Analysis in vitro of direct bonding system with cyanoacrylate ester and orthodontic wires

The aim of this study was to evaluate the tensile strength of orthodontic wires bonded onto the enamel with cyanoacrylate ester. To obtain the specimens, 120 human premolars (extracted for orthodontic or periodontal reasons) were included in acrylic blocks of rapid polymerization with three teeth each. Four groups were formed with ten specimens each. In the specimens, a dental splint model was made with cyanoacrylate ester and round stainless steel wire. In groups I, II and III, cyanoacrylate ester was used with round steel wires, with variation in diameter: 0.014 inches; 0.016 inches and 0.018 inches, respectively. In group IV, round steel wire 0.018 inches was used with photo polymerizing resin composite with previous acid etching. The adhesive force of the materials was measured in two points under the action of the tensiometer (ETM-USA). The number of loose wires was counted along with those that remained fixed according to the different levels of force applied because of the direction of the tensile force (vertical or horizontal) and the diameter of the wire used. The data obtained were first submitted to a descriptive analysis and then submitted to a statistical analysis (Friedman's Test and Dunn's Test of Multiple Comparison - Epi-info 3.2). Within the limitations of the experimental conditions presented, the cyanoacrylate ester or 'Super Bonder (R)' maintained bonded to enamel and steel wires (0.016 and 0.018 inches) during the tensile strength tests under different levels of applied forces.

Rehabilitation with ear prosthesis linked to osseointegrated implants

Background: The absence of an ear, which can be the result of a congenital malformation, surgical tumour resection or traumatic injury, is a significant aesthetic problem. Attachment of ear prostheses with adhesives can cause local irritation for the wearer and affect the colour of the prostheses. Use of implants in craniofacial reconstruction can improve the retention and stability of prostheses giving to patient greater comfort and security relative to adhesive attachment.Objective: The aim of this report was to present a clinical case of a mutilated patient who was rehabilitated by means of installing an ear prosthesis fixed through osseointegrated implants.Materials and methods: The patient had two implants installed in the mastoid region that were linked by a bar, and a clip-type system was used. The ear prosthesis was constructed from medical-use silicone, pigmented to match the patient's skin colour and linked to the retention system.Conclusion: The patient's rehabilitation was satisfactory from both a functional and an aesthetic point of view, making it possible for the patient to return to a normal social life and regain lost self-esteem.

Influence of customized composite resin fibreglass posts on the mechanics of restored treated teeth

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Long-term nano-mechanical properties of biomodified dentin-resin interface components

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bond strength between acrylic resin and maxillofacial silicone

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nanomechanical properties of biochemically modified dentin bonded interfaces

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Sodium Ascorbate on Tag Formation in Bleached Enamel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of enamel surface after bracket debonding and polishing

INTRODUÇÃO: a preservação da estrutura de esmalte após a remoção dos acessórios ortodônticos é obrigação do clínico. Portanto, procura-se um protocolo de descolagem com bases científicas. OBJETIVO: objetivou-se avaliar por microscopia eletrônica de varredura (MEV) a influência de quatro protocolos de remoção de braquetes e polimento da superfície do esmalte e propor um protocolo que minimize os danosà superfície do esmalte. MÉTODOS: doze incisivos permanentes bovinos foram divididos em quatro grupos de acordo com os instrumentos utilizados para a descolagem dos braquetes e remoção do remanescente adesivo. Os braquetes foram descolados com o alicate de descolagem reto (Ormco Corp.) nos grupos 1 e 2, e com o instrumento de descolagem Lift-Off (3M Unitek) nos grupos 3 e 4. Os remanescentes adesivos dos grupos 1 e 3 foram removidos com o alicate removedor de resina longo (Ormco Corp.) e dos grupos 2 e 4 com broca de carboneto de tungstênio (Beavers Dental) em alta-rotação. As superfícies, após cada etapa da descolagem e polimento, foram avaliadas em réplicas de resina epóxica e foram obtidas eletromicrografias com aumento de 50 e 200X. RESULTADOS: os quatro protocolos de remoção de acessórios ortodônticos e polimento ocasionaram irregularidades no esmalte. Conclusão: a remoção do braquete com o alicate de descolagem reto, seguido da remoção do remanescente adesivo com broca de carboneto de tungstênio e polimento final com pasta de pedra-pomes foi o procedimento que ocasionou menores danos ao esmalte, sendo o protocolo sugerido para a remoção dos acessórios ortodônticos.

Avaliação do Índice de Remanescente Adesivo utilizando braquetes com e sem tratamento na base e a interação com três sistemas de colagem

OBJETIVO: avaliar o Índice de Remanescente Adesivo (IRA) em dentes bovinos após a descolagem de braquetes com e sem tratamento na base. METODOLOGIA: foram utilizados três sistemas de colagem ortodôntica para os dois padrões de base. Os dentes bovinos foram divididos em seis grupos de 40, de acordo com a base do braquete e o sistema de colagem. Vinte e quatro horas após a colagem foram realizados os testes de compressão em uma máquina de ensaios. A avaliação do IRA foi realizada em um estereomicroscópio por três examinadores calibrados. Foi utilizado o teste não paramétrico de Kruskal-Wallis, seguido do método de Dunn, para fazer as comparações múltiplas entre todos os grupos. RESULTADOS E CONCLUSÕES: observou-se que o tratamento das bases dos braquetes com óxido de alumínio não foi determinante para o aumento da adesividade entre o braquete e o adesivo. O grupo em que se utilizou braquetes com tratamento na base e adesivo TXT (3M-Unitek) + Transbond Plus SEP (3M-Unitek) apresentou a maior parte das fraturas na interface dente-adesivo (escore 4).

Microleakage of adhesively bonded cervical amalgam restorations

Purpose: To evaluate dye penetration in adhesively bonded cervical amalgam restorations. Materials and Methods: the specimens were randomly divided into four groups and the adhesives Prime & Bond 2. 1, Prime & Bond 2.1 Dual Cure, Scotchbond Multi Purpose Plus and Amalgambond Plus were tested. After being restored and polished, the teeth were thermocycled 1,000 times at temperatures varying between 5degreesC +/- 2degreesC and 55degreesC +/- 2degreesC. Statistical analysis was carried out using the Kruskal-Wallis test and multiple comparisons. Results: Scotchbond Multi-Purpose Plus demonstrated lower levels of microleakage in enamel and dentin. The dual adhesives were more effective than the one bottle adhesive.

The influence of time interval between bleaching and enamel bonding

Objectives: the purpose of this study was to investigate the penetration of a conventional adhesive material into enamel bleached with 16% carbamide peroxide and 38% hydrogen peroxide using optical light microscopy.Methods: Extracted human teeth were randomly divided into eight experimental groups with six specimens each, according to the bleaching material and time interval after bleaching and before the bonding procedure. Groups were designated as follows: control group, restorations in unbleached teeth; restorations performed immediately after bleaching; restorations performed 7 days after bleaching; restorations performed 14 days after bleaching; and restorations performed 30 days after bleaching. The length of resin tags was measured with an Axiophot photomicroscope at 400x magnification for the calculation of the proportion of tags of study groups compared to the respective control groups. Analysis of variance was applied for comparison between groups; data were transformed into arcsine (p < 0.05).Results: the specimens of experimental groups, in which restorations were performed 7, 14, and 30 days after bleaching, showed better penetration of adhesive material into enamel than specimens restored immediately after bleaching. There was no statistically significant difference between the bleaching materials employed or in the interaction between bleaching agent and time interval.Conclusions: This suggests that a time interval of at least 7 days should be allowed between enamel bleaching and placement of adhesive bonding agents for accomplishment of composite resin restorations.

Short-term evaluation of the pulpo-dentin complex response to a resin-modified glass-ionomer cement and a bonding agent applied in deep cavities

Objectives. To evaluate the response of the pulpo-dentin complex following application of a resin-modified glass-ionomer cement or an adhesive system in deep cavities performed in human teeth.Methods. Deep class V cavities were prepared on the buccal surface of 26 premolars. In Group I the cavity walls (dentin) and enamel were conditioned with 32% phosphoric acid and the dentin adhesive system One Step (Bisco, Inc., Itasca, IL, USA) was applied. In Groups 2 and 3, before total etching and application of bonding agent, the cavity floor was lined with the resin-modified glass-ionomer cement-Vitrebond (3M ESPE Dental Products Division, St. Paul, MN, USA) or the calcium hydroxide cement-Dycal (control group, Dentsply, Mildford, DE, USA), respectively. The cavities were restored using light-cured Z-100 composite resin (3M ESPE). The teeth were extracted between 5 and 30 days and prepared for microscopic assessment. Serial sections were stained with H/E, Masson's trichrome, and Brown and Brenn techniques.Results. In Group 1, the inflammatory response was more evident than in Groups 2 and 3. Diffusion of dental material components across dentinal tubules was observed only in Group 1, in which the intensity of the pulp response increased as the remaining dentin thickness decreased. Bacteria were evidenced in the lateral walls of two samples (Group 2) which exhibited no inflammatory response or tissue disorganization.Conclusions. Based on the experimental conditions, it was concluded total acid etching followed by application of One Step bonding agent cannot be recommended as adequate procedures. In this clinical condition the cavity walls should be lined with a biocompatible dental material, such as Vitrebond or Dycal. 2003 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Shortening of primary dentin etching time and its implication on bond strength

Objective. The aim of this study was to investigate the influence of shortening the etching time on the bond strength of a conventional and a self-etching primer adhesive system used in primary tooth dentin.Methods. Flat dentin surfaces were obtained from 24 primary molars, randomly assigned to 4 experimental groups. The adhesive systems Single Bond and Clearfil SE Bond were applied in two groups according to the manufacturers' recommendations. In the other two groups, the adhesives were applied after half-time of acid etching, 7 s for Single Bond and 10 s for Clearfil SE Primer. Resin crowns were built up and after 24 h storage in water at 37 &DEG; C, the teeth were sectioned to produce beams with cross-sectional area of approximately 0.49 mm(2). Specimens were tested in tension at 0.5 mm/min until failure. Fractured specimens were analyzed to determine the failure mode.Results. Tensile bond strengths for Single Bond in primary dentin were higher than for Clearfil SE Bond. Shortening of acid etching time improved bond strength only for Single Bond, while no statistically significant difference was observed for Clearfil SE Bond when both etching times were compared.Significance. No detrimental effect on bond strength was observed when the time of acid etching was shortened in 50%. Shortening the time for a procedure in a small child without compromising the quality of the work is a very important finding for the practicing pediatric dentist. © 2004 Elsevier Ltd. All rights reserved.

Biocompatibility of resin-based materials used as pulp-capping agents

Aim To evaluate and compare the response of pulps of rats capped with resin-modified glass-ionomer cement (RMGIC) or self-etching adhesive system.Methodology Class I cavities were prepared on the occlusal surface of 54 maxillary first molars of 27 rats. Pulp exposure was performed on the cavity floor. The following resin-based materials were applied as pulp-capping agents: G1, Clearfil Liner Bond 2V (CLB 2V; Kuraray Co., Japan); G2, Vitrebond (VIT; 3M/ESPE, USA). In group 3 (control group), a calcium hydroxide/saline paste (CH; Labsynth, Brazil) was used. The cavities were restored with amalgam. After 7, 30 and 60 days, the animals were sacrificed and the jaws were processed for microscopic evaluation.Results Despite the inflammatory response caused by the experimental and the control materials at 7 days, pulpal healing associated with calcified barrier formation was observed at 60 days following the pulp therapy. Both resin-based materials promoted a large zone of cell-rich fibrodentine matrix deposition on the pulp horn related to the pulp exposure site, which was larger to VIT than to CLB 2V specimens. Tertiary dentine underneath the fibrodentine matrix was deposited by a layer of elongated pulpal cells. The remaining pulpal tissue exhibited normal histological characteristics. In the control group, healing and dentine-bridge formation was observed at 30 days. Pulpal breakdown occurred only when bacterial infection occurred.Conclusion Both experimental pulp-capping agents allowed pulpal healing characterized by cell-rich fibrodentine and tertiary dentine deposition as well as calcified barrier formation.