Synthesis and characterization of (phenolphthalein/4,4 '-thiodiphenol) PES copolymers

Copolymers based on monomers phenolphthalein (PP)/4,4'-thiodiphenol (Bis-T)/4,4'-dichlorodiphenylsulfone (DCDPS) were prepared by a route involving the toluene, N-methyl-2-pyrrolidone and anhydrous potassium carbonate synthesis. The range of optimum reaction temperature was between 185 and 195 degrees C. The copolymers were characterized by C-13 NMR, differential scanning calorimetry (DSC) and torsion braid analysis. It was found that all of the copolymers were random and homogeneous and their glass transition temperatures (T-g) decreased linearly with an increase of Bis-T contents in the copolymers. The thermal stability determined by thermogravimetry analysis in air atmosphere indicated that the copolymer had better resistance to thermo-oxidative degradation. Dynamic mechanical measurement showed that (PP/Bis-T) PES copolymers containing 0-50 mol% of Bis-T components had two secondary relaxations. (C) 1998 Elsevier Science Ltd. All rights reserved.

Morphology and properties of [PPO-PDMS-PHS](n) segmented ternary copolymers

The morphology and properties of [ PPO-PDMS-PHS](n) segmented ternary copolymers were investigated by DMA, TEM and SAXS techniques. It is shown that the continuous phase of [PPO-PDMS-PHS](n) is the compatible phase composed of PDMS, PPO and PHS segments, and that there exist two dispersed phases, i, e. the PDMS phase and a mixed phase of half hard ( PHS) and hard ( PPO) segments. The tan delta vs. T curve of the segmented ternary copolymer with 66.7% (W/W) PDMS shows a rather high plateau in the temperature range from -120 degrees C to 200 degrees C, which indicates that the copolymer has the characteristics of microphase separation as well as compatibility of block copolymers, respectively. Meanwhile, it has good tensile properties, which means that [PPO-PDMS-PHS](n) has overcome the weakness of low strength of block or segmented copolymers containing PDMS.

Barrier property and structure of acrylonitrile/acrylic copolymers

A series of acrylonitrile (AN) copolymers with methyl acrylate (MA) or ethyl acrylate (EA) as comonomer (5-23 wt%) was prepared by free-radical copolymerisation. The permeability coefficients of the copolymers to oxygen and carbon dioxide were measured at 1.0 MPa and at 30 degrees C, and those to water vapor also measured at 100% relative humidity and at 30 degrees C. All the AN/acrylic copolymers are semicrystalline. As the acrylate content increase, the permeability coefficients of the copolymers to oxygen and carbon dioxide are increased progressively, but those to water vapor are decreased progressively. The gas permeability coefficients of the polymers were correlated with free-volume fractions or the ratio of free volume to cohesive energy.

Studies on poly(ether ether ketone ketone) poly(ether biphenyl ether ketone ketone) copolymers and blends

We synthesized a series of polymers: poly(ether ether ketone ketone)(PEEKK), poly(ether biphenyl ether ketone ketone) (PEBEKK) and their copolymer by polycondensation, We also prepared a series of PEEKK-PEBEKK blends, By using DSC method, we found that T-g of the copolymers and the blends rose with the increasing of biphenyl contents in the polymers, T-c of the copolymers and the blends is higher than the corresponding homopolymer. From the results, we think that PEEKK-PEBEKK copolymer and blends are miscible and the copolymer is random.

Crystallization behavior of poly(propylene)/polyamide 1010 blends using poly(propylene)-graft glycidyl methacrylate as compatibilizer

Polyamide 1010/poly(propylene) (PA1010/PP) blends were investigated with and without the addition of poly(propylene)-graft-glycidyl methacrylate (PP-g-GMA). The effect of the compatibilizer on the thermal properties and crystallization behavior was determined by differential scanning calorimetry and wide-angle X-ray diffraction. From the results it is found that the crystallization of PA 1010 is significantly affected by the presence of PP-g-GMA. PP/PA 1010 (75/25) blends containing higher amounts of PP-g-GMA show concurrent crystallization at the crystallization temperature of PP. Isothermal crystallization kinetics also were performed in order to investigate the influence of the compatibilized process on the nucleation and growth mechanism. In the PP/PA 1010 (25/75) blends, concurrent crystallization behavior was not observed, even though the amount of PPg-GMA was high.

Characterization of propylene/ethylene copolymers sequentially polymerized with delta-TiCl3/Et2AlCl catalyst system

Morphological studies of a series of propylene/ethylene sequential polymers have been carried out by permanganic etching and transmission electron microscopy, as an aid to characterization, in conjunction with differential scanning calorimetry. The materials were synthesized using a titanium-based catalyst, with propylene and either ethylene or ethylene/propylene mixture introduced successively, with the aim of examining whether a proportion of block copolymer is obtained. These materials show a complicated phase structure which does not simply reflect polymerization time but varies greatly, especially in regard to the order of introduction of the monomers, and their morphology differs in a number of ways from that of typical commercial materials. Comparison of the materials, as synthesized and after extraction with heptane, suggests that there is a certain amount of material which can compatibilize polypropylene- and ethylene-rich phases, but it was not possible to decide whether it does in fact have block structure.

Synthesis of a series of chiral copolymers with azo groups and investigations of reversible liquid crystalline alignment induced by the LB films of these materials

A series of liquid crystalline copolymers, poly{2-hydroxyethyl methacrylate}-co-{6-[4-(S-2-methyl-1-butyloxycarbonylphenylazo)phenoxy]hexyl methacrylate} with an azobenzene moiety as photoreactive mesogenic unit, was prepared and investigated by using DSC, polarized optical microscopy and X-ray diffraction. The results show that these polymers exhibit smectic phases. Z-type Langmuir-Blodgett films of these copolymers were successfully deposited onto calcium fluoride and quartz. Reversible homeotropic and planar liquid crystal alignments were induced by using the photochromism of the LB films of one of the copolymers containing 20.6 mol % of the azo unit.

The double-melting behavior of poly(ether diphenyl ether ketone)

Poly(ether diphenyl ether ketone) (PEDEK) synthesized by the nucleophilic route has the following chemical structure: [GRAPHICS] At some given temperatures for a given time isothermally crystallized PEDEK sample exhibits two endothermic peaks which are similar to PEEK and PEEKK The melting behavior of PEDEK crystallized from the glassy state is investigated through differential scanning calorimeter (DSC). We consider that the high-melting peak is related to the perfect crystals and the low-melting peak is associated with a few imperfect crystals. (C) 1997 John Wiley & Sons, Inc.

Photoluminesence and electroluminescence of the blue emission of devices based on poly(p-phenylenevinylene) copolymers

Bright blue polymer light-emitting diodes have been fabricated by using the poly(p-phenylenevinylene)-based copolymers with 10 C long aliphatic chains as the electroluminescent layers, PBD in PMMA and Alq(3) as the electron-transporting layers, and aluminum as the cathode. The multilayer structure devices show 190 cd/m(2) light-emitting brightness at 460 nm, 15 V turn-on vol- tage. It is found that the intensities of photoluminescence and electroluminescence (EL) increase with increasing aliphatic chain length, the EL intensity and operation stability of these polymer light-emitting diodes can be improved by reasonable design of the structure.

Miscibility of linear low density polyethylene (LLDPE)-graft-poly(methyl methacrylate) with poly(vinylidene fluoride) (PVF2) and its application as compatibilizer LLDPE/PVF2 blends

Differential scanning calorimetry (DSC), Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) were used to study the miscibility of blends of a graft copolymer of poly(methyl methacrylate) on linear low density polyethylene (LLDPE-g-PMMA, G-3) with poly(vinylidene fluoride)(b) (PVF2) and the compatibilization of blends of LLDPE/PVF2. The specific interaction between PMMA side chains and PVF2 in G-3/PVF2 binary blends is weaker than that between the homopolymers PMMA and PVF2. There are two states of PVF2 in the melt of a G-3/PVF2 (60/40, w/w) blend, one as pure PVF2 and the other interacting with PMMA side chains. The miscibility between PMMA side chains and PVF2 affects the crystallization of PVF2. LLDPE-g-PMMA was demonstrated to be a good compatibilizer in LLDPE/PVF2 blends, improving the interfacial adhesion and dispersion in the latter. Diffusion of PMMA side chains into PVF2 in the interfacial region reduces the crystallization rate and lowers the melting point (T-m) and the crystallization temperature (T-c) of PVF2 in the blends.

Properties of ethylene-propylene copolymer/PA-1010 blends using ethylene-propylene copolymer-graft-acrylic acid as a compatibilizing agent

The modification of ethylene-propylene copolymer (EP) has been accomplished by radical EP-graft-acrylic acid (EP-g-AA) has been used to obtain ternary PA/EP/EP-g-AA blends by melt mixing. Different blend morphologies were observed by scanning electron microscopy; the domain size of the EP-dispersed phase in the polyamide 1010 matrix of compatibilized blends decreased compared with that of uncompatibilized blends. It is found that EP-g-AA used as the third component has a profound effect on the mechanical properties of the resulting blends. This behavior has been attributed to serious chemical interactions taking place between the two components. Thermal analysis shows that some thermal properties of PA in compatibilized PA/EP/EP-g-AA changed because of chemical reactions taken place during the blending process. Wide angle x-ray diffraction measurements also confirmed this result. (C) 1996 John Wiley & Sons, Inc.

Structure and thermal properties of vinylidene chloride/acrylics copolymers

A series of vinylidene chloride (VDC) copolymers with methyl acrylate (MA) or butyl acrylate (BA) as comonomer (not more than 10%) was prepared by free-radical suspension copolymerization. The effects of comonomer structure, copolymer composition, and reaction condition (such as polymerization temperature on crystallinity) and thermal properties (such as melting temperature and decomposition temperature) were investigated. All VDC/acrylics copolymers studied here are semicrystalline and have more than one crystalline structure. The melting temperature of MA/VDC copolymers is decreased progressively with increase in MA content. The decomposition temperature of MA/VDC copolymers is slight increased gradually with increase in MA content. MA/VDC copolymers have lower melting temperature compared with BA/VDC copolymers with same VDC composition. The melting temperature of VDC copolymers increases with increase in polymerization temperature and decomposition temperature of those is almost independent of polymerization temperature. (C) 1996 John Wiley & Sons, Inc.

Study of semicrystalline-amorphous diblock copolymers .1. Microphase separation, glass transition and crystallization of tetrahydrofuran methyl methacrylate diblock copolymers

The microphase separation, glass transition and crystallization of two series of tetrahydrofuran-methyl methacrylate diblock copolymers (PTHF-b-PMMA), one with a given PTHF block of M(n) = 5100 and the other with a given PTHF block of (M) over bar(n) = 7000, were studied in this present work. In the case of solution-cast materials, the microphase separation of the copolymer takes place first, with crystallization then gradually starting in the formed PTHF microphase. The T-g of the PMMA microphase shows a strong dependence on the molecular weight of the PMMA block, while the T-g of the PTHF microphase shows a strong dependence on the copolymer composition. The non-isothermal crystallization temperature (T-c) of the diblock copolymer decreases rapidly and continuously with the increase in the amorphous PMMA weight fraction; the lowest T-c of the copolymer is ca. 35 K lower than the T-c of the PTHF homopolymer. There also exists a T-c dependence on the molecular weight of the PTHF block. In addition, when the major component of the copolymer is PMMA, a strong dependence of the crystallizability of the copolymer on the molecular weight of the PTHF block is observed; the higher the molecular weight, then the stronger its crystallizability. The melting temperature of the block copolymer is dependent on the copolymer composition and the molecular weight of its crystallizable block. Copyright (C) 1996 Elsevier Science Ltd.

Synthesis and characterization of copolymers of dialkyl fumarates

Radical copolymerisations of di-iso-propyl fumarate (DiPF) with di-n-propyl fumarate (DnPF), di-n-butyl fumarate (DnBF), di-n-amyl-fumarate (DnAF), di-n-heptyl fumarate (DnHF) and di-ethyl-hexyl fumarate (DEHF) were studied. The reactivity ratios for the following monomer pairs, DiPF/DnPF, DiPF/DnBF, DiPF/DnAF, DiPF/DnHF and DiPF/DEHF, were determined. The structures of the copolymers were examined by H-1-NMR and WAXD. Some properties of the copolymers were examined.