Highly efficient separation of dsDNA fragments on glass chips by using an ultralow viscosity sieving matrix

A novel protocol has been established to separate dsDNA fragments with high efficiency on glass chips by using an ultralow viscosity sieving matrix with added glucose. Low-molecular-weight hydroxypropylmethylcellulose (HPMC), with a viscosity nearly equivalent to that of water, was used to electrophoretically separate fluorescent inter-calator-labeled double-stranded DNA (dsDNA) fragments on microfluidic glass chips. In comparison with conventional sieving protocols, low-molecular-weight HPMC as sieving matrix could result in reduced running cost and analysis time, in addition to a comparable separation efficiency of dsDNA fragments. In this paper, the addition of glucose was investigated to enhance the separation of DNA in the lowest viscosity polymer evaluated. The effect of staining dye and field strength were also evaluated. At an applied electric field strength of 200 V/cm, satisfactory resolution of the PBR322/HaeIII DNA marker could be achieved within 4 min by using 2% HPMC-5 with 6% glucose added. Coelectrophoresing PCR product along with phiX174/HaeIII DNA sizing marker was also demonstrated by using the ultralow viscosity HPMC-5 solution on a glass chip.

Crystal structure of microwave dielectric ceramics Ba[(Mg1-xCdx)(0.33)Nb-0.67]O-3

A series of complex perovskite solid solutions of Ba[(Mg1-xCdx)(0.33)Nb-0.67]O-3 have been synthesized by the columbite method. Detailed Rietveld refinement of their X-ray diffraction data show that Ba[(Mg1-xCdx)0(.33)Nb(0.67)]O-3 has an order trigonal structure. The ordering degree as determined by the B-site occupancies increases with the partial substitution of Cd for Mg.

Glass formation ability and mechanical properties of Ti40Cu40Zr10Ni10 alloy

Melt-spun ribbon and bulk samples in cylindrical rod form with diameter ranging from 2 mm to 4 mm of Ti40Cu40Zr10Ni10 alloy were prepared by melt-spinning technique and copper mould casting method, respectively. The microstructure, thermal stability and mechanical properties of the bulk samples were investigated. A completely glassy single phase is formed in the 2 mm rod sample. Increasing the diameter of the rod samples resulted in the formation of CuTi crystalline phase in the 3 mm and 4 mm rod samples.

Effect of shear on the crystallization behavior of glass bead filled polypropylene

Linkam CSS450 optical shearing stage, wide-angle X-ray diffraction (WAXD) and small-angle X-ray scattering(SAXS) were used to investigate the effect of shear on crystal structure and crystallization morphology of the glass bead filled polypropylene( PP). The results indicate that the glass bead worked as nucleating agent for the glass bead filled PP, compared with pure PP it restrained the formation of beta-crystal after shear treatment. When the mean size of glass bead is smaller(4 mu m) shear rate had less effect on the formation of beta-crystal of PP obviously.

Surface modification of bioactive glass nanoparticles and the mechanical and biological properties of poly(L-lactide) composites

Novel bioactive glass (13G) nanoparticles/poly(L-lactide) (PLLA) composites were prepared as promising bone-repairing materials. The BG nanoparticles (Si:P:Ca = 29:13:58 weight ratio) of about 40 run diameter were prepared via the sol-gel method. In order to improve the phase compatibility between the polymer and the inorganic phase, PLLA (M-n = 9700 Da) was linked to the surface of the BG particles by diisocyanate. The grafting ratio of PLLA was in the vicinity of 20 wt.%. The grafting modification could improve the tensile strength, tensile modulus and impact energy of the composites by increasing the phase compatibility.

Preparation, structure and dielectric properties of (Ba1-xSrx)(2)NaNb5O15 ceramics

In this study the tungsten-bronze type tetragonal (Ba1-xSrx)(2)NaNb5O15 system as a kind of lead-free ferroelectric ceramics has been synthesized by low-temperature combustion method. Microstructure and dielectric properties of (Ba1-xSrx)(2)NaNb5O15 system were also investigated. X-ray diffraction (XRD) study confirms the formation of single-phase tetragonal compounds in the crystal system at room temperature. The TEM photograph shows that the particles synthesized by low-temperature combustion method are uniform with an average particle size of 30nm in diameter.

Glass wafers bonding via Diels-Alder reaction at mild temperature

In this paper, we introduced a novel bonding method of glass wafers by Diels-Alder reaction at mild temperature. After standard hydroxylization and aminosilylation, two wafers were modified by 2-furaldehyde and maleic anhydride, respectively. Then they were brought into close contact and tightly held with a clamping fixture. A strong bonding could be achieved by annealing for 5 h at 200 degrees C. Bonding strength is as high as 1.78 MPa and sufficient for most application of microfluidic chips.

MICROSTRUCTURE AND MECHANICAL PROPERTIES OF TI-BASED METALLIC GLASS MATRIX COMPOSITES

Ti40Cu40Ni10Zr10-xScx (x = 0.5 and 1, at%) alloys were prepared by copper mould casting method. Microstructures of the phi 3 mm rod alloys were investigated by XRD and SEM. The results showed that the phi 3 mm rods were glassy matrix with TiCu crystalline phase. Mechanical properties were studied by compressive test. Ti40Cu40Ni10Zr9Sc1 alloy exhibited good compressive strength over 2200 MPa and superior compressive deformation is about 7.9%.

High-pressure sintered yttria stabilized zirconia ceramics

Fast densification of 8YSZ ceramics under a high pressure of 4.5 GPa was carried out at different temperatures (800, 1000, 1450 degrees C), by which a high relative density above 92% could be obtained. FT-Raman spectra indicate that the 8YSZ underwent a phase transition from partially tetragonal to partially cubic phase as temperatures increase from 1000 to 1450 degrees C when sintering under high pressure. The electrical properties of the samples under different high-pressure sintering conditions were measured by complex impedance method. The total conductivity of 0.92 x 10(-2) S cm(-1) at 800 degrees C has been obtained for 8YSZ under high pressure at 1450 degrees C, which is about 200 degrees C lower than that of the samples prepared by conventional pressureless sintering.