Fabrication, microstructure and mechanical properties of novel cemented hard alloy obtained by mechanical alloying and hot-pressing sintering

A novel cemented carbides alloy (W0.4Al0.6)C-0.65-Co were prepared by mechanical alloying and hot-pressing sintering in this work. Hot-pressing (HP) as a common technique was performed to fabricate the bulk bodies of the hard alloys. The hardness, bending strength, density of the novel hard alloy are also tested, and it has superior mechanical properties. The hardness of (W0.4Al0.6)C-0.65-Co hard alloy was very high, and the density, operate cost of the novel material were much lower than WC-Co, more important is the aluminum dissolving is not decrease the strength compared with the WC-Co system. There is almost no eta-phase in the (W0.4Al0.6)C-0.65-Co cemented carbides system even the carbon deficient reaches the astonishing value of 35%. This novel property will give us more choice to design and gain new materials that we needed.

Processing, microstructure and mechanical properties of W50Al50 bulk alloy obtained by mechanical alloying and hot-pressing

The Al50W50 alloy bulk bodies were fabricated by using mechanical alloying and hot-pressing in this work. The Al50W50 alloy had excellent thermal stability up to 1300 degreesC under vacuum and Its optimum microhardness, bending strength and compressive strength were 10.21 GPa, 570 MPa and 2.07 GPa, respectively.

Capillary electrophoresis coupled with electrochemiluminescence detection using porous etched joint

A new setup to couple capillary electrophoresis (CE) with electrochemiluminescence (ECL) detection is described in which the electrical connection of CE is achieved through a porous section at a distance of 7 mm from the CE capillary outlet. Because the porous capillary wall allowed the CE current to pass through and there was no electric field gradient beyond that section, the influence of CE high-voltage field on the ECL procedure was eliminated. The porous section formed by etching the capillary with hydrofluoric acid after only one side of the circumference of 2-3 mm of polyimide coating of the capillary was removed, while keeping the polyimide coating on the other part to protect the capillary from HF etching makes the capillary joint much more robust since only a part of the circumference of it is etched. A standard three-electrode configuration was used in experiments with Pt wire as a counter electrode, Ag/AgCl as a reference electrode, and a 300-mum diameter Pt disk as a working electrode. Compared with CE-ECL conventional decoupler designs, the present setup with a porous joint has no added dead volume created.