Composition and growth mode of MoSx sputtered films

MoS(x) lubricating thin films were deposited by nonreactive, reactive, and low energy ion-assisted radio-frequency (rf) magnetron sputtering from a MoS2 target. Depending on the total and reactive gas pressures, the film composition ranges between MoS0.7 and MoS2.8. A low working pressure was found to have effects similar to those of low-energy ion irradiation. Films deposited at high pressure have (002) planes preferentially perpendicular to the substrate, whereas films deposited at low pressure or under low-energy ion irradiation have (002) mainly parallel to it. Parallel films are sulfur deficient (MoS1.2-1.4). Their growth is explained in terms of an increased reactivity of the basal surfaces, itself a consequence of the creation of surface defects due to ion irradiation. The films exhibit a lubricating character for all compositions above MoS1.2. The longest lifetime in ball-on-disk wear test was found for MoS1.5.

The impact of navigator timing parameters and navigator spatial resolution on 3D coronary magnetic resonance angiography.

The impact of navigator spatial resolution and navigator evaluation time on image quality in free-breathing navigator-gated 3D coronary magnetic resonance angiography (MRA), including real-time motion correction, was investigated in a moving phantom. Objective image quality parameters signal-to-noise ratio (SNR) and vessel sharpness were compared. It was found that for improved mage quality a short navigator evaluation time is of crucial importance. Navigator spatial resolution showed minimal influence on image quality.

MP2RAGE Multiple Sclerosis Magnetic Resonance Imaging at 3 T.

OBJECTIVES: Lesion detection and characterization in multiple sclerosis (MS) are an essential part of its clinical diagnosis and an important research field. In this pilot study, we applied the recently introduced two inversion-contrast magnetization-prepared rapid gradient echo sequence (MP2RAGE) to patients with early-stage MS.¦MATERIALS AND METHODS: The MP2RAGE is a 3-dimensional (3D) magnetization-prepared rapid gradient echo derivative providing homogeneous T1 weighting and simultaneous T1 mapping. The MP2RAGE performance was compared with that of 2 clinical routine sequences (2D fluid-attenuated inversion recovery [FLAIR] and 3D magnetization-prepared rapid gradient echo [MP-RAGE]) and 2 state-of-the art clinical research sequences (the 3D FLAIR-SPACE [sampling perfection with application-optimized contrasts by using different flip-angle evolutions], a fluid-attenuated variable flip-angle fast spin echo technique, and the 3D double-inversion recovery SPACE). A cohort of 10 early-stage female MS patients (age, 31.6 ± 4.7 years; disease duration, 3.8 ± 1.9 years; median expanded disability status scale score, 1.75) and 10 age- and gender-matched controls were enrolled after approval of the local institutional review board was obtained. Multiple sclerosis lesions were identified and assigned to brain locations and tissue types by two experienced physicians in all 5 contrasts. Subsequently, lesions were manually delineated for comparison and statistical analysis of lesion count, volume and quantitative measures.¦RESULTS AND CONCLUSIONS: The results show that the 3D T1-weighted high-resolution MP2RAGE contrast provides a sensitive means for MS lesion assessment. The additional quantitative T1 relaxation time maps obtained with the MP2RAGE provide further potential diagnostic and prognostic information that could help (a) to better discriminate lesion subtypes and (b) to stage and predict the activity and the evolution of MS. Results also indicate that the T2-weighted double-inversion recovery and FLAIR-SPACE contrasts are attractive complements to the MP2RAGE for lesion detection.

Magnetic susceptibility to identify landscape segments on a detailed scale in the region of Jaboticabal, São Paulo, Brazil

The agricultural potential is generally assessed and managed based on a one-dimensional vision of the soil profile, however, the increased appreciation of sustainable production has stimulated studies on faster and more accurate evaluation techniques and methods of the agricultural potential on detailed scales. The objective of this study was to investigate the possibility of using soil magnetic susceptibility for the identification of landscape segments on a detailed scale in the region of Jaboticabal, São Paulo State. The studied area has two slope curvatures: linear and concave, subdivided into three landscape segments: upper slope (US, concave), middle slope (MS, linear) and lower slope (LS, linear). In each of these segments, 20 points were randomly sampled from a database with 207 samples forming a regular grid installed in each landscape segment. The soil physical and chemical properties, CO2 emissions (FCO2) and magnetic susceptibility (MS) of the samples were evaluated represented by: magnetic susceptibility of air-dried fine earth (MS ADFE), magnetic susceptibility of the total sand fraction (MS TS) and magnetic susceptibility of the clay fraction (MS Cl) in the 0.00 - 0.15 m layer. The principal component analysis showed that MS is an important property that can be used to identify landscape segments, because the correlation of this property within the first principal component was high. The hierarchical cluster analysis method identified two groups based on the variables selected by principal component analysis; of the six selected variables, three were related to magnetic susceptibility. The landscape segments were differentiated similarly by the principal component analysis and by the cluster analysis using only the properties with higher discriminatory power. The cluster analysis of MS ADFE, MS TS and MS Cl allowed the formation of three groups that agree with the segment division established in the field. The grouping by cluster analysis indicated MS as a tool that could facilitate the identification of landscape segments and enable the mapping of more homogeneous areas at similar locations.

Magnetic properties and martensitic transition in annealed Ni50Mn30Al20

We have studied the effect of heat treatment on the magnetic properties and on the martensitic transition of the Ni50Mn30Al20 alloy. A mixed L21+B2 state is obtained in the as-prepared sample, while no L21 order is retained in the sample quenched from high temperature. For the two heat treatments, the samples order antiferromagnetically, but there is evidence of coexisting ferromagnetic interactions. A martensitic transition occurs below the magnetic one for quenched samples. However, the martensitic transition is inhibited in the as-prepared sample.

Magnetic hardening mechanisms in Nd-Fe-B nanocrystalline material

Microstructural and magnetic measurements of the evolution by heat treatment of initially amorphous Nd16Fe76B8 alloys prepared by melt spinning are presented. Evidence of magnetic hardening above a threshold temperature induced by magnetic isolation of the Nd2Fe14B grains is provided. A thermodynamic and kinetic explanation of local melting of the intergranular nanostructured Nd¿rich eutectic phase at temperatures below 900 K based on capillary effects is presented. A subsequent Ostwald ripening process moves Nd to wet intimately the hard magnetic grains, becoming, on cooling, a real paramagnetic isolating thin film (~2.5 nm). By using a simple analogy, it is shown that the switching magnetization field in a single¿domain crystal can be drastically affected through the exchange coupling to neighboring grains with different orientation of the easy axis. This effect should be important enough to reinforce the coercive field of polycrystalline hard magnetic materials and explains the observed enhancement from 0.9 to 1.9 T.

A high-sensitivity differential scanning calorimeter with magnetic field for magnetostructural transitions

We have developed a differential scanning calorimeter capable of working under applied magnetic fields of up to 5 T. The calorimeter is highly sensitive and operates over the temperature range 10¿300 K. It is shown that, after a proper calibration, the system enables determination of the latent heat and entropy changes in first-order solid¿solid phase transitions. The system is particularly useful for investigating materials that exhibit the giant magnetocaloric effect arising from a magnetostructural phase transition. Data for Gd5(Si0.1Ge0.9)4 are presented.

Dynamics of driven three-dimensional thin films: from hdrophilic to superhydrophobic substrates

We study the forced displacement of a thin film of fluid in contact with vertical and inclined substrates of different wetting properties, that range from hydrophilic to hydrophobic, using the lattice-Boltzmann method. We study the stability and pattern formation of the contact line in the hydrophilic and superhydrophobic regimes, which correspond to wedge-shaped and nose-shaped fronts, respectively. We find that contact lines are considerably more stable for hydrophilic substrates and small inclination angles. The qualitative behavior of the front in the linear regime remains independent of the wetting properties of the substrate as a single dispersion relation describes the stability of both wedges and noses. Nonlinear patterns show a clear dependence on wetting properties and substrate inclination angle. The effect is quantified in terms of the pattern growth rate, which vanishes for the sawtooth pattern and is finite for the finger pattern. Sawtooth shaped patterns are observed for hydrophilic substrates and low inclination angles, while finger-shaped patterns arise for hydrophobic substrates and large inclination angles. Finger dynamics show a transient in which neighboring fingers interact, followed by a steady state where each finger grows independently.

Enhanced electron-electron correlations in nanometric epitaxial SrRuO3 epitaxial films

Epitaxial and fully strained SrRuO3 thin films have been grown on SrTiO3(100). At initial stages the growth mode is three-dimensional- (3D-)like, leading to a finger-shaped structure aligned with the substrate steps and that eventually evolves into a 2D step-flow growth. We study the impact that the defect structure associated with this unique growth mode transition has on the electronic properties of the films. Detailed analysis of the transport properties of nanometric films reveals that microstructural disorder promotes a shortening of the carrier mean free path. Remarkably enough, at low temperatures, this results in a reinforcement of quantum corrections to the conductivity as predicted by recent models of disordered, strongly correlated electronic systems. This finding may provide a simple explanation for the commonly observed¿in conducting oxides-resistivity minima at low temperature. Simultaneously, the ferromagnetic transition occurring at about 140 K, becomes broader as film thickness decreases down to nanometric range. The relevance of these results for the understanding of the electronic properties of disordered electronic systems and for the technological applications of SrRuO3¿and other ferromagnetic and metallic oxides¿is stressed.

Ellipsometric study of a-Si:H thin films deposited by square wave modulated rf glow discharge

Thin films of hydrogenated amorphous silicon (a‐Si:H), deposited by square wave modulated (SQWM) rf silane discharges, have been studied through spectroscopic and real time phase modulated ellipsometry. The SQMW films obtained at low mean rf power density (19 mW/cm2) have shown smaller surface roughness than those obtained in standard continuous wave (cw) rf discharges. At higher rf powers (≥56 mW/cm2), different behaviors depending on the modulating frequency have been observed. On the one hand, at low modulating frequencies (<40 Hz), the SQWM films have shown a significant increase of porosity and surface roughness as compared to cw samples. On the other, at higher modulating frequencies, the material density and roughness have been found to be similar in SQWM and cw films. Furthermore, the deposition rate of the films show more pronounced increases with the modulating frequency as the rf power is increased. Experimental results are discussed in terms of plasma negative charged species which can be relatively abundant in high rf power discharges and cause significant effects on the deposited layers through polymers, clusters, and powder formation.

Effect of substrate temperature on deposition rate of rf plasma-deposited hydrogenated amorphous silicon thin films

We present a study about the influence of substrate temperature on deposition rate of hydrogenated amorphous silicon thin films prepared by rf glow discharge decomposition of pure silane gas in a capacitively coupled plasma reactor. Two different behaviors are observed depending on deposition pressure conditions. At high pressure (30 Pa) the influence of substrate temperature on deposition rate is mainly through a modification of gas density, in such a way that the substrate temperature of deposition rate is similar to pressure dependence at constant temperature. On the contrary, at low pressure (3 Pa), a gas density effect cannot account for the observed increase of deposition rate as substrate temperature rises above 450 K with an activation energy of 1.1 kcal/mole. In accordance with laser‐induced fluorescence measurements reported in the literature, this rise has been ascribed to an increase of secondary electron emission from the growing film surface as a result of molecular hydrogen desorption.

Optical absorption and graphitic clusters of hydrogenated amorphophous carbon thin films

The optical absorption of hydrogenated amorphous carbon films (a‐C:H) was measured by spectroscopic ellipsometry. The a‐C:H films were deposited at different substrate temperatures by rf‐plasma of methane. A volume distribution of graphitic cluster size was assumed to reproduce the experimental spectra of the absorption coefficient. The changes in the absorption coefficient and the optical gap, induced by deposition temperature, have been interpreted in terms of changes in the graphitic cluster size of the network. The increase in the deposition temperature produces an increase in the size of the graphitic clusters.

Microstructure of highly oriented, hexagonal, boron nitride thin films grown on crystalline silicon by radio frequency plasma-assisted chemical vapor deposition

We present a high‐resolution electron microscopy study of the microstructure of boron nitride thin films grown on silicon (100) by radio‐frequency plasma‐assisted chemical vapor deposition using B2H6 (1% in H2) and NH3 gases. Well‐adhered boron nitride films grown on the grounded electrode show a highly oriented hexagonal structure with the c‐axis parallel to the substrate surface throughout the film, without any interfacial amorphous layer. We ascribed this textured growth to an etching effect of atomic hydrogen present in the gas discharge. In contrast, films grown on the powered electrode, with compressive stress induced by ion bombardment, show a multilayered structure as observed by other authors, composed of an amorphous layer, a hexagonal layer with the c‐axis parallel to the substrate surface and another layer oriented at random