Marginal deterioration of the silicone for facial prosthesis with pigments after effect of storage period and chemical disinfection

The failure of facial prostheses is caused by limitations in the properties of existing materials, especially flexibility and durability. Therefore, this study evaluated the marginal deterioration of a silicone used for fabrication of facial prostheses (Silastic MDX4-4210, Dow Corning Corporation, Midland, MI, USA) according to the influence of artificial aging, daily disinfection, and 2 types of pigmentation. Thirty specimens were fabricated and subdivided in 6 groups: without pigmentation, pigmented with make-up powder and iron oxide, and evaluated with and without the action of the disinfectant. Analysis of marginal deterioration was performed on a scanning electron microscope (magnification, ×5000) immediately 6 months and 1 year after fabrication of specimens, following the guidelines of ASTM International. After visual analysis of the photomicrographs, it was noticed that all groups presented marginal deterioration and alterations in surface texture with time. The use of disinfection did not contribute to the marginal deterioration of polymer (silicone), regardless of the pigmentation and artificial aging.

Tribocorrosion behaviour of hot pressed CoCrMo−Al2O3 composites for biomedical applications

Alumina/alumina wear couple can lower the wear rates and thus metallic ion releasing on load bearing metallic implant materials. However, the low fracture toughness of ceramics is still a major concern. Therefore, the present study aims to process and to triboelectrochemically characterise the 5 and 10 vol.-%Al2O3 reinforced CoCrMo matrix composites. Corrosion and tribocorrosion behaviour of the composites were investigated in 8 g L−1 NaCl solution at body temperature. Corroded and worn surfaces were investigated by a field emission gun scanning electron microscope equipped with energy dispersive X-ray spectroscopy. After tribocorrosion experiments, wear rates were calculated using a profilometer. Results suggest that Al2O3 particle addition decreased the tendency of CoCrMo alloy to corrosion under both static and tribocorrosion conditions. However, no significant influence on the corrosion and wear rates was observed in composites mainly due to increased porosity and insufficient matrix/reinforcement bonding.

Filmes de Langmuir-Blodgett de nanopartículas de prata

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Análise do acabamento superficial e da potência consumida na usinagem de fresamento frontal e cilíndrico tangencial da madeira de eucalipto

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudos biológicos de nanopartículas de óxido de zinco: interação com proteínas e avaliação de “Burst” oxidativo de leucócitos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Pollination of Anemopaegma album (Bignoniaceae) with focus on floral nectar as the mediator of interactions with mutualistic and antagonistic bees

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Avaliação in vitro do tempo de fotopolimerização com led de alta potência de bráquetes ortodônticos e remoção de adesivo remanescente sob luz ultravioleta

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Geologia do depósito de ouro de C1-Santaluz no greenstone belt do rio Itapicuru, Brasil

Pós-graduação em Geociências e Meio Ambiente - IGCE

Caracterização morfológica e cristalográfica da zircônia após desgaste com pedra diamantada e elaboração de um protocolo para tratamento térmico regenerativo

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Citotoxicidade do ácido peracético: avaliação metabólica, estrutural e de morte em fibroblastos L929

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeitos de lasers de alta potência na superfície de cerâmicas vítreas de dissilicato de lítio e sua resistência de união à dentina humana

Pós-graduação em Odontologia Restauradora - ICT

Efeitos de lasers de alta potência na superfície de cerâmicas vítreas de dissilicato de lítio e sua resistência de união à dentina humana

Pós-graduação em Odontologia Restauradora - ICT

Titanium surface topography after brushing with fluoride and fluoride-free toothpaste simulating 10 years of use

Objectives: To conduct a controlled study contrasting titanium surface topography after procedures that simulated 10 years of brushing using toothpastes with or without fluoride. Methods: Commercially pure titanium (cp Ti) and Ti-6Al-4V disks (6 mm circle divide x 4 mm) were mirror-polished and treated according to 6 groups (n = 6) as a function of immersion (I) or brushing (B) using deionised water (W), fluoride-free toothpaste (T) and fluoride toothpaste (FT). Surface topography was evaluated at baseline (pretreatment) and post-treatment, using atomic force microscope in order to obtain three-dimensional images and mean roughness. Specimens submitted to immersion were submerged in the vehicles without brushing. For brushed specimens, procedures were conducted using a linear brushing machine with a soft-bristled toothbrush. Immersion and brushing were performed for 244 h. IFT and BFT samples were analysed under scanning electron microscope with Energy-Dispersive X-ray Spectroscopy (EDS). Pre and post-treatment values were compared using the paired Student T-test (alpha = .05). Intergroup comparisons were conducted using one-way ANOVA with Tukey post-test (alpha = .05). Results: cp Ti mean roughness (in nanometers) comparing pre and post-treatment were: IW, 2.29 +/- 0.55/2.33 +/- 0.17; IT, 2.24 +/- 0.46/2.02 +/- 0.38; IFT, 2.22 +/- 0.53/1.95 +/- 0.36; BW, 2.22 +/- 0.42/3.76 +/- 0.45; BT, 2.27 +/- 0.55/16.05 +/- 3.25; BFT, 2.27 +/- 0.51/22.39 +/- 5.07. Mean roughness (in nanometers) measured in Ti-6Al-4V disks (pre/post-treatment) were: IW, 1.79 +/- 0.25/2.01 +/- 0.25; IT, 1.61 +/- 0.13/1.74 +/- 0.19; IFT, 1.92 +/- 0.39/2.29 +/- 0.51; BW, 2.00 +/- 0.71/2.05 +/- 0.43; BT, 2.37 +/- 0.86/11.17 +/- 2.29; BFT, 1.83 +/- 0.50/15.73 +/- 1.78. No significant differences were seen after immersions (p > .05). Brushing increased the roughness of cp Ti and of Ti-6Al-4V (p < .01); cp Ti had topographic changes after BW, BT and BFT treatments whilst Ti-6Al-4V was significantly different only after BT and BTF. EDS has not detected fluoride or sodium ions on metal surfaces. Conclusions: Exposure to toothpastes (immersion) does not affect titanium per se; their use during brushing affects titanium topography and roughness. The associated effects of toothpaste abrasives and fluorides seem to increase roughness on titanium brushed surfaces. (C) 2012 Elsevier Ltd. All rights reserved.

The filler content of the dental composite resins and their influence on different properties

The purpose of this study was to compare the inorganic content and morphology of one nanofilled and one nanohybrid composite with one universal microhybrid composite. The Vickers hardness, degree of conversion and scanning electron microscope of the materials light-cured using LED unit were also investigated. One nanofilled (Filtek (TM) Supreme XT), one nanohybrid (TPH (R) 3) and one universal microhybrid (Filtek (TM) Z-250) composite resins at color A2 were used in this study. The samples were made in a metallic mould (4 mm in diameter and 2 mm in thickness). Their filler weight content was measured by thermogravimetric analysis (TG). The morphology of the filler particles was determined using scanning electron microscope equipped with a field emission gun (SEM-FEG). Vickers hardness and degree of conversion using FT-IR spectroscopy were measured. Filtek (TM) Z-250 (microhybrid) composite resin shows higher degree of conversion and hardness than those of Filtek (TM) Supreme XT (nanofilled) and TPH (R) 3 (nanohybrid) composites, respectively. The TPH3 (R) (nanohybrid) composite exhibits by far the lowest mechanical property. Nanofilled composite resins show mechanical properties at least as good as those of universal hybrids and could thus be used for the same clinical indications as well as for anterior restorations due to their high aesthetic properties. Microsc. Res. Tech. 75:758765, 2012. (C) 2011 Wiley Periodicals, Inc

Production of Fructooligosaccharides by Aspergillus phoenicis Biofilm on Polyethylene as Inert Support

Aspergillus phoenicis biofilms on polyethylene as inert support were used to produce fructooligosaccharides (FOS) in media containing 25% (m/V) of sucrose as a carbon source. The maximum production of total FOS (122 mg/mL), with 68% of 1-kestose and 32% of nystose, was obtained in Khanna medium maintained at 30 degrees C for 48 h under orbital agitation (100 rpm). At high concentrations of sucrose (30%, m/V), the recovery of FOS was higher than that observed at a low concentration (5%, m/V). High levels of FOS (242 mg/mL) were also recovered when using the biofilm in sodium acetate buffer with high sucrose concentration (50%, m/V) for 10 h. When the dried biofilm was reused in a fresh culture medium, there was a recovery of approx. 13.7% of total FOS after 72 h of cultivation at 30 C, and 10% corresponded to 1-kestose. The biofilm morphology, analyzed by scanning electron microscope, revealed a noncompact mycelium structure, with unfilled spaces and channels present among the hyphae. The results obtained in this study show that A. phoenicis biofilms may find application for FOS production in a single-step fermentation process, which is cost-effective in terms of reusability, downstream processing and efficiency.