Influence of standard load micro and nanopatterned in surface roughness of bleached teeth and submitted to different surface treatments?

The aim of this study was evaluate the dental enamel after whitening treatment with Opalescence Boost PF® 38%, correlating the structural alterations in the surface of the enamel with its respective pH and verify if whitened teeth submitted to different finishing and polishing techniques show similar surface texture to healthy teeth (control group). Sixty premolars were divided in 6 groups (n = 10), which had been immersed in artificial saliva during all the experiment. Protocol whitening was performed according to the manufacturer recommendations, and then the specimens were submitted to different polishing technique with Sof-Lex Pop On® disks, Flex Diamond® felt disks using two different micrometric polishing pastes (Enamelize® and Diamond Polish®) and two nanometric polishing pastes (Lummina-E Diamond and Lummina-E Alumina), according to the groups. Representative specimens were analyzed in scanning electronic microscopy (SEM). Whitening gel used in this experiment had modified the morphologic aspect of the enamel surface. It was found that two nanometric polishing pastes (G5 and G6) promoted a less rough surface compared to control group even after the whitening process.

Long-term surface hardness and monomer conversion of a nonofilled and a microhybrid composite resin

Objective: This study aims to evaluate the degree of conversion (DC) and hydrolytic degradation through the Vickers hardness test (HV) of a nanofilled (Filtek™ Z-250, 3M) and a microhybrid (Filtek™Supreme-XT, 3M) composite resin. Materials and methods: Eight disk-shaped specimens (4 mm diameter × 2 mm thick, ISO 4049) of each material were prepared for each test. Composites were inserted into single increment in a metallic matrix and light-cured for 40 seconds. VH readings were performed for each specimen at predetermined intervals: immediately after polymerization (control), 1, 2, 3, 7, 14, 21, 30 and 180 days. After curing, initial hardness measurements were performed and the specimens were immersed in artificial saliva at 37°C. For DC (%), specimens were ground, pressed with KBr and analyzed by FT-IR spectrophotometer. Results: Student t-test showed that there was no difference between the resins for DC (p = 0.252). ANOVA analysis revealed that Z-250 VH means were all greater than S-XT, for both top and bottom surfaces, whatever the storage-period in artificial saliva (p < 0.001). After 180 days of storage, the hardness obtained for S-XT was similar with that at the baseline, for both top and bottom surfaces. While for Z-250 hardness was not significantly different from baseline only for top surface, but there was a significant decrease observed in hardness for bottom surface. Conclusion: The materials tested showed no evidence of hydrolytic degradation in a significant way, in a 6-month storagetime in artificial saliva. Nanofilled resin presents a monomer conversion comparable to the conventional microhybrid.

Action of the salivary microorganisms having sorbitol as substratum

Microorganisms living in the saliva are able to ferment some sweetener types and to promote the fall of pH that has its critical point around 5.5; in this situation, they equal the input and the calcium output in the processes of remineralization and demineralization. For iteration of the three essential factors to the installation of the dental caries (microorganism, host and diet) suggested the accomplishment of a work that involved one of these factors. This work aims to study this issue, through the indication of substitute sweetener of the saccharose, whenever possible, it solved to evaluate pH of the saliva, exposed to sorbitol.

Influence of light source and immersion media in surface roughness and hardness of a nanofilled composite resin

The study evaluated the influence of light curing units and immersion media on superficial roughness and microhardness of the nanofilled composite resin Supreme XT (3M/ESPE). Light curing units used were: XL 3000 (3M/ESPE), Jet Lite 4000 Plus (JMorita) and Ultralume Led 5 (Ultradent) and immersion media were artificial saliva, Coke®, tea and coffee, totaling 12 experimental groups. Specimens (10mm x 2mm) were immersed in each respective solution for 5 seconds, three times a day, during 60 days and so, were submitted to measure of superficial roughness (Ra) and Vickers hardness. Data were subjected to two-way ANOVA test (p<0.05). Results showed that only the light source factor showed statistically difference for hardness. It was observed that the hardness of the composite resin Filtek Supreme XT (3M/ESPE) was influenced by the light source (p<0.01) independently of the immersion media (p= 0.35) and the Jet Lite 4000 Plus (JMorita) was the light curing unit that presented lower values. In relation to surface roughness, it was noted no-significant statistical difference for light source (p=0.84), when specimens were immersed in different beverages (p=0.35).

Laboratory testes with quality data in Dentistry

In laboratory tests, just following the manufacturer’s instructions of materials or equipments may not be enough to obtain reliable data. Thus, intra and inter-examiners studies may be required. The aim of this study was to illustrate the application of the Intraclass Correlation Coefficient (r) in a study related to the color changing and hardness of composite resin conducted by two examiners. The color and hardness of 10 specimens of composite resin were evaluated by a colorimetric spectrophotometer and hardness tester, respectively, at two different times. Two trained examiners performed two measurements with an interval of one week. Specimens were stored in artificial saliva at 37±1ºC for 7 days. The Intraclass Correlation was used for analysis of intra and inter-examiner reproducibility. The intra-examiner reproducibility was 0.79, 0.44 and 0.76 for L, a and b color coordinates for the examiner 1 and 0.84, 0.23, 0.21 for examiner 2. For hardness, r-values were 0.00 and 0.23 for the examiner 1 and 2, respectively, showing unsatisfactory agreement on color and hardness evaluation for both examiners. It was noted that only the observation of protocol for use of equipment and examiners training were not sufficient to collect reliable information. Thus, adjustments in the experimental protocol were made and devices were produced to standardize the measurements. The reproducibility study was performed again. For examiner 1, values as 0.90, 0.59 and 0.79 were verified for L, a and b coordinates and, for examiner 2 were obtained values of 0.90, 0.75, 0.95. In relation to hardness, r-values of 0.75 and 0.71 were obtained for examiners 1 and 2, respectively. The inter-examiner reproducibility was 0.86, 0.87, 0.91 for L, a and b coordinates and 0.79 for hardness. It was concluded that intra and inter-examiner calibration is essential for obtaining quality measurements in laboratory tests.

Color stability of a nanofilled resin: influence of polishing and finishing and fluoride solutions according to time

Aim: The aim of the study was evaluate the finishing and polishing effect of the color stability of the composite resin Filtek Supreme XT, according to different fluoride solutions and time. Material and Methods: Specimens were prepared (n=140) with half of the samples finished and polished. The experimental groups were divided according to the presence or absence of finishing and polishing and immersion solutions (artificial saliva, sodium fluoride solution at 0.05% - manipulated, Fluordent Reach, Oral B, Fluorgard). The specimens remained in artificial saliva for 24 hours and were subjected to an initial color analysis using a spectrophotometer CIELab system. Then, they were immersed in the experimental solutions for 1 minute a day. The readings of the color change were made after 24 and 48 hours, 7, 14, 21, 30 and 60 days after the first immersion. The three-way mixed Analysis of Variance (ANOVA) ("finishing/polishing", "immersion medium" and “time”) were performed. For multiple comparisons, the Sidak test for repeated measure was used, with a 5% level of significance. Results: The finishing and polishing factor showed significant variability, independently of the immersion media (p<0.001). Cconclusion: Finishing and polishing procedures yielded better color stability to composite resin over time, regardless of the immersion media.

Roughness and morphology of composites: influence of type of material, fluoride solution, and time

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Chemical and morphological features of nanofilled composite resin: influence of finishing and polishing procedures and fluoride solutions

This study evaluated the influence of finishing and polishing procedures and differ-ent fluoride solutions on superficial morphology and chemistry of the nanofilled composite resinSupreme XT (3M) through the EDX analysis and SEM evaluation. Circular specimens (n 5 30) of 10mm diameter and 2 mm thickness were prepared, with half of the sample assays finished and polishedwith Super-Snap1sandpaper. The experimental groups were divided according to the presence or ab-sence of finishing and polishing and solutions (arti ficial saliva, 0.0 5% of manipulated sodium fluoridesolution, Fluordent Re ach, Oral B, Fluorgard). Specimens were immersed in each respective solutionfor 1 min per day, during 60 days and stored in artificial saliva at 37 6 18C between immersion peri-ods. Topography and chemical analysis was qualitative. It was observed that specimens submitted tofinishing and polishing procedures had lower superficial degradation. Fluoride solutio ns promoted su-perficial alterations on specimens, being the highest degradation obtained with Fluordent Reach. Itca n be concluded that finishing and polishing procedures and the immersion media influence the su-perficial morphology of composite resin tested; the Fluordent Reach was the flu oride solution thatmo st affected the material’s surface.

Influence of light curing units and fluoride mouthrinse on morphological surface and color stability of a nanofilled composite resin

Composite resin is a dental material susceptible to color change over time which limits the longevity of restorations made with this material. The influence of light curing units and different fluoride mouthrinses on superficial morphology and color stability of a nanofilled composite resin was evaluated. Specimens (N = 150) were prepared and polished. The experimental groups were divided according to the type of light source (halogen and LED) and immersion media (artificial saliva, 0.05% sodium fluoride solution-manipulated, Fluordent Reach, Oral B, Fluorgard). Specimens remained in artificial saliva for 24-h baseline. For 60 days, they were immersed in solutions for 1 min. Color readout was taken at baseline and after 60 days of immersion. Surface morphology was analyzed by Scanning Electron Microscopy (SEM) after 60 days of immersion. Color change data were submitted to two-way Analysis of Variance and Tukey tests (α = 0.05). Surface morphology was qualitatively analyzed. The factor light source presented no significant variability (P = 0.281), the immersion media, significant variability (P < 0.001) and interaction between factors, no significant variability (P = 0.050). According to SEM observations, no difference was noted in the surface of the specimens polymerized by different light sources, irrespective of the immersion medium. It was concluded that the light source did not influence the color stability of composite, irrespective of the immersion media, and among the fluoride solutions analyzed, Fluorgard was the one that promoted the greatest color change, however, this was not clinically perceptible. The immersion media did not influence the morphology of the studied resin. Microsc. Res. Tech. 77:941–946, 2014. © 2014 Wiley Periodicals, Inc.

Chemical and morphological features of dental composite resin: influence of light curing units and immersion media

Aims: The study evaluated the influence of light curing units and immersionmedia on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M)through the EDX analysis and SEM evaluation. Light curing units with different power densitiesand mode of application used were XL 3000 (480 mW/cm2), Jet Lite 4000 Plus (1230mW/cm2), andUltralume Led 5 (790 mW/cm2) and immersion media were artificial saliva, Coke1, tea and coffee,totaling 12 experimental groups. Specimens (10 mm 3 2 mm) were immersed in each respectivesolution for 5 min, three times a day, during 60 days and stored in artificial saliva at 378C 6 18Cbetween immersion periods. Topography and chemical analysis was qualitative. Findings: Groupsimmersed in artificial saliva, showed homogeneous degradation of matrix and deposition of calciumat the material surface. Regarding coffee, there was a reasonable chemical degradation with loss ofload particles and deposition of ions. For tea, superficial degradation occurred in specific areaswith deposition of calcium, carbon, potassium and phosphorus. For Coke1, excessive matrix degra-dation and loss of load particles with deposition of calcium, sodium, and potassium. Conclusion:Light curing units did not influence the superficial morphology of composite resin tested, but theimmersion beverages did. Coke1affected material’s surface more than did the other tested drinks.Microsc. Res. Tech. 73:176–181, 2010.

Effects of immersion media and repolishing on color stability and superficial morphology of nanofilled composite resin

This study evaluated the influence of fluoride mouth rinses and repolishing on the superficial morphology and color stability of nanofilled resin. About 150 specimens were prepared and polished using aluminum oxide discs for 15 s with a pressure of 2 kg. The experimental groups were divided according to the immersion medium (artificial saliva, 0.5% sodium fluoride, Fluordent Reach, Oral B, Fluorgard) and repolishing procedure (without and with). The specimens were continuously immersed for 1 week. Thereafter, half of each sample was repolished. A color reading was performed after 24 h of immersion in the artificial saliva baseline, after continuous immersion, and after repolishing. The superficial morphology was examined using scanning electron microscopy (SEM) in a qualitative way. Color change (∆E) data were submitted to a mixed analysis of variance using a Shapiro-Wilk test (p>0.05 for the different immersion media) and Sidak's test (p<0.05 for the differences between groups). In the interaction between the repolishing and the immersion media, Fluorgard showed a statistical difference between the ∆E values with and without repolishing (p<0.0001). On the SEM observations, both Fluordent Reach and Fluorgard caused degradation of the superficial resinous matrix of the composite after continuous immersion. This matrix was removed after repolishing.

The effect of chlorhexidine on plaque index and mutans streptococci in orthodontic patients: A pilot study

Aim: The purpose of this study was to assess chlorhexidine effects on plaque index and salivary levels of mutans streptococci (MS) when used as the immersion solution for removable orthodontic appliances and added to their acrylic resin composition. Methods: Forty-five patients (6 to 12 years old) were randomly assigned into three groups with 15 patients each. Group I (control)—without orthodontic appliances disinfection; Group II—removable orthodontic appliances which had been immersed in 0.12% chlorhexidine digluconate overnight (8 hours), and Group III—orthodontic appliances in which 0.12% chlorhexidine digluconate solution had been incorporated into their resin composition. Saliva was collected for quantification of MS and evaluation of plaque index was performed before and after installation of orthodontic appliance at 0, 2, 4, 6, 8, and 10 weeks. Data were analyzed by using analysis of variance. Results: Number of MS colonies in saliva and plaque index showed no statistically differences among groups at the different periods (p > 0.05). Conclusions: It could be concluded that chlorhexidine incorporation into the acrylic resin of removable orthodontic appliances at 0.12% concentration and immersion of the appliance into 0.12% chlorhexidine solution were not effective in reducing plaque index and the number of MS in saliva.

In vitro evaluation of Biosilicate® dissolution on dentin surface: a SEM analysis

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of finishing and polishing on color stability of a nanofilled resin immersed in different media

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Prevalence of Candida spp. during radiographic examination in Diabetes mellitus patients

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)