从理论上详细探讨了基质激光玻璃与包边玻璃的折射率匹配与剩余反射率的关系,并从实验上验证了折射率匹配越好,吸收系数与包边玻璃厚度的乘积越大,则剩余反射率越低,从而对激光放大器中寄生振荡的抑制越好,增益也就越高。

飞秒激光辐照ZnO晶体

利用飞秒激光对ZnO晶体进行辐照，对辐照前后的晶体样品进行发光光谱及拉曼光谱检测。辐照后发光光谱的某些发光峰强度有明显增强，但未产生新的发光峰，表明没有新的缺陷结构产生，但晶体内锌空位、间隙位锌、间隙位缺陷浓度增加。拉曼光谱结果表明，辐照后ZnO晶体未产生相变，但随着辐照激光功率的增大，拉曼峰327 cm-1，437 cm-1强度明显减弱，表明在飞秒激光辐照作用下氧化锌的结晶程度下降。但574 cm-1峰值却随着辐照功率的增大而变大，分析表明该拉曼峰很可能是由于晶体内间隙位缺陷所致。同时实验过程中观察到飞

Upconversion properties of TM3+/Yb3+ codoped fluorophosphate glasses with low phonon density of states

Fluorophosphate glasses codoped with Tm3+ and Yb3+ were prepared and their thermal stability, phonon states, and upconversion properties were studied. It is found that the increment of phosphate content is good for the thermal stability but increases the phonon density of states. However, the phonon density of states of these fluorophosphate glasses is very low due to the low phosphate content in their composition. The upconversion luminescence spectra were measured under excitation of 970 nm laser diode, and the intense blue (476 nm) and near infrared (794 nm) emission were simultaneous obtained at room temperature. The sensitizing mechanisms of Yb3+ to Tm3+ for blue and red emission contain both sequential and cooperative sensitization. The near infrared emission is a two-photon upconversion process. These researches suggest that when the phosphate content in the composition is low enough, fluorophosphate glass can be suitable host material of Tm3+ codoped with Yb3+ for blue and near infrared upconversion luminescence. (c) 2005 Elsevier B.V All rights reserved.

Spectroscopic properties of Er3+-doped tellurite glass for 1.55 mu m optical amplifier

Er3+-doped TeO2-BaO (Li2O, Na2O)-La2O3 tellurite glass system was prepared and their density, characteristic temperatures and optical properties were determined and investigated. For the TeO2-BaO-La2O3-Er2O3 system, composition with 10 mol% BaO presented the highest thermal stability and good infrared transmittance. Intense and broad 1.53 mu m infrared fluorescence were observed under 977 nm diode laser excitation and the most full width at half-maximum (FWHM) is similar to 60nm. According to absorption spectrum, we calculated the optical parameters by means of Judd-Ofelt and McCumber theory such as the fluorescence lifetimes which are about 2.72-3.25 ms and the maximum emission cross-sections which are similar to 1.0pm(2) at 1.531 mu m. The sigma(e) x FWHM value of composition with 10 mol% BaO for gain bandwidth is similar to 600 exceeding those in silicon and phosphate glasses. Our results indicated this kind of tellurite glasses could be used as an ideal host glass for optical amplifier. (c) 2005 Elsevier B.V. All rights reserved.

外差干涉仪混频误差分析

共光路外差干涉仪具有很高的分辨率．但因为安装、调试误差会产生非线性误差．影响系统的测量精度。着重分析了在共光路外差干涉仪中由激光光源的椭圆偏振化和沃拉斯顿棱镜的安装方位角误差同时存在的情况下，引起的频率混叠综合误差的大小及变化规律。结果发现其造成的非线性误差可达2．2nm，同时还发现两者造成的误差在某些情况下存在一定程度的相互抵消作用。讨论了提高测量系统精度的有效措施，对正确设计和调试激光外差测试系统、提高测量系统精度具有重要意义。

Méthodes simples de determination du CO2 total et du carbone organique dissous en eau saumâtre

Total CO2 of brackish water (Ebrié lagoon) is measured with a simple method: degassing and trapping CO2 in NaOh solution, the conductivity of which is a function of the trapped CO2 quantity. A relation CO2 versus salinity is deduced; it is nearly the same as the one deduced from CO2 measurements performed from alkalinity. Dissolved organic C is evaluated with a CHN analyser by evaporating 0.5 ml of acidified sample. Variation coefficient is near 10% for the lagoon values.

激光晶体的现状及发展趋势

在分析激光晶体的研究现状的基础上，指出其未来应用及主要发展趋势：面向先进制造技术、激光武器等应用的（1μm波段）高功率、大能量激光晶体；面向人眼安全、遥感、光通讯、医疗等应用的红外激光晶体；面向全色显示、光刻等应用的蓝绿紫和可见光激光晶体；LD泵浦超快激光增益和放大介质材料．

在Sr～2+α_BBO单晶衬底上生长β_BBO薄膜的研究

Crystalline beta-BBO thin films were successfully prepared on (001)-oriented Sr2+-doped alpha-BBO substrates by using liquid phase epitaxy, pulsed laser deposition and vapor transport equilibration techniques. The films were characterized by X-ray diffraction and X-ray rocking curve. The present results manifest that the beta-BBO thin films grown on Sr2+-doped alpha-BBO substrates have larger degree of orientation f value and smaller X-ray rocking curve FWHM than the ones grown on other reported substrates. Compared with other substrates, alpha-BBO has the similar structure, the same UV cutoff and the same chemical properties to beta-BBO. These results reveal that Sr2+-doped alpha-BBO single crystal may be a promising substrate proper to the growth of beta-BBO films.

Nd3+掺杂的氧化镧钇透明激光陶瓷的光谱性能研究

Nd3+-doped Y2-2x La-2x O-3 (x = 0.08) transparent ceramics were fabricated by conventional fabrication process. Spectroscopic properties of the samples were investigated. The absorption band of Nd3+ : Y1.84La0.16O3 was broad covering the wavelength range 780-850 nm. When doped with 1.5at% Nd3+, the cross sections of the sample at 820 nm and laser diode pumped 808 nm were 1.81 x 10(-20) cm(2) and 1.54 x 10(-20) cm(2), respectively. The strongest emission peak of the sample was centered at 1078 mn with long fluorescent lifetime, broad emission bandwidth and high quantum efficiency. Because of the additive La2O3, the spectroscopic quality parameter (X-Nd) of matrix was' decreased from 1.6 to 0.46, thus the fluorescence branch ratio of F-4(3/2) - (4) I-11/2 transition was increased to 56.82%. These properties of Nd3' : Y1.84La0.16O3 transparent ceramic are benefitial to achieve high efficient laser output and ultrashort modelocked pulse.

The water requirements of salmon in the River Lune

This report looks at the upstream movement in the River Lune of 9704 salmon which were monitored in the years 1960-1966. It explores the Broadraine Weir near Kirby Lonsdale with its fish monitoring station, the visual counting and trapping salmon, electronic monitoring of fish, and analysis of river flows.

Yb:YAP与Yb:YAG晶体光谱性能比较

应用中频感应提拉法生长出掺杂浓度为10 at.-%的Yb:YAG与Yb:YAP晶体，对比了室温下两种晶体的吸收和发射光谱特性。结果表明，Yb:YAG晶体比Yb:YAP晶体有更好的激光性能和低的阈值；同时对比发现，Yb:YAP晶体的吸收截面是Yb:YAG晶体的2.16倍，它容易实现LD泵；由于Yb:YAP晶体的各向异性，它有轴向效应明显，它可以产生偏振激光。

Statistical approach to bulk inclusion initialized damage in films

In experiments, we have found an abnormal relationship between probability of laser induced damage and number density of surface inclusion. From results of X-ray diffraction (XRD) and laser induced damage, we have drawn a conclusion that bulk inclusion plays a key role in damage process. Combining thermo-mechanical damage process and statistics of inclusion density distribution, we have deduced an equation which reflects the relationship between probability of laser induced damage, number density of inclusion, power density of laser pulse, and thickness of films. This model reveals that relationship between critical sizes of the dangerous inclusions (dangerous inclusions refer to the inclusions which can initialize film damage), embedded depth of inclusions, thermal diffusion length and tensile strength of films. This model develops the former work which is the statistics about surface inclusion. (c) 2006 Elsevier B.V. All rights reserved.

表面热透镜薄膜吸收测量灵敏度提高方法

为提高表面热透镜薄膜吸收测量仪的灵敏度，在表面热透镜衍射理论基础上，通过数值模拟给出了探测激光腰斑半径、探测激光腰斑到样品表面距离、样品到探测光纤端面距离等仪器参数的优化方法．经优化调整后该仪器能达到优于0．1ppm量级的薄膜吸收率测量灵敏度．

三种不同后处理方式对ZrO_2薄膜性能的影响

采用有氧热处理、激光预处理和离子后处理三种方式对电子束蒸发(EBE)制备的单层ZrO_2薄膜进行了后处理,并分别对样品的光学性能和抗激光损伤阈值(LIDT)特性进行了研究。实验结果表明,热处理方式可以有效排除膜层内吸附的水气,弥补薄膜制备过程中的氧损失,使得光谱短移、吸收减小、损伤阈值增高;激光预处理过程可以在一定程度上减少缺陷、提高损伤阈值,但对膜层的光谱和吸收情况没有明显的改善作用;而离子后处理能够提高膜层的堆积密度、减少缺陷、降低吸收从而提高损伤阈值。由于三种方式处理机制不同,在实际应用中应根据膜层的性能选择合适的处理方式。

Avaliação Comparativa dos Scanners 3D Artec MHT e Cyberware WBX para aplicações em Antropometria e Ergonomia

A partir das dimensões dos indivíduos pode-se definir dimensionamentos adequados para os produtos e postos de trabalho, proporcionando segurança e conforto aos usuários. Com o avanço da tecnologia de digitalização de imagens (escaneamento) 3D, é possível tirar algumas medidas de maneira mais rápida e com a redução da presença do entrevistado durante o processo. No entanto, faltam estudos que avaliem estas tecnologias no Brasil, sendo necessária a realização de uma comparação das tecnologias e das respectivas precisões para que seu uso em pesquisas. Com o objetivo de oferecer métodos comparativos para escolha dos marcadores e equipamentos a serem utilizados em uma pesquisa antropométrica tridimensional da população brasileira, no presente estudo estão comparadas duas tecnologias de escaneamento: o sistema a laser WBX da empresa norte americana Cyberware e o sistema MHT da empresa russa Artec Group. O método para avaliação da precisão dimensional dos dados advindos desses equipamentos de digitalização de imagens 3D teve cinco etapas: Estudo dos processos de escaneamento; Escaneamento dos marcadores de pontos anatômicos; Escaneamento utilizando um corpo de prova cilíndrico; Escaneamento de um manequim; Escaneamento de um voluntário que teve seus pontos anatômicos marcados para a retirada de medidas. Foi feita uma comparação entre as medidas retiradas manualmente, por meio de antropômetro e virtualmente, com o auxílio do software de modelagem tridimensional Rhinoceros. Em relação aos resultados obtidos na avaliação do manequim e do voluntário, concluiu-se que a magnitude do erro absoluto é semelhante para ambos os scanners, e permanece constante independentemente das dimensões sob análise. As principais diferenças são em relação às funcionalidades dos equipamentos.