Reliability assessment of Cobb angle measurements using manual and digital methods

BACKGROUND CONTEXT: The vertebral spine angle in the frontal plane is an important parameter in the assessment of scoliosis and may be obtained from panoramic X-ray images. Technological advances have allowed for an increased use of digital X-ray images in clinical practice. PURPOSE: In this context, the objective of this study is to assess the reliability of computer-assisted Cobb angle measurements taken from digital X-ray images. STUDY DESIGN/SETTING: Clinical investigation quantifying scoliotic deformity with Cobb method to evaluate the intra- and interobserver variability using manual and digital techniques. PATIENT SAMPLE: Forty-nine patients diagnosed with idiopathic scoliosis were chosen based on convenience, without predilection for gender, age, type, location, or magnitude of the curvature. OUTCOME MEASURES: Images were examined to evaluate Cobb angle variability, end plate selection, as well as intra- and interobserver errors. METHODS: Specific software was developed to digitally reproduce the Cobb method and calculate semiautomatically the degree of scoliotic deformity. During the study, three observers estimated the Cobb angle using both the digital and the traditional manual methods. RESULTS: The results showed that Cobb angle measurements may be reproduced in the computer as reliably as with the traditional manual method, in similar conditions to those found in clinical practice. CONCLUSIONS: The computer-assisted method (digital method) is clinically advantageous and appropriate to assess the scoliotic curvature in the frontal plane using Cobb method. (C) 2010 Elsevier Inc. All rights reserved.

Influence of visual feedback on pelvic floor muscle strength

Objective: The objective of this study is to evaluate the visual feedback influence on pelvic floor muscle contraction. Study design: Seventeen nulliparous, urinary-continent women participated in this study. Pelvic floor muscle strength with and without the use of visual feedback was measured with a dynamometric speculum in two directions (anteroposterior and left-right). To compare the mean strength values with and without the use of visual feedback, the t test was applied. Results: There was no significant difference between the pelvic floor muscle anteroposterior strength values with and without the use of visual feedback (p = 0.30), and no significant difference for the left-right strength (p = 0.37). Conclusion: There was no difference between the pelvic floor muscle strength values with and without the use of visual feedback. (C) 2010 Elsevier Ireland Ltd. All rights reserved.

Prognostic factors and survival analysis in a sample of oral squamous cell carcinoma patients

Objectives. The aims of this report were to describe the 5-year overall survival (OS) in a group of oral squamous cell carcinoma (OSCC) patients and to investigate the effects of age, gender, anatomic localization, tumor evolution time, smoking and alcohol intake, nodal status, tumoral recurrences, histologic classification, p53 and p63 immunoexpression, human papillomavirus DNA presence, and treatment on the prognostic outcome. Study design. Survival curves were generated using Kaplan-Meier method, and univariate and multivariate analyses were made using the log rank test and Cox regression, respectively. Results. The 5-year OS was 28.6%, and the univariate analysis showed significant results for p53 and p63 immunoexpression, age, and anatomic localization. The Cox regression demonstrated poor OS for tumors with p53 immunoexpression and for patients aged over 60 years. There were also significant differences in survival depending on the anatomic localizations. Conclusion. These results highlight the influence of p53 immunoexpression, age, and anatomic localization in OSCC evolution. (Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2008; 106: 685-95)

Evaluation of lignin contents in tropical forages using different analytical methods and their correlations with degradation of insoluble fiber

We compared the lignin contents of tropical forages by different analytical methods and evaluated their correlations with parameters related to the degradation of neutral detergent fiber (NDF). The lignin content was evaluated by five methods: cellulose solubilization in sulfuric acid [Lignin (sa)], oxidation with potassium permanganate [Lignin (pm)], the Klason lignin method (KL), solubilization in acetyl bromide from acid detergent fiber (ABLadf) and solubilization in acetyl bromide from the cell wall (ABLcw). Samples from ten grasses and ten legumes were used. The lignin content values obtained by gravimetric methods were also corrected for protein contamination, and the corrected values were referred to as Lignin (sa)p, Lignin (pm)p and KLp. The indigestible fraction of NDF (iNDF), the discrete lag (LAG) and the fractional rate of degradation (kd) of NDF were estimated using an in vitro assay. Correcting for protein resulted in reductions (P < 0.05) in the lignin contents as measured by the Lignin (sa), Lignin (pm) and, especially, the KL methods. There was an interaction (P < 0.05) of analytical method and forage group for lignin content. In general, LKp method provided the higher (P < 0.05) lignin contents. The estimates of lignin content obtained by the Lignin (sa)p, Lignin (pm)p and LKp methods were associated (P > 0.05) with all of the NDF degradation parameters. However, the strongest correlation coefficients for all methods evaluated were obtained with Lignin (pm)p and KLp. The lignin content estimated by the ABLcw method did not correlate (P > 0.05) with any parameters of NDF degradation. There was a correlation (P < 0.05) between the lignin content estimated by the ABLadf method and iNDF content. Nonetheless, this correlation was weaker than those found with gravimetric methods. From these results, we concluded that the gravimetric methods produce residues that are contaminated by nitrogenous compounds. Adjustment for these contaminants is suggested, particularly for the KL method, to express lignin content with greater accuracy. The relationships between lignin content measurements and NDF degradation parameters can be better determined using KLp and Lignin (pm)p methods. (C) 2011 Elsevier B.V. All rights reserved.

The Importance of Adhesive Area Delimitation in a Microshear Bond Strength Experimental Design

Purpose: The purpose of this study was to assess the influence of adhesive area delimitation on the microshear bond strength of different adhesives to dentin. Materials and Methods: Eighteen bovine incisors were sectioned and the exposed dentin surfaces were prepared with 600-grit SIC paper. These teeth were randomly divided into three groups, according to the adhesive to be applied: two-step etch-and-rinse Adper Single Bond 2 (3M ESPE), two-step self-etching Clearfil SE Bond (Kuraray), and one-step Clearfil S(3) Bond (Kuraray). On each dentin surface, 4 samples were built up with the composite resin Z100 (3M ESPE); on 2 of these, a suggested area delimitation technique was employed. After 24 h of storage in water at 37 degrees C, samples were subjected to the microshear bond strength test, and the failure modes were evaluated under optical and scanning electron microscopes. The obtained results were statistical analyzed using two-way ANOVA and Tukey`s test. Results: Groups without area delimitation presented significantly higher bond strength results (p < 0.05) and a higher incidence of cohesive failures. In these groups, fractures tended to occur beyond the limits of the actual adhesive area, while the area restriction technique succeeded in avoiding this phenomenon. The three adhesives performed similarly when area delimitation was employed (p > 0.05), but Clearfil S(3) Bond showed significantly higher bond strength results when no area delimitation was taken into account (p < 0.05). Conclusion: The extension of the adhesive area beyond the limits of the composite cylinder may play an important role in the results of microshear bond strength tests, while the suggested area delimitation technique may lead to less questionable outcomes.

Clinical versus laboratory adhesive performance to wet and dry demineralized primary dentin

Purpose: To evaluate the influence of dentin moisture on bond strengths of an etch-and-rinse bonding agent to primary dentin clinically and in the laboratory. Methods: The sample consisted of two groups of 20 caries-free primary second molars: molars in exfoliation period (clinical group) and extracted molars (laboratory group). Class I cavities were prepared in all specimens leaving a flat dentin surface on the pulpal floor. A two-step etch-and-rinse adhesive was vigorously rubbed on either dry (n= 5) or wet demineralized dentin (n= 5) under clinical or laboratory conditions. After restorative procedures, the teeth from the clinical group were extracted after 20 minutes. All samples were processed and underwent microtensile bond strength test and silver nitrate uptake evaluation under scanning electron microscopy. Results: Statistically higher bond strength values were observed when the bonding was performed under laboratory conditions and on a wet demineralized dentin. Most of the failures were adhesive and mixed irrespective of the experimental condition. Silver nitrate uptake occurred in all groups irrespective of the experimental condition. Resin-dentin bond strengths produced in the laboratory in primary teeth may overestimate those produced under clinical circumstances. (Am J Dent 2011;24:221-225).

Composite pre-heating: Effects on marginal adaptation, degree of conversion and mechanical properties

Objectives. This study evaluated the effect of composite pre-polymerization temperature and energy density on the marginal adaptation (MA), degree of conversion (DC), flexural strength (FS), and polymer cross-linking (PCL) of a resin composite (Filtek Z350, 3M/ESPE). Methods. For MA, class V cavities (4mmx2mmx2mm) were prepared in 40 bovine incisors. The adhesive system Adper Single Bond 2 (3M/ESPE) was applied. Before being placed in the cavities, the resin composite was either kept at room-temperature (25 degrees C) or previously pre-heated to 68 degrees C in the Calset (TM) device (AdDent Inc., Danbury, CT, USA). The composite was then light polymerized for 20 or 40s at 600mW/cm(2) (12 or 24 J/cm(2), respectively). The percentage of gaps was analyzed by scanning electron microscopy, after sectioning the restorations and preparing epoxy resin replicas. DC (n = 3) was obtained by FT-Raman spectroscopy on irradiated and non-irradiated composite surfaces. FS (n = 10) was measured by the three-point-bending test. KHN (n = 6) was measured after 24h dry storage and again after immersion in 100% ethanol solution for 24 h, to calculate PCL density. Data were analyzed by appropriate statistical analyses. Results. The pre-heated composite showed better MA than the room-temperature groups. A higher number of gaps were observed in the room-temperature groups, irrespective of the energy density, mainly in the axial wall (p < 0.05). Composite pre-heating and energy density did not affect the DC, FS and PCL (p > 0.05). Significance. Pre-heating the composite prior to light polymerization similar in a clinical situation did not alter the mechanical properties and monomer conversion of the composite, but provided enhanced composite adaptation to cavity walls. (C) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Bis-GMA co-polymerizations: Influence on conversion, flexural properties, fracture toughness and susceptibility to ethanol degradation of experimental composites

Objectives. The aim of this study was to evaluate the influence of monomer content on fracture toughness (K(Ic)) before and after ethanol solution storage, flexural properties and degree of conversion (DC) of bisphenol A glycidyl methacrylate (Bis-GMA) co-polymers. Methods. Five formulations were tested, containing Bis-GMA (B) combined with TEGDMA (T), UDMA (U) or Bis-EMA (E), as follows (in mol%): 30B:70T; 30B:35T:35U; 30B:70U; 30B:35T:35E; 30B:70E. Bimodal filler was introduced at 80 wt%. Single-edge notched beams for fracture toughness (FT, 25 mm x 5 mm x 2.5 mm, a/w = 0.5, n = 20) and 10 mm x 2 mm x 1 mm beams for flexural strength (FS) and modulus (FM) determination (10 mm x 2 mm x 1 mm, n = 10) were built and then stored in distilled water for 24 h at 37 degrees C. All FS/FM beams and half of the FT specimens were immediately submitted to three-point bending test. The remaining FT specimens were stored in a 75%ethanol/25%water (v/v) solution for 3 months prior to testing. DC was determined with FT-Raman spectroscopy in fragments of both FT and FS/FM specimens at 24 h. Data were submitted to one-way ANOVA/Tukey test (alpha = 5%). Results. The 30B:70T composite presented the highest K(Ic) value (in MPa m(1/2)) at 24 h (1.3 +/- 0.4), statistically similar to 30B:35T:35U and 30B:70U, while 30B:70E presented the lowest value (0.5 +/- 0.1). After ethanol storage, reductions in K(Ic) ranged from 33 to 72%. The 30B:70E material presented the lowest reduction in FT and 30B:70U, the highest. DC was similar among groups (69-73%), except for 30B:70U (52 +/- 4%, p < 0.001). 30B:70U and 30B:35T:35U presented the highest FS (125 +/- 21 and 122 +/- 14 MPa, respectively), statistically different from 30B:70T or 30B:70E (92 +/- 20 and 94 +/- 16 MPa, respectively). Composites containing UDMA or Bis-EMA associated with Bis-GMA presented similar FM, statistically lower than 30B:35T:35U. Significance. Composites formulated with Bis-GMA:TEGDMA:UDMA presented the best compromise between conversion and mechanical properties. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Shrinkage stress and mechanical properties of photoactivated composite resin using the argon ion laser

The objective of this study was to verify the influence of photoactivation with the argon ion laser on shrinkage stress (SS), followed by evaluation of Vickers microhardness (VM), percentage of maximum hardness (PMH), flexural strength (FS), and flexural modulus (FM) of a composite resin. The study groups were: L1-laser at 200 mW for 10 seconds; L2-laser at 200 mW for 20 seconds; L3-laser at 250 mW for 10 seconds; L4-laser at 250 mW for 20 seconds; H-halogen light at 275 mW for 20 seconds. Data were analyzed by ANOVA/Tukey`s test (alpha=5%). The values of SS (MPa) were statistically lower for the group L3 (1.3)c, followed by groups L1 (2.7)b, L4 (3.4)a, b, L2 (3.7)a, and H (4.5)a. There was no difference in the values of VM when the same time of photoactivation was used, with respective values being L1=70.1a, L2=78.1b, L3=69.9a, L4=78.1b and H=79.9b. All groups showed a PMH of at least 80%. Only the group L1 showed differences in FS (MPa) and FM (GPa), the respective values of 86.2 and 5.4 being lower. Therefore, the use of argon ion laser had influenced the composite resin polymerization. The L3 group presented adequate mechanical properties and minimum SS, reducing the clinical working time for photoactivation of restorations with the tested resin by 50%.

Subcritical crack growth in porcelains, glass-ceramics, and glass-infiltrated alumina composite for dental restorations

The objective was to compare fracture toughness (K(Ic)), stress corrosion susceptibility coefficient (n), and stress intensity factor threshold for crack propagation (K(I0)) of two porcelains [VM7/Vita (V) and d.Sign/Ivoclar (D)], two glass-ceramics [Empress/Ivolcar (E1) and Empress2/Ivlocar (E2)] and a glass-infiltrated alumina composite [In-Ceram Alumina/Vita (IC)]. Disks were constructed according to each manufacturer`s processing method, and polished before induction of cracks by a Vickers indenter. Crack lengths were measured under optical microscopy at times between 0.1 and 100 h. Specimens were stored in artificial saliva at 37A degrees C during the whole experiment. K(Ic) and n were determined using indentation fracture method. K(I0) was determined by plotting log crack velocity versus log K(I). Microstructure characterization was carried out under SEM, EDS, X-ray diffraction and X-ray fluorescence. IC and E2 presented higher K(Ic) and K(I0) compared to E1, V, and D. IC presented the highest n value, followed by E2, D, E1, and V in a decreasing order. V and D presented similar K(Ic), but porcelain V showed higher K(I0) and lower n compared to D. Microstructure features (volume fraction, size, aspect ratio of crystalline phases and chemical composition of glassy matrix) determined K(Ic). The increase of K(Ic) value favored the increases of n and K(I0).

Degree of conversion and mechanical properties of a BisGMA : TEGDMA composite as a function of the applied radiant exposure

Objective: Verify the influence of radiant exposure (H) on composite degree of conversion (DC) and mechanical properties. Methods: Composite was photoactivated with 3, 6, 12, 24, or 48 J/cm(2). Properties were measured after 48-h dry storage at room temperature. DC was determined on the flat surfaces of 6 mm x 2 mm disk-shaped specimens using FTIR. Flexural strength (FS) and modulus (FM) were accessed by three-point bending. Knoop microhardness number (KHN) was measured on fragments of FS specimens. Data were analyzed by one-way ANOVA/Tukey test, Student`s t-test, and regression analysis. Results: DC/top between 6 and 12 J/cm(2) and between 24 and 48 J/cm(2) were not statistically different. No differences between DC/top and bottom were detected. DC/bottom, FM, and KHN/top showed significant differences among all H levels. FS did not vary between 12 and 24 J/cm(2) and between 24 and 48 J/cm(2). KHN/bottom at 3 and 6 J/cm(2) was similar. KHN between top and bottom was different up to 12 J/cm(2). Regression analyses having H as independent variable showed a plateau region above 24 J/cm(2). KHN increased exponentially (top) or linearly (bottom) with DC. FS and FM increased almost linearly with DC/bottom up to 55% conversion. Conclusions: DC and mechanical properties increased with radiant exposure. Variables leveled off at high H levels. (C) 2007 Wiley Periodicals, Inc.

The 434(G > C) polymorphism in the eosinophil cationic protein gene and its association with tissue eosinophilia in oral squamous cell carcinomas

Objective: The aim of this study was to investigate the prevalence of the Eosinophil cationic protein (ECP)-gene polymorphism 434(G > C) in oral squamous cell carcinoma (OSCC) patients and its association with tumor-associated tissue eosinophilia (TATE), demographic, clinical, and microscopic variables. Methods: The ECP genotypes of 165 healthy individuals and 157 OSCC patients were detected by PCR-RFLP analysis after cleavage of the amplified DNA sequence with enzyme PstI. TATE was obtained by morphometric analysis. Chi-square test or Fisher`s exact test was used to analyze the association of ECP-gene polymorphism 434(G > C) with TATE, demographic, clinical, and microscopic variables in OSCC patients. Disease-free survival and overall survival were calculated by the Kaplan-Meier product-limit actuarial method and the comparison of the survival curves were performed using log rank test. Results: Most of healthy individuals (53.33%) and OSCC patients (57.97%) were heterozygous for the ECP 434(G > C) polymorphism. Based on numerical differences, our results showed that OSCC patients with intense TATE and at least one C allele had a higher frequency of bilateral neck dissection, local recurrence, vascular embolization, involved resection margins, and postoperative radiotherapy. No statistically significant differences on survival rates were found in OSCC patients presenting different ECP 434(G > C) genotypes. Conclusions: These results suggest a tendency towards a poor clinical outcome in OSCC patients with intense TATE and 434GC/CC genotypes, probably due to an ECP genetic variant with altered cytotoxic activity.

An in situ/ex vivo comparison of the ability of regular and light colas to induce enamel wear when erosion is combined with abrasion

Objective: To evaluate whether the type of cola drink (regular or diet) could influence the wear of enamel subjected to erosion followed by brushing abrasion, Method and !Materials: Ten volunteers wore intraoral devices that each had eight bovine enamel blocks divided into four groups; ER, erosion with regular cola; EAR, erosion with regular cola plus abrasion; EL, erosion with light cola; and EAL, erosion with light cola plus abrasion, Each day for 1 week, half of each device was immersed in regular cola for 5 minutes, Then, two blocks were brushed using a fluoridated toothpaste and electric toothbrush for 30 seconds four times daily, Immediately after, the other half of the device was subjected to the same procedure using a light cola, The pH, calcium, phosphorus, and fluoride concentrations of the colas were analyzed using standard procedures, Enamel alterations were measured by profilometry. Data were tested using two-way ANOVA and Bonferroni test (P < .05), Results: Regarding chemical characteristics, light cola presented pH 3.0, 13.7 mg Ca/L, 15.5 mg P/L, and 0.31 mg F/L, while regular cola had pH 2.6, 32.1 mg Ca/L, 1:8.1 mg P/L, and 0.26 mg F/L, The light cola promoted less enamel loss (EL, 0.36 pm; EAL, 0.39 pm) than its regular counterpart (ER, 0.72 pm; EAR, 0.95 pm) for both conditions, There was not a significant difference (P > .05) between erosion and erosion plus abrasion for light cola, However, for regular cola, erosion plus abrasion resulted in higher enamel loss than erosion alone,.nclusion: The data suggest that light cola promoted less enamel wear even when erosion was followed by brushing abrasion, (Quintessence Int 2011;42:xxx-xx)()

The composite Euler method for stiff stochastic differential equations

In this paper we present the composite Euler method for the strong solution of stochastic differential equations driven by d-dimensional Wiener processes. This method is a combination of the semi-implicit Euler method and the implicit Euler method. At each step either the semi-implicit Euler method or the implicit Euler method is used in order to obtain better stability properties. We give criteria for selecting the semi-implicit Euler method or the implicit Euler method. For the linear test equation, the convergence properties of the composite Euler method depend on the criteria for selecting the methods. Numerical results suggest that the convergence properties of the composite Euler method applied to nonlinear SDEs is the same as those applied to linear equations. The stability properties of the composite Euler method are shown to be far superior to those of the Euler methods, and numerical results show that the composite Euler method is a very promising method. (C) 2001 Elsevier Science B.V. All rights reserved.

Mechanical stability of adhesives under water storage

Objectives. To evaluate the effects of storage condition (wet or dry) and storage time (24 h and 3 months) on the ultimate tensile strength (UTS) of Single Bond (SB), 3M-ESPE; Opti Bond Solo Plus (OB), Kerr; One Step (OS), Bisco, and Prime & Bond NT (PB), Dentsply adhesive resins. Methods. Hourglass-shaped specimens were obtained from a metallic matrix. Each adhesive was dispensed to fill the molds completely and left undisturbed in a dark chamber for 4 min at 37 degrees C for solvent evaporation. They were individually light-cured for 80 s at 500 mW/cm(2) and randomly divided into three groups: 24 h of water storage; 3 months of water storage; 3 months of dry storage. The specimens were tested in tension at 0.5 mm/min using the microtensile method and data were analyzed by two-way ANOVA and SNK tests for each material. Results. Water storage for 3 months did not cause significant changes in the UTS of any of the adhesives (p-value). Values for water storage ranged from 25.9 MPa for Single Bond at 24 h to 32.7 MPa for Prime & Bond NT after 3 months. Dry storage for 3 months yielded significantly higher UTS for most adhesives, which ranged from approximately 20% for Opti Bond to 160% higher values for Single Bond compared to their 3 months wet storage values. Conclusion. The effects of storage condition and time on the UTS of adhesives were material-dependent. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.