Fatigue life studies in carbon dual-phase steels

An investigation has been conducted to examine the morphological influence on fatigue life of low carbon steel with dual phase microstructure. The results showed that dual-phase microstructure, composed by ferrite and martensite had superior symmetrical bending fatigue strength when compared with ferrite-pearlite steel. Through those tests, evidences of different mechanisms were verified (such as ferrite cyclic hardening, slip band formation and beginning of crack nucleation and propagation). Based on the fatigue tests results, various mechanisms stages were discussed associated with different microstructure morphology. Copyright (C) 1996 Published by Elsevier B.V. Limited.

Control of retention and fatigue-free characteristics in CaBi4Ti4O15 thin films prepared by chemical method

Ferroelectric CaBi4Ti4O15 (CBTi144) thin films were deposited on Pt/Ti/SiO2/Si substrates by the polymeric precursor method. The films present a single phase of layered-structured perovskite with polar axis orientation after annealing at 700 degrees C for 2 h in static air and oxygen atmosphere. The a/b-axis orientation of the ferroelectric film is considered to be associated with the preferred orientation of the Pt bottom electrode. It is noted that the films annealed in static air showed good polarization fatigue characteristics at least up to 10(10) bipolar pulse cycles and excellent retention properties up to 10(4) s. on the other hand, oxygen atmosphere seems to be crucial in the decrease of both, fatigue and retention characteristics of the capacitors. Independently of the applied electric field, the retained switchable polarization approached a nearly steady-state value after a retention time of 10 s. (C) 2006 Elsevier B.V. All rights reserved.

Analyses of fatigue data in 4340 high strength steel after cadmium electroplating

Bending fatigue tests were carried out to clarify the effects of heat treatment parameters: temperature and time after cadmium electroplating on a high strength steel, to avoid hydrogen embrittlement. Temperatures heat of 190 degrees C, 230 degrees C, 250 degrees C and 300 degrees C at 3, 8 and 24 hours together with the base material electroplated, with and without heat treatment, resulted in 14 conditions studied with respect to fatigue behaviour. Statistical data analysis was performed to identify the best combination temperature/time regarding fatigue strength of the ABNT 4340 steel and the results obtained revealed that the fatigue strength depend on temperature/time conditions.

Panoramic evaluation of mesiodistal axial inclinations of maxillary anterior teeth in orthodontically treated subjects

The objectives of this study were to evaluate, through panoramic radiographs, the mesiodistal axial inclinations of the maxillary anterior teeth at the beginning and end of nonextraction orthodontic treatment, and to compare the results with the mesiodistal axial inclinations of a control sample with normal (acceptable) occlusions. Methods: the experimental sample consisted of 40 white patients (20 male, 20 female; mean age, 14 years) with Class I maloccusions who were treated orthodontically with a standard edgewise (not preadjusted) technique without extractions. The mean treatment period was 1.6 years. The control sample comprised 42 white subjects (14 male, 28 female; age range, 12-17 years) with untreated normal (acceptable) occlusions. Panoramic radiographs were taken of the patients at the beginning (T1) and end (T2) of treatment. The mean values of the mesiodistal axial inclination at T1 were compared with the mean values at T2, and both were compared with the mesiodistal axial inclinations of the control sample. Results- the mesiodistal axial inclinations of the maxillary anterior teeth of the experimental group at T1 were different from those of the control group for 50% of the evaluated teeth. In contrast, the inclinations at T2 were consistent with the normal anatomical configuration of the controls. Conclusions: the panoramic radiograph is an effective tool for evaluating the mesiodistal axial inclinations of maxillary anterior teeth.

Evaluation of an electroless nickel interlayer on the fatigue & corrosion strength of chromium-plated AISI 4340 steel

Despite the fact that chromium electrodeposition results in protection against wear and corrosion, combined with chemical resistance and good lubricity, the reduction in fatigue strength of base metal and environmental requirements causes one to search for possible alternatives. To improve the fatigue and corrosion resistance of AISI 4340 steel, an experimental study has been made for an intermediate electroless nickel layer deposited on base metal. The objective of this study was to analyze the effect of nickel underplate on the fatigue and corrosion strength of hard-chromium-plated AISI 4340 steel. Deposition of the conventional wear-resistant hard chromium plating leads to a decrease in mechanical properties of the base metal, especially the fatigue strength. Rotating bending fatigue tests results indicate better performance for conventional hard chromium plating. Good corrosion resistance in salt fog exposure was obtained for the accelerated hard chromium plating. Experimental data showed higher fatigue and corrosion resistance for samples prepared with accelerated hard chromium plate over electroless nickel plate, when compared with samples without electroless nickel underplate.

Retention force and fatigue strength of overdenture attachment systems

This study evaluated retention force and fatigue resistance of two overdenture attachment systems. Twenty samples (O-ring and Bar-Clip) from two manufacturers (Conexao Sistemas de Protese and Lifecore Biomedical) were prepared and divided into four groups: (i) Conexao/O-ring; (ii) Conexao/Bar-Clip; (iii) Lifecore/O-ring and (iv) Lifecore/Bar-Clip, with five samples in each group. They were submitted to mechanical fatigue test using a servohydraulic machine performing 5500 cycles of insertion and removal (f=0.8 Hz), immersed in artificial saliva. Retention force values were obtained three times (0, 3000 and after 5500 cycles) simulating the clinical service, using a tensile strength at 1 mm min(-1) and load cell of 1 kN. Data were analysed with analysis of variance and Tukey's test at 5% level. Results showed that Conexao/Bar-Clip specimens had significantly higher retention values than Lifecore/Bar-Clip (44.61 and 18.44 N, respectively), Conexao/O-ring specimens had significantly lower values than Lifecore/O-ring (13.91 and 19.75 N, respectively). Conexao/Bar-Clip values were always significantly higher than those of Conexao/O-ring group (44.61 and 13.91 N, respectively). Lifecore (O-ring and Bar-Clip) presented similar values (19.75 and 18.44 N, respectively). The systems evaluated showed satisfactory retention force values, before and after fatigue testing. Conexao/Bar-Clip specimens presented the highest values. A 5-year simulation of insertion and removal did not decrease retention values or fracture components.

Effects of high intensity running to fatigue on isokinetic muscular strength in endurance athletes

The objective of this study was to examine the effects of high intensity exhaustive running exercise on the muscular torque capacity of the knee extensors for two types of contraction (concentric and eccentric) at different angular velocities (60 and 180 degrees/s) in well-trained runners. Eleven male runners specialized in middle and long-distance running volunteered to participate in this study. Initially each subject performed, on different days, two familiarization sessions on an isokinetic dynamometer and an incremental treadmill test to volitional exhaustion to determine the velocity associated with the onset of blood lactate accumulation (OBLA). The subjects then returned to the laboratory on two occasions, separated by at least seven days, to perform maximal isokinetic knee contractions at each of the velocities under eccentric (Ecc) and concentric (Con) conditions. Conducted randomly, one test was performed after a standardized warm-up period of 5 min at 50% VO2 max. The other test was performed 15 min after continuous running at OBLA until volitional exhaustion. Following this high intensity exercise there was a significant reduction of Con at 60 degrees/s and a significant reduction of Ecc at both velocities. Percent strength losses after running exercise were significantly different between contraction types only at 180 degrees/s. We can conclude that the reduction in isokinetic peak torque of the knee extensors after a session of high intensity exhaustive running exercise at OBLA depends on the contraction type and angular velocity.

Effect of post length on the fatigue resistance of bovine teeth restored with bonded fiber posts: A pilot study

This study evaluated the influence of the cementation length of glass fiber-reinforced composite (FRC) on the fatigue resistance of bovine teeth restored with an adhesively cemented FRC. Thirty roots of single-rooted bovine teeth were allocated to 3 groups (n = 10), according to the ratio of crown length/root length (post cementation length): group 1 = 2/3, group 2 = 1/2, and group 3 = 1/1. The roots were prepared, the fiber posts (FRC Postec Plus) were cemented, and the specimens were submitted to 2 million mechanical cycles. After fatigue testing, a score was given based on the number of fatigue cycles until fracture, and data were submitted to statistical analysis. All specimens were resistant to fatigue. Taking into account the methodology and results of this study, the evaluated fiber posts can be cemented based on the ratio of crown/root at 1/1. Further clinical studies must be conducted to verify this ratio.

MAPPING CORRELATION-FUNCTIONS OF SCHWINGER AND AXIAL MODELS

We show that all Green's functions of the Schwinger and axial models can be obtained one from the other. In particular, we show that the two models have the same chiral anomaly. Finally it is demonstrated that the Schwinger model can keep gauge invariance for an arbitrary mass, dispensing with an additional gauge group integration.

Fatigue-free behavior of Bi3.25La0.75Ti3O12 thin films grown on several bottom eletrodes by the polymeric precursor method

Fatigue-free Bi3.25La0.75Ti3O12 (BLT) thin films were grown on LaNiO3,RuO2, and La0.5Sr0.5CoO3 bottom electrodes in a microwave furnace at 700 degreesC for 10 min. The remanent polarization (P-r) and the drive voltage (V-c) were in the range of 11-23 muC/cm(2) and 0.86-1.56 V, respectively, and are better than the values found in the literature. The BLT capacitors did not show any significant fatigue up to 10(10) read/write switching cycles. (C) 2004 American Institute of Physics.

Fatigue crack growth of Al 7475 T761 under constant and variable amplitude loading

Experimental programs in constant and variable amplitude loading were performed to obtain a x N curves and to study retardation in fatigue crack growth due to overloads. The main aim of this research program was to analyse the effect of overload ratio and number of overload peaks. The effect of underloads, before and after the overload blocks was also studied. The generalised equation of Paris-Erdogan type was used for modelling of obtained data on crack propagation under constant amplitude load.