Color stability of a nanofilled resin: influence of polishing and finishing and fluoride solutions according to time

Aim: The aim of the study was evaluate the finishing and polishing effect of the color stability of the composite resin Filtek Supreme XT, according to different fluoride solutions and time. Material and Methods: Specimens were prepared (n=140) with half of the samples finished and polished. The experimental groups were divided according to the presence or absence of finishing and polishing and immersion solutions (artificial saliva, sodium fluoride solution at 0.05% - manipulated, Fluordent Reach, Oral B, Fluorgard). The specimens remained in artificial saliva for 24 hours and were subjected to an initial color analysis using a spectrophotometer CIELab system. Then, they were immersed in the experimental solutions for 1 minute a day. The readings of the color change were made after 24 and 48 hours, 7, 14, 21, 30 and 60 days after the first immersion. The three-way mixed Analysis of Variance (ANOVA) ("finishing/polishing", "immersion medium" and “time”) were performed. For multiple comparisons, the Sidak test for repeated measure was used, with a 5% level of significance. Results: The finishing and polishing factor showed significant variability, independently of the immersion media (p<0.001). Cconclusion: Finishing and polishing procedures yielded better color stability to composite resin over time, regardless of the immersion media.

Chemical and morphological features of nanofilled composite resin: influence of finishing and polishing procedures and fluoride solutions

This study evaluated the influence of finishing and polishing procedures and differ-ent fluoride solutions on superficial morphology and chemistry of the nanofilled composite resinSupreme XT (3M) through the EDX analysis and SEM evaluation. Circular specimens (n 5 30) of 10mm diameter and 2 mm thickness were prepared, with half of the sample assays finished and polishedwith Super-Snap1sandpaper. The experimental groups were divided according to the presence or ab-sence of finishing and polishing and solutions (arti ficial saliva, 0.0 5% of manipulated sodium fluoridesolution, Fluordent Re ach, Oral B, Fluorgard). Specimens were immersed in each respective solutionfor 1 min per day, during 60 days and stored in artificial saliva at 37 6 18C between immersion peri-ods. Topography and chemical analysis was qualitative. It was observed that specimens submitted tofinishing and polishing procedures had lower superficial degradation. Fluoride solutio ns promoted su-perficial alterations on specimens, being the highest degradation obtained with Fluordent Reach. Itca n be concluded that finishing and polishing procedures and the immersion media influence the su-perficial morphology of composite resin tested; the Fluordent Reach was the flu oride solution thatmo st affected the material’s surface.

Influence of light curing units and fluoride mouthrinse on morphological surface and color stability of a nanofilled composite resin

Composite resin is a dental material susceptible to color change over time which limits the longevity of restorations made with this material. The influence of light curing units and different fluoride mouthrinses on superficial morphology and color stability of a nanofilled composite resin was evaluated. Specimens (N = 150) were prepared and polished. The experimental groups were divided according to the type of light source (halogen and LED) and immersion media (artificial saliva, 0.05% sodium fluoride solution-manipulated, Fluordent Reach, Oral B, Fluorgard). Specimens remained in artificial saliva for 24-h baseline. For 60 days, they were immersed in solutions for 1 min. Color readout was taken at baseline and after 60 days of immersion. Surface morphology was analyzed by Scanning Electron Microscopy (SEM) after 60 days of immersion. Color change data were submitted to two-way Analysis of Variance and Tukey tests (α = 0.05). Surface morphology was qualitatively analyzed. The factor light source presented no significant variability (P = 0.281), the immersion media, significant variability (P < 0.001) and interaction between factors, no significant variability (P = 0.050). According to SEM observations, no difference was noted in the surface of the specimens polymerized by different light sources, irrespective of the immersion medium. It was concluded that the light source did not influence the color stability of composite, irrespective of the immersion media, and among the fluoride solutions analyzed, Fluorgard was the one that promoted the greatest color change, however, this was not clinically perceptible. The immersion media did not influence the morphology of the studied resin. Microsc. Res. Tech. 77:941–946, 2014. © 2014 Wiley Periodicals, Inc.

Chemical and morphological features of dental composite resin: influence of light curing units and immersion media

Aims: The study evaluated the influence of light curing units and immersionmedia on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M)through the EDX analysis and SEM evaluation. Light curing units with different power densitiesand mode of application used were XL 3000 (480 mW/cm2), Jet Lite 4000 Plus (1230mW/cm2), andUltralume Led 5 (790 mW/cm2) and immersion media were artificial saliva, Coke1, tea and coffee,totaling 12 experimental groups. Specimens (10 mm 3 2 mm) were immersed in each respectivesolution for 5 min, three times a day, during 60 days and stored in artificial saliva at 378C 6 18Cbetween immersion periods. Topography and chemical analysis was qualitative. Findings: Groupsimmersed in artificial saliva, showed homogeneous degradation of matrix and deposition of calciumat the material surface. Regarding coffee, there was a reasonable chemical degradation with loss ofload particles and deposition of ions. For tea, superficial degradation occurred in specific areaswith deposition of calcium, carbon, potassium and phosphorus. For Coke1, excessive matrix degra-dation and loss of load particles with deposition of calcium, sodium, and potassium. Conclusion:Light curing units did not influence the superficial morphology of composite resin tested, but theimmersion beverages did. Coke1affected material’s surface more than did the other tested drinks.Microsc. Res. Tech. 73:176–181, 2010.

Effects of immersion media and repolishing on color stability and superficial morphology of nanofilled composite resin

This study evaluated the influence of fluoride mouth rinses and repolishing on the superficial morphology and color stability of nanofilled resin. About 150 specimens were prepared and polished using aluminum oxide discs for 15 s with a pressure of 2 kg. The experimental groups were divided according to the immersion medium (artificial saliva, 0.5% sodium fluoride, Fluordent Reach, Oral B, Fluorgard) and repolishing procedure (without and with). The specimens were continuously immersed for 1 week. Thereafter, half of each sample was repolished. A color reading was performed after 24 h of immersion in the artificial saliva baseline, after continuous immersion, and after repolishing. The superficial morphology was examined using scanning electron microscopy (SEM) in a qualitative way. Color change (∆E) data were submitted to a mixed analysis of variance using a Shapiro-Wilk test (p>0.05 for the different immersion media) and Sidak's test (p<0.05 for the differences between groups). In the interaction between the repolishing and the immersion media, Fluorgard showed a statistical difference between the ∆E values with and without repolishing (p<0.0001). On the SEM observations, both Fluordent Reach and Fluorgard caused degradation of the superficial resinous matrix of the composite after continuous immersion. This matrix was removed after repolishing.

Effect of post-polymerization heat treatment on a denture base acrylic resin: histopathological analysis in rats

This work examined the histological effects, on the rat palatal mucosa, of a denture base acrylic resin, submitted or not to a post-polymerization heat-treatment. Methods: Fifteen adult female Wistar rats, with sixty days old, weighting 150 g – 250 g were divided in G1: animals being maintained under the same conditions as the experimental groups following described, but without the use acrylic palatal plates (control group); G2: use of heat-polymerized acrylic resin palatal plates made of Lucitone 550; G3: use of palatal plates identical to G2, but subjected to a post-polymerization treatment in a water bath at 55°C for 60 min. The plates covered all the palate and were fixed in the molar region with light-cured resin, thus being kept there for 14 days. After the sacrifice, the palate was removed, fixed in formaldehyde 10% and decalcified with EDTA. Sections were stained using haematoxylin and eosin. Images in duplicate were made from the central region of the cuts, to measure the thickness (μm) of the keratin layers (TKC), epithelium total (TET) and connective tissue (TCC). Statistical analyses were carried out by one-way ANOVA and Tukey post-tests (α=0.05). Results: According to the results there was significant difference in the thickness of keratin between G2 and G3, with G1 having the intermediate value and similar to the other groups. There was a significant difference in the connective tissue with G3 resin denture base investigated.

Radiopacity and flow of different endodontic sealers

The present study evaluated the radiopacity and flow of different endodontic sealers: AH Plus, Endo CPM, MTA Fillapex, Sealapex, Epiphany, and Epiphany SE. For the radiopacity test, six specimens measuring 10mm in diameter and 1mm in thickness were fabricated from each material. They were radiographed on an occlusal film alongside an aluminum step wedge. Radiographs were digitized to determine the radiopacity equivalence in millimeters of aluminum. To evaluate the flow, a 120 g load was placed on top of a glass slab containing 0.05 } 0.005ml of sealer. The diameters of each material were measured (mm) with a caliper and samples were photographed. Digitized images were analyzed using the UTHSCSA Image Tool for Windows software, to determine the sealer area (mm2). Data were submitted to ANOVA and Tukey's test at 5% significance. AH Plus and Epiphany SE presented the greatest radiopacity (12.5 mm Al and 12.0 mm Al, respectively) (p>0.05), followed by Epiphany (9.6 mm Al) and Fillapex (8.9 mm Al). Endo CPM (5.46 mm Al) and Sealapex (5.51 mm Al) presented lower radiopacity. MTA Fillapex presented significantly higher values of flow than other sealers (33.11 mm and 844.9 mm2). AH Plus, Epiphany, and Epiphany SE had similar values. Endo CPM (21.05 mm and 342.8 mm2) and Sealapex (19.98 mm and 352.5 mm2) presented the lowest flow values (p>0.05). All sealers presented radiopacity and flow values according to ISO and ANSI/ADA recommendations.

Colour stability of acrylic resin denture teeth after immersion in different beverages

The colour stability of acrylic resin denture teeth in beverages was investigated. A spectrophotometer measured the colour (CIE-L*a*b* system) of all specimens after storage in distilled water for 24 h at 37°C (T0). Specimens were then immersed in various beverages. After 15 days (T1) and 30 days (T2), for each material, the mean ∆E values were calculated and compared by two-way ANOVA and Tukey intervals (α=0.05). In the ∆T0T1 period, specimens stored in red wine were significantly discoloured, compared to distilled water (P=0.003). There was no difference between immersion solutions in ∆ET0T2 (P=0.772) and in ∆ET1T2 (P=0.058), and no difference between materials in all immersion periods.

Effectiveness of several solutions to prevent the formation of precipitate due to the interaction between sodium hypochlorite and chlorhexidine and its effect on bond strength of an epoxy-based sealer

To evaluate the effectiveness of isopropyl alcohol, saline or distilled water to prevent the precipitate formed between sodium hypochlorite (NaOCl) and chlorhexidine (CHX) and its effect on the bond strength of an epoxy-based sealer in radicular dentine. Methodology The root canals of 50 extracted human canines (n = 10) were instrumented. In G1, root canals were irrigated with 17% EDTA and 2.5% NaOCl; G2, as G1, except that 2% CHX was used as the final irrigant. In the other groups, intermediate flushes with isopropyl alcohol (G3), saline (G4) or distilled water (G5) were used between NaOCl and CHX. The specimens were submitted to SEM analysis to evaluate the presence of debris and smear layer, in the apical and cervical segments. In sequence, fifty extracted human canines were distributed into five groups (n = 10), similar to the SEM study. After root filling, the roots were sectioned transversally to obtain dentine slices, in the cervical, middle and apical thirds. The root filling was submitted to a push-out bond strength test using an electromechanical testing machine. Statistical analysis was performed using Kruskal–Wallis and Dunn's tests (α = 5%). Results All groups had similar amounts of residue precipitated on the canal walls (P > 0.05). The push-out bond strength values were similar for all groups, independently of the root third evaluated (P > 0.05). Conclusions Isopropyl alcohol, saline and distilled water failed to prevent the precipitation of residues on canal walls following the use of NaOCl and CHX. The residues did not interfere with the push-out bond strength of the root filling.

Push-out bond strength of calcium hydroxide and mineral trioxide aggregate based sealers

The adhesiveness of six root canal sealers: Acroseal, Endo CPM, Epiphany, White MTA, Sealapex and Sealer 26 to dentin, was evaluated in a push-out test design. Methods: Twenty eight roots of freshly extracted teeth were gauged with a size 5 Largo drill. With a cutting machine slices of 2 mm were prepared, rinsed with 5.25% NaOCl and a final rinse with 17% EDTA, dried and filled with one of the sealers. After setting their bond strength was measured in a mechanical testing machine. The data were statistically analyzed by using a One Way ANOVA and post hoc Tukey test. Results: The mean and standard deviation from values of bond strength was: Sealapex 2.2±0.4; Endo CPM 3.8±1.3; White MTA 6.0±1.4; Epiphany 10.9±2.6; Sealer 26 12.3±2.3; and Acroseal 12.2±1.4. Acroseal, Sealer 26 and Epiphany presented a significantly (P<0.01) greater bond strength compared with the other sealers. Also White MTA showed higher adhesiveness compared with Endo CPM and Sealapex (P<0.01). Conclusion: The bond strength between endodontic sealers and root dentin was maximal when Acroseal, Sealer 26 and Epiphany were used; Sealapex e Endo CPM, in turn, presented the lowest bond strength mean values.

Effect of finishing and polishing on color stability of a nanofilled resin immersed in different media

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Surface properties and color stability of an acrylic resin combined with an antimicrobial polymer

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of calcium hydroxide dressing on push-out bond strength of endodontic sealers to root canal dentin

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Is there difference of Streptococcus mutans count and adherence on amalgam and resin occlusal restorations? A blind clinical study

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Push-out bond strength of fiber posts to root dentin using glass ionomer and resin modified glass ionomer cements

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)