts with enhanced visible light photodegradation of Rhodamine B

The anatase phase of titania (TiO2) nano-photocatalysts was prepared using a modified sol gel process and thereafter embedded on carbon-covered alumina supports. The carbon-covered alumina (CCA) supports were prepared via the adsorption of toluene 2,4-diisocyanate (TDI) on the surface of the alumina. TDI was used as the carbon source for the first time for the carbon-covered alumina support system. The adsorption of TDI on alumina is irreversible; hence, the resulting organic moiety can undergo pyrolysis at high temperatures resulting in the formation of a carbon coating on the surface of the alumina. The TiO2 catalysts were impregnated on the CCA supports. X-ray diffraction analysis indicated that the carbon deposited on the alumina was not crystalline and also showed the successful impregnation of TiO2 on the CCA supports. In the Raman spectra, it could be deduced that the carbon was rather a conjugated olefinic or polycyclic hydrocarbons which can be considered as molecular units of a graphitic plane. The Raman analysis of the catalysed CCAs showed the presence of both the anatase titania and D and G band associated with the carbon of the CCAs. The scanning electron microscope micrographs indicated that the alumina was coated by a carbon layer and the energy dispersive X-ray spectra showed the presence of Al, O and C in the CCA samples, with the addition of Ti for the catalyst impregnated supports. The Brunauer Emmet and Teller surface area analysis showed that the incorporating of carbon on the alumina surface resulted in an increase in surface area, while the impregnation with TiO2 resulted in a further increase in surface area. However, a decrease in the pore volume and diameter was observed. The photocatalytic activity of the nanocatalysts was studied for the degradation of Rhodamine B dye. The CCA-TiO2 nanocatalysts were found to be more photocatalytically active under both visible and UV light irradiation compared to the free TIO2 nanocatalysts.

Comparison of rhodamine B degradation under UV irradiation by two phases of titania nano-photocatalyst

Titania (TiO2) nano-photocatalysts, with different phases, prepared using a modified sol-gel process were employed in the degradation of rhodamine at 10 mg L-1 concentration. The degradation efficiency of these nano-photocatalysts was compared to that of commercial Degussa P25 titania. It was found that the nanocatalysts calcined at 450 degrees C and the Degussa P25 titania had similar photoreactivity profiles. The commercial Degussa P25 nanocatalysts had an overall high apparent rate constant of (K-app) of 0.023 min(-1). The other nanocatalyst had the following rate constants: 0.017, 0.0089, 0.003 and 0.0024 min(-1) for 450, 500, 550 and 600 degrees C calcined catalysts, respectively. This could be attributed to the phase of the titania as the anatase phase is highly photoactive than the other phases. Furthermore, characterisation by differential scanning calorimetry showed the transformation of titania from amorphous to anatase and finally to rutile phase. SEM and TEM characterisations were used to study the surface morphology and internal structure of the nanoparticles. BET results show that as the temperature of calcinations was raised, the surface area reduced marginally. X-ray diffraction was used to confirm the different phases of titania. This study has led to a conclusion that the anatase phase of the titania is the most photoactive nanocatalyst. It also had the highest apparent rate constant of 0.017 min(-1), which is similar to that of the commercial titania.

Effect of Metal Ions (Ag, Co, Ni, and Pd) on the Visible Light Degradation of Rhodamine B by Carbon-Covered Alumina-Supported TiO2 in Aqueous Solutions

Metal-ion (Ag, Co, Ni, and Pd) doped TiO2 nanocatalysts were successfully embedded on carbon-covered alumina supports. The CCA-embedded catalysts were crystalline and had a high surface area compared to the free metal-ion doped titania nanocatalysts while they still retained the anatase phase of the core TiO2. These catalysts were photocatalytically active under solar light irradiation. Rhodamine B was used as a model pollutant and the reactivity followed a pseudo-first-order reaction kinetics. The reaction rate of the CCA-supported catalysts was Pd > Ag > Co > Ni. Among the ratios of the CCA:catalyst used, it was found that the 1:1 ratio had the fastest reaction rate, followed by the 1:2 ratio, while the 2:1 ratio exhibited the lowest reaction rate. The CCA/metal-ion doped titania were found to have photocatalytic activities comparable with those of CCA-supported titania.

Metal doped nanosized titania used for the photocatalytic degradation of rhodamine B dye under visible-light

Metal-doped anatase nanosized titania photocatalysts were successfully synthesized using a sal gel process. Different amounts of the dopants (0.2, 0.4, 0.6, 0.8 and 1.0%) of the metals (Ag, Ni, Co and Pd) were utilized. The UV-Vis spectra (solid state diffuse reflectance spectra) of the doped nanoparticles exhibited a red shift in the absorption edge as a result of metal doping. The metal-doped nanoparticles were investigated for their photocatalytic activity under visible-light irradiation using Rhodamine B (Rh B) as a control pollutant. The results obtained indicate that the metal-doped titania had the highest activity at 0.4% metal loading. The kinetic models revealed that the photodegradation of Rh B followed a pseudo first order reaction. From ion chromatography (IC) analysis the degradation by-products Rhodamine B fragments were found to be acetate, chloride, nitrite, carbonate and nitrate ions.

Requirements-based development of an improved engineering change management method

Engineering changes (ECs) are essential in complex product development, and their management is a crucial discipline for engineering industries. Numerous methods have been developed to support EC management (ECM), of which the change prediction method (CPM) is one of the most established. This article contributes a requirements-based benchmarking approach to assess and improve existing methods. The CPM is selected to be improved. First, based on a comprehensive literature survey and insights from industrial case studies, a set of 25 requirements for change management methods are developed. Second, these requirements are used as benchmarking criteria to assess the CPM in comparison to seven other promising methods. Third, the best-in-class solutions for each requirement are investigated to draw improvement suggestions for the CPM. Finally, an enhanced ECM method which implements these improvements is presented. © 2013 © 2013 The Author(s). Published by Taylor & Francis.

Structuring technological information for technology roadmapping: Data mining approach

Most research on technology roadmapping has focused on its practical applications and the development of methods to enhance its operational process. Thus, despite a demand for well-supported, systematic information, little attention has been paid to how/which information can be utilised in technology roadmapping. Therefore, this paper aims at proposing a methodology to structure technological information in order to facilitate the process. To this end, eight methods are suggested to provide useful information for technology roadmapping: summary, information extraction, clustering, mapping, navigation, linking, indicators and comparison. This research identifies the characteristics of significant data that can potentially be used in roadmapping, and presents an approach to extracting important information from such raw data through various data mining techniques including text mining, multi-dimensional scaling and K-means clustering. In addition, this paper explains how this approach can be applied in each step of roadmapping. The proposed approach is applied to develop a roadmap of radio-frequency identification (RFID) technology to illustrate the process practically. © 2013 © 2013 Taylor & Francis.

模拟增温与UV-B 辐射增强对云杉种子萌发和幼苗生长的影响

臭氧层损耗导致的地球表面UV-B辐射增强以及温室气体增多引起的气候变暖是当今两大全球环境问题。UV-B辐射增强和气候变暖对陆地植物和生态系统产生深远影响，并已成为全球变化研究的重要议题。作为世界第三极的青藏高原，UV-B 辐射增强以及气候变暖现象尤为突出。本试验所在林区是青藏高原东缘的主要林区，具有大面积的亚高山人工针叶成熟林，在全球变化背景下该森林的天然更新潜力如何是急待回答的重要问题。基于此，本研究围绕森林树种的种子和幼苗这一更新的重要阶段，开展了气候变暖、UV-B辐射增强和联合胁迫对云杉种子萌发及幼苗定居影响的研究，旨在全球变化背景下，探讨全球变暖、UV-B 辐射增强和联合胁迫是否对西南地区大面积人工亚高山针叶林更新的种子萌发和幼苗定居阶段产生影响。 本文以青藏高原东缘亚高山针叶林主要树种云杉为研究对象，研究云杉种子萌发及幼苗的生长和生理对UV-B辐射增强与气候变暖的响应。采用UV-B荧光灯（UV-lamp）来模拟增强的UV-B 辐射，此外，采用开顶式有机玻璃罩（OTCs）来模拟气候变暖。本试验包括四个处理：（1）大气UV-B 辐射+大气温度（C）；（2）大气UV-B 辐射+模拟气候变暖（W���；（3）增强的UV-B辐射+大气温度（U）；（4）增强的UV-B辐射+模拟气候变暖（U+W���。 根据本试验结果，UV-B辐射增强对云杉种子萌发没有显著影响，它对萌发云杉幼苗的影响主要体现在幼叶展开以后。根据两年的试验结果，增强的UV-B辐射降低了云杉幼苗抗氧化酶活性，降低了抗氧化物质的含量，此外，造成了膜质的过氧化，表现为MDA在针叶中的积累。增强的UV-B照射处理萌发云杉幼苗两年后，幼苗的生长受到显著抑制。我们的结果显示，OTCs分别提高了空气（10 cm）和土壤（5 cm）温度1.74℃和0.94 ℃。增温显著地促进了云杉种子提前萌发，提高了萌发速率和萌发比率，而且，明显地促进了幼苗的生长，表现为株高和生物量累积的显著增长。此外增温还有利于云杉幼苗根的伸长生长以及生物量的累积，这可以使云杉幼苗更好地利用土壤中的水分和营养元素。 根据本试验结果，温度升高显著地促进了增强UV-B辐射下云杉萌发幼苗的生长，这说明，温度升高缓解了UV-B辐射增强对云杉萌发幼苗的负面影响。这种缓解作用可能是温度升高对UV-B辐射增强处理下幼苗的抗氧化系统活性改善的结果。温度升高还缓解了高UV-B辐射对云杉幼苗根生长的抑制作用，这也可能是增温缓解伤害的原因之一。此外，根据我们的试验结果，增温与UV-B辐射增强联合作用（U+W���下云杉萌发幼苗的生长状况好于大气温度与大气UV-B辐射联合（C）处理，表现为株高、地径、根长和生物量积累均高于C处理，因此可以推断，UV-B辐射增强与气候变暖同时存在对萌发幼苗在两年之内的生长没有产生抑制作用，也就是说，气候变暖的缓解作用完全弥补了UV-B辐射增强的有害作用。 同样，增强的UV-B辐射显著影响了云杉幼苗的光合作用，表现为净光合速率（Pn）和表观量子效率（Φ）的提高，此外，根据我们的试验结果，它还造成了PSII的光抑制。增强的UV-B辐射显著抑制了云杉幼苗对营养元素的吸收，表现为大量营养元素、碳、钙、镁和锌含量的降低，但是，它却显著促进了铁在植株体内的积累。增温显著地提高了净光合速率，但是，它对光系统II（PSII）的光化学效率影响不大。温度升高缓解了UV-B增强对云杉幼苗光合作用的伤害，表现为净光合速率、表观量子效率以及PSII光化学效率的提高。此外，温度升高还缓解了UV-B辐射增强对离子吸收的抑制作用。 Enhanced UV-B radiation due to the reduction of O3 layer and global warming induced by increased greenhouse gases in the air have become the two pressing aspects of global climate changes. Moreover, enhanced UV-B radiation and warming have profound and long-term impacts on terrestrial plants and ecosystems, and the studies focusing on the two factors have attracted many attentions. Qinghai-Tibetan Plateau is the third in elevation in the world, and enhanced UV-B radiation and climate warming are especially prominent in this region. Our research located in the main forest belt in the eastern Qinghai-Tibetan Plateau where large areas of subalpine coniferous forests distributed. Based on that, we carried out a research to study the effects of enhanced UV-B radiation and climate warming on seed germination and seedlings growth of seedlings which are the important basic stage in forest regeneration. This research was arranged by a complete factorial design and included two factors (UV-B radiation and temperature) with two levels. The UV-lamps were used to manipulate the supplemental UV-B radiation and open-top chambers (OTCs) were adopted to increase temperature. The four treatments were: (1) C, ambient UV-B without warming; (2) U, enhanced UV-B without warming; (3) W, ambient UV-B with OTCs warming; (4) U+W, enhanced UV-B with OTCs warming. The main results were exhibited as follows: 1. Based on our results in this research, OTCs increased temperature on average 1.74℃ in air (10 cm above ground) and 0.92 ℃ in soil (5 cm beneath ground). Furthermore, OTCs also slightly reduced soil moisture and relative air humidity, however, the differences was not statistically significant. 2. Our results showed that enhanced UV-B had no significant effects on the seeds germination of P. asperata. Enhanced UV-B affected sprouts of P. asperata until the needles unfolded. During two years, enhanced UV-B inhibited the efficiency of the antioxidant defense systems, and as a result, it induced oxidant stress and the accumulation of MDA in needles. After two years of exposure to enhanced UV-B, the growth of P. asperata sprouts was markedly restrained compared with those under ambient UV-B radiation and temperature (C). Warming significantly stimulated the germination speed and increased the germination rate of P. asperata seeds. In the next place, it prominently facilitated the growth of P. asperata sprouts, represented as improvements in stem elongation and biomass accumulation. Furthermore, warming also increased root growth of P. asperata sprouts, which could made sprouts more efficient to use water and nutrient elements in soil. In this research, warming alleviated the deleterious effects of enhanced UV-B on P. asperata sprouts. It markedly stimulated the growth of P. asperata sprouts exposed to enhanced UV-B. The ease effects of warming on the abilities of the antioxidant defense systems might account for its amending effects on growth. After two years of exposure to enhanced UV-B radiation and warming, the growth of P. asperata sprouts was better than those under ambient UV-B radiation without warming (C), which could be seen from the higher plant height, basal diameter, root length and total biomass accumulation compared with C. 3. Enhanced UV-B radiation significantly influenced the photosynthesis processes of two-year old P. asperata seedlings. Our results showed that enhanced UV-B reduced the net photosynthetic rate (Pn) and the apparent quantum efficiency (Φ), and induced photoinhibition of photosynthetic system II (PSII). Enhanced UV-B significantly decreased the concentration of nitrogen (N), phosphorous (P), potassium (K), calcium (Ca), magnesium (Mg) and zinc (Zn), however, it increased the accumulation of iron (Fe) in the whole plant of P. asperata seedlings. Warming significantly stimulated Pn of P. asperata seedlings but it had no prominent impacts on the photochemical efficiency of PSII. In our research, warming also alleviated the harmful effects of enhanced UV-B on photosynthesis and absorption of ions of P. asperata seedlings. It increased Pn, Φ and the photochemical efficiency of PSII in seedlings exposed to enhanced UV-B. Moreover, warming also increased the absorption of ions of the seedlings exposed to enhanced UV-B radiation.

W stronę uniwersytetu jako instytucji dobra wspólnego. Filozoficzne podstawy krytycznych badań nad szkolnictwem wyższym

Wydział Nauk Społecznych: Instytut Filozofii

Ochrona i konserwacja zasobu w archiwach państwowych w Polsce

Wydział Historyczny

Geografisk och historisk karta öfver Finland till skolornes bruk 1858

1 kartta kahdessa osassa :, vär. ;, 53,3 x 44,1 cm, lehti 59 x 48 cm