Yb:Y2-2xLa2xO3激光透明陶瓷的光谱性能

It was first reported the spectral properties of a low-temperature sintered transparent Yb: Y2-2x La-2x O-3 laser ceramics. Yb: Y2-2x La-2x O-3 laser ceramics have broad absorption band and large absorption cross- section of 4.0 x 10(-20) cm(2) at wavelengths 977nm of the highest absorption peak. Its fluorescence lifetime is 1.1 ms, and the emission cross-sections are 1.0 x 10(-20) cm(2) and 0.7 x 10(-20) cm(2) at wavelengths 1033nm and 1077nm, respectively. All the optical properties are similar to those of single crystals.

Investigation of the spectroscopic properties of Yb3+-doped yttrium lanthanum oxide transparent ceramic

Spectroscopic properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic were studied. Two main absorption peaks of the specimen are centered at 940 and 970 nm, which are suitable for InGaAs laser diode pumping. The main emission peaks were located at 1032 and 1075 nm with larger emission cross-section and longer fluorescence lifetime than those of Yb:Y2O3. These properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic are favorable to achieve high efficiency and high power laser output. (c) 2007 Elsevier B.V. All rights reserved.

Growth and spectral properties of Yb : FAP single crystal

In this paper, single crystal of ytterbium (Yb) doped Ca-5(PO4)(3)F (FAP) has been grown along the c-axis by using the Czochralski method. The segregation coefficients of Yb3+ in the Yb:FAP crystal has been determined by ICP-AES method. The absorption spectrum, fluorescence spectrum and fluorescence lifetime of the Yb:FAP crystal has been also measured at room temperature. In the absorption spectra, there are two absorption bands at 904 and 982 nm, respectively, which are suitable for InGaAs diode laser pumping. The absorption cross-section (sigma(abs)) is 5.117 x 10(-20) cm(2) with an FWHM of 4 nm at 982 nm. The emission cross-section is (sigma(em)) 3.678 x 10(-20) cm(2) at 1042 nm. Favorable values of the absorption cross-section at about 982 nm are promising candidates for laser diode (LD) pumping. (c) 2005 Elsevier B.V. All rights reserved.

Yb∶Y3Al5O12晶体晶格振动光谱的研究

采用提拉法生长Y3Al5O12(YAG)晶体和Yb3+掺杂原子数分数分别为5%, 10%, 15%, 20%, 25%, 50%和100%的Yb∶Y3Al5O12(Yb∶YAG)晶体。系统表征和分析了Yb3+掺杂浓度对拉曼光谱的影响。随着Yb3+掺杂浓度的增加,晶体的振动模式没有明显的变化,晶体结构没有改变;在370 cm-1和785 cm-1附近,振动吸收峰的半峰全宽逐渐增大。分析得出,Yb3+掺杂浓度对晶体的晶格、对称性、荧光寿命均有影响,从而可能影响到晶体的光谱和激光性能。

Spectroscopic properties of Yb:YAP crystal

The 10at% Yb-YAP crystal has been grown by the Czochralski method. The absorption and emission spectra and fluorescence lifetime of Yb:YAP crystal at room temperature were studied. There is a strong absorption band centered at 959 nm and the absorption cross-section of 1.51 × 10^-20 cm². The emission cross-section at 1040 nm is 0.6 × 10^-20 cm² and the fluorescence lifetime is about 1.2 ms. The effects of O₂-annealing on the spectral properties were studied. The spectroscopic properties strongly depended on the axis direction and b axis was the best direction for laser output. The spectrum parameters of Yb:YAP and Yb:YAG crystal were compared.}

Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷的光谱性能研究

采用传统无压烧结工艺制备了Er^3＋／Yb^3＋共掺的氧化镧钇透明陶瓷并对其光谱性能进行了研究．样品具有较大的吸收和发射截面．La2O3的添加使样品的荧光寿命（τs）与玻璃接近，当Yb^3＋和Er^3＋的掺杂量分别为5at％和0．5at％时，测得τs=9．65ms．这种荧光寿命长、发射截面大和线宽窄的特性有利于微型、可集成化和大功率激光输出的实现．

Judd-Ofelt analysis of spectra and experimental evaluation of laser performance of Tm3+ doped Lu2SiO5 crystal

This paper reports that the TM3+:Lu2SiO5 (Tm:LSO) crystal is grown by Czochralski technique. The room-temperature absorption spectra of Tm:LSO crystal are measured on a b-cut sample with 4 at.% thulium. According to the obtained Judd-Ofelt intensity parameters Omega(2)=9.3155 x 10(-20) cm(2), Omega(4)=8.4103 x 10(-20) cm(2), Omega(6)=1.5908 x 10(-20) cm(2), the fluorescence lifetime is calculated to be 2.03 ms for F-3(4) -> H-3(6) transition, and the integrated emission cross section is 5.81 x 10(-18) cm(2). Room-temperature laser action near 2 mu m under diode pumping is experimentally evaluated in Tm:LSO. An optical-optical conversion efficiency of 9.1% and a slope efficiency of 16.2% are obtained with continuous-wave maximum output power of 0.67 W. The emission wavelengths of Tm:LSO laser are centred around 2.06 mu m with spectral bandwidth of similar to 13.6 nm.

Spectral investigation of Yb-doped calcium pyroniobate crystal

Ytterbium-doped calcium pyroniobate single crystal has been grown for the first time. Spectral properties of Yb: Ca2Nb2O7 were investigated by emission and absorption spectra. Its cooperative luminescence and fluorescence lifetime were also studied. Yb ions in Ca2Nb2O7 showed very broad absorption and emission bandwidth and relatively large absorption and emission cross-sections. Along with other optical properties, this Yb-doped crystal would be a potential self-frequency doubling femtosecond laser gain material. (C) 2007 Published by Elsevier B.V.

Tm:Y_2SiO_5晶体的生长和光谱性质研究

采用中频感应提拉法生长了高质量的Tm:Y2SiO5(Tm:YSO)晶体,测定了晶体的晶格常数和分凝系数.运用劳厄照相法确定了单斜晶系Tm:YSO晶体的三个偏振轴〈010〉,D1和D2,在室温下测量了三个偏振轴方向的吸收光谱、荧光光谱和荧光寿命,计算了晶体吸收峰的吸收线宽和吸收截面.研究发现,相对于其他两个偏振轴方向,D1方向在790 nm处出现较强的吸收峰,同时在2μm附近出现了一定强度的发射峰,D1方向的吸收截面较大,荧光寿命较长.Tm:YSO晶体适用于AlGaAs二极管抽运固体激光器,在2μm波段固体激光器的应用上将有很大的发展潜力.

利用窄得-奥菲特理论研究Tm:Lu_2SiO_5晶体的光谱特性

采用丘克拉斯基(Czochralski)技术生长了掺铥硅酸镥(Tm∶Lu2SiO5,Tm∶LSO)晶体;测量了LSO晶体在室温下的非偏振吸收光谱和非偏振荧光光谱;利用窄得-奥菲特(Judd-Ofelt)理论计算了Tm∶LSO晶体的窄得-奥菲特强度参数、振子强度、自发辐射概率、辐射寿命、积分吸收截面和积分发射截面.Tm∶LSO晶体的强度参数为Ω2=9.1355×10-20cm2,Ω4=8.4103×10-20cm2,Ω6=1.5908×10-20cm2;Tm∶LSO晶体在1.9μm附近有明显的发射峰(3F4→3H6跃迁),相应的辐射寿命为2.03 ms,积分发射截面为5.81×10-18cm2,半峰全宽(FWHM)为250 nm.用Tm∶LSO晶体在77 K温度下实现了激光运转.利用792 nm的激光二极管(LD)作为抽运源,获得中心波长为1960 nm的激光输出,抽运阈值为2.13 kW/cm2.

Polarized spectral analysis of Ho3+ ions in biaxial YAlO3 crystal for 2 mu m lasers

An Ho3+-doped YAlO3 (Ho : YAP) single crystal has been grown by the Czochralski technique. The polarized absorption spectra, polarized fluorescence spectra and fluorescence decay curve of the crystal are measured at room temperature. The spectroscopic parameters are calculated based on Judd-Ofelt theory, and the effective phenomenological intensity parameters Omega(2,eff), Omega(4,eff) and Omega(6,eff) are obtained to be 2.89 x 10(-20), 2.92 x 10(-20) and 1.32 x 10(-20) cm(2), respectively. The room-temperature fluorescence lifetime of the Ho3+ 5I(7) -> I-5(8) transition is measured to be 8.1 ms. Values of the absorption and emission cross-sections with different polarizations are presented for the I-5(7) manifold, and the polarized gain cross-section curves are also provided and discussed.

Judd-Oflet analysis of spectrum and laser performance of Ho:YAP crystal end-pumped by 1.91-mu m Tm:YLF laser

The Ho:YAP crystal is grown by the Czochralski technique. The room-temperature polarized absorption spectra of Ho:YAP crystal was measured on a c-cut sample with 1 at% holmium. According to the obtained Judd-Ofelt intensity parameters Omega(2) = 1.42 x 10(-20) cm(2), Omega(4) = 2.92 x 10(-20) cm(2), and Omega(6) = 1.71 x 10(-20) cm(2), this paper calculated the fluorescence lifetime to be 6 ms for I-5(7) -> I-5(8) transition, and the integrated emission cross section to be 2.24 x 10(-18) cm(2). It investigates the room-temperature Ho:YAP laser end-pumped by a 1.91-mu m Tm:YLF laser. The maximum output power was 4.1 W when the incident 1.91-mu m pump power was 14.4W. The slope efficiency is 40.8%, corresponding to an optical-to-optical conversion efficiency of 28.4%. The Ho:YAP output wavelength was centred at 2118 nm with full width at half maximum of about 0.8 nm.

Development of functionalized terbium fluorescent nanoparticles for antibody labeling and time-resolved fluoroimmunoassay application

Silica-based functionalized terbium fluorescent nanoparticles were prepared, characterized and developed as a fluorescence probe for antibody labeling and time-resolved fluoroimmunoassay. The nanoparticles were prepared in a water-in-oil (W/O) microemulsion containing a strongly fluorescent Tb3+ chelate. N,N.N-1,N-1-12,6-bis(3'-aminomethyl-1'-pyrazolyl)phenylpyridine] tetrakis(acetate)-Tb3+ (BPTA-Tb3+), Triton X-100, octanol, and cyclohexane by controlling copolymerization of tetraethyl orthosilicate (TEOS) and 3-[2-(2- aminoethylamino)-ethylamino]propyl-trimethoxysilane (AEPS) with ammonia water. The characterizations by transmission electron microscopy and fluorometric quantum methods show that the nanoparticles are spherical and uniform in size, 45 +/- 3 nm in diameter, strongly fluorescent with fluorescence yield of 10% and a long fluorescence lifetime of 2.0 ms. The amino groups directly introduced to the nanoparticle's surface by using AEPS in the preparation made the surface modification and bioconjugation of the nanoparticles easier. The nanoparticle-labeled anti-human alpha-fetoprotein antibody was prepared and used for time-resolved fluoroimmunoassay of (x-fetoprotein (AFP) in human serum samples. The assay response is linear from 0.10 ng ml(-1) to about 100 ng ml(-1) with the detection limit of 0.10 ng ml(-1). The coefficient variations (CVs) of the method are less than 9.0%. and the recoveries are in the range of 84-98% for human serum sample measurements. (C) 2004 Elsevier B.V. All rights reserved.

Synthesis and photoluminescent properties of silica-coated LaCeF3 : Tb nanocrystals

La0.45Ce0.45F3:Tb (10 mol% Tb) nanoparticles was synthesized via sonochemical method and then coated with silica (SiO2) shells through a microemulsion process, resulting in the formation of core/shell structured LaCeF3:Tb/SiO2 nanoparticles. The obtained core/shell LaCeF3:Tb/SiO2 nanoparticles are spherical and uniform in size (average size about 60 nm), strongly fluorescent, and long fluorescence lifetime (1.87 ms). This kind of nanoparticles was water-soluble, which could be applied in biological labeling and other fields.

One-step synthesis of Ru(2,2 '-bipyridine)(3)Cl-2-immobilized silica nanoparticles for use in electrogenerated chemiluminescence detection

One-step synthesis of Ru (bpy)(3) Cl-2-immobilized (bpy = 2,2'-bipyridine) silica nanoparticles (Ru-silica nanoparticles) for use in electrogenerated-chemiluminescence (ECL) detection is reported. Ru-silica nanoparticles are prepared by using the Stober method. Compared with free Ru(bpy)(3)Cl-2, Ru-silica nanoparticles are seen to exhibit a red-shift of the UV-vis absorbance peak and a longer fluorescence lifetime, which are attributed to the electrostatic interaction of Ru(bpy)(3)(2+) and silica. Because silica nanoparticles are used as immobilization matrices, the surfaces of Ru-silica nanoparticles are easily modified or functionalized via the assembly of other nanoparticles, such as Au. For ECL detection, Au-colloid-modified Ru-silica nanoparticles are immobilized on a 3-mercaptopropyl-trimethoxysilane-modified indium tin oxide electrode surface by Au-S interaction; the surface concentration of electroactive Ru(bpy)(3)Cl-2 is obviously higher than that in silica films.