Cassava is a widely grown root crop which accumulates two cyanogenic glucosides, linamarin and lotaustralin. Linamarin accounts for more than 80% of the cassava cyanogenic glucosides. It is a β-glucoside of acetone cyanohydrin and ethyl-methyl-ketone-cyanohydrin. Linamarin β-linkage can only be broken under high pressure, high temperature and use of mineral acids, while its enzymatic break occurs easily. Linamarase, an endogenous cassava enzyme, can break this β-linkage. The enzymatic reaction occurs under optimum conditions at 25°C, at pH 5.5 to 6.0. Linamarin is present in all parts of the cassava plant, being more concentrated on the root and leaves. If the enzyme and substrate are joined, a good detoxification can occur. All the cassava plant species are known to contain cyanide. Toxicity caused by free cyanide (CN-) has already been reported, while toxicity caused by glucoside has not. The lethal dose of CN- is 1 mg/kg of live weight; hence, cassava root classification into toxic and non-toxic depending on the amount of cyanide in the root. Should the cyanide content be high enough to exceed such a dose, the root is regarded as toxic. Values from 15 to 400 ppm (mg CN-/kg of fresh weight) of hydrocyanic acid in cassava roots have been mentioned in the literature. However, more frequent values in the interval 30 to 150 ppm have been observed. Processed cassava food consumed in Brazil is safe in regard to cyanide toxicity.

Superconducting vortex fluctuations in YBa2Cu3O7-δ

Measurements of magnetization in YBa2Cu3O7-δ single crystals were performed for applied fields H parallel and perpendicular to the ab planes. The data show a temperature T = T* at which the magnetization M(T*) is independent of the applied field. This result is interpreted as due to vortex fluctuations of an anisotropic 3-D superconductor.

Microstructural development of ZnO varistor during reactive liquid phase sintering

The microstructural evolution, grain growth and densification for the varistor systems ZnO-Bi2O3 (ZB), ZnO-Bi2O3-Sb2O3 (ZBS), ZnO-Bi2O3-Sb2O3-MnO-Cr 2O3-CoO (ZBSCCM) were studied using constant heating rate sintering, scanning electron microscopy (SEM) and in situ phase formation measurement by high temperature X-ray diffraction (HT-XRD). The results showed that the densifying process is controlled by the formation and decomposition of the Zn2Bi3Sb3O14 pyrochlore (PY) phase for the ZBS and ZBSCCM systems. The addition of transition metals (ZBSCCM system) alters the formation and decomposition reaction temperatures of the pyrochlore phase and the morphology of the Zn7Sb2O12 spinel phase. Thus, the spinel grains act as inclusions and decrease the ZnO grain growth rate. Spinel grain growth kinetics in the ZBSCCM system showed an n value of 2.6, and SEM and HT-XRD results indicate two grain growth mechanisms based on coalescence and Ostwald ripening. © 1996 Chapman & Hall.

Metal-insulator transitions in pressed pellets of BF4 - doped poly(3-methylthiophene)

From Electron Spin Resonance (ESR) data in pressed pellets of BF4 - doped Poly(3-methylthiophene) (P3MT) we obtained simultaneously the paramagnetic susceptibility and. the microwave conductivity. We observed a transition from a high-temperature insulator state to a room-temperature metallic state. Around 240K. evidence of a Peierls transition is observed, but if the sample is slowly cooled, this transition is partially suppressed. DC conductivity data taken with the sample quenched to 79 K show a non-linear I-V response for very small electric fields, suggesting depinning of Charge-Density Wave (CDW). The data for heating and cooling the system above room temperature, indicate the formation of bipolarons.

Universal scaling in BCS superconductivity in three dimensions in non-s waves

The solutions of a renormalized BCS equation are studied in three space dimensions in s, p and d waves for finite-range separable potentials in the weak to medium coupling region. In the weak-coupling limit, the present BCS model yields a small coherence length ξ and a large critical temperature, T c, appropriate for some high-T c materials. The BCS gap, T c, ξ and specific heat C s(T c) as a function of zero-temperature condensation energy are found to exhibit potential-independent universal scalings. The entropy, specific heat, spin susceptibility and penetration depth as a function of temperature exhibit universal scaling below T c in p and d waves.

Carriers escape mechanisms in shallow InGaAs/GaAs quantum wells grown on vicinal (001) GaAs substrates

We used photoluminescence spectroscopy in order to investigate the carriers escape mechanisms in In0.15Ga0.85As/GaAs quantum wells grown on top of nominal (001) and 2°-, 4°-and 6°-off (001) towards (111)A GaAs substrates. We described the escape processes using two models that fit the Arrhenius plot of the integrated PL intensity as a function of the inverse of the sample temperature. In the first model, we considered equal escape probability for electrons and holes. In the second one, we assumed that a single type of carrier can escape from the well. At high temperature, the first model fits the experimental data well, whereas, between 50 K and 100 K, the second model has to be taken into account to describe the data. We observed that the escape activation energy depends on the misorientation angle. An unusual behavior was noted when the full width at half maximum of the photoluminescence main emission was plotted as a function of the sample temperature. We showed that the escape process of the less-confined carriers drives this behavior. © 1999 Academic Press.

Ceramic coating for refractories protection against carbon oxidation, Part 1: Protection mechanisms

For retarding carbon oxidation in refractories during the preheating of metallurgical furnaces, a ceramic coating, made mainly of sodium phosphosilicate and clay was developed. The coating presents high adherence to the substrate with no swelling. The coating was characterized by thermal analysis, X-ray diffraction at room temperature (XRD) and at high temperature (HTXRD), X-ray fluorescence and scanning electronic microscopy (SEM). The glass transition temperature is reached at 800 °C and only glassy phase is observed above this temperature. Thus the mechanism of protection seems to be the formation of a glassy phase on the surface of the refractory, and the coating tends to be more efficient at temperatures higher than 800 °C.

Preparation and characterization of glass-ceramic materials in the BaO-Li2O-ZrO2-SiO2 system and their dependence on treatment temperatures

The preparation and characterization of transparent glass-ceramics in the composition of 30Li2O:5ZrO2:xBaO:(100-x) SiO2 with x = 0, 5, 10, 15, and 20 mol% are described. Glasses were melted in a platinum crucible at 1100°C for 2 h and then heat-treated at 900°C for 3 h. The characterizations were performed by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman and infrared spectroscopy, and scanning electron microscopy (SEM). The experimental results indicate that there was a structural change in the glass-ceramics as the BaO concentration in the mixture increased. In the XRD patterns of samples without heat treatment, only the halo was observed. After heat treatment, the appearance of the materials was verified by X-ray diffraction peaks. The reorganization of the amorphous solid was confirmed by Raman and IR spectroscopy along with XPS and SEM, with a more homogeneous phase formation being observed.

Influence of heat treatment on LiNbO3 thin films prepared on Si(111) by the polymeric precursor method

The effects of heat-treatment temperature on LiNbO3 thin films prepared by the polymeric precursor method were investigated. The precursor solution was deposited on Si(111) substrates by dip coating. X-ray diffraction and thermal analyses revealed that the crystallization process occurred at a low temperature (420 °C) and led to films with no preferential orientation. High-temperature treatments promoted formation of the LiNb3O8 phase. Scanning electron microscopy, coupled with energy dispersive spectroscopy analyses, showed that the treatment temperature also affected the film microstructure. The surface texture - homogeneous, smooth, and pore-free at low temperature - turned into an `islandlike' microstructure for high-temperature treatments.

Thermal inactivation of Phytophthora nicotianae

Phytophthora nicotianae was added to pasteurized soil at the rate of 500 laboratory-produced chlamydospores per gram of soil and exposed to temperatures ranging from 35 to 53°C for 20 days. The time required to reduce soil populations to residual levels (0.2 propagule per gram of soil or less) decreased with increasing temperatures. Addition of cabbage residue to the soil reduced the time required to inactivate chlamydo spores. Temperature regimes were established to simulate daily temperature changes observed in the field, with a high temperature of 47°C for 3 h/day, and were good estimators of the efficacy of soil solarization for the control of P. nicotianae in soil. Cabbage amendment reduced the time required to inactivate chlamydospores of P. nicotianae and its effect was more pronounced at lower temperature regimes.

Direct amorphous-to-cubic perovskite phase transformation for lead titanate

The phase evolution of lead titanate processed by the polymeric precursor method was investigated by thermal analysis, X-ray diffraction, and high-resolution transmission electron microscopy. The results showed that the cubic perovskite PbTiO3 (PT) phase is formed from an inorganic amorphous precursor at a temperature of 444 °C. A gradual transition from cubic to tetragonal perovskite PT was observed with the increase of calcination time at this temperature. HRTEM results showed that the cubic PT particles have a size of around 5 nm. The identification of cubic PT as an intermediate phase supports the hypothesis that the chemical homogeneity was kept at the molecular level during the synthesis process, with no cation segregation.

Thermal analysis of conductive blends of PVDF and poly(o-methoxyaniline)

The thermal behavior of blends of poly(vinylidene fluoride), or PVDF, and poly(o-methoxyaniline) doped with toluene sulfonic acid was studied by thermogravimetic analysis, electrical conductivity measurements, differential scanning calorimetry, X-ray diffraction and scanning electron microscopy. Blends with thermal and electrical conductivity stabler than the conductive polymer alone were obtained. Nevertheless, degradation occurs after a long period of time (500 h) at high temperatures. The possible association of the conductivity decay with dopant loss, degradation and structural and morphological changes of the blend is discussed. (C) 2000 Elsevier Science Ltd.

Pressure-induced phase transitions in Zr-rich PbZr1-xTixO3 ceramics

A Raman study of structural changes in the Zr-rich PbZr1-x TixO3 (PZT) system under hydrostatic pressures up to 5.0 GPa is presented. We observe that externally applied pressure induces several phase transitions in PZT ceramics among phases with orthorhombic (Ao), rhombohedral low-temperature (RLT), and rhombohedral high-temperature (RHT) symmetries (all found in PZT at ambient pressure and room temperature). Each of the compositions investigated (0.02 ≤ x ≤ 0.14) exhibits a high-pressure phase with orthorhombic (OI′) symmetry. We further report a detailed study of the pressure dependence of Raman frequencies to elucidate the phase transitions and to provide a set of pressure coefficients for the high-pressure phases.

Genetic interactions of yeast eukaryotic translation initiation factor 5a (eIF5A) reveal connections to poly(A)-binding protein and protein kinase C signaling

The highly conserved eukaryotic translation initiation factor eIF5A has been proposed to have various roles in the cell, from translation to mRNA decay to nuclear protein export. To further our understanding of this essential protein, three temperature-sensitive alleles of the yeast TIF51A gene have been characterized. Two mutant eIF5A proteins contain mutations in a proline residue at the junction between the two eIFSA domains and the third, strongest allele encodes a protein with a single mutation in each domain, both of which are required for the growth defect. The stronger tif51A alleles cause defects in degradation of short-lived mRNAs, supporting a role for this protein in mRNA decay. A multicopy suppressor screen revealed six genes, the overexpression of which allows growth of a tif51A-1 strain at high temperature; these genes include PAB1, PKC1, and PKC1 regulators WSC1, WSC2, and WSC3. Further results suggest that eIFSA may also be involved in ribosomal synthesis and the WSC/PKC1 signaling pathway for cell wall integrity or related processes.

Maturity degree of composts from municipal solid wastes evaluated by differential scanning calorimetry

Differential scanning calorimetry (DSC) in association with chemical analysis was applied to assess the maturity reached by the organic fraction of Municipal Solid Wastes (MSW) subjected to composting processes with manual and fixed aeration and sampled at different composting times. Thermograms showed that the difference in the treatments, i.e., the manual aeration and the fixed aeration, had no relevant effect on the stabilization and maturation of OM in the substrates. Common thermal effects observed were: a low temperature endotherm assigned to dehydration and/or loss of peripheral polysaccharides chains; a medium temperature exotherm assigned to loss of peptidic structures, and a high temperature exotherm assigned to oxydation and polycondensation of aromatic nuclei of the molecule. Results obtained suggest that in the experimental conditions used, a shorter time of composting (about 30 d) appears adequate, in order to limit the extended mineralization of OM, whereas a prolonged composting time (up to 132 d) would produce a compost of poor quality with high ash content and low OM content.