Bond strength of AH Plus and Epiphany sealers on root dentine irradiated with 980 nm diode laser

Aim To evaluate the bond strength of AH Plus and Epiphany sealers to human root canal dentine irradiated with a 980 nm diode laser at different power and frequency parameters, using the push-out test. Methodology Sixty canine roots were sectioned below the cementoenamel junction to provide 4-mm-thick dentine discs that had their root canals prepared with a tapered bur and irrigated with sodium hypochlorite, ethylenediaminetetraacetic acid and distilled water. The specimens were assigned to five groups (n = 12): one control (no laser) and four experimental groups that were submitted to 980 nm diode laser irradiation at different power (1.5 and 3.0 W) and frequency (continuous wave and 100 Hz) parameters. Half of specimens in each group had their canals filled with AH Plus sealer and half with Epiphany. The push-out test was performed and data (MPa) were analysed statistically by ANOVA and Tukey`s test (P < 0.05). The specimens were split longitudinally and examined under SEM to assess the failure modes after sealer displacement. Results The specimens irradiated with the diode laser and filled with AH Plus had significantly higher bond strength values (8.69 +/- 2.44) than those irradiated and filled with Epiphany (3.28 +/- 1.58) and the nonirradiated controls (3.86 +/- 0.60). The specimens filled with Epiphany did not differ significantly to each other or to the control (1.75 +/- 0.69). There was a predominance of adhesive failures at Epiphany-dentine interface (77%) and mixed failures at AH Plus-dentine interface (67%). Conclusions The 980 nm diode laser irradiation of root canal dentine increased the bond strength of AH Plus sealer, but did not affect the adhesion of Epiphany sealer.

Interfacial evaluation of experimentally weakened roots restored with adhesive materials and fibre posts: An SEM analysis

Objectives: To evaluate the bonding interface in experimentally weakened roots reinforced with adhesive restorative materials and quartz fibre posts, varying the light-exposure time of the composite resin used for root reinforcement. Methods: Twelve extracted human maxillary incisors teeth were used. The crowns were removed and the roots were endodontically treated. After post space preparation, the roots were assigned to four groups. The thickness of the root dentine was reduced and adhesively restored with composite resin light-activated through a translucent fibre post for either 40 s (group 1), 80 s (group 2) or 120 s (group 3). In the case of control (group 4), the roots were not weakened. One day after post cementation, the specimens were sectioned transversally in three slices and processed for scanning electron microscopic analysis to observe bonding interface formation, quality of the hybrid layer and density of resin tags using a four-step scale method. Results: Formation of a hybrid layer and resin tags were evident in all groups. There was no statistically (p > 0.05) significant difference between the regions analysed in each group (Friedman test) and between groups in each section depth (Kruskal-Wallis test). Furthermore, comparison of the flared/reinforced groups showed that the different time;; used for composite resin cure did not affect the results significantly (Kruskal-Wallis test, p = 0.2139). Conclusions: Different light-exposure times used for composite resin polymerisation during root canal reinforcement did not affect significantly the formation and quality of the dentine/adhesive/composite resin bonding interface. (C) 2008 Elsevier Ltd. All rights reserved.

Effects of light exposure time on composite resin hardness after root reinforcement using translucent fibre post

Objectives: The purpose of this in vitro study was to evaluate the Vickers hardness (VHN) of a Light Core (Bisco) composite resin after root reinforcement, according to the light exposure time, region of intracanal reinforcement and lateral distance from the light-transmitting fibre post. Methods: Forty-five 17-mm long roots were used. Twenty-four hours after obturation, the root canals were emptied to a depth of 12 mm and the root dentine was artificially flared to produce a 1 mm space between the fibre post and the canal walls. The roots were bulk restored with the composite resin, which was photoactivated through the post for 40 s (G1, control), 80 s (G2) or 120 s (G3). Twenty-four hours after post-cementation, the specimens were sectioned transversely into three slices at depths of 2, 6 and 10 mm, corresponding to the coronal, middle and apical regions of the reinforced root. Composite VHN was measured as the average of three indentations (100 g/15 s) in each region at lateral distances of 50, 200 and 350 mu m from the cement/post-interface. Results: Three-way analysis of variance (alpha = 0.05) indicated that the factors time, region and distance influenced the hardness and that the interaction time x region was statistically significant (p = 0.0193). Tukey`s test showed that the mean VHN values for G1 (76.37 +/- 8.58) and G2 (74.89 +/- 6.28) differed significantly from that for G3 (79.5 +/- 5.18). Conclusions: Composite resin hardness was significantly lower in deeper regions of root reinforcement and in lateral areas distant from the post. Overall, a light exposure time of 120 s provided higher composite hardness than the shorter times (40 and 80 s). (C) 2008 Elsevier Ltd. All rights reserved.

Temperature variation at the external root surface during 980-nm diode laser irradiation in the root canal

Objective: To assess the temperature variation in the cervical, middle and apical thirds of root external wall, caused by 980-nm diode laser irradiation with different parameters. Methods: The roots of 90 canines, had their canals instrumented and were randomly distributed into 3 groups (n = 30) according to the laser potency (1.5 W, 3.0 W and 5.0 W). Each group was subdivided into 3 (n = 10) according to the frequency (CM, 100 Hz and 1000 Hz), and each subgroup divided into 2 (n = S): dried canal or filled with distilled water. The maximum temperature values were collected by 3 thermocouples located at each third of the root external wall and recorded by digital thermometers. Results: The groups irradiated in the continuous mode (CM) presented the highest values (11.82 +/- 5.78), regardless of the canals were dry or not, which were statistically different (p < 0.01) from those obtained with 100 Hz (6.22 +/- 3.64) and 1000 Hz (6.00 +/- 3.36), which presented no statistical difference between them (p > 0.01). The groups irradiated with 5.0 W presented the greatest temperature variation (12.15 +/- 5.14), followed by 3.0 W (7.88 +/- 3.92) and 1.5 W (4.02 +/- 2.16), differing between them (p < 0.01). The cervical third of the root presented the highest temperature rises (9.68 +/- 5.80), followed by the middle (7.66 +/- 4.87) and apical (6.70 +/- 4.23), with statistical difference among them (p < 0.01). After 30 s from the end of irradiation, all the specimens presented temperature variation lower than 10 degrees C. Conclusions: Application of 980-nm diode laser in the root, at 1.5 W in all operating modes, and 3.0 W, in the pulsed mode, for 20 s, can safely be used in endodontic treatment, irrespective of the presence of humidity. (C) 2008 Elsevier Ltd. All rights reserved.

The role of dentists in-diagnosing osteogenesis imperfecta in patients with dentinogenesis imperfecta

Background. Osteogenesis imperfecta (OI), also known as ""brittle bone disease,"" can be difficult to diagnose in its mild form. The authors describe a clinical case of a diagnosis of dentinogenesis imperfecta (DI), In which a literature review combined with an analysis of dental alterations led to indications of OI involvement. Case Description. Since DI can be associated with OI, the authors reviewed correlated studies and obtained a new medical history from the patient. They then conducted a radiographic and clinical examination of the dentition and submitted an affected third molar to scanning electron microscopy analysis. They compared their findings with descriptions of OI type I dental alterations in the literature and confirmed their diagnosis by means of a medical evaluation. Clinical Implications. In cases in which DI is diagnosed, patients should be examined carefully and the occurrence of OI should be considered `since, in its mild form, it might be misdiagnosed.

Effect of 980-nanometer diode laser on root canal permeability after dentin treatment with different chemical solutions

This study evaluated the effect of 980-nm diode laser at different parameters on root canal dentin permeability associated with different irrigants. Seventy-five canines were sectioned at 15 mm from the apex, prepared mechanically up to #40 .02 instrument, and irrigated with 2 mL distilled water. Final irrigation (10 mL) was used as follows: (1) distilled water; (2) 1% NaOCl; (3) 17% ethylenediaminetetraacetic acid + a cationic surfactant cetyltrimethylammonium bromide (EDTAC). Laser was applied at 1.5 or 3.0 W as either continuous wave or pulsed wave (100 Hz). The teeth were then processed histochemically, the percentage of copper ion penetration into the dentin of the canal walls was counted, and the data were analyzed statistically with the Tukey-Kramer test (alpha < .01). When laser was associated with water, an increase in permeability was found, whereas permeability decreased when associated with EDTAC. Dentin permeability after laser irradiation was directly dependent on the solution used for final irrigation.

Influence of Filling Materials on the Bonding Interface of Thin-walled Roots Reinforced with Resin and Quartz Fiber Posts

Introduction: A common complication during the restoration of severely destroyed teeth is the loss of coronal root dentine. The aim of this study was to evaluate the influence of different sealers on the bonding interface of weakened roots reinforced with resin and fiber posts. Methods: Sixty extracted maxillary canines were used. The crowns were removed, and the thickness of root dentine was reduced in the experimental (n = 40) and positive control (n = 10) groups. The specimens of experimental group were assigned to four subgroups (n = 10) according to the filling material: gutta-percha + Grossmann`s sealer, gutta-percha + AH Plus (Dentsply De Trey Gmbh, Konstanz, Germany), gutta-percha + Epiphany (Pentron Clinical Technologies, Wallingford, CT), and Resilon (Resilon Research LLC, Madison, CT) + Epiphany. In the negative control group (n = 10), canals were not filled. After post space preparation, the roots were restored with composite resin light-activated through a translucent fiber post. After 24 hours, specimens were transversally sectioned into 1-mm-thick slices. Push-out test and scanning electron microscopic (SEM) analyses of different regions were performed. Data from push-out test were analyzed by using Tukey post hoc multiple comparison tests. The percentage of failure type was calculated. Data from SEM analysis were compared by Friedman and Kruskal-Wallis tests (alpha = 0.05). Results: The mean bond strength was significantly higher in the negative control group as compared with the other groups (P < .05). In all groups, the most frequent type of failure was adhesive. Overall, apical and middle regions presented a lower density of resin tags than the coronal region (P < .05). Conclusions: The push-out bond strength was not affected by sealer or region. The canal region affected significantly the resin tag morphology and density at the bonding interface. (J Endod 2011;37:531-537)

Influence of shaft design on the shaping ability of 3 nickel-titanium rotary systems by means of spiral computerized tomography

Objective. To evaluate the influence of shaft design on the shaping ability of 3 rotary nickel-titanium (NiTi) systems. Study design. Sixty curved mesial canals of mandibular molars were used. Specimens were scanned by spiral tomography before and after canal preparation using ProTaper, ProFile, and ProSystem GT rotary instruments. One-millimeter-thick slices were scanned from the apical end point to the pulp chamber. The cross-sectional images from the slices taken earlier and after canal preparation at the apical, coronal, and midroot levels were compared. Results. The mean working time was 137.22 +/- 5.15 s. Mean transportation, mean centering ratio, and percentage of area increase were 0.022 +/- 0.131 mm, 0.21 +/- 0.11, and 76.90 +/- 42.27%, respectively, with no statistical differences (P > .05). Conclusions. All instruments were able to shape curved mesial canals in mandibular molars to size 30 without significant errors. The differences in shaft designs seemed not to affect their shaping capabilities.

Assessment of the biocompatibility of Epiphany root canal sealer in rat subcutaneous tissues

Objective. The aim of this study was to evaluate the biocompatibility of the root canal sealer Epiphany in rat subcutaneous tissues. Study design. Polyethylene tubes were filled with the sealer (I: Epiphany; II: photoactivated Epiphany; III: Epiphany associated with self-etch primer; IV: photoactivated Epiphany associated with primer; and V: control group) and later implanted into 4 different regions of the dorsum of 15 adult male rats (Rattus novergicus, Albinus Wistar). After 7, 21, and 42 days, 5 animals were killed, obtaining 4 samples per group, in addition to the control group, at each analyzed time. Results. In all periods, Epiphany induced a mild inflammatory reaction. However, in group II, in which the primer was not used, extensive necrosis and a moderate to intense inflammatory reaction were observed, mainly after 7 and 21 days. Conclusion. Epiphany sealer appears biocompatible when tested on rat subcutaneous tissues.

Clinical management and subsequent healing of teeth with horizontal root fractures

Horizontal root fractures are uncommon, mainly occurring on the cervical and middle third of the root of permanent upper incisors. The diagnosis is essentially radiographic and requires different healing patterns, depending on some pre- and postinjury factors. The aim of this article was to report the clinical management and different healing types in three cases of horizontal root fractures on permanent dentition. In case 1, the pulp tissue was vital and no treatment was necessary. In case 2, a root canal treatment of the cervical fragment was necessary and in case 3, pulpal necrosis was verified and an apical surgery was performed.

Influence of different endodontic filling materials on root fracture susceptibility

Objective: To evaluate the influence of different endodontic materials on root fracture susceptibility. Methods: Seventy-two mandibular incisors were sectioned 1 mm below the cementoenamel junction to obtain roots of 12 mm length. Roots were submitted to chemomechanical preparation with the rotary instruments of Profile system. The obturation of root canals were performed with the following filling materials (n = 12): GI, unfilled teeth (control); GII, Endofill + gutta-percha; GIII, Sealer 26 + gutta-percha; GIV, AH Plus + gutta-percha; GV, Epiphany + gutta-percha; GVI, Epiphany + Resilon. After the sealers setting time, each root was embedded in acrylic resin. The specimens were then submitted to fracture resistance test using an Instron testing machine at 1 mm/min. Results: The ANOVA test showed no significant statistical difference (p > .05) among GI (162.16 +/- 41.4N), GII (168.46 +/- 37.5N), GIII (164.83 +/- 35.7N), GIV (168.29 +/- 38.7N), GV (172.36 +/- 20.6N) and GVI (193.11 +/- 42.8N). Conclusion: The core materials (gutta-percha or Resilon) combined with the tested endodontic sealers are not able to increase the root fracture resistance in canals submitted to chemomechanical preparation. (c) 2007 Elsevier Ltd. All rights reserved.

Shear Bond Strength of A Sealant to Contaminated-Enamel Surface: Influence of Erbium : Yttrium-Aluminum-Garnet Laser Pretreatment

Salivary contamination is one of the factors that can disturb the sealing process and interfere in the longevity of pit and fissure sealants. Erbium : yttrium-aluminum-garnet (Er : YAG) laser could influence the bond strength of enamel and increase the acid resistance. To evaluate the influence of Er : YAG laser on the shear bond strength of a sealant to a salivary contaminated enamel surface. Twenty-four third molars had the roots sectioned 2 mm coronal to the cementoenamel junction. The crowns were mesiodistally sectioned providing 48 halves that were embedded in polyester resin. Enamel was flattened and a 2-mm diameter bonding area was demarcated. Specimens were randomly assigned to two groups according to the superficial pretreatment-37% phosphoric acid (A) and Er : YAG laser (80 mJ/2 Hz) + phosphoric acid (L), which were subdivided into two groups (N = 12), without salivary contamination (C) and with salivary contamination (SC). To contaminate the specimens, 0.25 mL of human fresh saliva was applied for 20 seconds and then dried. Fluroshield sealant was applied in all specimens. After storage, shear bond strength of samples were tested in a universal testing machine. Means in MPa were: AC-14.61 (+/- 2.52); ASC-6.66 (+/- 2.34); LC-11.91 (+/- 1.34); and LSC-2.22 (+/- 0.66). Statistical analysis revealed that surfaces without salivary contamination and with acid treatment had the highest mean (p < 0.05). The group with salivary contamination treated by Er : YAG laser followed by phosphoric acid application presented the lowest bond values (p < 0.05). The phosphoric acid etching under dry condition yielded better bonding performance. Er : YAG laser was not able to increase the effectiveness of conventional acid etching of enamel in the bond of sealants in both dry and wet conditions. Under the conditions of this study, the conventional etching protocol (phosphoric acid without salivary contamination) is still preferable to laser-conditioning enamel surface prior to sealant application.

Bleaching Agents with Varying Concentrations of Carbamide and/or Hydrogen Peroxides: Effect on Dental Microhardness and Roughness

To evaluate the effect of low and highly concentrated bleaching agents on microhardness and surface roughness of bovine enamel and root dentin. According to a randomized complete block design, 100 specimens of each substrate were assigned into five groups to be treated with bleaching agents containing carbamide peroxide (CP) at 10% (CP10); hydrogen peroxide (HP) at 7.5% (HP7.5) or 38% (HP38), or the combination of 18% of HP and 22% of CP (HP18/CP22), for 3 weeks. The control group was left untreated. Specimens were immersed in artificial saliva between bleaching treatments. Knoop surface microhardness (SMH) and average surface roughness (Ra) were measured at baseline and post-bleaching conditions. For enamel, there were differences between bleaching treatments for both SMH and Ra measurements (p = 0.4009 and p = 0.7650, respectively). SMH significantly increased (p < 0.0001), whereas Ra decreased (p = 0.0207) from baseline to post-bleaching condition. For root dentin, the group treated with CP10 exhibited the significantly highest SMH value differing from those groups bleached with HP18/CP22, HP7.5, which did not differ from each other. Application of HP38 resulted in intermediate SMH values. No significant differences were found for Ra (p = 0.5975). Comparing the baseline and post-bleaching conditions, a decrease was observed in SMH (p < 0.0001) and an increase in Ra (p = 0.0063). Bleaching agents with varying concentrations of CP and/or HP are capable of causing mineral loss in root dentin. Enamel does not perform in such bleaching agent-dependent fashion when one considers either hardness or surface roughness evaluations. Bleaching did not alter the enamel microhardness and surface roughness, but in root dentin, microhardness seems to be dependent on the bleaching agent used.

Effect of Chelating Solutions on the Microhardness of Root Canal Lumen Dentin

Introduction: The greatest reduction in microhardness of the most superficial layer of dentin of the root canal lumen is desired. The use of chelating agents during biomechanical preparation of root canals removes smear layer, increasing the access of the irrigant into the dentin tubules to allow adequate disinfection, and also reduces dentin microhardness, facilitating the action of endodontic instruments. This study evaluated the effect of different chelating solutions on the microhardness of the most superficial dentin layer from the root canal lumen. Methods: Thirty-five recently extracted single-rooted maxillary central incisors were instrumented, and the roots were longitudinally sectioned in a mesiodistal direction to expose the entire canal extension. The specimens were distributed in seven groups according to the final irrigation: 15% EDTA, 10% citric acid, 5% malic acid, 5% acetic acid, apple vinegar, 10% sodium citrate, and control (no irrigation). A standardized volume of 50 mu L of each chelating solution was used for 5 minutes. Dentin microhardness was measured with a Knoop indenter under a 10-g load and a 15-second dwell time. Data were analyzed statistically by one-way analysis of variance and Tukey-Kramer multiple-comparison test at 5% significance level. Results: EDTA and citric acid had the greatest overall effect, causing a sharp decrease in dentin microhardness without a significant difference (p > .05) from each other. However, both chelators differed significantly from the other solutions (p < .001). Sodium citrate and deionized water were similar to each other (p > .05) and did not affect dentin microhardness. Apple vinegar, acetic acid, and malic acid were similar to each other (p > .05) and presented intermediate results. Conclusion: Except for sodium citrate, all tested chelating solutions reduced microhardness of the most superficial root canal dentin layer. EDTA and citric acid were the most efficient. (J Endod 2011;37:358-362)

Microtensile Bond Strength of Glass Fiber Posts Cemented with Self-adhesive and Self-etching Resin Cements

Purpose: To evaluate the bond strength of glass fiber posts to intraradicular dentin when cemented with self-etching and self-adhesive resin cements. Materials and Methods: Forty-eight single-rooted human teeth were decoronated, endodontically treated, post-space prepared and divided into 8 groups (n = 6). The glass fiber posts used were: Exacto (EA) (Angelus) and everStick (ES) (StichTeck), which were cemented with two self-adhesive resin cements: BisCem (BIS) (Bisco) and Rely-X Unicem (UNI) (3M/ESPE), and two self-etching resin cements: Esthetic Cementing System NAC100 (NAC) (Kuraray) and Panavia-F (PAN) (Kuraray). Specimens were thermocycled between 5 degrees C and 55 degrees C for 1000 cycles and stored in water at 37 degrees C for 1 month. Four 1-mm-thick (in cross section) rods were obtained from the cervical region of the roots. Specimens were then subjected to microtensile testing in a special machine (BISCO; Schaumburg, IL, USA) at a crosshead speed of 0.5 mm/min. Microtensile bond strength (mu TBS) data were analyzed with two-way ANOVA and Tukey`s tests. Results: Means (and SD) of mu TBS (MPa) were: EA/PAN: 10.3 (4.1), EA/NAC: 14 (5.1) EA/BIS: 16.4 (4.8), EA/UNI: 19.8 (5.1), ES/PAN: 25.9 (6.1), ES/NAC: 29.1 (7), ES/BIS: 28.9 (6), ES/UNI: 30.5 (6.6). ANOVA indicated significant differences among the groups (p < 0.001). Mean mu TBS values obtained with ES post were significantly higher than those obtained with EA (p < 0.001). For EA, Tukey`s test indicated that higher mu TBS means were obtained with the self-adhesive resin cements (BIS and UNI), which were statistically significantly different (p < 0.05) from values obtained with the self-etching resin cements (PAN and NAC). Different cements had no significant effects on the bond strength values of ES post (p > 0.05). mu TBS values obtained with ES post were significantly higher than those obtained with EA post irrespective of the resin cement used. Conclusion: everStick posts resulted in the highest mean mu TBS values with all cements. Self-adhesive cements performed well in terms of bond strength.