Realization of biferroic properties in La0.6Sr0.4MnO3/0.7Pb(Mg1/3Nb2/3)O3–0.3(PbTiO3) epitaxial superlattices

A set of symmetric and asymmetric superlattices with ferromagnetic La0.6Sr0.4MnO3 (LSMO) and ferroelectric 0.7Pb(Mg1/3Nb2/3)O3–0.3(PbTiO3) as the constituting layers was fabricated on LaNiO3 coated (100) oriented LaAlO3 substrates using pulsed laser ablation. The crystallinity, and magnetic and ferroelectric properties were studied for all the superlattices. All the superlattice structures exhibited a ferromagnetic behavior over a wide range of temperatures between 10 and 300 K, whereas only the asymmetric superlattices exhibited a reasonably good ferroelectric behavior. Strong influence of an applied magnetic field was observed on the ferroelectric properties of the asymmetric superlattices. Studies were conducted toward understanding the influence of conducting LSMO layers on the electrical responses of the heterostructures. The absence of ferroelectricity in the symmetric superlattice structures has been attributed to their high leakage characteristics. The effect of an applied magnetic field on the ferroelectric properties of the asymmetric superlattices indicated strong influence of the interfaces on the properties. The dominance of the interface on the dielectric response was confirmed by the observed Maxwell-Wagner-type dielectric relaxation in these heterostructures.

Ferroelectric interaction and polarization studies in BaTiO3/SrTiO3 superlattice

Ferroelectric superlattice structures consisting of alternating layers of BaTiO3 and SrTiO3 with variable interlayer thickness were grown on Pt (111)/TiO2/SiO2/Si (100) substrates by pulsed laser deposition. The presence of superlattice reflections in the x-ray diffraction pattern clearly showed the superlattice behavior of the fabricated structures over a range of 6.4–20 nm individual layer thicknesses. Depth profile conducted by secondary ion mass spectrometry analysis showed a periodic concentration of Ba and Sr throughout the film. Polarization hysteresis and the capacitance-voltage characteristics of these films show clear size dependent ferroelectric characteristics. The spontaneous (Ps) and remnant (Pr) polarizations increase gradually with decreasing periodicity, reach a maximum at a finite thickness and then decrease. The competition between the size effect and long-range ferroelectric interaction is suggested as a possible reason for this phenomenon. The temperature dependence of Ps and Pr shows a single ferroelectric phase transition, and the Curie temperature is estimated to be about 316 K. The curve shows that the ferroelectric superlattice tends to form an artificial material, responding as a single structure with an averaged behavior of both the parent systems.

Bi4Ti3O12–5BiFeO3 Aurivillius intergrowth: Structural and ferroelectric properties

Aurivillus intergrowth Bi4Ti3O12–5BiFeO3 was demonstrated to be ferroelectric that evoked the possibility of achieving high temperature magnetoelectric property in this family of compounds. X-ray diffraction studies confirmed its structure to be orthorhombic [Fmm2; a = 5.5061(11) Å, b = 5.4857(7) Å, c = 65.742(12) Å]. However, transmission electron microscopy established the random incidence of intergrowth at nanoscale corresponding to n = 6 and n = 7 members of the Aurivillius family. Diffuse ferroelectric orthorhombic to paraelectric tetragonal phase transition around 857 K was confirmed by dielectric and high temperature x-ray diffraction studies. Polarization versus electric field hysteresis loops associated with 2Pr of 5.2 μC/cm2 and coercive field of 42 kV/cm were obtained at 300 K.

Ferro electriclike and pyroelectric behavior of CaCu3Ti4O12 ceramics

A ferroelectriclike hysteresis loop was obtained at room temperature for CaCu3Ti4O12 (CCTO) ceramic. The remnant polarization and coercive field for 1100 °C/5 h sintered CaCu3Ti4O12 ceramics were 0.063 μC/cm2 and 195 V/cm, respectively. Remnant polarization increased while the coercive field decreased with increase in sintering temperature/duration, implying that these were microstructural dependent. The observation of the hysteresis loop for CCTO ceramic was corroborated by its pyroelectric behavior, and the pyroelectric current at room temperature was −0.0028 nA. These findings were attributed to the presence of mixed-valent Ti ions, apart from off center displacement of Ti ions in TiO6 octahedra.

Dielectric response of BaZrO3/BaTiO3 and SrTiO3/BaZrO3 superlattices

Dielectric materials with high tunability, low loss, and desired range of permittivity are an attractive class of materials for a variety of applications in microwave components such as tunable filters, phase shifters, antennas, etc. In this article, we have investigated the low frequency dielectric properties of BaZrO3/BaTiO3 and SrTiO3/BaZrO3 superlattices of varying modulation periods for the potential application toward electrically tunable devices. The dielectric response of the superlattices as a function of temperature revealed remarkable stability for both types of superlattices, with no observed dielectric anomalies within that range. Dielectric losses were also nominally low with minimal variation within the measured temperature range. Sufficiently high tunability of ∼ 40% was observed for the BaZrO3/BaTiO3 superlattices at the lowest individual layer thicknesses. In comparison, the SrTiO3/BaZrO3 superlattices showed a minimum tunability for lowest period structures. It showed maximum tunability of ∼ 20% at 10 kHz and room temperature at an intermediate dimension of 3.85 nm periodicity superlattice. The tunability value degraded with increasing as well as decreasing periodicities for the SrTiO3/BaZrO3 superlattices. The dielectric response has been explained on the basis of size effects, interlayer coupling between dissimilar materials, domain contribution, and depolarizing electric fields.

Dielectric properties of (110) oriented PbZrO3 and La-modified PbZrO3 thin films grown by sol-gel process on Pt(111)/Ti/SiO2/Si substrate

Highly (110) preferred orientated antiferroelectric PbZrO3 (PZ) and La-modified PZ thin films have been fabricated on Pt/Ti/SiO2/Si substrates using sol-gel process. Dielectric properties, electric field induced ferroelectric polarization, and the temperature dependence of the dielectric response have been explored as a function of composition. The Tc has been observed to decrease by ∼ 17 °C per 1 mol % of La doping. Double hysteresis loops were seen with zero remnant polarization and with coercive fields in between 176 and 193 kV/cm at 80 °C for antiferroelectric to ferroelectric phase transformation. These slim loops have been explained by the high orientation of the films along the polar direction of the antiparallel dipoles of a tetragonal primitive cell and by the strong electrostatic interaction between La ions and oxygen ions in an ABO3 perovskite unit cell. High quality films exhibited very low loss factor less than 0.015 at room temperature and pure PZ; 1 and 2 mol % La doped PZs have shown the room temperature dielectric constant of 135, 219, and 142 at the frequency of 10 kHz. The passive layer effects in these films have been explained by Curie constants and Curie temperatures. The ac conductivity and the corresponding Arrhenius plots have been shown and explained in terms of doping effect and electrode resistance.

Structural and electrical properties of low pressure metalorganic chemical vapor deposition grown Eu2O3 films on Si(100)

Structural and electrical properties of Eu2O3 films grown on Si(100) in 500–600 °C temperature range by low pressure metalorganic chemical vapor deposition are reported. As-grown films also possess the impurity Eu1−xO phase, which has been removed upon annealing in O2 ambient. Film’s morphology comprises uniform spherical mounds (40–60 nm). Electrical properties of the films, as examined by capacitance-voltage measurements, exhibit fixed oxide charges in the range of −1.5×1011 to −6.0×1010 cm−2 and dielectric constant in the range of 8–23. Annealing has resulted in drastic improvement of their electrical properties. Effect of oxygen nonstoichiometry on the film’s property is briefly discussed.

Structure and temperature dependence of conductivity of Ag2.5Se‐Se composite

Rapid solidification of Ag‐53 at. % Se alloy resulted in the formation of a composite mixture of Ag2.5Se and Se. The microstructure consists of spherical Se grains of 2–20 μm size, randomly distributed in a matrix of Ag2.5 Se. The Se grains were found to be layered hexagonal while the Ag2.5 Se had an orthorhombic crystal structure. The unit cell size of this phase, however, was twice that reported for the equilibrium orthorhombic Ag2 Se compound. The conductivity σ variation with temperature in the range 80–320 K was found to be similar to that observed in degenerate semiconductors. The σ decreased from 295 Ω−1 cm−1 at room temperature to a saturation value of 70 Ω−1 cm−1 for temperatures <80 K. The results are discussed in terms of percolation conduction in the Ag2.5 Se phase.

Interface dominated biferroic La0.6Sr0.4MnO3/0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 epitaxial superlattices

Superlattices composed of ferromagnetic La0.6Sr0.4MnO3 and ferroelectric 0.7Pb(Mg1/3Nb2/3)O3–0.3(PbTiO3) layers were fabricated on (100) LaAlO3 substrates by pulsed laser deposition technique. The ferromagnetic and frequency independent ferroelectric hysteresis characteristics established the biferroic nature of the superlattices. Influence of magnetic field was observed in tuning the P-E characteristics of the superlattices. A similar effect was observed on application of a high dc electric field to the samples. The nature of the observed ferroelectric properties and their modulation by applied magnetic and electric fields were thus discussed in connection to the ferroelectric/ferromagnetic interfaces.

Leakage current behavior in pulsed laser deposited Ba(Zr0.05Ti0.95)O3 thin films

Barium zirconium titanate [Ba(Zr0.05Ti0.95)O3, BZT] thin films were prepared by pulsed laser ablation technique and dc leakage current conduction behavior was extensively studied. The dc leakage behavior study is essential, as it leads to degradation of the data storage devices. The current-voltage (I-V) of the thin films showed an Ohmic behavior for the electric field strength lower than 7.5 MV/m. Nonlinearity in the current density-voltage (J-V) behavior has been observed at an electric field above 7.5 MV/m. Different conduction mechanisms have been thought to be responsible for the overall I-V characteristics of BZT thin films. The J-V behavior of BZT thin films was found to follow Lampert’s theory of space charge limited conduction similar to what is observed in an insulator with charge trapping moiety. The Ohmic and trap filled limited regions have been explicitly observed in the J-V curves, where the saturation prevailed after a voltage of 6.5 V referring the onset of a trap-free square region. Two different activation energy values of 1.155 and 0.325 eV corresponding to two different regions have been observed in the Arrhenius plot, which was attributed to two different types of trap levels present in the film, namely, deep and shallow traps.

Relaxor characteristics of layered Ba1-(3/2)xLaxBi2Nb2O9 ceramics

Barium lanthanum bismuth niobate Ba1−(3/2)xLaxBi2Nb2O9 (x = 0, 0.05, 0.1, and 0.15) powders have been prepared via solid state reaction route. The monophasic layered perovskite nature of each composition of these was confirmed by x-ray diffraction studies. A continuous decrease in the lattice parameter c of parent BaBi2Nb2O9 with increase in La3+ doping level was noteworthy. A decrease in dielectric constant maximum (εm), a shift in dielectric anomaly to lower temperatures (from 488 to 382 K), and an increase in the diffuseness (γ) (from 1.58 to 1.84) of dielectric anomaly were encountered on increasing x from 0 to 0.15. Vogel-Fulcher analyses showed a decrease in freezing temperature (Tf) (from 157 to 40 K) and an increase in the activation energy (0.53 to 1.12 eV) for frequency dispersion with increase in La3+ content. A downward shift in the peak position of the pyroelectric coefficient with increasing La3+ doping level was observed. The observed changes in the above physical properties were attributed to the increase in A-site chemical heterogeneity as a result of aliovalent La3+ doping on Ba2+ sites and associated A-site vacancy formation.

Improved microwave dielectric properties of (Mg1-(x+y)CaxLay)(Ti1-yAly)O3 ceramics

Phase-singular solids of the composition, (Mg1−(x+y) Cax Lay)(Ti1−yAly)O3 (x = 0 to 0.88; y = 0.05 to 0.35) having the cubic perovskite-type structure were prepared by the substitution of La3+ and Al3+ in equivalent quantities which brought about complete miscibility between MgTiO3 and CaTiO3. These ceramics showed relative permittivities of 16.5 to 50 (at 6 GHz) with increasing Ca content, high Q values of 10 000 to 30 000 and retained near-zero temperature coefficients in permittivity at optimum y values. Their dielectric characteristics are better accountable in terms of the positional disorder rather than the tolerance factor of perovskite structure.

Morphology Dependence of Ag-Ni Solid Solubility

Electrodeposition produced features with a dendritic morphology and features with a branched wire like morphology made up of about 20 nm sized particles. Both the features contained Ag and Ni atoms in a solid solution arrangement. However, the feature made up of nanoparticles contained a greater concentration of Ni as compared to the Ni content in the dendritic feature. The greater Ni content in the Ag-Ni solid solution for the features with nanoparticles when compared to the dendritic morphology features strongly indicated the effect of curvature in increasing the extent of miscibility between bulk immiscible atoms. (C) 2011 The Electrochemical Society. [DOI: 10.1149/2.003202esl] All rights reserved.

Viscous effects in the inception of cavitation

The inception of cavitation in the steady flow of liquids around bodies is seen to depend upon the real fluid flow around the bodies as well as the supply of nucleating cavitation sources—or nuclei—within the fluid. A primary distinction is made between bodies having a laminar separation or not having a laminar separation. The former group is relatively insensitive to the nuclei concentration whereas the latter is much more sensitive. Except for the case of fully separated wake flows and for gaseous cavitation by diffusion the cavitation inception index tends always to be less than the magnitude of the minimum pressure coefficient and only approaches that value for high Reynolds numbers in flows well supplied with nuclei.

Anisotropic electrical transport properties of poly(methyl methacrylate) infiltrated aligned carbon nanotube mats

We report the electrical anisotropic transport properties of poly(methyl methacrylate) infiltrated aligned carbon nanotube mats. The anisotropy in the resistivity increases with decreasing temperature and the conduction mechanism in the parallel and perpendicular direction is different. Magnetoresistance (MR) studies also suggest anisotropic behavior of the infiltrated mats. Though MR is negative, an upturn is observed when the magnetic field is increased. This is due to the interplay of electron weak localization and electron-electron interactions mechanisms. Overall, infiltrated carbon nanotube mat is a good candidate for anisotropically conductive polymer composite and a simple fabrication method has been reported. (C) 2012 American Institute of Physics. [doi: 10.1063/1.3675873]