Upconversion luminescence in Ho3+/Yb3+- and Tb3+/Yb3+-codoped fluorogermanate glass and glass ceramic

Energy-transfer excited upconversion luminescence in Ho3+/Yb3+- and Tb3+/Yb3+ -codoped PbGeO3-PbF2-CdF2 glass and glass-ceramic under infrared excitation is investigated. In Ho3+/Yb3+-codoped samples, green (545 nm), red (652 nm), and near-infrared (754 nm) upconversion emission corresponding to the S-5(2) (F-5(4)) -> I-5(8), F-5(5) -> I-5(8), and S-5(2)(F-5(4)) -> I-5(7) transitions, respectively, was observed. Blue (490 nm) emission assigned to the F-5(2,3) -> I-5(8) transition was also detected. In the Tb3+/Yb3+-codoped system, bright UV-visible emission around 384, 415, 438, 473-490, 545, 587, and 623 nm, identified as due to the D-5(3)((5)G(6)) -> F-7(J)(J = 6, 5, 4) and D-5(4) -> F-7(J)(J = 6, 5, 4, 3) transitions, was measured. The comparison of the upconversion process in glass ceramic and its glassy precursor revealed that the former samples present much higher upconversion efficiencies. The dependence of the upconversion emission upon pump power, and doping contents was also examined. The results indicated that successive energy-transfer between ytterbium and holmium ions and cooperative energy-transfer between ytterbium and terbium ions followed by excited-state absorption are the dominant upconversion excitation mechanisms herein involved. The viability of using the samples for three-dimensional solid-state color displays is also discussed. (c) 2007 Elsevier B.V. All rights reserved.

Cr3+ and Cr4+ luminescence in glass ceramic silica

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Crystallization study of SrSnO3:Fe

Alkaline earth stannates have recently become important materials in ceramic technology due to its application as humidity sensor. In this work, alkaline earth stannates doped with Fe3+ were synthesized by the polymeric precursor method, with calcination at 300 A degrees C/7 h and between 400 and 1100 A degrees C/4 h. The powder precursors were characterized by TG/DTA after partial elimination of carbon. Characterization after the second calcination step was done by X-ray diffraction, infrared spectroscopy, and UV-vis spectroscopy. Results confirmed the formation of the SrSnO3:Fe with orthorhombic perovskite structure, besides SrCO3 as secondary phase. Crystallization occurred at 600 A degrees C, being much lower than the crystallization temperature of perovskites synthesized by solid state reaction. The analysis of TG curves indicated that the phase crystallization was preceded by two thermal decomposition steps. Carbonate elimination occurred at two different temperatures, around 800 A degrees C and above 1000 A degrees C.

Broadband NIR Emission in Sol-Gel Er(3+)-Activated SiO(2)-Ta(2)O(5) Glass Ceramic Planar and Channel Waveguides for Optical Application

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Ceramic materials in dentistry: historical evolution and current practice

Dental ceramics are presented within a simplifying framework allowing for facile understanding of their development, composition and indications. Engineering assessments of clinical function are dealt with and literature is reviewed on the clinical behaviour of all-ceramic systems. Practical aspects are presented regarding the choice and use of dental ceramics to maximize aesthetics and durability, emphasizing what we know and how we know it.

Characterization of dense lead lanthanum titanate ceramics prepared from powders synthesized by the oxidant peroxo method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Rietveld refinement, microstructure, conductivity and impedance properties of Ba[Zr0.25Ti0.75]O-3 ceramic

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Application of compression test in analysis of mechanical and color changes in grapefruit juice powder as related to glass transition and water activity

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Yellow ZnxNi1-xWO4 pigments obtained using a polymeric precursor method

New tungstate-based ceramic pigments, displaying ZnxNi1-xWO4 stoichiometry, were obtained at low temperature using a polymeric precursor method. The powder precursors were milled in an attritor mill in an alcoholic rnedium and heat treated for 12 h. yielding homogeneous and crystalline powder pigments. Characterization (TG/DTA, XRD, IR and colorimetry) showed that mass loss increased with increasing Zn contents. Despite the presence of secondary phases and impurities, the wolframite phase was present in all samples. IR analysis revealed bands related to Me-O and [WO6](6-) group stretching was observed. The intensity of the yellow color of the pigments increased with increasing amount of nickel. (c) 2007 Elsevier Ltd. All fights reserved.

Ceramic raw materials from the State of Maranhao, Brazil. Part 1: chemical and mineralogical characterization and technological properties of clays from Sao Luis, Rosario, Pinheiro and Mirinzal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Adhesive Quality of Self-adhesive and Conventional Adhesive Resin Cement to Y-TZP Ceramic Before and After Aging Conditions

Purpose: This study evaluated the adhesive quality of simplified self-adhesive and conventional resin cements to Y-TZP in dry and aged conditions. Methods: Y-TZP ceramic blocks (N=192) (5 x 5 x 2 mm) were embedded in acrylic resin and randomly divided into two groups, based on surface conditioning: 96% isopropanol or chairside tribochemical silica coating and silanization. Conditioned ceramics were divided into four groups to receive the resin cements (Panavia F 2.0, Variolink II, RelyX U100 and Maxcem). After 24 hours, half of the specimens (n=12) from each group were submitted to shear bond strength testing (0.5 nun/minute). The remaining specimens were tested after 90 days of water storage at 37 degrees C and thermocycling (12,000x, 5 degrees C-55 degrees C). Failure types were then assessed. The data were analyzed using three-way ANOVA and the Tukey's test (alpha=0.05). Results: Significant effects of ceramic conditioning, cement type and storage conditions were observed (p<0.0001). The groups cleaned using alcohol only showed low bond strength values in dry conditions and the bond strength was reduced dramatically after aging. Groups conditioned using silica coating and silanization showed higher bond strengths both in dry and aged conditions. A high number of specimens failed prematurely prior to testing when they were cleaned using 96% isopropanol. Conclusion: Overall, silica coating and silanization showed higher, stable bond strengths with and without aging. The durability of resin-ceramic adhesion varied, depending on the adhesive cement type.

Quantitative Phase Analyses Through The Rietveld Method with X-Ray Powder Diffraction Data of Heat-Treated Carbamazepine Form III

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nanomechanical properties of glass-ceramic films obtained by pressure impregnation of oxide powders on commercial float glass surfaces

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Optical and dielectric relaxor behaviour of Ba(Zr0.25Ti0.75)O-3 ceramic explained by means of distorted clusters

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

IR reflectance characterization of glass-ceramic films obtained by high pressure impregnation of SnO2 nanopowders on float glass

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)