磷酸盐激光玻璃聚（CH3）2Si（OC2H5）2防潮膜

以（CH3）2Si（OC2H5）2为前驱体，采用溶胶-凝胶与有机合成相结合的方法，制得稳定性良好的涂膜液。采用旋转涂膜法在掺钕磷酸盐激光玻璃棒端面涂制防潮膜，膜层固化后透过率达96．5％，获得的膜层表面粗糙度优良，均方根表面粗糙度（RMS）为1．659nm，平均粗糙度（RA）平均为1．321nm；在激光波长1053nm，脉冲宽度1 ns条件下膜层的激光破坏闽值可达10～14 J／cm^2。经过“神光Ⅱ”高功率激光器物理实验运行，膜层使用期为五年，并且已经在我国“神光Ⅲ”原型装置上试用。

磷酸盐激光玻璃凝胶防潮膜和减反膜

采用溶胶-凝胶方法制备（CH3）2Si（OC2H5）2预聚体涂膜液以及掺入SiO2悬胶体涂膜液改性，采用旋转法在掺钕磷酸盐激光玻璃棒端面涂制防潮膜，热处理后膜层固化。SiO2改性的CH3O防潮膜，热处理后的膜层耐摩擦性能明显改善。然后旋转涂制第二层多空性SiO2减反膜，涂膜胶体通过硅酸乙脂碱催化水解缩聚制得，减反膜的折射率为约1．25，玻璃棒涂膜后激光波长1053nm减少表面反射率6．5％-7．5％，双层膜激光破坏阈值12J／cm^2，1053nm／1ns，膜层表面粗糙度（RMS）2．523nm。直径20

高激光损伤阈值溶胶-凝胶ZrO2薄膜

采用醇热法水解氧氯化锆（ZrOCl2·8H2O）制备ZrO2溶胶，提拉法涂膜。采用粘度、粒度分布、折射率、IR、DSC、AFM等测试手段对溶胶和薄膜性能进行表征。结果表明，ZrO2溶胶颗粒的平均粒径为18．9nm，薄膜经300℃热处理后折射率可高达1．95，膜层表面均匀平整，表面平均粗糙度仅为0．561nm，膜层的激光损伤阈值为14J／cm^2（1064nm，1ns）。

Optical properties of dye-doped zirconia films by spectroscopic ellipsometry

The optical properties of zirconia films doped with rhodamine 6G and oxazine 725 by the sol-gel process were investigated using spectroscopic ellipsometry (SE). Accurate refractive index n and the extinction coefficient k were determined using a three-oscillator classical Lorentz model in the wavelength range of 300-800 nm. The derived refractive index of dye-doped films exhibited anomalous dispersion in the absorption region. Wavelength tunable output lasing action yellow and near-infrared wavelength region was achieved by DFB configuration using zirconia films doped with R6G and oxazine 725. (c) 2006 Elsevier B.V. All rights reserved.

Optical properties of zirconia-titania-ORMOSIL films for temperature tuning distributed feedback waveguide lasers

The zirconia-titania-ORMOSIL waveguide thin films with considerable optical quality were prepared by the sol-gel process. The refractive index (n) and the extinction coefficient (k) were determined by a scanning ellipsometer. Wavelength tunable output of distributed feedback waveguide lasing was demonstrated in Rhodamine 6G doped ZrO2 TiO2-ORMOSIL thin films by varying the temperature, and about 5.5 nm wavelength tuning range was achieved around the emission wavelength of 599 nm. The thermal-optic coefficient (dn/dT) of the active ZrO2-TiO2-ORMOSIL films was deduced. (c) 2005 Elsevier B.V. All rights reserved.

Effect of processing parameters on the optical properties of TiO2/ormosil planar waveguide

Hybrid TiO2/ormosil waveguiding films have been prepared by the sol-gel method at low thermal treatment temperature of 150° C. The influence of processing parameters including the molar ratios of titanium butoxide (Ti(OBu)(4))/3-glycidoxypropyltrimethoxysilane (GLYMO) and H2O/Ti(OBu)(4) (expressed as R), especially aging of sot on the optical properties was investigated. The optical properties of films were measured with scanning electron microscope (SEM), UV/VIS/NIR spectrophotometer (UV-Vis), m-line and the scattering-detection method. The results indicate that the film thickness increases with the increase of sol aging time, but the variation of refractive index as a function of sot aging time depends on the relative ratios of GLYMO to Ti(OBu)(4). Higher transmittance and lower attenuation of the planar waveguide can be obtained in the sol with lower Ti(OBu)(4) contents and shorter aging time.

Study of hybrid TiO2/ormosil films doped with laser dyes

TiO2/ormosil films doped with laser dyes have been prepared by the sol-gel method. Spectroscopic properties of the entrapped dyes are studied by the absorption and emission techniques. The results indicate that the absorption and fluorescence spectra of kiton red depend strongly on the properties of the ormosil matrices. The heat-treatment of the kiton red-doped film obviously leads to the increasing fluorescence intensity and the largest fluorescence intensity is obtained after heat-treatment of 150 degrees C for 2 h. However, the fluorescence intensity of the rhodamine 6G-doped film decreases with the increase of the heat-treatment temperature. (c) 2005 Elsevier B.V. All rights reserved.

Preparation and characterization of hybrid ZnO/ormosils films

Hybrid ZnO/ormosils Elms are prepared by the sol-gel method. A FT-IR spectrometer, 900 UV/VIS/NIR spectrophotometer, atomic force microscope, and ellipsometer are employed to investigate microstructure and optical properties of the films fired at different temperatures. The results show that the films with high transmittance and low surface roughness could be obtained at the heat-treatment temperature of 150 degrees C, the refractive index and thickness of the film are 1.413, 2.11 mu m, respectively. Higher temperatures (350 degrees C, 550 degrees C) change the Elm microstructure severely, and then decrease the transmittance of the films.

低损耗TiO2/Ormosil平面波导的制备及表征

abstract = {TiO₂/ormosil planar waveguide was prepared by sol-gel method at low thermal treatment temperature ( less than or equal 200°C). Scanning electron microscope, FT-IR spectrometer, spectrophotometer, atomic force microscopy, thermal analyzer, and dark m-line spectroscopy were used with the method of scattering-detection to investigate optical and structural properties. High optical quality waveguide film was obtained. The propagation loss of film was 0.569 dB/cm at a wavelength of 632.8 nm.

凝胶-燃烧法合成YAG：Eu^3＋纳米荧光材料的结构和发光性能

Y3Al5O12:Eu nanophosphors were synthesized by a gel combustion method. The structure of phosphors was characterized by XRD and FTIR. YAG phase came to occur when YAG:Eu precursors were sintered at 800 ℃, although the phase was mainly amorphous. The organ

NiFeMnO4系列热敏电阻的溶胶-凝胶制备技术研究

用溶胶-凝胶（Sol-gel）技术以及柠檬酸自燃方法制备了NiMn2.0-xFexO4（x=0、0．1、0．15、0．2、0．3）纳米氧化物粉体，并将得到的超细粉体进行压片、烧结、封装等工艺制得热敏电阻。用XRD、SEM、电阻测量等手段表征了烧结体材料的晶相、微观形貌以及电阻性能。电阻测量结果表明：随着铁离子的增加，所得热敏电阻的阻值增大。在所有获得的材料中，其灵敏度B值大于4300K，可认为是一种具有实际应用价值的负系数热敏电阻。

Nd：YAG透明陶瓷的烧成及其显微结构

由溶胶一凝胶／燃烧合成结合法合成了Nd：YAG(掺钕钇铝石榴石，neodymium—doped yttrium aluminium garnet)粉体，用真空烧结法制备了Nd：YAG透明陶瓷。研究了显微结构随烧结温度和保温时间的变化，并对透明陶瓷的晶界结构和成分分布进行了表征。随着烧结温度的提高和保温时间的延长，Nd：YAG陶瓷的密度增大，晶形发育完整，透过率提高。晶粒内部和晶界的化学组成基本相同。所制备的Nd：YAG透明陶瓷在激光工作波长1064nm的透过率达到75％。

溶胶-凝胶法制备MgxZn1-xO及其特性

采用溶胶-凝胶法制备了不同组分（x=0．1—0．3）的MgxZn1-xO前驱体，并对它进行不同温度的热处理（550℃-1000℃）。X射线衍射（XRD）结果表明，Mg0.1Zn0.9O具有和ZnO一样的衍射谱，为六方纤锌矿结构，而且随着热处理温度的升高，ZnO衍射峰的强度逐渐增强，半高宽不断减小；Mg元素掺杂浓度增大后，出现了MgO的峰位。扫描电子显微镜（SEM）显示Mg0．1Zn0.9O晶粒粒径分布较均匀；热处理温度升高，晶粒的尺寸不断变大。用室温荧光光谱（PL）分析了经过550—1000℃热处理获得的

Synthesis and characterization of room-temperature ferromagnetism in Fe- and Ni-co-doped In2O3

Observation of room-temperature ferromagnetisin in Fe- and Ni-co-doped In2O3 samples (In0.9Fe0.1-xNix)(2)O-3 (0 <= x <= 0.1) prepared by citric acid sol-gel auto-igniting method is reported. All of the samples with intermediate x values are ferromagnetic at roomtemperature. The highest saturation magnetization (0.453 mu B/Fe + Ni ions) moment is reached in the sample with x = 0.04. The highest solubility of Fe and Ni ions in the In2O3 lattice is around 10 and 4 at%, respectively. The 10 at% Fe-doped sample is found to be weakly ferromagnetic, while the 10at% Ni-doped sample is paramagnetic. Extensive structure including Extended X-ray absorption fine structure (EXAFS), magnetic and magneto-transport including Hall effects studies on the samples indicate the observed ferromagnetism is intrinsic rather than from the secondary impurity phases. (c) 2007 Elsevier Ltd. All rights reserved.

ZnO纳米线的水热法生长

本文采用两步湿化学法在玻璃衬底上制备了ZnO纳米线.首先,利用Sol-gel方法在载玻片上制备含有ZnO纳米颗粒的薄膜作为“种子”衬底.然后,利用水热法在“种子”衬底上生长了高度取向的ZnO纳米线.并对“种子”衬底和随后生长的ZnO纳米线进行了X射线衍射（XRD）、扫描电子形貌图（SEM）和原子力显微镜（AFM）等分析.结果表明“种子”衬底为大范围内纳米颗粒均匀一致的ZnO 薄膜.通过水热法制备的ZnO纳米线的直径在50～80nm,平均直径为60nm,长度大约为2μm.该ZnO纳米线除了具有很强的紫外发光