Laser-induced damage threshold of ZrO2 thin films prepared at different oxygen partial pressures by electron-beam evaporation

ZrO2, films were deposited by electron-beam evaporation with the oxygen partial pressure varying from 3 X 10(-3) Pa to I I X 10(-3) Pa. The phase structure of the samples was characterized by x-ray diffraction (XRD). The thermal absorption of the films was measured by the surface thermal lensing technique. A spectrophotometer was employed to measure the refractive indices of the samples. The laser-induced damage threshold (LIDT) was assessed using a 1064, nm Nd: yttritium-aluminium-garnet pulsed laser at pulse width of 12 ns. The influence of oxygen partial pressure on the microstructure and LIDT of ZrO2 films was investigated. XRD data revealed that the films changed from polycrystalline to amorphous as the oxygen partial pressure increased. The variation of refractive index at 550 nm wavelength indicated that the packing density of the films decreased gradually with increasing oxygen partial pressure. The absorptance of the samples decreased monotonically from 125.2 to 84.5 ppm with increasing oxygen partial pressure. The damage threshold, values increased from 18.5 to 26.7 J/cm(2) for oxygen partial pressures varying from 3 X 10(-3) Pa to 9 X 10(-3) Pa, but decreased to 17.3 J/cm(2) in the case of I I X 10(-3) Pa. (C) 2005 American Vacuum Society.

Laser-induced damage threshold of ZrO2 thin films prepared at different oxygen partial pressures by electron-beam evaporation

ZrO2, films were deposited by electron-beam evaporation with the oxygen partial pressure varying from 3 X 10(-3) Pa to I I X 10(-3) Pa. The phase structure of the samples was characterized by x-ray diffraction (XRD). The thermal absorption of the films was measured by the surface thermal lensing technique. A spectrophotometer was employed to measure the refractive indices of the samples. The laser-induced damage threshold (LIDT) was assessed using a 1064, nm Nd: yttritium-aluminium-garnet pulsed laser at pulse width of 12 ns. The influence of oxygen partial pressure on the microstructure and LIDT of ZrO2 films was investigated. XRD data revealed that the films changed from polycrystalline to amorphous as the oxygen partial pressure increased. The variation of refractive index at 550 nm wavelength indicated that the packing density of the films decreased gradually with increasing oxygen partial pressure. The absorptance of the samples decreased monotonically from 125.2 to 84.5 ppm with increasing oxygen partial pressure. The damage threshold, values increased from 18.5 to 26.7 J/cm(2) for oxygen partial pressures varying from 3 X 10(-3) Pa to 9 X 10(-3) Pa, but decreased to 17.3 J/cm(2) in the case of I I X 10(-3) Pa. (C) 2005 American Vacuum Society.

Laser-induced damage morphology of high-reflective optical coatings

Two different kinds of 1064 nm high-reflective (HR) coatings, with and without SiO2 protective layer, were prepared by electron beam evaporation. Three-dimensional damage morphology, caused by a Nd:YAG pulsed laser, was investigated for these HR coatings. Development of laser-induced damage on HR coatings was revealed by both temperature field calculation and discrete meso-element simulation. Theoretical results met experimental very well. (C) 2004 Elsevier B.V. All rights reserved.

脉冲激光辐照光学薄膜的缺陷损伤模型

建立了缺陷吸收升温致薄膜激光损伤模型，该模型从热传导方程出发，考虑了缺陷内部的温度分布以及向薄膜的传导过程，通过引入散射系数简化了Mie散射理论得出的吸收截面．对电子束蒸发沉积的ZrO2：Y2O3单层膜进行了激光破坏实验，薄膜样品的损伤是缺陷引起的，通过辉光放电质谱法对薄膜制备材料的纯度分析发现材料中的主要杂质元素为铂，其含量为0．9％．利用缺陷损伤模型对损伤过程进行了模拟，理论模型和实验结果取得了较好的一致性．

High laser-induced damage threshold HfO2 films prepared by ion-assisted electron beam evaporation

HfO2 films were deposited by electron beam evaporation with different deposition parameters. The properties such as refractive index, weak absorption, and laser induced damage thresholds (LIDTs) of these films have been investigated. It was found that when pulsed Nd:YAG 1064 nm laser is used to investigate LIDT of films: Metallic character is the main factor that influences LIDTs of films obtained from Hf starting material by ion-assisted reaction, and films prepared with higher momentum transfer parameter P have fewer metallic character; The ion-assisted reaction parameters are key points for preparing high LIDT films and if the parameters are chose properly, high LIDT films can be obtained. (c) 2004 Elsevier B.V. All rights reserved.

1064nm倍频波长分离膜的制备与性能研究

通过对主膜系添加匹配层并借助计算机对膜系进行优化，设计出结构规整、性能优良的1064ilm倍频波长分离膜。用电子束蒸发及光电极值监控技术在K9玻璃基底上沉积薄膜，将样品置于空气中在260℃温度下进行3h热退火处理。然后用Lambda 900分光光度计测量了样品的光谱性能；用表面热透镜(STL)技术测量了样品的弱吸收值；用调Q脉冲激光装置测试了样品的抗激光损伤阈值(LIDT)。实验结果发现，样品的实验光谱性能与理论光谱性能有很好的一致性。退火前后其光谱性能几乎没有发生温漂，说明薄膜的温度稳定性好；同时退火使

Caracterização de juntas soldadas por TIG autógeno manual com arco pulsado e arco não pulsado do aço inoxidável hiperduplex SAF 2707 HD.

O aço inoxidável hiperduplex, SAF 2707 HD, foi desenvolvido com o intuito de se obter novas ligas com maior resistência à corrosão do que a disponível nos aços inoxidáveis duplex / superduplex. Além da melhorada resistência à corrosão, este tb oferece propriedades mecânicas superiores. Os aços hiperduplex são aços de última geração que possuem elevados teores de elementos de liga, principalmente cromo, molibdênio e nitrogênio. Este tipo de aço caracteriza-se por apresentar estrutura bifásica, constituída de proporções praticamente iguais de ferrita e austenita devido à distribuição controlada dos elementos alfagênicos e gamagênicos. O interesse por esses aços cresce gradativamente com a necessidade de novos materiais para diversas aplicações na indústria petrolífera. Porém, quando expostos e mantidos a temperaturas elevadas, na faixa entre 600C e 1000C, algumas fases intermetálicas podem se formar, em que a fase sigma () é a mais proeminente. Possui uma estrutura cristalina tetragonal complexa rica em Cr e Mo, tendo efeito deletério no material afetando tanto a resistência à corrosão, quanto as propriedades mecânicas. Para este fim, faz-se necessário estudos da junta soldada para delinear as limitações desses aços e aperfeiçoar a aplicação. Essa pesquisa teve como objetivo caracterizar a junta soldada por TIG autógeno manual com arco pulsado e não pulsado do aço inoxidável hiperduplex SAF 2707 HD. As técnicas empregadas foram a metalografia por ataque eletrolítico (reagente NaOH) e color etching (reagente Behara), medidas de microdureza e quantificação microestrutural por Processamento Digital de Imagem. Os aspectos microestruturais foram observados por microscopia óptica (MO) e microscopia eletrônica de varredura (MEV), estes passaram por etapas de processamento digital de imagens (PDI) para quantificar a fração volumétrica da fase austenita. Realizou-se análise química semi-quatitativa por EDS. Os resultados foram analisados estatisticamente através do teste de hipóteses com distribuição t de Student. Pela técnica color etching observou-se que a fase austenita foi gerada com distribuição mais homogênea para o arco pulsado, que o não pulsado. O ataque eletrolítico não revelou uma terceira fase (fase ) na junta soldada, a análise química por EDS não identificou uma variação significativa nos elementos presentes ao longo da zona de transição do metal de base para a zona de fusão. Através do PDI foram obtidos os valores médios da fração volumétrica de austenita de 36,38% (desvio padrão 6,40%) e 32,41% (desvio padrão 6,67%) para os dois métodos, pulsado e não pulsado, respectivamente. Foram obtidos os valores de microdureza para o metal de base 355,10 HV (desvio padrão 28,60) e para a zona de fusão 343,60 HV (desvio padrão 20,51) da amostra soldada pelo modo pulsado, para o modo não pulsado foram apresentaram os valores médios de 370,30 HV (desvio padrão 34,51) para o metal de base e de 345,20 HV (desvio padrão 41,33) para a zona de fusão. A análise estatística indicou que não houve variação significativa da fração volumétrica da fase austenita no cordão de solda para as duas condições testadas e não houve variação da microdureza entre a zona de fusão e o metal de solda das amostras submetidas aos dois processos.

高真空室中的水蒸气对HfO2薄膜性能的影响

本文研究了在镀膜过程中真空室内水蒸气的含量对HfO2薄膜物理性能的影响。用电子束蒸发和光电极值监控的方法在BK7基底上制备HfO2薄膜。利用残余气体分析仪在线监测了真空室内的残余气氛组成。分别用Lambda 900光谱仪、X射线衍射方法、表面热透镜技术和1064nm的激光器测试了薄膜的光学性能、微结构、吸收和激光损伤阈值。实验发现，附加冷阱装置有助于我们有效控制镀膜过程中的水汽含量，且在水蒸气含量较少的真空室内镀制的薄膜具有较高的折射率，较小的晶粒尺寸，较低的弱吸收值和较高的损伤阈值。

Mechanism initiated by nanoabsorber for UV nanosecond-pulse-driven damage of dielectric coatings

A model of plasma formation induced by UV nanosecond pulselaser interaction with SiO2 thin film based on nanoabsorber is proposed. The model considers the temperature dependence of band gap. The numerical results show that during the process of nanosecond pulsed-laser interaction with SiO2 thin film, foreign inclusion which absorbs a fraction of incident radiation heats the surrounding host material through heat conduction causing the decrease of the band gap and consequently, the transformation of the initial transparent matrix into an absorptive medium around the inclusion, thus facilitates optical damage. Qualitative comparison with experiments is also provided. (C) 2008 Optical Society of America.

Caracterização fenotípica e molecular de amostras de Enterococcus isoladas em hospitais da cidade do Natal/ RN

O gênero Enterococcus tem emergindo como um dos mais importantes patógenos em infecções relacionadas à assistência à saúde no mundo. Estes microrganismos apresentam habilidade de adquirir genes de resistência a vários antimicrobianos, incluíndo à vancomicina, além de possuir diversos fatores associados à virulência, que contribuem sobremaneira para a sua permanência no hospedeiro, facilitando sua disseminação, particularmente, no ambiente hospitalar. Os objetivos deste estudo foram caracterizar, por testes fenotípicos e genotípicos, amostras de Enterococcus isoladas de quadros infecciosos em pacientes atendidos em quatro instituições de saúde localizadas na cidade do Natal, RN, no período de setembro de 2010 a junho de 2011. As espécies de Enterococcus foram caracterizadas por testes fisiológicos convencionais e por reação em cadeia da polimerase (PCR) multiplex, utilizando oligonucleotídeos específicos para caracterização do gênero e espécies. O perfil de susceptibilidade aos antimicrobianos foi avaliado por testes de difusão em ágar. Os valores de concentração inibitória mínima (CIM) para vancomicina, teicoplanina e linezolida foram determinados pelo emprego do teste E; e o genótipo de resistência à vancomicina foi analisado por PCR. Genes associados à virulência (asa1, cylA, esp, gelE e hyl) foram detectados por ensaios de PCR multiplex. O polimorfismo genético das amostras bacterianas foi avaliado por metodologia de eletroforese em campo pulsado (PFGE), com a utilização da enzima SmaI. Foram obtidas 117 amostras, a partir de quadros infecciosos em 116 pacientes. Os resultados revelaram que a espécie E. faecalis foi a prevalente (91,4%). Os testes de susceptibilidade revelaram que as taxas de resistência mais elevadas estiveram associadas à tetraciclina (58,2%) e a níveis elevados de estreptomicina (36,7%). A resistência à vancomicina foi detectada em uma amostra de E. faecium, portadora do genótipo vanA, correspondendo ao primeiro isolamento de amostra com essa característica de resistência no RN. Esta amostra foi isolada em um caso de co-infecção com E. faecalis sensível à vancomicina. Adicionalmente, susceptibilidade intermediária a linezolida foi identificada em três amostras de E. faecalis. Dentre os determinantes de virulência identificados, gelE foi o prevalente (83,8%). De acordo com as espécies E. faecalis o perfil mais detectado foi gelE + esp (31,6%), na espécie E. faecium foi o perfil esp (28,6%) e a única amostra de E. gallinarum apresentou dois determinantes de virulência (asa1 + cylA). O gene hyl não foi identificado em nenhuma das amostras. A análise do polimorfismo genético das amostras por PFGE evidenciou uma elevada policlonalidade. Diante das características de resistência e de virulência observadas e da sinalização da emergência de mecanismos de resistência importantes no Estado do RN, este estudo chama atenção para a necessidade de rastreamento, particularmente entre portadores sadios, e estabelecimento de políticas de controle da disseminação dessas amostras nas instituições de saúde, mesmo em regiões onde tais características ainda sejam pouco frequentes.

Aspectos clínico-epidemiológicos e microbiológicos de processos infecciosos causados por Corynebacterium spp em pacientes de centro de referência oncológico Rio de Janeiro, Brasil

Os resultados permitiram a redação de quatro artigos. Aspectos microbiológicos e clínicos de corinebacterioses em pacientes com câncer observados durante cinco anos foram descritos no Artigo 1. No Artigo 2 foram apresentados casos de bacteremia causados por corinebactérias invasivas não toxigênicas em dois períodos com intervalo de sete anos. As infecções em pacientes com câncer por C. diphtheriae, causando casos clínicos atípicos foram descritas no Artigo 3, além do estudo dos principais fatores de virulência de uma cepa de C. diphtheriae isolada de infecção associada ao cateter de nefrostomia foi descrita no Artigo 4. Resumidamente no Artigo 1, além dos aspectos clínico-epidemiológicos foram avaliados os perfis de resistência aos antimicrobianos e o potencial de virulência dos micro-organismos. Em cinco anos, 932 amostras de corinebactérias, com perfis de resistência aos antimicrobianos testados, foram isoladas de pacientes com câncer. As espécies predominantes foram Corynebacterium amycolatum (44,7%), Corynebacterium minutissimum (18,3%) e Corynebacterium pseudodiphtheriticum (8,5%). O uso de catéteres de longa permanência e a neutropenia, foram às condições importantes para infecção por corinebactérias. As doenças de base mais comuns foram os tumores sólidos. Pacientes hospitalizados apresentaram risco seis vezes maior de morrer, quando relacionadas às taxas de mortalidade com 30 dias (RC= 5,5; IC 95%= 1,15-26,30; p= 0,033). As bacteremias (Artigo 2) causadas por corinebactérias foram observadas em dois períodos: 2003-2004 (n=38) e de 2012-2013 (n=24). As espécies multirresistentes C. amycolatum e Corynebacterium jeikeium foram os principais responsáveis pelos quadros de bacteremia. Havia 34 pacientes com tumores sólidos e 28 pacientes com doenças linfoproliferativas, sendo que 21 deles apresentavam neutropenia e 54 utilizavam cateter venoso central. Em 41 pacientes havia infecção relacionada ou associada aos dispositivos intravasculares. Os pacientes com bacteremia responderam ao tratamento com vancomicina após a remoção do cateter. O comportamento agressivo da neoplasia, o tempo de internação hospitalar e o uso de CVC aumentaram o risco de bacteremias por Corynebacterium spp. No Artigo 3, 17 casos de infecções atípicas causadas por Corynebacterium diphtheriae foram diagnosticadas de 1996 a 2013. A incidência de C. diphtheriae correspondeu a 15,8 casos/100.000 admissões, 465 vezes maior que a incidência de difteria na população brasileira. Sintomas toxêmicos foram observados em nove pacientes, embora quadros de difteria clássica e endocardite não fossem observados. O perfil eletroforético em campo pulsado (PFGE) demonstrou um perfil de distribuição endêmica, apesar de haver dois casos de pacientes com o mesmo perfil eletroforético sugerindo transmissão relacionada aos cuidados à saúde. A adesão em superfícies bióticas e abióticas e produção de biofilme em cateter de poliuretano (Artigo 4) foi demonstrada em C. diphtheriae não toxigênico no sítio de inserção do cateter de nefrostomia. Os dados desses artigos permitiram concluir que (i) diferentes espécies de corinebactérias multirresistentes foram capazes de causar infecções em pacientes com câncer, incluindo bacteremias; (ii) C. diphtheriae foi capaz de causar infecções graves em indivíduos imunocomprometidos, incluindo infecções relacionadas ao uso de dispositivos invasivos em populações de risco, tais como pacientes com câncer.

Eletrodeposição de ligas Zn-Co por corrente contínua e pulsada simples, a partir de banhos ambientalmente não agressivos

Revestimentos produzidos a partir de ligas de Zn-Co são comumente utilizados em indústrias (aeronáutica, de isoladores elétricos e automobilística, por exemplo) devido à sua ótima resistência à corrosão, principalmente quando comparados aos tradicionais revestimentos de Zn puro. Na co-deposição de zinco com metais, como o ferro, cobalto e níquel, ocorre o que se chama de deposição anômala, onde o metal menos nobre (zinco) é preferencialmente depositado, independente do modo de corrente aplicada (contínua ou pulsada). Recentemente, diversos trabalhos relacionam a produção de eletrodepósitos de liga Zn-Co a partir de banhos ambientalmente não agressivos, a fim de substituir os banhos alcalinos extremamente tóxicos, a base de cianeto. Na presente dissertação foram produzidos revestimentos de ligas de Zn-Co sobre substrato de aço carbono, empregando corrente contínua ou corrente pulsada simples, a partir de banhos contendo diferentes concentrações de Co2+ (0,05 mol/L e 0,10mol/L), 0,05 mol/l de Zn2+ e citrato de sódio (0,10 mol/L) como agente complexante, sob condições agitadas. Quatro diferentes valores de densidade de corrente (10 A/m2, 20 A/m2, 40 A/m2 e 80 A/m2) e de frequência de pulso (100 Hz, 500 Hz, 1000 Hz, 2000 Hz) foram aplicados para a produção da liga a partir dos dois banhos, tendo como objetivo avaliar a influência dos parâmetros de deposição(concentração de Co (II), densidade de corrente aplicada e, no caso de deposição por corrente pulsada simples, também da frequência de pulso), nas variáveis eficiência de corrente catódica, composição da liga, densidade de corrente de corrosão, microestrutura e morfologia dos depósitos de liga Zn-Co. As cores das camadas obtidas variaram do cinza claro ao escuro, quase sempre sem brilho, independente do modo de corrente empregado. Foi verificado que o processo normal de eletrodeposição foi prevalente na produção de revestimentos por corrente contínua, enquanto que apenas deposição anômala foi observada quando do uso de corrente pulsada. A maior eficiência de corrente catódica (60%) foi obtida, para corrente contínua, nas condições de menor concentração de Co2+ (0,05 mol/L) e maior densidade de corrente (80 A/m2). Nestas mesmas condições foi determinada uma eficiência de corrente catódica de 98% para corrente pulsada simples na freqüência de 2000 Hz. Maiores teores do metal mais nobre (cobalto) foram alcançados em maiores densidades de corrente para todas as condições empregadas. Os revestimentos assim obtidos apresentavam os menores valores de tamanho de grão, para cada uma das soluções estudadas. Os demais parâmetros estudados também influenciaram na granulometria e na morfologia das ligas obtidas. Revestimentos com melhor resistência à corrosão, contendo teores de cobalto entre aproximadamente 8 e 10% m/m, foram produzidos a partir do banho com maior concentração de Co2+, sob corrente pulsada simples

Identificação da fase sigma em uma junta soldada pelo processo TIG manual autógeno de um aço hiperduplex SAF 2707HD (UNS S32707) por difração de raios-x.

O aço inoxidável hiperduplex possui alta resistência a corrosão por pite em ambientes contendo cloretos, quando comparado a outros aços inoxidáveis comercialmente conhecidos. Possui boas propriedades mecânicas, com limite de escoamento superior a 700MPa e limite de resistência a tração em torno de 1000MPa. Essas propriedades o tornam muito atrativos para aplicações em ambientes contendo cloretos, e por isso tem tido destaque na indústria de óleo e gás, refinarias, plataformas offshore, etc. A liga hiperduplex é composta por uma estrutura bifásica, contendo proporções aproximadamente iguais de ferrita e austenita. Esse material possui boa soldabilidade, mas por ser termodinamicamente metaestável, em altas temperaturas pode ocorrer a precipitação de fases intermetálicas não desejáveis, o que resulta em perda de propriedades mecânicas e diminuição da resistência a corrosão. A fase sigma tem sido fortemente estudada, pois é comum sua precipitação nos aços inoxidáveis da família duplex durante o procedimento de soldagem se este não for muito bem controlado. A fase sigma precipita preferencialmente na fase ferrítica, devido a maior concentração de Cr e Mo, que são os elementos formadores da fase. A resistência a corrosão é reduzida e as propriedades mecânicas do material são alteradas o tornando frágil devido a presença da fase sigma. É formada entre 600C e 1000C e possui uma estrutura tetragonal complexa. O objetivo do trabalho foi identificar a possível presença da fase sigma na junta soldada do aço inoxidável hiperduplex SAF 2707 HD (UNS S32707) pelo processo TIG autógeno manual através da difração de raios-x. Nessa pesquisa, foram analisadas uma junta soldada do material pelo processo TIG autógeno manual com arco pulsado. Complementando o estudo foram analisadas seis amostras do aço inoxidável superduplex, sendo que cinco amostras sofreram tratamento térmico para a proposital formação da fase sigma. O refinamento do resultado da difração das amostras foi feito utilizando o método de Rietveld no software Topas Academic versão 4.1. O resultado da amostra soldada de hiperduplex apresentou as fases austenita, ferrita e alguns prováveis óxidos. Os resultados das amostras de superduplex tratadas termicamente apresentaram a fase sigma, conforme esperado na pesquisa, e as fases austenita e ferrita.

Estudo de atributos de virulência e resistência a antimicrobianos em amostras de P. aeruginosa

P. aeruginosa é um importante agente de infecções relacionadas à assistência em saúde. Habitualmente, o estabelecimento de infecções agudas é precedido pela colonização das mucosas dos pacientes. Não se sabe, porém, se os processos infecciosos são causados pelas próprias cepas bacterianas colonizadoras ou por outras com que os pacientes entrem em contato, dotadas ou não de maior potencial de virulência ou de resistência a antimicrobianos que as tornem mais eficientes como agentes infecciosos. Assim, este estudo teve como objetivos i) investigar a existência de potenciais diferenças entre amostras de P. aeruginosa que causaram apenas colonização e aquelas responsáveis por infecção, isoladas de um mesmo paciente, quanto a seus fenótipos de virulência e de não susceptibilidade a antimicrobiamos; ii) pesquisar a existência de associação entre características dos paciente, incluindo o tipo de evolução clínica, com as demais variáveis estudadas. No estudo foram incluídos 21 pacientes que desenvolveram infecção por P. aeruginosa durante sua internação no Centro de Terapia Intensiva do Hospital Universitário Clementino Fraga Filho, entre abril de 2007 e abril de 2008. De cada paciente foram selecionadas duas amostras bacterianas: a primeira isolada durante o episódio de infecção e a amostra colonizadora obtida imediatamente antes da ocorrência da infecção. As amostras selecionadas foram estudadas quanto a i) expressão de três mecanismos de virulência (citotoxicidade, aderência a células epiteliais respiratórias humanas e capacidade de formação de biofilme); ii) presença de genes codificadores das proteínas efetoras do sistema de secreção do tipo 3 (SST3 - exoS, exoT, exoU e exoY); iii) perfil de susceptibilidade a antimicrobianos, iv) perfil de fragmentação do DNA cromossômico por eletroforese em gel de campo pulsado (PFGE). As amostras bacterianas obtidas de infecções agudas foram significativamente mais citotóxicas que aquelas obtidas de colonização. Embora sem diferença estatística, a citotoxicidade das amostras que causaram infecção em pacientes que evoluíram para óbito foi superior à citotoxicidade das amostras de pacientes que sobreviveram. O gene que codifica a toxina ExoU foi detectado em 16 amostras (38%), sendo nove de colonização e sete de infecção. Não houve diferença significativa entre as amostras de colonização e infecção quanto à aderência, produção de biofilme, expressão dos genes do SST3 e não-susceptibilidade às diferentes classes de antimicrobianos. Também não foi encontrada associação entre a não-susceptibilidade à quinolona, ou a outras classes de antimicrobianos, e a presença do gene exoU. As 42 amostras de P. aeruginosa estudadas foram incluídas em 20 genótipos. Em 10 deles foi detectado o gene exoU. Amostras de um mesmo genótipo foram uniformes quanto à expressão dos genes do SST3 e a não-susceptibilidade aos antimicrobianos, mas não quanto às outras variáveis estudadas. Em apenas sete pacientes (33,3%), as amostras de colonização e de infecção pertenciam ao mesmo genótipo. Assim, nesse estudo, o estabelecimento do processo infeccioso resultou não da perda do equilíbrio estabelecido entre os mecanismos de agressão das amostras colonizadoras e os de defesa do hospedeiro e sim da introdução de nova cepa bacteriana no organismo hospedeiro, cepa esta dotada de maior potencial citotóxico.

Padronização do Direito em tempos de grande encarceramento: os influxos da nova ordem global

O presente trabalho pretende analisar alguns reflexos da incorporação dos influxos da nova ordem globalizada e do neoliberalismo na ordem jurídica nacional. Será demonstrado que os valores sugeridos ainda que essa sugestão tenha caráter quase cogente pelo Banco Mundial, por meio de sua atividade paranormativa, são incorporados pela ordem legal brasileira através de reformas processuais que priorizam a justiça quantitativa. Essas reformas, somadas a outros fatores tais como o aumento das demandas levadas ao Poder Judiciário, a influência da economia na análise do Direito, a utilização equivocada, irrefletida e mecânica de discursos de fundamentação prévia, a pobreza do ensino jurídico e a submissão dos juízes ao que ditam os tribunais, resultam em um patamar de jurisdição padronizada. Paralelamente a esse processo, a população carcerária brasileira cresce em acelerado ritmo, o que pode ser relacionado com o avanço dos valores neoliberais e da retração do estado do bem estar social.Diante desse quadro, é proposto, como forma de aproximação da teoria jurídica com a prática forense e de maneira a proporcionar abertura do direito penal ao mundo dos fatos, a dogmática funcional redutora, de modo que o Direito Penal atue como dique de contenção do estado de polícia que subjaz a cada estado de direito. Ademais, propõe-se que essa adoção se dê nas salas de aula dos cursos de direito, utilizando-se, tanto quanto possível, de diversos recursos didáticos para tornar mais palpáveis e inteligíveis os conceitos e ideias propostos.