A solid nickel(II) complex with methionine sulfoxide

Solid Ni(C(5)H(10)NO(3)S)(2) . 2H(2)O complex was prepared and characterized. Electronic absorption spectrum shows an octahedral geometry for the complex. Infrared spectroscopy analysis shows that the metal atom is coordinated to the ligand through (COO(-)) and (S = O) groups. Thermal analysis confirmed the composition of the complex and suggests that the water molecules are not coordinated to the metal ion. The complex shows extremely high solubility in water. (C) 2000 Elsevier B.V. S.A. All rights reserved.

Phase formation and characterization of BaBi2Ta2O9 obtained by mixed oxide procedure

Ferroelectric layefed-perovskite BaBi2Ta2O9 (BBT) has been prepared successfully by solid-state reaction. The influence of pressure and temperature/time annealing regime on the BBT phase formation was analyzed. The powders were characterized by thermal analysis and Xray diffraction and the sintered pellets by scanning electron microscopy. The crystalline BBT phase, free of secondary phases was obtained at 950 degreesC for 2 h. For an applied field strength of 380 kV/cm, a remnant polarization of 7.6 muC/cm(2) and an electric coercive field of 45.7 kV/cm were obtained. (C) 2004 Elsevier B.V. All rights reserved.

Mechanically activating formation of layered structured bismuth titanate

Bismuth titanatc-Bi(4)Ti(3)O(12) (BIT) with wide application in the electronic industry as capacitors, memory devices and sensors is the simplest compound in the Aurivillius family, which consists of (Bi(2)O(2))(2+) sheets alternating with (Bi(2)T(i)3O(10))(2-) perovskite-like layers. The synthesis of more resistive BIT ceramics would be preferable advance in obtaining of well-densified ceramic with small grains randomly oriented to limit the conductivity along the (Bi(2)O(2))(2+) layers. Having in mind that the conventional ceramic route for the synthesis can lead to non-stoichiometry in composition, in consequence of the undesirable loss in bismuth content through volatilization of Bi(2)O(3) at elevated temperature, our efforts were addressed to preparation of BIT by mechanical activation the constituent oxides. The nucleation and phase formation of BIT, crystal structure, microstructure, powder particle size and specific surface area were followed by XRD, Rietveld refinement analysis, thermal analysis, scanning electron microscopy (SEM) and the BET specific surface area measurements. (c) 2005 Elsevier B.V. All rights reserved.

Development of an experimental glass ionomer cement containing niobium and fluoride

Glass ionomer cements (GICs) are currently used for various dental applications such as luting cements or as restorative materials. The calcium fluoro-alumino-silicate system is the basis for degradable glasses used to obtain the GICs. The purpose of the present paper is to add niobium to conventional glass system because according to previous papers niobium addition improves the chemical resistance and the mechanical properties of glasses. Therefore, the GICs prepared from these glasses would result in cements with higher chemical and mechanical resistance. The niobium fluoride powders were prepared using the sol-gel process and were characterized by X-ray diffraction, differential thermal analysis (DTA) and Al-27 and Si-29 MAS NMR. The results obtained by XRD showed that the powders prepared by this method are glass-ceramic. In the DTA curve was detected the presence of T-g and T-c temperatures. The analysis of MAS NMR spectra indicated that the framework of the powders is formed by SiO4 and AlO4 linked tetrahedra which are essential structures to yield the cements. Thus, we concluded that niobium fluoride silicate powders can be used in the preparation of GICs. (c) 2005 Elsevier B.V. All rights reserved.

Polymerization of photocurable commercial dental methacrylate-based composites - Photocalorimetry study

Due to their excellent aesthetics, photopolymers have been extensively used in several dentistry applications. However, several problems are reported, e.g. low mechanical and abrasion resistance, shrinkage during polymerization, etc. Properties of the final restorations are intrinsically related to the polymerization stage, which can be conveniently studied by photocalorimetry. In the present work the polymerization reaction and the filler content of different photocurable commercial dental methacrylate-based composites were studied by means of photocalorimetry and thermogravimetry, respectively. The results show that the values of curing rate, the heat of polymerization and the filler content vary significantly from one composite to another.

Influence of the precursor salts in the synthesis of CaSnO3 by the polymeric precursor method

CaSnO3 was synthesized by the polymeric precursor method, using different precursor salts as (CH3COO)(2)Ca. H2O, Ca(NO3)(2). 4H(2)O, CaCl2. 2H(2)O and CaCO3, leading to different results. Powder precursor was characterized using thermal analysis. Depending on the precursor different thermal behaviors were obtained. Results also indicate the formation of carbonates, confirmed by IR spectra. After calcination and characterization by XRD, the formation of perovskite as single phase was only identified when calcium acetate was used as precursor. For other precursors, tin oxide was observed as secondary phase.

Thermogravimetric investigations during the synthesis of silica-based MCM-41

MCM-41 material was synthesized starting from hydrogel containing colloidal fumed silica, sodium silicate, cetyltetramethylammonium bromide (CTMABr) as surfactant, and distilled water as solvent. These reactants were mixed to obtain a gel with the following composition: 4SiO(2):1Na(2)O:1CTMABr:200H(2)O. The hydrogel with pH=14 was hydrothermally treated at 100 degreesC, for 4 days. Each day, the pH was measured, and then adjusted to 9.5-10 by using 30% acetic acid solution. Thermogravimetry was the main technique, which was used to monitor the participation of the surfactant on the MCM-41 nanophase, being possible to determine the temperature ranges relative to water desorption as well as the surfactant decomposition and silanol condensation.

Physicochemical properties of sildenafil citrate (Viagra) and sildenafil base

Sildenafil citrate (Viagra) [I] and sildenafil base [II] are easily and unequivocally characterized by a set of physicochemical methods that include X-ray diffractometry, infrared spectroscopy, and thermal analysis. Monoclinic lattice constants: [I]: a = 26.98 Angstrom; b = 11.95 Angstrom; c = 16.68 Angstrom; beta = 106.97degrees. [II]: a = 8.66 Angstrom; b = 34.27 Angstrom; c = 8.93 Angstrom; beta = 96.63'. Both compounds decompose at 189.4degreesC [I] and 251.9degreesC [II]. Densities and refractive indices are given. (C) 2003 Wiley-Liss, Inc.

Mono- and dinuclear palladium(II) compounds containing nitrogen ligands. Crystal and molecular structure of [Pd(N,C-dmba)(NCO)(2,3-lut)] and [Pd(H2CCOMe)Cl(2,2 '-bipy)]

The cyanate-bridged cyclopalladated compound [Pd(N,C-dmba)(mu-NCO)](2) (1) (dmba = PhCH2NMe2) reacts in CH2Cl2 with 2,3-lutidine (2,3- lut), 3,4-lutidine (3,4-lut), 2,2'-bipyridine (2,2'-bipy) and 4,4'-bipyridine (4,4'-bipy), to give [Pd(N, C-dmba)(NCO)(2,3-lut)] (2), [Pd(N,C-dmba)(NCO)(3,4-lut)] (3), [{Pd(N,C-dmba)(NCO)}(2)(mu-2,2'-bipy)] .CH2Cl2 (4) and [{Pd(N,C-dmba)(NCO)}(2)(mu-4,4'-bipy)] . CH2Cl2 (5), respectively. The compounds were characterized by elemental analysis, i.r. and n. m. r. spectroscopy and also by t.g.a. The i.r. spectra of (2 - 5) display typical bands of monodentate N-bonded cyanate groups, whereas the n. m. r. data of (4) are consistent with the presence of a bridging 2,2'-bipyridine ligand. Complex (4) decomposes slowly in acetone. One of the products formed, [Pd(H2CCOMe) Cl(2,2'-bipy)] (6), was characterized by X-ray diffraction. As inferred from the t.g.a., the thermal stability decreases in the order: [{Pd(N,C-dmba)(NCO)}(2) (mu-4,4'-bipy)]. CH2Cl2 (5) > [Pd(N,C-dmba)(2,3-lut)( NCO)] (2) = [Pd(N, C-dmba)(3,4-lut)(NCO)] (3) > [{Pd(N,C-dmba)(NCO)}(2)(mu- 2,2'-bipy)] .CH2Cl2 (4). According to thermal analysis and X-ray diffraction patterns compounds (2 - 3) decompose into metallic palladium Pd(0), whereas (4 - 5) decompose with the formation of PdO. The X-ray crystal and molecular structure of [Pd(N, C-dmba)( NCO)(2,3-lut)] (2) was determined. The lutidine unit is perpendicular to the coordination plane.

Sublimation/volatilisation kinetics of 8-hydroxyquinolines and their nitro-derivatives

5-Nitro-8-hydroxyquinoline (B) and 5,7-dinitro-8-hydroxyquinoline (C) were obtained from nitration of 8-hydroxyquinoline (A) and purified in acetone medium and under heating in which the formation of (B) or (C) depends on the amount of HNO3 added. TG curves present mass loss in only one step before and after the melting point (T-m=76 degreesC (A) and 180 degreesC (B)) in different proportions as a function of the heating rate, characterising the sublimation and the volatilisation processes, respectively. The thermal stability of the compounds follow the order: A (77 degreesC)

Physicochemical properties and morphology of spongolite from Mato Grosso do Sul (Brazil)

The physicochemical properties and morphology of spongolite, a fibrous hollow material from Mato Grosso do Sul State (Brazil) have been studied. The results of thermal analysis, scanning electron microscopy (SEM), X-ray diffraction and NMR spectroscopy indicated that external and internal surfaces of silica spicules are covered by silica gel layers. The water evolved in the range 120-350degreesC is the result of silanol groups condensation to siloxane bonds. Total homogenization of the needles is achieved by heating spongolite over 900degreesC. This mineral may be considered as a natural composite material containing surface-immobilized reactive species. The presence of active silica gel layers opens the possibilities of attaching functional groups to spongolite surface. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Photoluminescence in disordered Zn2TiO4

In this work, the polymeric precursor method Was used to obtain disordered Zn2TiO4 powders, either Undoped or doped with Sn4+, Cr3+ and V5+, to be applied its photoluininescent material. The characterization was undertaken by means of thermal analysis (TG and DTA), X-ray diffraction (XRD), infrared spectroscopy (IR) and photoluminescence (PL). Previous works stated that titanate octahedra containing a short Ti-O distance show efficient luminescence at roorn temperature if these octahedra are isolated from each other. In the present work, the phenomenon was observed in condensed octahedra, sharing edges. The room temperature PL noticed in undoped Zn2TiO4 had its intensity increased by the dopant addition-the increase was of about 300% for V5+ doping 400% for Cr3+ and 800% for Sn4+. (c) 2005 Elsevier B.V. All rights reserved.

Sintering and crystallite growth of nanocrystalline copper doped tin oxide

The effect of Cu2+ contents and of firing temperature on sintering and crystallite growth of nanocrystalline SnO2 xerogels was analyzed by thermoanalysis (mass loss (TG), linear shrinkage, and differential thermal analysis (DTA)), X-ray powder diffraction (XRPD), and EXAFS (extended X-ray absorption fine structures) measurements. Samples were prepared by two methods: (a) coprecipitation of a colloidal suspension from aqueous solution containing both Sn(IV) and Cu(II) ions and (b) grafting copper(II) species on the surface of tin pride gel. The thermoanalysis has shown that the shrinkage associated with the mass loss decreases by increasing the amount of copper. The EXAFS measurements carried out at the Cu K edge have evidenced the presence of copper in substitutional solid solution for the dried xerogel prepared with 0.7 mol % of copper, while for higher concentration of doping, copper has been observed also at the external surface of crystallites. The solid solution is metastable and copper migrates toward the surface during firing. The XRPD and DTA results have shown a recrystallization process near 320 degrees C, which leads to crystallite growth. The presence of copper segregated near the crystallite surface controls its growth.

Synthesis of SnO2 by chemical routes and its use in varistors production

Tin oxide, SnO2. is a very used compound in industry and one of its uses is as varistor. For the current requirements of the technology is necessary a strict control of the chemical purity and the particle size of the raw material; for that reason the great interest that exists at the moment to develop synthesis methods that allow to get these requirements. In this work, ceramic powders of the Sn-Co-Nb-Ti-Al system using the controlled precipitation and polymeric precursor (Pechini) methods were synthesized. The raw material obtained was characterized using X-ray diffraction (XRD), thermal analysis (DTA/FG) and scanning electron microscopy (SEM). The sintering samples shown a good varistor behavior with non-linear coefficient (alpha) values similar to 22, and Er 2083 V/cm(2). (c) 2007 Elsevier Ltd. All rights reserved.

Solid state reactions in the platinum-mercury system

Thermogravimetry, Differential Scanning Calorimetry and other analytical techniques (Energy Dispersive X-ray Analysis; Scanning Electron Microscopy; Mapping Surface; X-ray Diffraction; Inductively Coupled Plasma Atomic Emission Spectroscopy and Cold Vapor Generation Atomic Absorption Spectroscopy) have been used to study the reaction of mercury with platinum foils. The results suggest that, when heated, the electrodeposited Hg film reacts with Pt to form intermetallic compounds each having a different stability, indicated by at least three mass loss steps. Intermetallic compounds such as PtHg4, PtHg and PtHg2 were characterized by XRD. These intermetallic compounds were the main products formed on the surface of the samples after partial removal of bulk mercury via thermal desorption. The Pt(Hg) solid solution formation caused great surface instability, attributed to the atomic size factor between Hg and Pt, facilitating the acid solution's attack to the surface.