Fabrication and Infrared Optical Properties of Nano Vanadium Dioxide Thin Films

Vanadium dioxide thin films were fabricated by ion beam sputtering on Si3N4/SiO2/Si after a post reductive annealing process in a nitrogen atmosphere. X-ray Diffraction (XRD), scanning electron microscope (SEM), and X-ray photoelectron spectroscopy (XPS) were employed to analyze the effects of post annealing temperature on crystallinity, morphology, and composition of the vanadium oxide thin films. Transmission properties of vanadium dioxide thin films were measured by Fourier transform-infrared (FT-IR) spectroscopy. The results showed that the as-deposited vanadium oxide thin films were composed of non-crystalline V2O5 and a tetragonal rutile VO2. After annealing at 400 degrees C for 2 h, the mixed phase vanadium oxide (VOx) thin film changed its composition and structure to VO2 and had a (011) oriented monoclinic rutile structure. When increasing the temperature to 450 degrees C, nano VO2 thin films with smaller grains were obtained. FT-IR results showed that the transmission contrast factor of the nano VO2 thin film was more than 0.99 and the transmission of smaller grain nano VO2 thin film was near zero at its switched state. Nano VO2 thin film with smaller grains is an ideal material for application in optical switching devices.

Experimental study of mode field evolution of dual-core photonic crystal fiber

The accurate mode field profile of high negative dispersion dual-core photonic crystal fiber (DCPCF) is measured. The mode field evolution of DCPCF with wavelength is studied experimentally for the first time. The measurement result shows that no individual inner core mode or outer core mode exists, but two modes coexist simultaneously, and either one of them is dominant. The mode field evolution versus wavelength indicates that the wavelength range where the modes coupling takes place between inner core and outer core is broader than that of theoretical design.

面向有差异群体的联合决策方案

公平性、透明性是联合决策的基本安全需求.结合多机构商务合作背景,利用具有同态性质的Paillier公钥密码系统和门限密码技术,提出了面向有差异群体的联合决策策略与方案,并对其安全性进行了分析和证明.

PHOTOLUMINESCENCE OF ORDERED GA0.5IN0.5P GROWN BY METALORGANIC VAPOR-PHASE EPITAXY

Optical properties of ordered Ga0.5In0.5P epitaxial layers grown by metalorganic vapor phase epitaxy are investigated by photoluminescence (PL) in a temperature range of 10-200 K using excitation power densities between 0.35 W/cm(2) and 20 W/cm(2). It is found that the intensity of the highest-energy PL peak of the ordered Ga0.5In0.5P epilayer decreases first, then increases and finally goes down again with increasing temperature. A model of ordered Ga0.5In0.5P epitaxial layers is proposed, in which the ordered Ga0.5In0.5P epilayer is regarded as a type-II quantum well structure with band-tail states, and the dependence of PL spectra on the temperature and excitation intensity is reasonably explained. (C) 1995 American Institute of Physics.

纳米二氧化钒薄膜的制备及红外光学性能

采用双离子束溅射方法在Si_3N_4/SiO_2/Si基底表面沉积氧化钒薄膜,在氮气气氛下热处理获得二氧化钒薄膜.利用x射线衍射(XRD)、扫描电子显微镜(SEM)和X射线光电子能谱(XPS)研究了热处理温度对氧化钒薄膜晶体结构、表面形貌和组分的影响,利用傅里叶变换红外光谱(FT-IR)对二氧化钒薄膜的红外透射性能进行了测试分析.结果表明,所制备的氧化钒薄膜以非晶态V_2O_5;和四方金红石结构VO_2为主,经400℃、2 h热处理后获得了(011)择优取向的单斜金红石结构纳米VO_2薄膜,提高热处理温度至450℃,纳米结构VO_2薄膜的晶粒尺寸减小.FT-IR结果显示,纳米VO_2薄膜透射率对比因子超过0.99,高温关闭状态下透射率接近0.小晶粒尺寸纳米VO_2:薄膜更适合在热光开关器件领域应用.

Wet Oxidation of AlxGa1-xAs/GaAs Distributed Bragg Reflectors

The wet oxidation of AlGaAs with high Al content in a distributed Bragg reflectors （DBR） is studied by scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. Some voids distribute along the oxide/GaAs interfaces due to the stress induced by the wet oxidation of the AlGaAs layers. These voids decrease the shrinkage of the Al2O3 layers to 8% instead of the theoretical 20% when compared to the unoxidized AlGaAs layers. With the extension of oxidation time, the reactants are more completely transported to the front interface and the products are more completely transported out along the porous interfaces. As a result,the oxide quality is better.

Design and Fabrication of Thermo-Optic 4×4 Switching Matrix in Silicon-on-Insulator

A rearrangeable nonblocking thermo-optic 4×4 switching matrix,which consists of five 2×2 multimode interference-based Mach-Zehnder interferometer(MMI-MZI) switch elements，is designed and fabricated.The minimum and maximum excess loss for the matrix are 6.6 and 10.4dB,respectively.The crosstalk in the matrix is measured to be between －12 and －19.8dB.The switching speed of the matrix is less than 30μs.The power consumption for the single switch element is about 330mW.