Synthesis, characterization, EPR, photo and thermoluminescence properties of YAlO3:Ni2+ nanophosphors

YAlO3:Ni2+ (0.1 mol%) doped nanophosphor was synthesised by a low temperature solution combustion method. Powder X-ray diffraction (PXRD) confirms the orthorhombic phase of yttrium aluminate (YAlO3) along with traces of Y3Al5O12. Scanning Electron microscopy (SEM) shows that the powder particles appears to be spherical in shape with large agglomeration. The average crystallite sizes appeared to be in the range 45-90 nm and the same was confirmed by transmission electron microscopy (TEM) and Williamson-Hall (W-H) plots. Electron Paramagnetic Resonance (EPR) and photoluminescence (PL) studies reveal that Ni2+ ions are in octahedral coordination. Thermoluminescence (TL) glow curve consists of two peaks with the main peak at similar to 224 degrees C and a shouldered peak at 285 degrees C was recorded in the range 0.2-15 kGy gamma-irradiated samples. The TL intensity was found to be increasing linearly for 224 degrees C and 285 degrees C peaks up to 1 kGy and thereafter it shows sub-linear (up to 8 kGy) and saturation behavior. The trap parameters namely activation energy (E), order of kinetics (b), frequency factor (s) at different gamma-doses were determined using Chens glow peak shape and Luschiks methods then the results are discussed in detail. Simple glow peak structure, the 224 degrees C peak in YAlO3:Ni2+ nanophosphor can be used in personal dosimetry. (C) 2012 Elsevier B.V. All rights reserved.

Synthesis, structural and thermoluminescence properties of YAlO3:Dy3+ nanophosphors

Thermoluminescence properties of YAlO3:Dy3+ nanophosphor prepared by a low temperature solution combustion (SC) method using oxalyl dihydrazide as a fuel were studied and the results were compared to bulk phosphor prepared by solid state (SS) synthesis. Powder X-ray diffraction patterns confirm the orthorhombic phase of SC and SS methods. Rietveld refinement was used to estimate the cell parameters of undoped and Dy3+ doped YAlO3. Scanning electron micrographs reveal dumbbell shape particles. Electron paramagnetic resonance spectra of YAlO3:Dy3+ nanophosphors were studied at 293 K, 77 K and 10 K. Thermoluminescence responses of SC and SS prepared phosphor were studied using gamma irradiation in the dose range 0.1-6 kGy at a warming rate of 1 degrees C s (1) at room temperature (RT). The optimized concentrations of Dy3+ ions in YAlO3 was found to be 3 mol%. The trapping parameters (i. e. activation energy, frequency factor, order of kinetic) of all the individual peaks of the glow curves have been analysed by using Chen's method. The low fading and linear response in the wide range (0.1-1 kGy) suggests the possibility of usage of SC prepared phosphor in dosimeter applications. (C) 2013 Elsevier B. V. All rights reserved.

Nanodiamond-Based Thermal Fluids

Dispersions of nanodiamond (average size similar to 6 nm) within dielectric insulator mineral oil are reported for their enhanced thermal conductivity properties and potential applications in thermal management. Dynamic and kinematic viscosities-very important parameters in thermal management by nanofluids-are investigated. The dependence of the dynamic viscosity is well-described by the theoretical predictions of Einstein's model. The temperature dependence of the dynamic viscosity obeys an Arrhenius-like behavior, where the activation energy and the pre-exponential factor have an exponential dependence on the filler fraction of nanodiamonds. An enhancement in thermal conductivity up to 70% is reported for nanodiamond based thermal fluids. Additional electron microscopy, Raman spectroscopy and X-ray diffraction analysis support the experimental data and their interpretation.

Stepwise Crystallization: Illustrative Examples of the Use of Metalloligands Cu-6(mna)(6)](6-) and (Ag-6(Hmna)(2)(mna)(4)](4-) (H(2)mna=2-Mercapto Nicotinic Acid) in the Formation of Heterometallic Two- and Three-Dimensional Assemblies with brucite, pcu, and sql Topologies

Three new inorganic coordination polymers, {Mn(H2O)(6)]-Mn-2(H2O)(6)](Cu-6(mna)(6)]center dot 6H(2)O}, 1, {Mn-4(OH)(2)(H2O)(10)] (Cu-6(mna)6]center dot 8H(2)O}, 2, and {Mn-2(H2O)(5)]Ag-6(Hmna)(2)(mna)(4)]center dot 20H(2)O}, 3, have been synthesized at room temperature through a sequential crystallization route. In addition, we have also prepared and characterized the molecular precursor Cu-6(Hmna)(6)]. Compounds 1 and 3 have a two-dimensional structure, whereas 2 has a three-dimensional structure. The formation of 2 has been achieved by minor modification in the synthetic composition, suggesting the subtle relationship between the reactant composition and the structure. The hexanudear copper and silver duster cores have Cu center dot center dot center dot Cu and Ag center dot center dot center dot Ag distances close to the sum of the van der Waals radii of Cu1+ and Ag1+, respectively. The connectivity between Cu-6(mna)(6)](6-) cluster units and Mn2+ ions gives rise to a brucite related layer in 1 and a pcu-net in 2. The Ag-6(Hmna)(2)(mna)(4)](4-) cluster in 3, on the other hand, forms a sql-net with Mn2+. Compound 1 exhibits an interesting and reversible hydrochromic behavior, changing from pale yellow to red, on heating at 70 degrees C or treatment under a vacuum. Electron paramagnetic resonance studies indicate no change in the valence states, suggesting the color change could be due to changes in the coordination environment only. The magnetic studies indicate weak antiferromagnetic behavior. Proton conductivity studies indicate moderate proton migrations in 1 and 3. The present study dearly establishes sequential crystallization as an important pathway for the synthesis of heterometallic coordination polymers.

Inter molecular azide-diisocyanate coupling: new insights for energetic solid propellants

Hydroxyl terminated azide binders can undergo a spurious reaction with diisocyanates to form tetrazoline-5-one via an inter molecular 1,3-dipolar cycloaddition reaction apart from urethane/allophanate groups which has been overlooked. This has serious implications on solid propellants. The computed activation barrier using density functional theory (DFT) for urethane formation reaction is 28.4 kJ mol(-1) and that for tetrazoline-5-one formation reaction is 108.0 kJ mol(-1). DFT studies reveal that the rate limiting step of the reaction is 1,3-dipolar cycloaddition between azide and isocyanate. A dual cure was observed in the temperature ranges 42-77 degrees C and 78-146 degrees C by differential scanning calorimetry (DSC) and rheological studies, confirming multiple reactions. Tetrazoline-5-one formation was confirmed by Fourier transform infrared spectroscopy (FTIR) and solid state nuclear magnetic resonance spectroscopy (NMR).

Temperature-Dependent Magnetic and EPR Studies of Bulk and Nanoparticles of Bi0.1Ca0.9MnO3

We report temperature-dependent magnetic and electron paramagnetic resonance (EPR) properties of bulk and nanoparticle samples of Bi0.1Ca0.9MnO3 (BCMO). The nanoparticles of BCMO (dia similar to 50 nm) were prepared by the standard sol-gel technique and bulk samples by solid-state reaction method. We have investigated the magnetic ordering in the two samples by carrying out temperature-dependent magnetic and EPR studies and compared their properties. According to earlier reports, antiferromagnetic and ferromagnetic orders coexist in the bulk sample of Bi0.1Ca0.9MnO3. Our magnetization and EPR results show the existence of ferromagnetism in the bulk sample which is present in the nanosample as well but with somewhat weakened strength with the size reduction.

Effect of Size Reduction on Magnetic Ordering in Sm1-x Ca (x) MnO3 (x=0.35, 0.65 and 0.92) Manganites: Magnetic and EMR Studies

We have employed the highly sensitive electron magnetic resonance technique complimented by magnetization measurements to study the impact of size reduction on the magnetic ordering in nanosized Sm1-x Ca (x) MnO3 (x = 0.35, 0.65 and 0.92). In the bulk form, x = 0.35 sample shows a charge ordering transition at 235 K followed by a mixed magnetic phase, the sample with x = 0.65 exhibits charge order below 275 K and shows an antiferromagnetic insulator phase below 135 K while that with x = 0.92 has a ferromagnetic-cluster glass ground state. Thus, a comparative study of magnetic ground states of bulk and nanoparticles (diameter similar to 25 nm) enables us to investigate size-induced effects on different types of magnetic ordering. It is seen that in the bulk samples the temperature dependences of the EPR parameters are quite different from each other. This difference diminishes for the nanosamples where all the three samples show qualitatively similar behavior. The magnetization measurements corroborate this conclusion.

Conductivity studies on microwave synthesized glasses

Conductivity measurements have been made on x V O-2(5) - (100-x) 0.5 Na2O + 0.5 B2O3] (where 10 a parts per thousand currency sign x a parts per thousand currency sign 50) glasses prepared by using microwave method. DC conductivity (sigma) measurements exhibit temperature-and compositional-dependent trends. It has been found that conductivity in these glasses changes from the predominantly `ionic' to predominantly `electronic' depending upon the chemical composition. The dc conductivity passes through a deep minimum, which is attributed to network disruption. Also, this nonlinear variation in sigma (dc) and activation energy can be interpreted using ion-polaron correlation effect. Electron paramagnetic resonance (EPR) and impedance spectroscopic techniques have been used to elucidate the nature of conduction mechanism. The EPR spectra reveals, in least modified (25 Na2O mol%) glasses, conduction is due to the transfer of electrons via aliovalent vanadium sites, while in highly modified (45 Na2O mol%) glasses Na+ ion transport dominates the electrical conduction. For highly modified glasses, frequency-dependent conductivity has been analysed using electrical modulus formalism and the observations have been discussed.

Cross-sectional structure of tetrahedral amorphous carbon thin films

A cross-sectional transmission electron microscope study of the low density layers at the surface and at the substrate-film interface of tetrahedral amorphous carbon (ta-C) films grown on (001) silicon substrates is presented. Spatially resolved electron energy loss spectroscopy is used to determine the bonding and composition of a tetrahedral amorphous carbon film with nanometre spatial resolution. For a ta-C film grown with a substrate bias of -300 V, an interfacial region approximately 5 nm wide is present in which the carbon is sp2 bonded and is mixed with silicon and oxygen from the substrate. An sp2 bonded layer observed at the surface of the film is 1.3 ± 0.3 nm thick and contains no detectable impurities. It is argued that the sp2 bonded surface layer is intrinsic to the growth process, but that the sp2 bonding in the interfacial layer at the substrate may be related to the presence of oxygen from the substrate.

Stress reduction and bond stability during thermal annealing of tetrahedral amorphous carbon

A comprehensive study of the stress release and structural changes caused by postdeposition thermal annealing of tetrahedral amorphous carbon (ta-C) on Si has been carried out. Complete stress relief occurs at 600-700°C and is accompanied by minimal structural modifications, as indicated by electron energy loss spectroscopy, Raman spectroscopy, and optical gap measurements. Further annealing in vacuum converts sp3 sites to sp2 with a drastic change occurring after 1100°C. The field emitting behavior is substantially retained up to the complete stress relief, confirming that ta-C is a robust emitting material. © 1999 American Institute of Physics.

Analysis of the ellipsometric spectra of amorphous carbon thin films for evaluation of the sp3-bonded carbon content

Using spcctroscopic ellipsometry (SE), we have measured the optical properties and optical gaps of a series of amorphous carbon (a-C) films ∼ 100-300 Å thick, prepared using a filtered beam of C+ ions from a cathodic arc. Such films exhibit a wide range of sp3-bonded carbon contents from 20 to 76 at.%, as measured by electron energy loss spectroscopy (EELS). The Taue optical gaps of the a-C films increase monotonically from 0.65 eV for 20 at.% sp3 C to 2.25 eV for 76 at.% sp3 C. Spectra in the ellipsometric angles (1.5-5 eV) have been analyzed using different effective medium theories (EMTs) applying a simplified optical model for the dielectric function of a-C, assuming a composite material with sp2 C and sp3 C components. The most widely used EMT, namely that of Bruggeman (with three-dimensionally isotropic screening), yields atomic fractions of sp3 C that correlate monotonically with those obtained from EELS. The results of the SE analysis, however, range from 10 to 25 at.% higher than those from EELS. In fact, we have found that the volume percent sp3 C from SE using the Bruggeman EMT shows good numerical agreement with the atomic percent sp3 C from EELS. The SE-EELS discrepancy has been reduced by using an optical model in which the dielectric function of the a-C is determined as a volume-fraction-weighted average of the dielectric functions of the sp2 C and sp3 C components. © 1998 Elsevier Science S.A.

Analysis of amorphous carbon thin films by spectroscopic ellipsometry

Using spectroscopic ellipsometry (SE), we have measured the optical properties of amorphous carbon (a-C) films ∼ 10-30 nm thick prepared using a filtered beam of C+ ions from a cathodic arc. Such films exhibit a wide range of sp3-bonded carbon contents from 20 to 76 at.% as measured by electron energy loss spectroscopy (EELS), and a range of optical gaps from 0.65 eV (20 at.% sp3 C) to 2.25 eV (76 at.% sp3 C) as measured by SE. SE data from 1.5 to 5 eV have been analyzed by applying the most widely used effective medium theory (EMT) namely that of Bruggeman with isotropic screening, assuming a model of the material as a composite with sp2 C and sp3 C components. Although the atomic fractions of sp3 C deduced by SE with the Bruggeman EMT correlate monotonically with those obtained by EELS, the SE results range from 10 to 25 at.% higher. The possible origins of this discrepancy are discussed within the framework of an optical composite. Improved agreement between SE and EELS is obtained by employing a simple form for the EMT, in which the effective dielectric function is determined as a volume-fraction-weighted average of the dielectric functions of the two components. © 1998 Elsevier Science B.V. All rights reserved.

Two-dimensional simulation of inductive plasma sources with self-consistent power deposition

A time averaged two-dimensional fluid model including an electromagnetic module with self-consistent power deposition was developed to simulate the transport of a low pressure radio frequency inductively coupled plasma source. Comparsions with experiment and previous simulation results show, that the fluid model is feasible in a certain range of gas pressure. In addition, the effects of gas pressure and power input have been discussed.

Behavior of ar plasma formed in a high-density plasma source - an ecr reactor

In order to develop the ultra-large scale integration(ULSI), low pressure and high density plasma apparatus are required for etching and deposit of thin films. To understand critical parameters such as the pressure, temperature, electrostatic potential and energy distribution of ions impacting on the wafer, it is necessary to understand how these parameters are influenced by the power input and neutral gas pressure. In the present work, a 2-D hybrid electron fluid-particle ion model has been developed to simulate one of the high density plasma sources-an Electron Cyclotron Resonance (ECR) plasma system with various pressures and power inputs in a non-uniform magnetic field. By means of numerical simulation, the energy distributions of argon ion impacting on the wafer are obtained and the plasma density, electron temperature and plasma electrostatic potential are plotted in 3-D. It is concluded that the plasma density depends mainly on both the power input and neutral gas pressure. However, the plasma potential and electron temperature can hardly be affected by the power input, they seem to be primarily dependent on the neutral gas pressure. The comparison shows that the simulation results are qualitatively in good agreement with the experiment measurements.

Metal-Free Polymethyl Methacrylate (PMMA) Nanoparticles by Enamine "Click" Chemistry at Room Temperature

"Click" chemistry has become an efficient avenue to unimolecular polymeric nanoparticles through the self-crosslinking of individual polymer chains containing appropriate functional groups. Herein we report the synthesis of ultra-small (7 nm in size) polymethyl methacrylate (PMMA) nanoparticles (NPs) by the "metal-free" cross-linking of PMMA-precursor chains prepared by reversible addition-fragmentation chain transfer (RAFT) polymerization containing beta-ketoester functional groups. Intramolecular collapse was performed by the one-pot reaction of beta-ketoester moieties with alkyl diamines in tetrahydrofurane at r.t. (i.e., by enamine formation). The collapsing process was followed by size exclusion chromatography and by nuclear magnetic resonance spectroscopy. The size of the resulting PMMA-NPs was determined by dynamic light scattering. Enamine "click" chemistry increases the synthetic toolbox for the efficient synthesis of metal-free, ultra-small polymeric NPs.